Article
The Effect of PVC Powder content on the Elastic Moduli and Acoustic Impedance of Epoxy Composites
دراسة تأثير أضافة مسحوق PVC على معاملات المرونة والممانعة الصوتية لمتراكبات الايبوكسي

Author: Kawakib Jassim Majeed كواكب جاسم مجيد
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2009 Volume: 7 Issue: 8 Pages: 43-48
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The primary purpose of the present research was to study the effect of polyvinyl chloride (PVC) powder content on ultrasonic wave velocity in PVC/Epoxy composites. The second part is concerned with the relations of dynamic elastic moduli with the ultrasonic wave velocities, to determine how ultrasonic waves can affect them. Experimental data have been obtained using the sonic viewer (model -5217 A) device to generate two types of waves, longitudinal waves of frequency 63 kHz and transverse waves of frequency 33 kHz and to measure the transit time required for those waves to travel through individual sample. The experimental results have shown that the propagation of the ultrasonic velocity increases directly with PVC content in the tested specimens, due to the changes in the dynamical properties that were investigated from the calculated values of the elastic moduli of the composites. The influence of PVC content on the acoustical impedance I of the medium was also investigated.

الهدف من اجراء البحث هو دراسة تأثير اضافة مسحوق PVC على سرعة الموجات فوق الصوتية لمتراكبات PVC/Epoxy . ثم ايجاد معاملات المرونة من العلافات التي تربط هذه المعاملات بسرعة الموجات الصوتية في الوسط.استخدم جهاز sonic viewer (model -5217 A) لتوليد نوعين من الموجات. طولية بتردد 63 kHz وأخرى مستعرضة بتردد 33 kHz وكذلك قياس الزمن اللازم لمرور الموجات فوق الصوتية خلال العينة.أظهرت نتائج الفحص ان سرعة انتقال الموجات فوق الصوتية خلال المتراكبات تزداد بزياة نسب المسحوق نتيجة لتغير معاملات المرونة. كذلك أظهرت نتائج الفحص زيادة في قيم الممانعة الصوتية بزياة نسب اضافة المسحوق بسبب زيادة الكثاقة.


Article
SOME OF DIELECTRIC PROPERTIES OF POLYMER/FERROELECTRIC COMPOSITES

Author: Inaan M. Abdulmajeed
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2012 Volume: 12 Issue: 1 Pages: 63-72
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

BaTiO3, synthesized in polycrystalline form, using stoichiometric mixture of oxide with traditional ceramic technique and characterized by X-ray diffraction, tetragonal structure of prepared powder were found. Moreover, particle size of ceramic powder determined using laser particle size analyzer. The particle size distribution was found in the range (0.427-3.195)µm. The epoxy ceramic composite system was prepared. BaTiO3 with content 10%, 20%, 30%, 40%, 50% wt and 60% wt. respectively used as filler. Permittivity of the composites was investigated at frequencies from 2KHz to 5 MHz The dielectric loss tangent (tanδ) was determined as a function of frequency, compositions. It was found that the weight percent of BaTiOcomposite effect on the dielectric properties. At low frequencies, BaTiO33 filler in ceramic/epoxy /Epoxy composites have much higher dielectric constant. Dielectric constant increases considerly with the addition of BaTiO3 fillers, however, the higher conductivity of BaTiOconductivity with increases BaTiO33 than epoxy lead to an increase in ac content, the increase in both properties was attributed to the presence of the high permittivity ferroelectric phase


Article
Experimental Investigation and Mathematical Modeling of Tensile Properties of Unsaturated Polyester Reinforced by Woven Glass Fibers
التقصي العملي والنمذجه الرياضيه لخصائص الشد للبولي استر الغير مشبع المقوى بالياف الزجاج الحصيرية

Authors: Jawad Kadhim Oleiwi --- Emad Saadi Al- Hassani --- Alaa Abd Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 3 Part (A) Engineering Pages: 653-666
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research studied the tensile properties of glass fiber reinforced unsaturated polyester with different fiber volume fraction Vf, and angle of fibers for coarse and fine woven fibers reinforcement. The composite specimens were prepared by hand lay-up technique and cutting according to (ASTM D – 638) for tensile test to obtain modulus of elasticity, ultimate tensile strength and elongation percentage of the composite specimens. Mathematical models were done by using statistical analysis which shows the tensile properties of the composite specimens as a function of volume fraction and fiber angle.The results show that the maximum value of the modulus of elasticity was (11.5 GPA) and the maximum value of ultimate tensile strength was (240 MPa) which happed at (11% VF) for fine woven fibers and for (0º/90º) fibers angle, and vice versa for percentage elongation was (2.5%).

في هذا البحث تم دراسة خواص الشد للبولي استر غير مشبع مقوى بالياف الزجاج عند تغير كل من الكسر الحجمي وزاوية الليف لنوعين من التقوية الحصيرة الخشنه والناعمه. حضرت العينات المركبة بالطريقة اليدوية وقطعت وفق المواصفه (ASTM D – 638) لفحص الشد للحصول على معامل المرونة واقصى أجهاد شد والاستطالة النسبية لهذه العينات. تم عمل نماذج رياضية باستخدام التحليل الأحصائي الذي يبين خواص الشد كدالة لكسر الحجمي وزاوية الليف. بينت النتائج بان اقصى قيمة لمعامل المرونة كانت(11.5 GPa) واقصى اجهاد شد كان(240 MPa) يحصلان عند الكسر حجمي (11%) عند التقوية بالحصيرة الناعمة ولزاوية ليف (0º/90º) والعكس بالعكس للاستطاله النسبية حيث كانت 2.5%) ).


Article
Modeling and Buckling Analysis of Polymeric Composite Columns
نمذجة وتحليل الأنبعاج للأعمدة المتراكبة البوليمرية

Authors: Jawad Kadhim Oleiwi --- Emad Saadi Al- hassani --- Alaa Abd Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 5 Part (A) Engineering Pages: 1180-1196
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research studied the buckling of composite columns made from glass fiber reinforced unsaturated polyester. The composite specimens were prepared by hand lay-up technique with different fiber volume fraction Vf, aspect ratio and angle of fibers when reinforced with coarse and fine woven fibers. Mathematical models were done by using statistical analysis which show the critical load of the composite column as a function of volume fraction, fiber angle and aspect ratio. The results show that the maximum value of the critical load can be observed at volume fraction Vf =11%, aspect ratio L/T = (3.5) and fiber angle θ = (0º/90º) for fine fiber was (500.72 N). Also its found the maximum critical load for coarse fiber can be observed at Vf =8%, L/T= (3.5) and θ = (0º/90º) was (400.4 N).

في هذا البحث تم دراسة الأنبعاج للأعمدة المركبة تتكون من البولي أستر الغير مشبع مقوى بالياف زجاج. حضرت العينات المركبة بالطريقة اليدوية عند تغير كل من الكسر الحجمي والنسبة الباعية وزاوية ليف لنوعين من التقوية الحصيرة الخشنة والناعمة. تم عمل نماذج رياضية باستخدام التحليل الأحصائي الذي بين الحمل الحرج للعمود المركب كدالة للكسر الحجمي وزاوية ليف والنسبة الباعية. بينت النتائج بأن أقصى قيمة للحمل الحرج حدثت عند الكسر الحجميVf =11%)) والنسبة الباعية (L/T=3.5) وزاوية ليف0º/90º)) عند التقوية باليف الناعم كانت (500.72N). أيضا وجد بأن أقصى قيمة للحمل الحرج عند التقوية بالحصيرة الخشنة حدثت عند الكسر الحجمي (Vf =8%) والنسبة الباعية L/T=3.5)) وزاوية ليف 0º/90º)) كانت (400.4 N) .


Article
Mechanical, Thermal and Wear Characteristics of Polymer Composite Material Reinforced with Calcium Carbonate Powder
الخواص الميكانيكية والحرارية وخاصية البلى لمادة بوليميري متراكبة مدعمة بمسحوق كاربونات الكالسيوم

Authors: Aseel B. Al-Zubaidi --- Ahmed A. Al-Tabbakh --- HanaaA. Al-Qaessy --- Ragad N. Al-Kaseey
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 3 Part (B) Scientific Pages: 519-532
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Quick mast–105 is a well-known epoxy-based adhesive used in fabric reinforcement, bonding of wooden parts and variety of metals. Its mechanical and thermal properties are still limiting factors for extended technological and industrial applications. Enhancement of mechanical, wear and thermal characteristics of this epoxy resin using a cheap filler of CaCO3powder is the focus of the present study. The mechanical properties are demonstrated in terms of the flexural modulus, hardness and impact strength of the reinforced cured compound while thermal properties are presented through thermo gravimetric analysis and thermal conductivity coefficient. Results show that addition of 15% by weight of CaCO3 to the epoxy resin improves the mechanical properties and the thermal resistance of the end product paving the way for wider applications in industry and technology. Wear characteristics show that the reinforced product is suitable for high-speed applications.

يعد ايبوكسيي (quick mast 105) من المواد الايبوكسية اللاصقة المعروفة والمستخدمة في مجال تدعيم النسائج ولصق الاجزاء الخشبية والمواد الاخرى . وتعتبر الخواص الميكانيكية والحرارية لهذا الايبوكسي من العوامل المحددة في مجال التطبيقات التكنولوجية والصناعية لهذه المادة . تهدف هذه الدراسة الى تحسين الصفات الميكانيكية والحرارية وخواص البلى لهذا الايبوكسي باستخدام مادة حشو رخيصة التكلفة من مسحوق كاربونات الكالسيوم . لقد تم في هذا البحث استعراض الخواص الميكانيكية من خلال دراسة معاملات الانحناء والصلابة ومقاومة الصدمة للعينات الايبوكسية المدعمة فيما تمت دراسة الخصائص الحرارية من خلال التصرف الحراري – الوزني ومعامل التوصيلية الحرارية للعينات المدعمة . وقد اوضحت النتائج ان اضافة كاربونات الكالسيوم بنسبة وزنية تعادل 15% من وزن الايبوكسي تؤدي الى تحسين الخواص الميكانيكية والحرارية للعينات المدعمة مفسحا المجال لاستخدامها في مجالات صناعية وتكنلوجية اوسع . اما دراسة خاصية البلى فقد بينت ان مادة الايبوكسي المدعمة مناسبة للتطبيقات عالية السرعة.


Article
Experimental Study to the Effect of Natural Particles Added to Unsaturated Polyester Resin of a Polymer Matrix Composite
دراسة عملية لتاثير اضافة دقائق طبيعية لراتنج البولي أستر غير المشبع لمادة متراكبة بوليمرية

Author: Orhan S. Abdullah أورهان صباح عبد الله
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2017 Volume: 13 Issue: 1 Pages: 42-49
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Experimental investigations had been done in this study to demonstrate the effect of natural particles used as a reinforcement material to unsaturated polyester resin. The tensile test and water absorption were investigated according to (ASTM D638) and (ASTM D570), respectively. The influence of sunflower husk and pomegranate husk particles, used as a reinforcement material, on the tensile strength, Young's modulus and water absorption with different weight fraction (3%, 7% and 10%) and particle grain size (50µm, 100 µm and 150 µm), has been investigated. The water absorption of polymer composites was studied by measuring the specimen weight before and after immersion in water for one hundred days. In the experiments of tensile test, all specimens loading was performed with (50KN) operating at a crosshead speed of 10 mm/min. It is observed that the addition of sunflower husk up to 10% and pomegranate husk particles up to 7% as reinforcement materials to polyester resin, leads to increase the tensile strength and Young's modulus of the composite material prepared and the use of sunflower husk as a reinforcement material increased the tensile strength, Young's modulus and water absorption were better than pomegranate husk at the same percentage of addition. The decrease in reinforcement material grain size led to increase the tensile strength, Young's modulus and water absorption. Therefore, all the best result seen in composites containing reinforcement material with (50µm). Finally, the best result obtained in tensile strength, Young's modulus and water absorption were with the addition of 10% sunflower husk as a reinforcement material to polyester resin.

في هذا البحث تمت دراسة تأثير اضافة دقائق تدعيم طبيعية لراتنج البولي أستر غير المشبع وعند كسر وزنية وحجوم حبيبية مختلفة. تم دراسة اختبار الشد وامتصاصية الماء للعينات المحضرة وفقا للمواصفات العالمية ASTM D638 و ASTM D570على التوالي. تم دراسة تاثير دقائق قشور حب عبادالشمس وقشور الرمان المستخدمة بوصفها مادة تدعيم على متانة الشد, معامل المرونة وامتصاصية الماء بكسور وزنية 3%, 7%, 10%)) وحجوم حبيبية مختلفة (50µm, 100 µm, 150 µm) تم قياس قابلية امتصاص الماء للمادة المتراكبة عن طريق اخذ اوزان للعينات قبل وبعد الغمر في الماء لمدة مئة يوم. اما بالنسبة لاختبار الشد فقد تم تسليط حمل مقدارة (50KN) وبسرعة تشغيل 10mm/min. ومن خلال النتائج يمكن ملاحظة ان اضافة دقائق قشور حب عباد الشمس لغاية 10% ودقائق قشور الرمان لغاية 7% ادى الى زيادة في متانة الشد ومعامل المرونة للمادة المتراكبة المحضرة. ومن خلال النتائج تبين أيضا ان إضافة دقائق قشور حب عباد الشمس اعطت نتائج افضل من دقائق قشور الرمان في جميع الاختبارات. ومن خلال المقارنة بين تاثير الحجم الحبيبي لمواد التدعيم يمكن ملاحظة ان استخدام حجم حبيبي (50µm) اعطى نتائج افضل من (100µm) و (150µm) في جميع الاختبارات. أن افضل نتائج سجلت لمتانة الشد, معامل المرونة وامتصاصية الماء كانت عند استخدام دقائق قشور حب عباد الشمس بنسبة (10%) كسر وزني وحجم حبيبي (50µm).


Article
Investigation of Flexural Properties and Thermal Conductivity for Wood Dust Filled Epoxy.

Author: Ban M. Al-Shabander
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2013 Volume: 16 Issue: 3 Pages: 104-109
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

This paper presents the flexural properties and thermal conductivity of composites made from wood dust filler particles and epoxy resin. The flexural tests of composites, based on wood dust filler particles at different filler contents viz. (0, 1, 3, 5, 7 and 10) Wt%, were carried out using an Instron universal testing machine according to ASTM D790 and their results were presented. Experimental results showed that the flexural strength of the composites decreased with the increase of the filler particle content. Concerning the relation between the Young’s modulus and percentage of filler for flexural tests, it was found to be directly proportional at low concentrations of wood dust, at concentrations of 7 Wt% and 10 Wt% wood dust, the Young’s modules decreases with increasing wood dust, with values of (1.870) and (1.824) GPa respectively.Thermal tests were done using Lee’s disk to determine the coefficient of thermal conductivity. The results obtained showed that the increasing weight percentage of wood dust in the composite leads to decreasing the thermal conductivity.

يعنى هذا البحث بدراسة خواص الالتواء والتوصيلية الحرارية لمتراكبات مكونه من جسيمات غبار الخشب والايبوكسي. وقد قمنا بأختبار متراكبات تحوي نسب مختلفه من جسيمات غبار الخشب و قدرها (0, 1, 3, 5, 7, 10) Wt% وذلك بأجراء اختبارات عالمية طبقا لتوصيف محدد ASTM D 790. وقد اظهرت هذه الاختبارات ان متانة الانحناء تتناقص مع زياده نسبة الجسيمات الممزوجة. اما بخصوص العلاقه بين معامل يونك والنسبة المئوية للمادة الممزوجة فأنها تزداد بزيادة نسبه جسيمات الخشب عند التراكيز الواطئة اما عند التراكيز العالية (7) Wt% و (10) Wt%فأن معامل يونك يتناقص مع زيادة نسبه جسيمات الخشب وتساوي (1.870) و (1.824) GPa على الترتيب. اجريت اختبارات حرارية تضمنت استخدام قرص لي لحساب معامل التوصيل الحراري واظهرت النتائج المستحصلة انخفاض التوصيلية الحرارية مع زيادة نسبة جسيمات الخشب.


Article
Studying The Mechanical And Electrical Properties Of Polyester Resin Reinforced With Silica Particals
دراسة الخواص الميكانيكية والكهربائية لراتنج البولي استر المدعم بدقائق السليكا

Author: Shayma. H. Mohammad شيماء حميد محمد
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2013 Volume: 17 Issue: 6 Pages: 201-214
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

A study has been made on mechanical properties of polyester resin matrix reinforced with weight fraction (10,20, 30&40) % of silica particles. The specimens were subjected to tensile test bending test (three point method), and hardness test .The experimental results indicate that the tensile strength of the matrix material were found to be significantly higher than those of the composite material (36%,36.1%,52%,57.5) while the young modulus of matrix material were found to be less than of composite material (14%,33%,42%, 45%). Test result also indicate that the flexural strength of the matrix material were found to be significantly higher than those of the composite material (6%,27%,29%,51) while the young modulus of matrix material were found to be less than of composite material(41%,50%,57.6%, 63%) . hardness of the composite materials are significantly higher than those of the matrix material (20%,28.6%,34%,43%) the enhancement in these properties are found to be directly proportional to the weight fraction of reinforcement materials. Test results also indicate that the electrical conductivity increased with increasing the silica concentrations.

تم في هذا البحث دراسة الخواص الميكانيكية والكهربائية لراتنج البولي استر المدعم بدقائق السليكا وبنسب وزنيه (10, 20, 30 &40 ). تعرضت العينيات إلى اختبار الشد وجساءة الانحناء (ثلاثي النقاط ) والصلادة حيث أظهرت النتائج إن متانة الشد للمادة الأساس أعلى من المادة المركبة بمقدار (57.5%,52%,36.1%,36%) إما معامل المرونة للمادة الأساس اقل من المادة المركبة بمقدار (14%,33%,42%, 45%) .إما في اختبار الانحناء أظهرت النتائج إن متانة الانحناء للمادة الأساس أعلى من المادة المركبة بمقدار (51%,29%,27%,6%) إما معامل المرونة للمادة الأساس اقل من المادة المركبة بمقدار (41%50%,57.6%, 63%) .إما نتائج اختبارات الصلادة أظهرت إن صلادة المواد المركبة أعلى بكثير من المادة الأساس 43%,34%,28.6%,20% ))وان التحسن في الخواص يتناسب طرديا مع الكسر ألوزني للمواد المدعمة إما بالنسبة لاختبار التوصيل الكهربائي فقد أظهرت النتائج إن خاصية التوصيل الكهربائي للمادة المركبة اعلى من المادة الأساس وتزداد بزيادة النسبة الوزنية لدقائق التدعيم .


Article
MICROMECHANICAL MODELING OF SHORT –FIBER REINFORCED POLYMERIC
النمذجة الميكانيكية الدقيقة لمركب مسلح بألواح البوليمر

Author: Kareem N. Hussien كريم نجم حسين
Journal: Muthanna Journal of Engineering and Technology(MJET) مجلة المثنى للهندسة والتكنولوجيا ISSN: 25720317 25720325 Year: 2013 Volume: 2 Issue: 2 Pages: 73-82
Publisher: Al-Muthanna University جامعة المثنى

Loading...
Loading...
Abstract

This paper presents a method considering the effect of fiber geometry and volume fraction for predicting the tensile strength, shear stress and Von Mises stress. The finite element scheme for the micromechanical modeling of the behavior of fiber reinforced polymeric composites under external load is developed. The model is used to estimate the stress distribution throughout the composite domain and to identify the location where maximum stresses occur. The ratio between fiber modulus and matrix modulus must be high enough to improve the mechanical properties and to reduce the premature interfacial failure. The prediction of the stress distribution by using a simulation tool could be helpful for more understanding the real reasons behind failure of polymer composites.

يقدم هذا البحث طريقة لحساب تأثير أبعاد الألياف ونسبتها الحجمية للتنبؤ بقيم مقاومة الشد, أجهاد القص وأجهاد فون ميسيس. اعتمد هذا البحث على تطوير طريقة العناصر المحدودة لنمذجة التصرف المايكروميكانيكي للبوليمر المقوى بالألياف تحت تأثير الحمل الخارجي. أستخدم النموذح العددي لتقدير توزيع الأجهاد على مدى المادة المركبة بغرض تحديد أماكن الأجهاد الاقصى. تعتبر النسبة العالية بين معامل الليف الى البوليمر أساسا لتحسين الخواص الميكانيكية ولمنع الأنهيار المبكر . أن التنبؤ بتوزيع الأجهاد باستخدام نماذج المحاكاة الدقيقة يساهم في زيادة الفهم لأسباب الأنهيار للمواد البوليمرية المركبة.


Article
Preparation of Chloro Penta Amine Cobalt (III) Chloride and Investigate its Influence on the Structural Properties and Acoustical Parameters of Polyvinyl Alcohol

Authors: Nada K. Abbas ندى كاظم عباس --- Majeed Ali Habeeb مجيد علي حبيب --- Alaa J. Kadham Algidsawi الأء جواد كاظم
Journal: Journal of Kufa - physics مجلة الكوفة للفيزياء ISSN: 20775830 Year: 2015 Volume: 7 Issue: 2 English and Arabic Pages: 81-96
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

Chloro penta amine Cobalt (III) Cloride [Co(NH3)5Cl]Cl2 was prepared then characterized by FTIR and XRD . The obtained results indicated the formation of Orthorhombic [Co(NH3)5Cl]Cl2 nano particles of ≈ 28.75 nm size .Polymeric films based on polyvinyl alcohol PVA doped with Chloro penta amine Cobalt (III) Cloride [Co(NH3)5Cl]Cl2 at different weight percent ratios were prepared using the solvent cast technique. The structural properties of these polymeric films were examined by XRD, FTIR and SEM studies. The complexation of the additive with the polymer was confirmed by FTIR and SEM studies. The XRD pattern revealed that the amorphousicity of PVA polymer matrix increased with raising the [Co(NH3)5Cl]Cl2 content. Ultrasonic pulse technique of variable frequency (25, 30, 35 and 40) kHz were performed to study the influence of ultrasonic frequency on the mechanical properties of PVA/ [Co(NH3)5Cl]Cl2 composite. Some properties such as ultrasonic velocity, acoustic impedance ,bulk modulus and transmittance and relaxation amplitude were found to be decreasing with frequency while absorption coefficient and compressibility were increasing with frequency .Results showed that ultrasonic wave made degradation to the randomly coiled polymer chains ,when ultrasonic frequency increase there were more degradation that increasing the number of un-tied chains as a result of absorbing composite ultrasonic waves ,for this reason it could be pointed that PVA/[Co(NH3)5Cl]Cl2 composite as a good ultrasonic absorber. It was found that there was significant relationship between ultrasonic velocity and material properties

Listing 1 - 10 of 17 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (17)


Language

English (14)

Arabic and English (2)

Arabic (1)


Year
From To Submit

2017 (4)

2016 (2)

2015 (2)

2014 (4)

2013 (3)

More...