Article
Dielectric properties of EpTiO2;EpMgOnano composites
الخصائص العزلية لمتراكبات الايبوكسي- TiO2; MgO النانوية

Loading...
Loading...
Abstract

The Dielectric properties of EP/TiO2 and MgO nanocomposite at a frequency range of (102-106 Hz) were studied. The composite were prepared with the state volume ratio (0, 0.05, 0.1) for EP/TiO2 and MgO respectively. The impedance, dielectric constant and dielectric loss were founddecrease with frequency increase.

تم دراسة الخواص العزليه للمتراكبات النانويه الايبوكسي - TiO2 ; MgO ولمدى من الترددات (102-106 Hz) وبدرجة حرارة الغرفة المتراكبات تم تحضيرها بنسب حجميه (0,0.05,0.1). وقد أظهرت الدراسة أن قيمة الممانعة تقل بزيادة التردد وكذلك ثابت العزل بجزأيه الحقيقي والخيالي.


Article
The effect of Gamma radiation on The Dielectric Properties of SiO2 Ep: TiO2 Ep Nanocomposite
تأثير أشعة كاما على الخصائص العزلية لمتراكبات الايبوكسيTio2; Sio2 النانوية

Authors: Ahmed Q. Abd Allah أحمد قاسم عبد الله --- Hayder S. Hussain حيدر سليم حسين --- Khadijha S. Mohan خديجة صبيح موحان
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2017 Volume: 58 Issue: 2B Pages: 843-847
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This research investigates the dielectric properties (impedance, dielectric constant and dielectric loss) of SiO2 Ep :TiO2 Ep nanocomposite over the frequency range of (102-106 Hz ) at room temperature. The dielectric material used is epoxy resin, while nano-sized titanium dioxide (TiO2) with grain size ( 30nm) , oxide silicon (SiO2) with grain size (12nm) in state volume ratio (0,0.05 ,0.1) .The effect of gamma by using (CS137) for period time (17) day was studied Radiation caused decreasing in real and imaginary parts of dielectric constant and impedance .

تم في هذا البحث دراسة الخواص الكهربائية (الممانعة، ثابت العزل بجزأيه الحقيقي و الخيالي ) ولمدى من الترددات(102-106 Hz)وبدرجة حرارة الغرفة. المادة العزليه المستخدمة هي راتنج الايبوكسي بينما المادة المالئة هي ثنائي أوكسيد التيتانيوم ذو الحجم النانوي (nm30) و ثنائي اوكسيد السيليكون ذو الحجم النانويnm) 21) وبنسب حجميه (0,0.05 ,0.1 ) وتم دراسة تأثير التشعيع بأشعة كاما المنبعثة من مصدرالسيزيوم (137) و لمدة (17 ) يوم وقد أظهرت النتائج الحالية أن التشعيع يؤدي الى نقصان في قيمة ثابت العزل بجزأيه الحقيقي والخيالي وكذلك الممانعة .


Article
Dielectric Behavior and Functionality of PVC / Cellulose acetate Composite

Authors: Abdullwahab A. Sultan --- Rajaa M. abdullah --- Abdullah A. Hussein
Journal: Journal of Basrah Researches (Sciences) مجلة ابحاث البصرة ( العلميات) ISSN: 18172695 Year: 2018 Volume: 44 Issue: 1A Pages: 20-32
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

Cellulose acetate powder which is extracted from the cigarette (insulator part as a filler) has been used with polymer to produce PVC Cement/cellulose acetate composite. The dielectric behavior of this composite is analyzed as a function of weight ratio of cellulose acetate powder (0.1, 0.2, 0.3, 0.4, and 0.5 wt%), temperature range (30 - 120) ◦C and frequency (120Hz 2MHz). Impedance and AC conductivity (ζac.) of the composites behaviors as function of frequency and temperature have also studied. The results show that, the real permittivity, dielectric loss and loss tangent for all composites increase the with increasing of cellulose acetate filler content


Article
Comparison of Fatigue Life Behavior between Two Different Composite Materialssubjected to Shot Peening at Different Times
مقارنة سلوك عمر الكلال لمادتين مركبتين مختلفتين تحت تأثير أزمنة مختلفة للسفع بالكرات

Authors: Mahdi N. M. Shareef مهدي نعمان مسلم --- Ahmed N. Al-Khazraji أحمد نايف ابراهيم الخزرجي
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2014 Volume: 10 Issue: 3 Pages: 1-12
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This paper investigated the fatigue life behavior of two composite materials subjected to different times of shot peening (2, 4 and 6 min).The first material prepared from unsaturated polyester with E-glass reinforcement by 33% volume fraction. While, the second one was prepared from unsaturated polyester with aluminum powder by2.5% volume fraction. The experimental results showed that the improvement in endurance limit was obtained (for the first material) at 2, 4 and 6 min shot peening times where the percentage of maximum improvement was 25% at shot peening time of 6 min. While, the endurance limit of the second material decreased at shot peening times of 2, 4 and 6 min where the percentage of maximum reduction was 29 % at shot peening time of 6 min. The verification of experimental results was done using ANSYS.14 workbench with a good agreement in behavior between the experimental and numerical.

تم في هذا البحث دراسة تأثر سلوك عمر الكلال لمادتين مركبتين خاضعتين لأزمنة مختلفة من السفع بالكرات (2 و 4 و 6 دقائق). المادة المركبة الاولى حُضرت من مادة البولي أستر غير المشبع مع مدعمات من الليف الزجاجي بكسر حجمي 33 %. بينما كانت المادة الاخرى محضرة من البولي أستر غير المشبع مع مسحوق الالمنيوم بكسر حجمي 2.5 %. أظهرت النتائج العملية بأن التحسن في حد الكلال قد حصل للمادة الاولى عند أزمنة سفع بالكرات (2 و 4 و 6 دقائق) حيث كانت أقصى نسبة مئوية للتحسن 25 % عند زمن سفع بالكرات قدره 6 دقائق. بينما قلّ حد التحمل للمادة الثانية عند أزمنة السفع بالكرات (2 و4 و 6 دقائق) حيث كان أقصى نقصان بنسبة مئوية 29 % عند زمن سفع بالكرات قدره 6 دقائق. وتمت برهنة النتائج العملية باستخدام برنامج (ANSYS.14 workbench) وبمقبولية جيدة بين العملي والتحليل النظري.


Article
The Effect of Adding Alumina Phases (alpha and amorphous) to Improve the Mechanical Properties (Compressive Strength and Hardness) of Polyester Matrix Composites
تأثير إضافة أطوار الألومينا (الألفا واللابلورية) على الخواص الميكانيكية (مقاومة الكبس والصلادة) لمتراكبات البولي استر

Authors: Hanaa Dakhel Ahmed هناء داخل --- Manal Flayeh Hasan منال فليح حسن
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2014 Volume: 18 Issue: 6 Pages: 202-211
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

In this research work a polyester composite material was prepared contains a matrix which is a polyester resin and reinforced with (15, 25, 35, and 45) (wt %) of alumina particles phases (crystal structure & amorphous).All samples were prepared according to standard measurement. Mechanical tests were done for the polyester composite materials to calculate the compressive strength and hardness, and the results showed a significant improvement in the properties of the polyester composite material reinforced with alumina with phase crystal (corundum-α), also noted the positive effect of the increase in the weight of the particles on the properties of the polyester composite material with that this increase has given better results.

تم في هذا البحث تحضير مادة متراكبة تحتوي على مادة أساس هي راتنجات البولي أستر مقواة بمادة الألومينا ذات الطورين (البلوري والعشوائي), وبحجم حبيبي مختلف 25, 15) 35, 45) وزنا. ان جميع العينات كانت قد حضرت اعتمادا على الاختبارات القياسية .اجريت اختبارات ميكانيكية لمتراكبات البولي أستر لحساب متانة الضغط والصلادة, واظهرت النتائج تحسنا كبيرا في خواص المادة المتراكبة المقواة بمادة الالومينا ذات الطور البلوري (corundum-α) , كذلك لوحظ التأثير الايجابي للزيادة الوزنية للدقائق على خواص المادة المتراكبة حيث ان هذه الزيادة اعطت نتائج افضل.

Listing 1 - 5 of 5
Sort by
Narrow your search

Resource type

article (5)


Language

Arabic and English (2)

English (1)


Year
From To Submit

2018 (1)

2017 (1)

2016 (1)

2014 (2)