Article
Some properties of accelerated cured no fine Lightweight concrete
بعضخصائصالخرسانة خفیفة الوزن الخالیھ من الركام الناعم المعجلة الانضاج

Author: Zena K.A.Al Anbori زینة خضیر عباس
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 13 Part (A) Engineering Pages: 213-224
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Thermal insulation is one of the main problems facing the engineers working inbuilding and housing sector spatially for the high summer temperature in the mostArab Gulf and spatially in Iraq, so the study of lightweight aggregate thermalinsulation (No fine concrete) is important. The experimental work consist of concretemixes (cement: porcelinite aggregate) ratios (1:4), (1:5) and (1:6) and for each mixescement content changes (200, 300 and 400) Kg/m3. Dependence on mixing (1:5) andcement content (300Kg/m3) change the water to cement ratio (0.4, 0.45 and 0.5) byweight. The research presents the tests of density, absorption, porosity, ultrasonicpulse velocity, accelerated compressive strength according to British standard (BS1881: Part 112: 1983), normal compressive strength at 7, 28 and 90-day. Light weightconcrete was obtained of density ranging from (721-770) kg/m3 and thermalconductivity ranging from (0.17- 0.24) W/ (m.K). The good correlation betweenaccelerated compressive strength at one day with normal compressive strength at 28-day is approximately (0.245 ±0.005) for water bath at 55°C and (0.335±0.05) forwater bath at 82°C.


Article
NO-FINE LIGHTWEIGHT AGGREGATE CONCRETE MODIFIED WITH STYRENE BUTADIENE RUBBER
الخرسانة الخالية من الركام الناعم المصنوعة من الركام خفيف الوزن والمطورة بالبوليمر

Authors: Ali T. Jasim --- Qusay A. Jabal
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2010 Volume: 1 Issue: 2 Pages: 33-44
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

No-fines concrete is a form of lightweight concrete obtained when fine aggregate is omitted. No-fine concrete mainly used for both load bearing and non-load bearing for external walls and partitions and in in-filling panels in framed structures. The essential objective of this work is to investigate the effect of incorporation of polymer (SBR) on the performance of no-fine concrete made from lightweight aggregate (porcelinite) and to suggest possible applications of this type of concrete. Three concrete mixes with different aggregate/cement ratios (A/C) (6:1, 8:1 and 10:1) by volume were selected. Each of these mixes included six mixes which differed in polymer/cement ratios, (0%, 5%, 10%, 15% and 20%) by weight to find the optimum polymer/cement ratio. Density, compressive strength, splitting tensile strength and drying shrinkage were conducted on all concrete mixes. The test results showed that the compressive strength of no-fine lightweight aggregate concrete increased with the increase in polymer/cement ratio up to 15%, and the compressive strength reduced at polymer /cement ratio of 20% . At polymer/cement ratio of 15%, the percentage of increase in compressive strength measured relative to reference mixes was about 50%. On the other hand, the splitting tensile strength was increased with the increase in polymer/cement ratio for all mixes. The percentage of increase in splitting tensile strength compared with reference mixes increased from about 30 to 90% with the increase of polymer/cement ratio from 5 to 20 %. Also the drying shrinkage strains of no-fine concrete decrease, with the increase in polymer/cement ratio. The percentages of decrease in drying shrinkage strain at 56 days were from 5 to 30% with the increase of polymer/cement ratio from 5 to 20%.

تعد الخرسانة الخالية من الركام الناعم احد أنواع الخرسانة خفيفة الوزن حيث يتم ا لحصول عليها بحذف الركام الناعم من الخرسانة الاعتيادية. . ان الهدف الرئيسي من هذا البحث هو دراسة تأثير إضافة احد أنواع البوليمر المعروف باسم ستايرين بيوتادين على اداء الخرسانة الخالية من الركام الناعم والمصنوعة أيضا من الركام خفيف الوزن ومن ثم اقتراح التطبيقات المناسبة لهذا النوع من الخرسانة. تم استعمال ثلاث خلطات خرسانية بنسب مختلفة من الركام/ الاسمنت (( 10:1, 8:1 , 6:1 وكل خلطة من هذه الخلطات تضمنت نسب مختلفة من البوليمر/ الاسمنت (5 ,10 ,15 , و20%). بعد المعالجة الرطبة تم إجراء فحوصات الكثافة الجافة, مقاومة الانضغاط, مقاومة الشد الانشطاري, وانكماش الجفاف. أظهرت النتائج بان مقاومة الانضغاط تزداد بزيادة نسبة البوليمر/ الاسمنت ولغاية نسبة 15% بعد هذه النسبة تبدأ بالانخفاض إن نسبة الزيادة في مقاومة الانضغاط عند نسبة البوليمر/ الاسمنت 15% كانت تقريبا 50%. من جانب أخر إن مقاومة الشد الانشطاري تزداد بزيادة نسبة البوليمر/ الاسمنت حيث تراوحت الزيادة من 30 إلى 90% عند زيادة نسبة البوليمر/ الاسمنت من 5 إلى 20% . أشارت النتائج أيضا إن قيم انكماش الجفاف تنخفض بزيادة نسبة البوليمر/ الاسمنت حيث لوحظ بان نسبة الانخفاض بعمر 56 يوم تراوحت من 5 إلى 30% عند زيادة نسبة البوليمر/ الاسمنت من 5 إلى 20%.


Article
Performance of Fiber Light-Weight Aggregate Concrete Exposed to Elevated Temperatures
أداء الخرسانة خفيفة الوزن الحاوية على الألياف والمعرضة إلى درجات حرارة عالية

Authors: Shakir A. Salih --- Ali T. Jasim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 13 Pages: 2393-2410
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Two major problems arise when concrete is exposed to elevatedtemperatures. One is the deterioration in mechanical properties of concrete and the other problem is spalling of concrete. In recent times, the inclusion of polypropylene fibers had been reported to be a feasible method to prevent spalling of concrete subjected to elevated temperature. Additional problems arise due to the fact that by adding polypropylene fibers, the residual properties of heated concretemay be adversely affected. The essential objective of this work is to investigate the effect of incorporation of polypropylene fibers or/and steel fibers on the residual properties of lightweight concrete made from porcelinite aggregate after subjected to elevated temperatures. The concrete specimens heated to target temperatures of 100, 200, 400, 600 and 800 oC, at a rate of 10 oC per minute. When the targettemperature was reached, the specimens were kept at that temperature for 2 hours and then allowed to cool to room temperature by natural cooling. For each type of concrete, compressive strength, splitting tensile strength, static modulus of elasticity, and thermal expansion strains were determined before and after exposing the concrete to the target elevated temperatures. Experimental results indicated thatpolypropylene fiber-reinforced LWAC showed more reduction in its residual mechanical properties compared to plain LWAC. These different are more pronounced at exposure temperature of 200 and 400 oC. Average differences of 30,25 and 20 percent were observed in static modulus of elasticity, splitting tensile strength and compressive strength respectively, for specimens heated up to 400 oC. The addition of steel fibers inside the polypropylene fiber concrete would improvethe residual mechanical properties of heated concrete at temperature range 200 to 600 oC. On average, the improvement ranged from 9 to 20 percent.

هنالك مشكلتان رئيسيتان عند تعرض الخرسانة إلى درجات الحرارة العالية. المشكلة ألأولى هي تدهور الخواص الميكانيكية للخرسانة و المشكلة الأخرى هي تشظي الخرسانة. لقد وجد مؤخرا″ إن إضافة ألياف البولي بروبلين إلى الخرسانة هي طريقة مناسبة لمنع تشظي الخرسانة عند تعرضها إلى درجات الحرارة العالية. تظهر مشكلة أخرى نتيجة انصهار هذه الألياف حيثتوثر سلبا″ على خواص الخرسانة المعرضة للحرارة العالية. إن الغرض الرئيسي من هذا البحث هو التعرف على تأثير إضافة ألياف البولي بروبلين و/او ألياف الحديد على أداء الخرسانة خفيفة الوزن المنتجة من ركام البورسيلينايت بعد تعرضها إلى درجات الحرارة العالية. تم تسخين و بمعدل تسخين 10 o 600 و 800 م ,400 ,200 , النماذج الخراسانية إلى درجات حرارة 100 دقيقة وتم الإبقاء على درجة الحرارة المطلوبة لفترة ساعتين بعدها تم تبريدها بشكل طبيعي / o مإلى درجة حرارة الغرفة. تم في هذا البحث إجراء عدة فحوص تضمنت مقاومة الانضغاط, مقاومة الشد الانشطاري, معامل المرونة الساكن, والتمدد الحراري قبل وبعد تعرض النماذج إلى الحرارة العالية. سببت إضافة ألياف البولي بروبلين أكثر انخفاضا في الخواص الميكانيكية للخرسانة المسخنة مقارنة مع الخرسانة غير الحاوية على ألياف البولي بروبلين. هذا الانخفاض , حيث كان الاختلاف حوالي 30 o كان أكثر وضوحا عند درجات حرارة التعرض 200 و 400 م25 و 20 % في معامل المرونة الساكن, مقاومة الشد الانشطاري ومقاومة الانضغاط على أدت إضافة ألياف الحديد إلى الخرسانة الحاوية على . o التوالي للنماذج المسخنة لغاية 400 م ألياف البولي بروبلين إلى تحسين الخواص الميكانيكية للخرسانة المعرضة إلى درجات حرارة . % حيث كان معدل التحسن من 9 إلى 20 ,o 200 إلى 600


Article
Insulating Light Weight Aggregate Concrete
تطویر خرسانة خفیفة الوزن عازلة للحرارة

Authors: زین العابدین محمد رؤوف --- ندى مھدي فوزي --- محمد حمزة حسین
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 13 Pages: 678-691
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The weather in Iraq is hot in summer and cold in winter. Therefore , thethermal insulation is of the main problems facing the engineers working inbuilding and housing sectorThe paper presents an experimental investigation, It includes preparation ofseveral concrete mixes using lightweight aggregate (siporex and porcelinite &suwdast ) to obtain light weight concrete of two densities ranging from (350-880kg/m3), which provides a good thermal insulation. Based on the analysis ofexperimental results several graphs and Tables have been prepared and presentedwhich can be used in the mix design of similar siporex concrete of densities from(350-880 kg/m3) . The physical properties of siporex concrete , have been foundwhich included density (765-822kg/m3) , compressive strength (1.51-2.2 N/mm2)& (2.8-3.7 N/mm2) ,thermal conductivity ( 0.19-0.39 W/M.K) for the two groupsrespectively.

يعاني مناخ العراق بجوه الحار صيفا والبارد شتاءا وتعتبر مشكلة العزل الحراري إحدىالمشاكل الهندسية الرئيسية التي تحتاج إلى المزيد من البحث في مجال الإسكان والبناء.يتضمن البحث عدة تجارب منها تحضير خلطات خرسانية من مواد خفيفة الوزن مثل (ركاممكسر الثرمستون وركام المخلوط من البورسيلينايت ونشارة الخشب) للحصول على خرسانة880 ) كغم/م 3 بحيث توفر عزلا حراريا جيدا , وان لهذا - ذات كثافة قليلة تتراوح بين( 350النوع من الخرسانة واطئه الكثافة استخدامات كثيرة في البناء , وكثير من المنشآت تتطلبمعالجات حرارية وصوتية باستخدام المواد خفيفة الوزن التي توفر عزل حراري .وعلى ضوء نتائج التجارب تم وضع جداول ومنحنيات تساعد في تصميم خلطات من خرسانة880 ) كغم/م 3 وشمل البحث دراسة الخواص - ركام الثرمستون المكسر ضمن مدى كثافة ( 350822 كغم/م 3) , ومقاومة الانضغاط مابين - الفيزياوية مثل الكثافة والتي تتراوح مابين ( 7650.39 ) واط _ 3.7 نيوتن/ملم 2) والموصلية الحرارية ( 0.19 - 2.2-1.51 نيوتن /ملم 2) و( 2.8 )/ متر.كلفن للمجموعتي

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

Arabic (2)

English (2)


Year
From To Submit

2013 (1)

2010 (2)

2009 (1)