Article
Evaluation of Using Waste of Bottles in Concrete as Sustainable Construction

Authors: Zainab Hasan Abdulabbas --- Shereen Qasim Abd-Alridha
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2016 Volume: 24 Issue: 3 Pages: 782-797
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

In the current study attention was focused on effects of using wastes of plastic and glass of juices and soft drink bottles in concrete, and the optimum percent's of the wastes were detected giving the best properties of concrete. Total number of concrete mixes was (12), which have different wastes additions details. These mixes included: three mixes have plastic fibers (1, 2, 3)% by cement weight, three mixes have glass with ratios of (10, 15, 20)% as a replacement of sand volume, three mixes have pieces of plastic bottle caps with ratios of (15, 20, 25)% as a replacement of gravel volume. The mix that has the optimum properties in these three groups, was selected to merge these types of wastes in one mix. Therefore, two additional mixes were prepared; one mix contains addition of 2% plastic fibers and 15% glass; and the other mix contains 20% plastic bottle caps and 15% glass, in addition to the reference mix without any waste additions. The achieved tests comprise; compressive strength, modulus of elasticity, flexural strength, ultrasonic pulse velocity, density, absorption and fire resistance. Tests results give good indications about using these waste in concrete; when two types of wastes are added to the mixes (plastic fiber with glass C11 or pieces of bottle caps and glass C12) the compressive strength is improved noticeably, the residual compressive strength is about (75% and 83%) with total ratio of wastes about 35% at age of 7 and 28 days, respectively, in mix C12, and (76 .7% and 70.5%) with total ratio of wastes about 17% at age of 7 and28 days, respectively, in mix C11

تركَز الاهتمام في الدراسة الحالية على تأثيرات إضافة المخلفات البلاستيكية والزجاجية لعلب العصائر والمشروبات الغازية على الخرسانة ومعرفة النسب المثلى للمخلفات المضافة التي تعطي أفضل خصائص للخرسانة. العدد الكلي للخلطات الخرسانية المفحوصة كان (12) خلطة بمختلف النسب للمخلفات المضافة. هذه الخلطات تتضمن: ثلاث خلطات تحتوي (1, 2, 3)% ألياف بلاستيكية كنسبة من وزن السمنت, وثلاث خلطات تحتوي (10, 15, 20)% مخلفات زجاجية كنسبة مستبدلة من حجم الرمل, وثلاث خلطات تحتوي (15, 20, 25)% قطع أغطية العلب البلاستيكية أضيفت كنسبة مستبدلة من حجم الحصى, الخلطة التي لها افضل خواص في هذه المجاميع الثلاثة، تم اختيارها لدمج هذه الانواع من المخلفات في خلطة واحدة بحيث تم تحضير خلطتين اضافيتين؛ خلطة تحتوي 2% ألياف بلاستيكية و15% مخلفات زجاجية, وخلطة تحتوي 20% قطع أغطية العلب البلاستيكية و15% زجاج, بالإضافة للخلطة المرجعية التي لا تحتوي على مخلفات. الفحوصات المنجزة شملت مقاومة الانضغاط، معامل المرونة، مقاومة الانثناء, الموجات فوق الصوتية، الكثافة، الامتصاص، ومقاومة الحريق. نتائج الفحوصات اعطت مؤشرات جيدة حول استعمال هذه المخلفات في الخرسانة ؛ فعند إضافة نوعين من المخلفات للخلطات (الياف بلاستيكية مع الزجاج C11 أو قطع أغطية العلب مع الزجاج C12) تحسنت مقاومة الانضغاط بشكل ملحوظ إذ أن مقاومة الانضغاط المتبقية بحدود (75% و 83%) لمجموع نسبة مخلفات بحدود30% بعمر 7و28 يوم على التوالي في الخلطة C12 و (76,7% و 70,5%) لمجموع نسبة مخلفات بحدود 17% بعمر 7و28 يوم على التوالي في الخلطة C11.


Article
A Study of the Effect of Recycled Mix Glass on the Mechanical Properties of Green Concrete

Authors: Aseel B. Al-Zubaidi --- Kadhum Muttar Shabeeb --- Aynoor Ibrahim Ali Jan
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 2 Pages: 265-272
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

In this paper we utilized mixing of different types of recycled glass such as (neon glass, brown glass, and green glass) that has high percentage of silicon dioxide (SiO2) with different concentrations. Utilization these landfall materials can be considered as keeping on resources. Different waste glasses used as a partial replacement of cement with different concentrations 11%, 13%, and 15% of cement weight for each type, and study the effect of it on the mechanical properties of concrete. After mixing, casting, and curing in water at (20±2)°C for (7, 14, and 28) days, the mechanical properties showed that the compressive strength and flexural showed highest results at 13% from cement weight of neon glass, whereas splitting tensile strength showed the highest value at the same percentage, but from green glass.

في هذه الورقة البحثية تم استخدام خليط من الزجاج ڪ( زجاج شمعات النيون (الفلورسنت, الزجاج الجوزي و الزجاج الاخضر) والذي يحتوي على نسب سيليكا عالية(SiO2). استخدام هكذا مواد تالفة معاد تدويرها يعد من المحافظة على المصادر الطبيعية. تم استخدام مسحوق خليط الزجاج كبديل جزئي للاسمنت بثلاث تراكيز (11%, 13%, و 15%). من وزن الاسمنت. بعد عملية الخلط والصب والمعالجة بالماء العادي بثلاث اعمار (7, 14, و 28) يوم. أظهرت الخواص الميكانيكية ان مقاومة الانضغاط و متانة الانحناء اعلى قيمة لها عند النسبة (13%) لزجاج النيون من وزن الاسمنت. في حين متانة الانشطار (فحص شد بصورة غير مباشرة), اظهرت النتائج اعلى قيمة لهما عند نفس النسبة السابقة لكن من الزجاج الاخضر.


Article
Partial and Full Replacement of Silica Sand by Fine Recycled Glass in Cementitious Composites
الإستبدال الجزئي والكلي لرمل السيليكا في المركبات الأسمنتية بزجاج ناعم معاد

Loading...
Loading...
Abstract

One of the major concerns currently and within the close future is the adequate management and efficient reuse and recycling of wastes, which reduces the natural sources and energy consumption. Millions of tons of waste glass are discharged around the world annually. One of the successful policies of the recycling of waste glass is the use in the construction industry where it can be used as aggregate or cement replacement. In the current study, fine recycled glass with granular size of 0.075 to 0.3 mm was used as silica sand replacement in cementitious composites incorporated fly ash and no coarse aggregate. Cube and prism specimens were prepared with four replacement ratios of 0, 25, 50, and 100% to evaluate the compressive strength, the modulus of rupture, and the expansion. The test results showed that 50% and 100% replacements of silica sand by fine glass enhanced both the compressive strength and the modulus of rupture. For mixtures with 100% fine recycle glass, the compressive strength and the modulus of rupture increased by 25% and 33.6%, respectively, compared to mixtures with 100% silica sand. Moreover, the expansion was found to be reduced by approximately 30% as the silica sand was fully replaced by fine glass

إحدى أهم المشاكل الحالية وفي المستقبل القريب هي الإدارة السليمة والتدوير وإعادة الاستخدام الكفوءة لمخلفات المدن والذي يؤدي الى تقليل استهلاك الموارد والطاقة. في كل عام يتم طرح ملايين الأطنان من مخلفات الزجاج حول العالم. إحدى أهم السياسات في تدوير مخلفات الزجاج تكمن في إستخدامها في الصناعات الإنشائية حيث يمكن إستخدامها كتعويض عن الركام او الأسمنت. تم إستخدام ركام زجاج ناعم بقياس 0.075 الى 0.3 ملم في هذه الدراسة كتعويض عن رمل السيليكا في المركبات الأسمنتية التي تحوي رماد متطاير ولا تحوي ركام خشن. تم إعداد نماذج مكعبة وموشورية بأربعة نسب تعويض تساوي 0, 25, 50 و 100% لدراسة مقاومة الانضغاط, معاير الكسر والتمدد. بينت نتائج الفحوصات أن تعويض رمل السيليكا بركام الزجاج الناعم بنسب تساوي 50 و 100% حسنت كل من مقاومة الإنضغاط و معاير الكسر. في الخلطات التي تحوي على 100% ركام الزجاج الناعم إزدادت مقاومة الإنضغاط ومعاير الكسر بمقدار 25% و 33.6% على التوالي مقارنة مع الخلطات التي تحوي 100% رمل السيليكا. بالإضافة الى ذلك فإن التمدد قل بما يقارب 30% في حالة التعويض الكامل لرمل السيليكا بركام الزجاج الناعم.