Improvement of Iraqi Red Kaolin as a Refractory Material
تحسین خصائص الكاؤلین الاحمر العراقي كمادة حراریة

Authors: Amel S. Merzah --- Younis Muhsin --- Yasamin k. Mahmood
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 4 Part (A) Engineering Pages: 952-959
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work refractory material was prepared from Iraqi red kaolin with the addition of different proportions of silica and alumina (10, 15, 20 %) for each one and the red kaolin 70%. The powders were mixed in a ball mill, sieved, formed, dried at 110 oC for 8 hrs and then fired at different temperatures 800, 900, 1000 and 1100oC for 2 hrs. The physical properties(linear and volumetric shrinkage ,apparent density and porosity) were calculated from the measured data .It was found that the higher the firing temperature the better the properties of the prepared samples for a given mixture ,the best properties obtained in this work was 70%red kaolin,10%silica and 20%alumina).

في هذا البحث تم تحضير مادة حرارية من الكاؤلين الاحمر العراقي مع اضافة نسب مختلفة من السليكا والالومينا (10و15و20%)لكل منهما و70 % كاؤلين احمر.تم مزج المساحيق حسب النسب المذكورة بواسطة طاحونة ذات الكرات ونخلت ,شكلت,جففت بدرجة 110 درجة مئوية لمدة 8 ساعات ثم حرقت بدرجات حرارية مختلفة 800,900,1000 و1100 درجة مئوية لمدة ساعتان .تم حساب الخصائص الفيزياوية(الانكماش الخطي والحجمي والكثافة الظاهرية والمسامية) للنماذج المحروقة من القيم المقاسة.وجد انه كلما زادت درجة حرارة الحرق حصلنا على خواص افضل ولقد وجد بأن افضل نتائج تم الحصول عليها للنموذج ذو المحتوى (70% كاؤلين و10% سليكا و20% الومينا).