Article
Synthesis of Biodiesel by Nanoporous Catalysts Supported Alkali Metals and its Hydroxides
انتاج وقود الحيوي باستخدام العوامل المساعدة النانوية المسامية المحملة على المعادن واكاسيدها المائية

Authors: Talib M. Albayati1 --- Aidan M. Doyle2
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 4 Part (B) Scientific Pages: 788-800
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The alkali metals make up first group of the periodic table. This family consists of the elements lithium, sodium, potassium, rubidium, cesium, and francium (Li, Na, K, Rb, Cs, and Fr, respectively).The influence of alkali metals and its hydroxides supported on catalysts prepared SBA-15 for the synthesis of agro or biodiesel fuels from vegetable oil were investigated via heterogeneous catalytic reaction. The structural and textural features encapsulated Nanoporous Material SBA-15were studied by X-ray diffraction, scanning electron microscopy (SEM), EDAX, nitrogen adsorption-desorption (BET) and FTIR characterization were also carried out on the catalysts before and after loading. Mild conditions (atmospheric pressure and 65 ᴼC) were chosen for catalytic activity reaction testing in a batch reactor. The results show that all the catalysts were found active for the esterification reaction of vegetable oil conversion around (85-94%).This study shows that the alkali metals and its hydroxides supported catalysts on SBA-15 based catalyst have proven to be a promising one for the transesterification of vegetable oil with methanol.

تشكل الفلزات القلويةالمجموعة الاولى من الجدول الدوري. تتكون هذه العائلةمن العناصرالليثيوم(Li) ، الصوديوم(Na) ، البوتاسيوم(K) ، الروبيديوم(Rb)، السيزيومCs))،والفرانسيوم(Fr)على الترتيب.ان تأثيرالفلزات القلويةوهيدروكسيداتهاالمحملة عل العامل المحفز (العامل المساعد)SBA-15لصناعة وقود الديزل الحيوي من الزيوت النباتية تم دراستها عن طريق التفاعل المحفزالغير المتجانس. ان تركيب المادة ومميزات السطح الخارجي للمادة النانوية المسامية تم دراستها قبل وبعدالتحميل. بواسطة الاشعة السينية XRD بالاضافة الى دراسة المسح الالكتروني المجهريSEM وتحليل نسبة العناصرEDAX. وكما تم قياس المساحة السطحية وقطر المسامات بواسطة غاز النيتروجين بعملية الامتزاز وازالة الامتزازBET . بالاضافة الى قياس المجاميع الفعالة بواسطة FT-IR.وقد تم اختيارظروف معتدلةلعملية التشغيل ( عند الضغط الجويودرجة حرارة 65 مئوي) لدراسة فعالية العامل المساعد. واظهرت النتائج التي تم الحصول عليها في جميع انواع العوامل الحفازة التي اختبرت في تفاعل الاسترة بان تحويل الزيت النباتي الى البايوديزل او الوقود الحيوي كان بحدود(85-94٪).وتبين هذه الدراسة أن الفلزات القلوية وهيدروكسيداتهاالمحملة كمحفزات على المادة النانوية المسامية SBA-15قد اثبتلتكون واحدة من العوامل المحفزة الجيدة لتفاعلات الأسترة لانتاج الوقود الحيوي من تفاعل الزيوت النباتية مع الميثانول.


Article
Removal of Cobalt (Co(II)) from Aqueous Solution by Amino Functionalized SBA-15

Authors: Anaam A. Sabri --- Talib M. Albayati --- Dalia B. Abed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 7 Part (A) Engineering Pages: 703-708
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Mesoporous silica SBA-15 material was synthesized and functionalized by post synthesis method with amino functional group (3-aminopropyltriethoxysilane) to investigate its potential use as an adsorbent for cobalt (Co(II)) removal from aqueous solution. Several characterization methods were used for identifying the material characteristics before and after functionalization, such as X-ray diffraction (XRD), scanning electron microscopy (SEM) and Fourier transform infrared (FTIR) spectroscopy. Batch adsorption experiments were conducted and different variables that affected the removal of cobalt ions were studied, such as pH (1-6), contact time (0-150min), initial concentration (20-120mg/L) and adsorbent dose (0.025-0.3g). It was found that amino functional group was very effective in increasing the percentage removal of (Co(II)) as compared with non-functionalized SBA-15. The percentage removal of these ions were increased with the increasing of pH (up to 5), contact time and NH2-SBA-15 dose, while the increase of the initial concentration of Co(II) ions led to decrease in it.


Article
Hydroisomerization and Hydrocracking of n-Heptane over Nanoporous Trimetallic (Pt-Ni-Co/SBA-15 Catalyst)
عملية ألأزمرة والتكسيرالحراري للهبتان الاعتيادي فوق العامل المساعد النانوي المسامي ثلاثي المعادن Pt-Ni-Co/SBA-15))

Authors: Talib M.Albayati --- Aidan M. Doyle
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 18 Part (A) Engineering Pages: 36-52
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The heterogeneous hydroisomerization and hydrocracking of n-heptane was carried out within the pores of the mesoporous SBA-15 silicas, within which was encapsulated trimetallic nanoparticles of Pt-Ni-Co. The structural and textural features of the nanoporoussilicas, both with and without encapsulated nanoparticles, were characterised using small angle X-ray diffraction, scanning electron microscopy (SEM), EDAX, nitrogen adsorption-desorptionporosimetry/BET surface area analysis,Fourier-transform infrared (FTIR) spectroscopyand transmission electron microscopy (TEM).Catalytic testing was conducted using a plug-flow reactor in a catalyst testing rig under tightly controlled conditions of temperature, reactant flow rate and pressure.Species were leaving the reactor andanalysed by Gas Chromatography. The results show thatPt-Ni-Co/SBA-15 had a high activity for conversion of n-heptane (around 85%). The catalyst was found to be stable to heating and did not undergo any significant deactivation during reaction at temperatures up to 400 °C.

ان عملية الازمرة والتكسير الحراري للهبتان الاعتيادي في تفاعلات غير متجانسة (متباينة) الاطوار وبوجود العامل المساعد قد حدثت ضمن مسامات المادة النانوية المسامية SBA-15 التي تم حشوتها بجسيمات او جزيئات المعادن النانوية الثلاثية 1% (البلاتين-النيكل-الكوبلت). ان تركيب المادة النانوية المسامية SBA-15 ومميزات السطح الخارجي لها تم دراستها بواسطة الاشعة السينية XRD بالاضافة الى دراسة المسح الالكتروني المجهريSEM وتحليل نسبة العناصرEDAX. وكما تم قياس المساحة السطحية وقطر المسامات بواسطة غاز النيتروجين بعملية الامدصاص وازالة الامدصاصBET . بالاضافة الى قياس المجاميع الفعالةFT-IR وكذلك تم استخدام المجهر الالكتروني الناقل (TEM). ان جميع هذه الخصائص تم دراستها قبل وبعد عملية التحميل بالمعادن.ان عملية اختبار العامل المساعد قد اجريت في المفاعل الانبوبي وفي ظروف مسيطرة عليها مثل الضغط ، درجة الحرارة، ومعدل التدفق. النتائج اظهرت ان فعالية تقييم العامل المساعد في المفاعل الانبوبي توحي بان المعادن الثلاثية المحملة 1% (Pt-Ni-Co)/SBA-15 لها فعالية عالية اثناء تحويل الهبتان الاعتيادي بحدود 85% في المفاعل الانبوبي.اوجدت النتائج استقرارية العامل المساعد للتسخين ولم يخضع لاي عملية تعطيل مؤثرة في درجة حرارة التفاعل لحد 400 درجة مئوية.