INFLUENCE OF CURING REGIMES ON THE COMPRESSIVE STRENGTH OF THE REACTIVE POWDER CONCRETE (RPC) USED IN RIGID PAVEMENTS
تأثير طرق الإنضاج على مقاومة انضغاط الخرسانة الحاوية على مواد ناعمة فعالة (RPC) التي تستخدم في البلاطات الصلدة

Authors: Mohameed Seffo --- Nadia Salim Ismaeel --- Ali hussain Ali
Journal: AL-TAQANI مجلة التقني ISSN: 1818653X Year: 2012 Volume: 25 Issue: 3 Pages: E56-E68
Publisher: Foundation of technical education هيئة التعليم التقني

Loading...
Loading...
Abstract

Experimental and analytical works were done in order to study the effect of different curing methods and determine the best curing method which characterize the mechanical properties (compressive strength) of Reactive Powder Concrete (RPCs), in order to use it in rigid pavements (Airport Pavements) in Iraq. RPCs specimens were subjected to five types of curing regimes, Modified Curing (C1), specimens are immersed in hot water at 60oC for 7 days starting at one day after cast, specimens are then stored at 23oC & 100% RH until testing, Normal Curing (C2), specimens are allowed to remain in a standard environment conditions (23oC & 95% RH) starting at one day after cast until testing, Delayed Curing (C3), specimens are subjected to Normal Curing (C2) for 10 days after casting then specimens are subjected to Steam Curing (C4) for 48 hours, Steam Curing (C4), specimens are subjected to thermal steam treatment for 48 hrs at 90oC & 100% RH starting at one day after cast, specimens are then stored at 23oC & 100% RH until testing, and the Steam Pressure Curing (C5), specimens are autoclaved at 120oC & 1.0 MPa for 3 hours starting at one day after cast, specimens are then stored at 23 oC & 100% RH until testing. Test results show that the highest compressive strength were obtained by both the C1 and C3 curing methods. Depending upon mix proportions and age of test, the percentages of increasing in the compressive strength of RPCs specimens with respect to curing types were as follows: (a) For mixes without polymers: C1 recorded (59.03, 14.69, 32.16, and 14.67)% higher 28-day compressive strength than (C2, C3, C4, and C5) respectively; and C3 recorded (39.42, 20.70, and 23.38)% higher 28-day compressive strength than (C2, C4, and C5) respectively. (b) For mixes with polymers: C1 recorded (20.99, 5.83, 30.59, and 26.07)% higher 28-day compressive strength than (C2, C3, C4, and C5) respectively; and C3 recorded (28.59, 38.78, and 57.34)% higher 28-day compressive strength than (C2, C4, and C5) respectively.

تم اجراء الفحوصات المختبرية و تحليل نتائجها لغرض دراسة تأثير انواع الانضاج (curing methods) على مقاومة الخرسانة الحاوية على مواد ناعمة فعالة (RPC) واختيار افضل طريقة انضاج لغرض استخدامها في البلاطات الصلبة (مدارج الطائرات) في العراق. تم تعريض النماذج المختبرية الى خمسة انواع من الانضاج، المعالجة المعدلة [C1]، الانضاج الذي يتضمن غمر النماذج المختبرية في الماء الساخن بدرجة حرارة (60)0م لمدة (7) أيام، المعالجة الاعتيادية [C2]، الانضاج الذي يتضمن غمر النماذج في الماء بدرجة حرارة (23oC) و رطوبة نسبية (100%) لحين فحصها، المعالجة المتأخرة [C3]، الانضاج الذي يتضمن تعريض النماذج المختبرية للمعالجة الاعتيادية لمدة (10) أيام ومن ثم تعريض هذه النماذج الى الانضاج بالبخار لمدة (48) ساعة، المعالجة بالبخار [C4]، الانضاج الذي يتضمن تعريض النماذج للبخار الحراري بدرجة حرارة (90oC) و رطوبة نسبية (100%) لمدة (48) ساعة، و اخيرا المعالجة بالبخار و الضغط [C5]، الانضاج الذي يتضمن معالجة النماذج بالمحمم المائي بدرجة حرارة (120oC) و ضغط (1.0 MPa) لمدة (3) ساعات. نتائج الفحوصات اظهرت بأن اعلى القيم لمقاومة الانضغاط لهذا النوع من الخرسانة قد تم الحصول عليها بأتباع كل من طرق الانضاج [C1] و [C3]. واعتمادا على نسب الخلط وعمر الفحص، تبين بأن نسب الزيادة في مقاومة الانضغاط كانت كما يلي: آ- للخلطات بدون البولمرات: [C1] سجلت مقاومة انضغاط بعمر (28) يوم اعلى بمقدار (14.67 & 32.16 ,14.69 ,59.03)% من (C5 & C4 ,C3 ,C2) على التوالي; وان [C3] قد سجلت مقاومة انضغاط بعمر (28) يوم اعلى بمقدار (23.38 & 20.70 ,39.42)% من (C5 & C4 ,C2) على التوالي. ب- للخلطات بالبولمرات: [C1] سجلت مقاومة انضغاط بعمر (28) يوم اعلى بمقدار (26.07 & 30.59 , 5.83 , 20.99)% من (C5 & C4 ,C3 ,C2) على التوالي; وان [C3] قد سجلت مقاومة انضغاط بعمر (28) يوم اعلى بمقدار (57.34 & 38.78 , 28.59)% من (C5 & C4 ,C2) على التوالي.الكلمات المفتاحية: طرق انضاج الخرسانة، مقاومة الانضغاط، (SCMs)، الخلطات التجريبية، البلاطات الصلبة.


Article
Impact Strength for the 3D Textiles Fiber Reinforced Cementitious Composites Plates
تحمل الصدمة للصفائح السمنتية المركبة والمسلحة بنسيج زجاجي ثلاثي الابعاد

Loading...
Loading...
Abstract

The use of textile reinforcement made from non-corrosive materials, such as carbon and glass can reduce the required concrete material; this is known as Textile Reinforced Concrete (TRC). This study deals with plate specimens having dimension of 500×500×40mm tested under impact load at 28 and 90 days age under two conditions of ends, simply supported and fixed. Cement mortar with about 60 MPa, 7cm cube compressive strength at 28 days was designed for casting the plates. Plate specimens were divided into four groups, they consist of reference plates (no reinforcement) and plates reinforced with 3D glass fabric having three different thicknesses 6, 10 and 15mm.The results indicate that using 3D textile glass fabric cause an increase in number of blows, reduce in final stage deflection, an improvement in toughness and energy absorption under impact loads. Using 3D textile glass fiber with 10mm thickness gave higher number of blows for 28 and 90 days as compared with 6 and 15 mm. Plates with slice 6mm 3D textile glass fiber in two way reinforced has significantly enhancement in number of blows, the improvement was about (80 - 125%) and (128.5- 114. 3%) for 28 and 90 days respectively. The specimens showed increase in the energy absorption, besides the number and width of cracks was reduced and only few cracks are propagated up to the edge of the plates.

ان استخدام الالياف اوالنسيج بابعاد ثلاثية مصنوعة من مواد زجاجية اوكاربونية ذات طبيعة كيميائية خاملة يؤدي الى تقليل بكمية المواد السمنتية الداخلة بالخلطة الخرسانية. حيث تضمنت هذه الدراسة قياس تحمل الصدمة لصفائح بابعاد 500*500*40 ملم وبعمر 28 و90 يوم بواقع نوعين من الشروط الحدودية (بسيطة وثابتة). وتم صب الصفائح باستخدام مونة اسمنتية ذات مقاومة انضغاط 60 ميكاباسكال بعمر 28 يوم. قسمت الصفائح الى اربع مجاميع مؤلفة من صفائح بدون استخدام اي الياف لغرض المقارنة وصفائح مسلحة بثلاث اسماك مختلفة (6و10و15ملم) من الياف زجاجية ثلاثية الابعاد. فحصت الصفائح تحت تاثير حمل الصدمة واظهرت النتائج ان استخدام نسيج زجاجي ثلاثي الابعاد ادى الى تحسن في خواص الصفائح وذلك بزيادة عدد الضربات وتقليل الانحرافات وزيادة في مقدار الطاقة الممتصة. ان استخدام الياف زجاجية بسمك 10 ملم تطلب زيادة في عدد الضربات المطلوبة للفشل بعمر فحص 28 و90 يوم مقارنة مع سمك 6 و15 ملم. كما ان استخدام نسيج ثلاثي الابعاد على شكل شراح بطبقتين وبسمك 6 ملم ابدى قوى ربط اكبر وتحسن بعدد الضربات ، حيث كان التحسن بمقدار 80-128 % و128.5-114.3% لاعمار 28 و90 يوم اضافة الى ان جميع الصفائح اظهرت زيادة في امتصاص الطاقة ونقصان في سمك وعدد الشقوق خلال الفحص .


Article
PUNCHING SHEAR BEHAVIOR OF THREE DIMENSION TEXTILES REINFORCED CEMENTITIOUS COMPOSITE PLATES

Authors: Nadia Moneem --- Waleed A. Abbas --- Ikbal N. Gorgis
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2018 Volume: 9 Issue: 4 Pages: 45-64
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

Self compacting mortars (SCMs) plate specimens with dimension of (500×500×40) mm were cast with three-dimension (3D) textile glass fiber having three diverse thicknesses 6, 10, and 15mm to measure their punching strength. Plates with one and two layers of chicken wires, as well as micro steel fiber of 0.75 % volume fraction were tested under punching for comparison. Punching shear tests have been carried out by applying concentrated load with steel cylinder of 50mm diameter and 10 mm height. The mechanical behavior of SCMs plate was discussed in terms of observed behavior, ultimate load, load - deflection curves, and crack pattern. The results indicated an enhancement in the ultimate load at (28 and 90) day ages by about (7.82% and 24%), respectively. The maximum ultimate load was increased by about (58.4 and 54.1) % for plates reinforced by micro steel fiber at 28 and 90 days, respectively as compared with reference. The maximum deflection at the center of the Self-compact mortars plates for all tested plates was improved.