Capability of Forging Technique to Produce Round Shape Flange Using (POM) Material Under Cold and Hot Conditions

Author: Talib.H.Rashid
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2008 Volume: 14 Issue: 4 Pages: 3112-3120
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The paper studied capability of forging process to produce round shape flange using acetal (celconR¬) polymer which is an engineering crystalline material having a good ductility if it is preheated The process done under cold & hot conditions This kind of technique guarantees a product with high strength and stiffness better than what injection molding could achieve. The products showed crack and curling traces on the flange under cold forging, but a good product was achieved by heating the billet and the tools to (100Co)with improvement in the mechanical properties. The paper discussed also through (stress – strain) curves manner of deformation through forging action. The results explained that POM (celconR¬) is forgeable polymer if it is preheated at (100 Co ) using slow speed press by closed die forging process under applied pressure of 170Mpa to produce round shape flange, while this technique failed to forge same polymer at room temperature.

درست الورقة امكانية طريقة الكبس بالقوالب المغلقة فى انتاج (شفة دائرية) من مادة (اسيتيل سيلكون) وهي مادة بلاستيكية هندسية بلورية لها القابلية على مطاوعة الكبس كلما كانت ساخنة. وقد اجريت التجربة وذلك بالكبس على البارد مرة وبالكبس بعد تسخين القطعة المشغولة مرة اخرى . هذه الطريقة تضمن صلادة و مقاومة للمنتج افضل مما تفعله طريقة البثق . كانت النماذج المنتجة تحت ظروف درجة حرارة الغرفة تحوى عيوب التكسر والالتواء, بينما كانت النماذج في الحالة الثانية حيث تم تسخين القطعة المشغولة والقالب لدرجة100مئوى كاملة الشكل والأبعاد مع تحسن في الخصائص الميكانيكية. الورقة درست كذلك سلوك المادة اثناء عملية الكبس من خلال منحنيات الجهد والاجهاد. النتائج اوضحت ان الاسيتل له المطاوعه الكافيه اذا تم تسخينه لدرجة(100مئوى) لكى ينتج شفة دائرية بواسطة طريقة الكبس بالقوالب المغلقة تحت صغط ( 170 ميكاباسكال ), بينما فشلت النماذج التى انتجت دون تسخين مسبق باستخدام نفس طريقة الصنع .

Keywords

Forging --- POM --- recovery --- dwell time --- billet --- SPF.


Article
Thermal Properties of Polyvinyl acetate (PVA) and Toluene Diisocyanate (TDI) With Prepared Solfonated Phenol Formaldehyde Resin (SPF) as Composites.
الخصائص الحرارية لمكون البولي فينايل اسيتيت/تلوين داي ايسوسيانيت مع راتنج الفينول-فورمالديهايد المسلفن المحضر

Author: Thamir Salman Bachari ثامر سلمان بجاري
Journal: basrah journal of science البصرة للعلوم ISSN: 18140343 Year: 2015 Volume: 33 Issue: 1A Pages: 47-69
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

Two similar specimens of polyvinyl acetate (PVA) and toluene diisocyanate (TDI) blend and prepared solfonated phenol formaldehyde resin (SPF) as a mixture composite. SPF was diagnosed by infrared Fourier transformation (FTIR) spectrophotometer. The specimens were subjected to thermal heating by using copper electric heater; this was connected to d.c power supply. Three copper-constantan thermocouples were connected from junctions in two copper plates with dimension 4.2x 3.5x 0.2 cm3. in length, width and thickness respectively, to voltmeters for measuring the temperature across two similar specimens, with respect to the ambient and ice point temperatures. Negative electric potential (voltage) -2.7 mv and -3.1 mv dependence for thermal conductivity of the composite has indicated at 0.3%wtSPF. The calculated thermal conductivity were 0.0043 W.m-1.k-1 and 0.00239 W.m-1.k-1 at temperature 303 k and 203 k. for 0.2%wtSPF and 0.3%SPF respectively to 0.007 W.m-1.k-1 and 0.001 W.m-1.k-1 at 602.985 k and 582.999 k for 0.4%wtSPF and 2%wtSPF respectively. Maximum extrapolation is 0.07 W.m-1.k-1 for 1%wtSPF.

تم عمل نموجين متشابهين من مزج البولي فينايل اسيتيت و تلوين داي ايسوسيانيت مع نسب وزن مختلفة من راتنج الفينول-فورمالديهايد المسلفن المحضر لعمل خليط المكون. تم سكب الخلائط في قالبين متشابهين تم عملهما في صفيحتين من البولي اثلين, لتحضير نموذجين متشابهين لكل خليط. تم تشخيص البولي فينايل أسيتيت/تلوين داي أيسوسيانيت مع راتنج الفينول-فورماليهايد المسلفن بأستخدام جهاز مطياف تحويلات فورير للاشعة تحت الحمراء. تم تعريض النماذج للتسخين الحراري بأستخدام مسخن من النحاس والذي تم أيصاله الى مجهز قدرة. ثلاث مزدوجات حرارية تم أيصالها عبر نقاط في صفيحتين متشابهتين من النحاس بابعاد 0.2x 3.5x 4.2 سم3 في الطول, العرض والسمك على التوالي, الى فولتمترين لقياس درجة الحرارة النموذجين المتشابهين والمتماثلين لابعاد المسخن بالنسبة الى درجة حرارة المسخن والمحيط داخل المستودع ونقطة أنجماد الجليد. تم تعيين جهد سالب -2.7 ملي فولت -3.7 ملي فولت عند النسبة .0.3%wtSPFتم حساب التوصيلية الحرارية, 0.0043 واط.م-1. كلفن-1, , 0.00239 واط.م-.كلفن-1, عند درجة حرارة 313 كلفن و203 كلفن, للنسبة للنسبة 0.2%wtSPF و0.3%wtSPF. على التوالي و 0.007 واط.م-1.كلفن-1 و 0.001 واط.م-1.كلفن-1. عند درجة حرارة 602.985 كلفن و 582.999 كلفن للنسبة 0.4%wtSPF و 2%wtSPF على التوالي. أعلى قيمة استقرائية للمكون 0.07 واط.م-1زكلفن-1 للنسبة 1%wtSPF.