Article
ENGINEERING PROPERTIES OF SUSTAINABLE SELF- COMPACTING CONCRETE WITH CLAY BRICKS WASTE AGGREGATE

Authors: Thaer A. Al-Daebal --- Wasan I. Khalil
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2018 Volume: 9 Issue: 3 Pages: 223-239
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

The present study covers the use of different percentages (25, 50, 75 and 100%) of clay bricks waste as replacement by volume of coarse natural aggregates to produce sustainable self- compacted concrete (SCC). All mixes used containing 10% silica fume as a replacement by cement weight. The properties of SCC studied were, workability, fresh density, dry density, water absorption, compressive strength, splitting tensile strength, flexural strength, modules of elasticity and thermal conductivity. The results show that the flow ability, filing ability, and passing ability of self -compacted concrete through steel reinforcement are decrease with the increase of clay brick waste content. In addition, the segregation resistance decreases with the increase of clay brick waste content of SCC. The use of clay brick waste aggregate causes reduction in density, compressive strength, splitting tensile strength, flexural strength, modules of elasticity and thermal conductivity of SCC. The percentage reduction increases with the increase of clay bricks waste content in self-compacted concrete.


Article
Effect of Fire Flame (High Temperature) on the Behaviour of Axially loaded Reinforced SCC Short Columns

Author: Amer F. Izzat
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2012 Volume: 18 Issue: 8 Pages: 889-904
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Experimental research was carried out to investigate the effect of fire flame (high temperature) on specimens of short columns manufactured using SCC (Self compacted concrete). To simulate the real practical fire disasters, the specimens were exposed to high temperature flame, using furnace manufactured for this purpose. The column specimens were cooled in two ways. In the first the specimens were left in the air and suddenly cooled using water, after that the specimens were loaded to study the effect of degree of temperature, steel reinforcement ratio and cooling rate, on the load carrying capacity of the reinforced concrete column specimens. The results will be compared with behaviour of columns without burning (control specimens). The results showed that, the ultimate load capacity of columns exposed to fire decreases with increasing the fire flame temperature. At burning temperature 300 , 500 and 700 , the average residual ultimate load capacity for gradually cooled specimens were 91%, 81% and 71% respectively. By increasing the ratio of longitudinal reinforcement 44% , the maximum improvement in the ultimate load capacity was 24% and 17% for the gradually and sudden cooling respectively at. For the same longitudinal reinforcement ratio and fire burning temperature, the ultimate capacity for the sudden cooling specimens was less than that of gradually cooled specimens by about 10%.Key word: self compacted concrete (SCC), elevated temperature, fire flame.

بحث عملي اجرى لدراسة تاثير درجات الحرارة العالية (الحريق) ,على نماذج من الاعمدة الخرسانية القصيرة المسلحة والمصنعة باستخدام الخرسانة الذاتية الرص. النماذج عرضت الى لهب بدرجات حرارة عالية , باستخدام فرن صنع لهذا الغرض.لمحاكات كارثة الحريق الحقيقية في الموقع تم تبريد النماذج بطريقتين , تبريد بطيء وتبريد فجائي باستخدام الماء.ومن ثم يتم تحميلها لدراسة تاثير :تاثير لهب الحريق في درجات حرارة مختلفة,نسب حديد مختلفة بعد الحرق , ومعدل التبريد (تدريجي و فجائي).على قوة تحمل الاعمدة الخرسانية المسلحة ومقارنة النتائج مع نماذج السيطرة( الاعمدة التي لم تتعرض للحريق). اظهرت النتائج , ان مقاومة تحمل العمود للاحمال تقل كلما زادت درجة الحرارة, حيث وصلت الى 71%, 81% و 91% للنماذج المعرضة الى , و . بزيادة نسبة حديد التسليح الطولي بمقدار 44% كانت اعلى زيادة في قوة تحمل العمود 24% و 17% للنموذج المبرد تدريجيا وفجائيا بالتتابع عند درجة حرارة C◦500 .. وجد انه عند استخدام نسبة مماثلة من الحديد الطولي ولنفس درجة الحرارة فان الاعمدة المبردة فجائيا اقل تحملا للاحمال من المبردة تديجيا بمقدار 10%.


Article
Effect of External Sulfate Attack on Self Compacted Concrete
تأثير مهاجمة الاملاح الخارجية على الخرسانة ذاتية الرص

Author: Zena K. Abbas Al-Anbori
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 6 Part (A) Engineering Pages: 1092-1106
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Self-compacting concrete (SCC) is an innovative concrete that does not require vibration for placing and compaction. It is able to flow under its own weight, completely filling formwork and achieving full compaction, even in the presence of congested reinforcement. The effect of external sulfate attack was studied-Es (very sever exposure SO4>10000ppm) according to ACI 318-11. The mix design method of SCC used is according to EFNARC 2002, and then must satisfy the criteria of filling ability, passing ability and segregation resistance. The experimental program focuses to study two different chemical composition of sulfate resistance Portland cement with different percentage of silica fume replacement by weight of cement and W/cm (0.3 and 0.35). The SCC mixes with cement type 1(C3S= 46.39 and C3S/C2S = 1.78) shows more resistance to Es than mixes with cement type 2 (C3S= 61.22 and C3S/C2S =4.44). The SCC mixes containing 10% SF as replacement of cement shows more resistance to external sulfate attack. The percentage of increase is 17.95% for SCC mixes with type 1 cement and W/cm =0.3 and 17.88% for SCC mixes with type 2 cement and W/cm =0.3 compared to reference concrete mixes

الخرسانة ذاتية الرص هي خرسانة غير تقليدية لا تحتاج الى عملية أهتزاز أو رص في التنفيذ. تكون لها القابلية على الانسياب تحت تأثير وزنها, ولها القابلية على ملئ القالب كاملاً حتى في وجود تسليح كثيف . تم دراسة تأثير مهاجمة الاملاح الخارجية القاسية (SO4 > 1000ppm) وحسب متطلبات الجمعية الامريكية 318 لعام 2011 . الخلطات الخرسانية مصممة حسب متطلبات EFNARC لعام 2002 والتي يجب ان تتوافق مع قابليتها على الملئ , الانسياب و مقاومتها للانعزال. البرنامج العملي يركز على دراسة تأثير التركيب الكيماوي للسمنت البورتلاندي المقاوم ,أضافة نسب من ابخرة السيلكا كأستبدال من وزن السمنت و بنسب وزن ماء الى سمنت 0,3 و 0,35.الخلطات الخرسانية ذاتية الرص الحاوية على النوع 1 من السمنت (46,39=C3S و C3S/C2S=1,78) أظهرت مقاومة أعلى لمهاجمة الاملاح الخارجية من الخلطات الحاوية على النوع 2 (61,22=C3S و C3S/C2S=4,44).الخطات الخرسانية ذاتية الرص الحاوية على 10% من أبخرة السيليكا كانت أكثر مقاومة لمهاجمة الاملاح الخارجية و كانت نسبة الزيادة قد وصلت الى 17,95 للنوع 1 من السمنت و 17,88 للنوع 2 من السمنت لنسبة ماء الى سمنت (0,3).


Article
Mechanical Properties of Self-Compacted Concrete

Authors: Ammar SaleemKhazaal --- Alyaa Abbas Ali --- Assim Mohammed Lateef
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2016 Volume: 23 Issue: 1 Pages: 40-52
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

In this research, trial mixes were conducted according to Self-Compacted Concrete (SCC) specifications, a mix that gave a higher compressive strength to the age of seven days has been selected. Then after selecting the appropriate mix, concrete samples had poured and were distributed into five groups; each group consists of six cubes, six cylinders, and six prisms. The samples of each group are testing for compressive, tensile splitting, and flexure strengths respectively for the ages of 7, 14, 28, 60, and 90 days respectively. Before of conduction of destructive tests, the samples were tested using ultrasonic waves to determine the relationship between the concrete strength and pulse velocity and in the same way for all ages in above. Experimental results showed that, all concrete mechanical properties have improved, and the maximum improve was in flexural strength followed by compressive strength and tensile splitting strength. The cube compressive strength increased according to (G1 at 7 days curing) from 34.3% to 71.8%, the percentage of increase of tensile strength according to (G1 at 7 days curing) from 16.8% to 64.3% , modulus of rupture increased according to (G1 at 7 days curing) from 34.6% to 98.7% for ages (14, 28, 60, 90 days) respectively. Pulls velocity increased according to (G1 at 7 days curing): For cube from 5.1% to 23.9%, for cylinder from 21.4% to 40.3%, for prisms from 7.1% to 29.2%.


Article
EXPERIMENTAL COMPARISON BETWEEN FLEXURAL CRACKS BEHAVIOR OF SELF-COMPACTING CONCRETE AND NORMAL CONCRETE BEAMS
مقارنة عملية لتصرف تشققات الانحناء للعتبات الخرسانة الذاتية الرص والخرسانة الاعتيادية

Author: Ali Farhan Atshan
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2017 Volume: 21 Issue: 4 Pages: 30-45
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Eight reinforced concrete rectangular beams were designed and tested to study the effect of using self-compacting concrete (SCC) and normal concrete (NC) on the flexural cracking behavior under two concentrated load. All beams have the same longitudinal and vertical steel ratio and gross section area of (15000) mm2. The tested beams were divided into two groups; the first group consists of four self-compacting concrete beams (SCC) while the second group consists of four normal strength concrete (NSC). Each group was divided into two series according to clear span to effective depth ratio (ln/d), each series includes of two compressive strength (f_c^' ). It was found that the beams which made from SCC was more stiffer as compared with the beam which made from NCC with same of the clear span to effective depth ratio, longitudinal steel ratio, vertical steel ratio and relative compressive strength. The first crack in the SCC beams about 26.95% from the ultimate load while the first crack in the NSC beams about 20% from the ultimate load, the ACI 318-08 equation is conservative as compared with the experimental study, the max crack width of SCC beams is lesser than the NC beams, the number of crack in SCC beams is lesser than the NC beams, the Z factor value in different exposure in ACI formula is more conservative than obtained from experimental study, the experimental cracking moment of SCC beams are greater than the experimental cracking of NSC. As compared with theoretical cracking moment predicated from cracking moment predicated from ACI formula, the maximum crack width of SCC increased about 20.833%, 26.16% when the clear span to the effective depth ratio (ln/d) increase from 8.4 to 10 at compressive strength (f_c^') 23.81 and 17.9 MPa respectively while the maximum crack width of NSC increased about 8.1%, 11.42% when the clear span to the effective depth ratio (ln/d) increase from 8.4 to 10 at compressive strength (f_c^') 22.41 and 16.2 MPa respectively and the ultimate load capacity of SCC increased about 9.433%, 14.285% when the compressive strength (f_c^') increased from (17.9) to (23.81) MPa at clear span to effective depth ratio (ln/d) (8.4),(10) respectively while the maximum crack width of NSC increased about 2.56%,5.714% when the compressive strength (f_c^') increased from (16.2) to (22.41) MPa at clear span to effective depth ratio (ln/d) (8.4),(10) respectively.

يتناول البحث دراسة تأثير ثمان عتبات خرسانية مسلحة ذات مقطع مستطيلة الشكل وبأبعاد (100mm x 150mm) صممت وفحصت لدراسة تأثير استخدام الخرسانة الذاتية الرص والخرسانة الاعتيادية على تصرف تشققات الانثناء تحت تأثير حملين مركزين جميع العتبات تحوي على نفس الحديد الطولي والحديد العمودي وذات مساحة مقطع 15000 ملم2 .قسمت العتبات المفحوصة الى مجموعتين المجموعة الأولى تحتوي على اربع عتبات ذاتية الرص بينما المجموعة الثانية تتكون من اربع عتبات ذات خرسانة اعتيادية. كل مجموعة قسمت الى متواليتين حسب نسبة الفضاء الى العمق الفعال. كل متوالية تتكون من اربع عتبات كل عتبتين منها ذات نفس مقاومة الانضغاط تقريبا وتبين ان العتبات الذاتية الرص اكثر قساوة بالمقارنة مع العتبات ذات الخرسانة الاعتيادية على الرغم من كون نسبة الفضاء الصافي الى العمق الفعال ونسبة الحديد الطولي والعمودي ومقاومة الانضغاط متساوية. التشقق الأول في الخرسانة الذاتية الرص تقريبا 26,95% من الحمل الأقصى بينما التشقق الأول في الخرسانة الاعتيادية حوالي 20% من الحمل الأقصى للعتبات. باستخدام المدونة الامريكية (ACI 318-08) وجد بأنها متحفظة مقارنة مع النتائج المستحصلة من الجانب العملي. عرض التشقق الأكبر للعتبات الخرسانية الذاتية الرص اقل منها في العتبات ذات الخرسانة الاعتيادية وقيمة معامل Z حسب قاعدة (ACI) اكثر تحفظ من النتائج المستحصلة من النتائج العملية وعزم التشققات التجريبي للعتبات الخرسانية الذاتية الرص اكبرمنها في العتبات ذات الخرسانة الاعتيادية بالمقارنة مع عزم التشقق النظري المستحصل من قاعة (ACI) وعرض اكبر تشقق للعتبات الذاتية الرص يزداد حوالي 20,833% و 26,16% عند نسبة طول صافي الى عمق فعال يتغير من 8,4 الى 10 وذات مقاومة انضغاط 23,81 و 17,9 (Mpa) على التوالي بينما عرض التشقق الأكبر لعتبة ذات خرسانة اعتيادية يزداد حوالي 8,1% و 11,42% عند نسبة طول صافي الى عمق فعال يتغير من 8,4 الى 10 عندما تكون مقاومة الانضغاط 22,41 و16,2 (Mpa) على التوالي وسعة التحمل القصوى لعتبات ذات خرسانة ذاتية الرص تزداد حوالي 9,433% و 14,285% عندما تكون مقاومة الانضغاط تزداد من 17,9 الى 23,81 (Mpa) عندما تكون نسبة طول صافي الى عمق فعال 8.9 و 10 على التوالي بينما عرض التشقق الأكبر للخرسانة الاعتيادية يزداد حوالي 2,56% و 5,714 عندما مقاومة الانضغاط تزداد من 16.2 الى 22,41 (Mpa) عندما تكون نسبة طول صافي الى عمق فعال 8.9 و 10 على التوالي.


Article
EXPERIMENTAL COMPARISON OF SHEAR BEHAVIOR BETWEEN NORMAL AND SELF-COMPACTED CONCRETE BEAMS

Author: Ahmed Hussein Al-Janabi
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2017 Volume: 21 Issue: 5 Pages: 39-53
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

This study deals with shear behavior between normal and self-compacted concrete beams. The experimental work includes design and testing of twelve reinforced concrete rectangular beams to study the effect of using self-compacted concrete (SCC) and normal concrete (NC) on the. shear behavior under two. concentrated load. All beams have same longitudinal and vertical steel ratio and cross sectional area of (17000) mm2. The tested. beams were divided into two. groups; SCC and NC beams. Each group. was divided into three series according to clear span. to effective depth ratio (ln/d), each. series consist of two compressive. strength of concrete ( ). It was found. that the beams which made from. SCC was more stiffer as compared. with the beam which made from NCC with same of the clear span. to effective depth ratio, longitudinal steel ratio, vertical steel ratio and relative compressive. strength. This equation is conservative. as compared with. for NC beams. tested while the ACI 318 equation. is more conservative as compared. with the for SCC beams tested. It was .found that the. ultimate shear strength of SCC .increased about 16.66%, 20.33%,20.88% when. the compressive strength ( ) increased from (29.39) to (42.1) MPa while the shear strength of NC .increased about 9.3%,12.9%,14.9% when the compressive strength ( ) increased from (27.8) to (39.1) MPa at clear span to. effective depth ratio (ln/d) (7.534),(6.164),(5.584) respectively. It was found that the shear strength of SCC increased about 12.5%, 18.75% when the. clear span to the effective depth ratio (ln/d) decreed from 7.534 to 5.48 at compressive strength ( ) 29.39 MPa while the shear strength of SCC increased. about 16.07%, 25% when the clear span to the effective depth ratio (ln/d) decreed from 7.534 to 5.48 at. compressive. strength ( ) 42.1 MPa however, the shear strength of NC increased about 18.02%, 23.84% when the clear span to the effective depth ratio (ln/d) decreed from 7.534 to 5.48 at compressive. strength ( ) 27.8 MPa.while the shear strength of NC increased about 21.9%, 30% when the. clear span to the effective depth ratio (ln/d) decreed from. 7.534 to 5.548 at compressive strength (

تتناول هذه الدراسة تصميم واختبار. اثنا عشر عتبة خرسانية .مسلحة ذات مقطع مستطيل لدراسة تأثير. الخرسانة ذاتية الرص والخرسانة .الاعتيادية على تصرف القص تحت تأثير قوتين مركزتين. علما انه جميع العتبات تحتوي نفس حديد. التسليح الطولي والعمودي والمساحة الكلية للمقطع العرضي لجميع العتبات هو 17000 ملم2 . العتبات المفحوصة قسمت .الى مجموعتين: .المجموعة الأولى مكونة من ست عتبات ذات خرسانة ذاتية الرص. والمجموعة الثانية مكونة من ست عتبات .ذات خرسانة اعتيادية كل مجموعة. قسمت الى ثلاث متواليات. حسب الطول الصافي الى العمق الفعال؛. كل متوالية تحوي قيمتين لمقاومة الانضغاط بعمر. 28 يوم. وجد بانه. العتبات المصنوعة .من الخرسانة ذاتية الرص اكثر قساوة مقارنة. بالعتبات المصنوعة من الخرسانة الاعتيادية على الرغم من كون نسبة الفضاء الصافي الى العمق الفعال ونسبة الحديد الطولي. والعمودي ومقاومة الانضغاط متساوية. . باستخدام المدونة الامريكية (ACI-318) . وجد بأنها متحفظة مقارنة .مع النتائج المستحصلة من الجانب العملي للعتبات ذات الخرسانة الاعتيادية ومتحفظة اكثر مقارنة مع العتبات ذات الخرسانة ذاتية الرص. ووجد ان سعة التحمل القصوى العتبات ذات خرسانة ذاتية. الرص تزداد حوالي 16.66%، 20.33%. و 20.88% عندما تزداد مقاومة الانضغاط. من 29.39 الى 42.1 (Mpa). اما في حالة العتبات ذات الخرسانة الاعتيادية فان سعة التحمل القصوى تزداد حوالي 9.3%، 12.9% و 14.9% عندما تزداد مقاومة الانضغاط من 27.8 الى 39.1 (Mpa) .عندما تكون نسبة طول صافي الى عمق فعال 7.534 ، 6.164 و5.584 على التوالي. وكذلك وجد ان مقاومة القص القصوى للعتبات ذاتية .الرص تزداد حوالي 12.5% و 18.75% عندما تقل نسبة. .الطول صافي الى العمق. الفعال من 7.534 الى 5.584 عندما تكون مقاومة الانضغاط 29.39 (Mpa) بينما مقاومة القص. القصوى للعتبات ذاتية الرص تزداد حوالي 16.07% و 25% عندما تقل نسبة الطول صافي الى العمق الفعال .من 7.534 الى 5.584 عندما تكون مقاومة الانضغاط 42.1 (Mpa) .بينما على الجهة الأخرى وجد ان مقاومة القص القصوى للعتبات ذات الخرسانة الاعتيادية تزداد حوالي 18.02% و 23.84% عندما تقل نسبة الطول صافي الى العمق الفعال من 7.534 الى 5.584 عندما تكون مقاومة الانضغاط 27.8 (Mpa) بينما مقاومة القص القصوى للعتبات ذات الخرسانة الاعتيادية تزداد حوالي 21.9% و 30% عندما تقل نسبة الطول. صافي الى العمق الفعال من 7.534 الى 5.584 عندما تكون مقاومة الانضغاط 39.1 (Mpa).


Article
Experimental Study of the Shear Behavior of Self Compacted Concrete T-Beams
دراسة عملية لسلوك القص على عتبة كونكريتية مضغوطة ذاتيا مقطعها على شكل حرف (T)

Author: Kamal Sh. Mahmoud كمال شحاذة
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2012 Volume: 16 Issue: 1 Pages: 120-137
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Twelve self compacted concrete (SCC) T-section beams were design and tested to determine the effect of using SCC on the shear behavior under two concentrated loads. All beams have the same longitudinal steel ratio of (0.018823) and gross section area of (20000) mm2. The tested beams were divided into two groups- with and without stirrups. The first group consists of three beams without stirrup and with different values of compressive strength (f'c).While the second group consists of nine beams with stirrups. It were divided into three series according to the compressive strength (f'c ) each series have three beams with different value of clear span to effective depth ratio (ln/d). It was found that The ultimate shear strength predicated from ACI 318M-08 is conservative prediction than the experimental values, The clear span to the effective depth ratio (ln/d) has a significant influences on the ultimate shear strength, The ultimate shear strength of SCC T-beams with stirrups increased about 28.57%.10.714%and 10.169%; when the compressive strength (f'c ) increased from (29.36 to 49.2 MPa), the ultimate shear strength of SCC T-beams without stirrups increased about 55.55%; when the compressive strength (f'c ) increased from (29.36 to 49.2 MPa).

اثنتا عشر عتبة خرسانية ذات مقطع (T) ذاتية الرص صممت وفحصت تحت حملين مركزين .تحوي جميع العتبات على نسبة حديد واحدة وهي(0.018823) ومساحة المقطع العرضي هي(20000) ملم2 . قسمت العتبات المفحوصة إلى مجموعتين مجموعة مسلحة بحديد تسليح القص (الأطواق) والأخرى غير مسلحة بحديد تسليح القص(الأطواق). تحوي المجموعة الأولى على ثلاثة عتبات خرسانية ذاتية الرص بدون حديد تسليح القص(الأطواق) بمقاومة انضغاط مختلفة، بينما تحوي المجموعة الأخرى على تسعة عتبات خرسانية ذاتية الرص قسمت إلى ثلاثة متواليات حسب مقاومة الانضغاط كل متوالية تحوي على ثلاثة عتبات بنسب مختلفة من الطول الصافي إلى العمق الفعال.وجد خلال نتائج الفحص إن مقاومة القص القصوى المستحصلة باستخدام معادلة المدونة الأمريكية (318M-08) متحفظة مقارنة مع النتائج المستحصلة من الجانب العملي وان نسبة الطول الصافي إلى العمق الفعال ذات تأثير مهم على مقاومة القص القصوى وان مقاومة القص القصوى للعتبات الخرسانية المسلحة والحاوية على حديد تسليح القص (الأطواق) تزداد عند زيادة مقاومة الانضغاط حيث إن مقاومة القص القصوى تزداد بمقدار 28.57% و 10.714 % و 10.169% عند زيادة مقاومة الانضغاط من 29.36 إلى 49.2 نت/ملم2 بينما مقاومة القص القصوى للعتبات الخرسانية الغير حاوية على تسليح القص (الأطواق) تزداد بمقدار(55.55%) عندما تزداد مقاومة الانضغاط للخرسانة من 29.36 إلى 49.2 نت/ملم2


Article
Effect of Elevated Temperature on Punching Shear of Regular and Irregular Shaped Self-Compacted Concrete Slabs
تاثير التدرج الحراري على مقاومة القص الثاقب للبلاطات المنتظمة وغير المنتظمة الشكل والمكونة من الخرسانة الذاتية الرص

Author: Luma Fadhil H
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 19 Pages: 5893-5906
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The exposure of reinforced concrete slabs to high temperature causes changesin their structural behavior.This work aims to study the post-heating behavior of self compacted concrete(SCC) regular (square) and irregular (trapezoidal) shaped flat plates and assessingthe residual punching shear strength of these slabs.Twenty four reduced scale reinforced concrete slab specimens divided intotwo main groups (square and trapezoidal slabs), each of which consists of twelveslab identical in size and shape but different in concrete compressive strength(30,50,70) MPa. These specimens are subjected to different temperature levels(100, 300, 500) 0C and still heated in that temperature level for one hour using anelectric furnace and the results are compared with specimens tested at roomtemperature 25 0C.The effect of specimen shape, heating level, concrete compressive strength onthe punching shear resistance of slabs are discussed in details.Results indicate that the reduction in punching shear strength is ranged between(0 and 16) %, for square slab, at maximum temperature exposure (500) 0C, whilethis rate is ranged between (6.3 and 40.4) % for trapezoidal slabs. This indicatesthat the punching shear resistance of regular shaped slabs is higher than that ofirregular shaped slabs.

ان تعرض البلاطات الخرسانية المسلحة الى درجات الحرارة العالية تسبب تغيرا واضحا في اداء وظيفتها. يهدف هذا البحث الى دراسة مقاومة القص الثاقب للبلاطات الخرسانية ذاتية الرص (منتظمة وغير منتظمة الشكل), بالاضافة الى دراسة تاثير الحرارة على مقاومة القص الثاقب لهذه البلاطات. تم اجراء الدراسة على 24 بلاطة خرسانية مسلحة مقسمة الى مجموعتين رئيسيتين تختلف عن بعضهما في شكل النموذج ( مربع وشبه منحرف), كل مجموعة تحتوي على 12 بلاطة متماثلة في الشكل والابعاد ولكن تختلف عن بعضها في مقاومة الانضغاطتم تعريض جميع هذه النماذج الى درجات حرارة مختلفة . MPa ( للخرسانة ( 30,50,70 ( (100,300,500) 0 م لمدة ساعة كاملة ثم تم مقارنتها مع تلك النماذج التي تم فحصها بدرجة حرارة الغرفة 0 25 م . في هذا البحث تم دراسة تاثير شكل النموذج, درجة حرارة الحرق ومقاومة الانضغاط للكونكريت على مقاومة القص الثاقب للبلاطات بشكل مفصل. حيث لوحظ - 16 )% للبلاطات المربعة و ( 6،4 - انخفاض واضح في مقاومة القص الثاقب بمقدار ( 0 0 م، ( 40،4 )% للنماذج الشبه منحرفة عند اعلى درجة حرارة تعرضت لها النماذج وهي ( 500وهذا يدل على ان مقاومة القص الثاقب للبلاطات المنتظمة الشكل اعلى منها للبلاطات الغير منتظمة الشكل.


Article
Properties of Fresh and Hardened High Strength Steel Fibres Reinforced Self-Compacted Concrete

Authors: Saad Ali Al-Ta'an --- Wail Nourildean Al-Rifaie --- Khalid Ahmed Al-Neimee
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2016 Volume: 23 Issue: 2 Pages: 29-37
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

Fresh and hardened properties of high strength steel fibrous self-compacted concrete were studied in this investigation. One reference high strength self-compacted concrete mix is used, with five percent (by weight of cement) silica fume and eight percent of the cement replaced by limestone powder. Three steel fibres percentages by volume of concrete are used (0.4, 0.8, and 1.2). The used steel fibres were a shelled Harex type with irregular cross-section, equivalent diameter of 0.9278 mm, and 32 mm long. Super plasticizer was used to improve the workability and flow ability of the mixes. The test results showed that the presence of steel fibres decrease the flow ability, and increase the time of spreading, segregation, and passing ability of the fresh concrete. For the fibres percentages used, the fresh properties were within the recommended specifications for the self-compacted concrete. The test results showed an early strength development rate more than that for plain normal concrete due to the presence of the fine materials. As for normal concrete, the test results showed also that the increase in the splitting strength is more than the increase in the compressive strength due to the presence of the steel fibres. The brittle mode of failure of the plain unreinforced specimens changed to a ductile one due to the presence of the steel fibres.


Article
Influence of Internal Sulfate Attack on Some Properties of Self Compacted Concrete
تأثير مهاجمة الاملاح الداخلية على بعض خواص الخرسانة ذاتية الرص

Author: Hadeel Khalid Awad Al-Obaidy هديل خالد عواد العبيدي
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2017 Volume: 23 Issue: 5 Pages: 27-46
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Self-compacted concrete (SCC) is a highly flowable concrete, with no segregation which can be spread into place by filling the structures framework and permeate the reinforcement without any compaction or mechanical consolidation ACI 237R-14. One of the most important problems faced by concrete industry in Iraq and Gulf Arab land is deterioration due to internal sulfate attack (ISA) that causes damage of concrete and consequently reduces its compressive strength, increases expansion and may lead to its cracking and destruction. The experimental program was focused to study two ordinary Portland cements with different chemical composition with (5, 10 and 15) % percentage of high reactivity metakaoline (HRM) as a cement replacement and with W/Cm ratio 0.35. The SCC mixes with AL Shemalia OPC cement that produced in Saudi Arabia (C3A=7.02%) shows higher resistance to ISA than mixes with Tasluja OPC cement that is produced in Iraq (C3A=4.13%). The results indicate that the SCC mixes containing 15% HRM shows higher opposition to ISA. A good correlation was obtained between concrete splitting tensile strength and compressive strength from the results of this study.

تعرف الخرسانة ذاتية الرص بأنها خرسانة ذات أنسيابية عالية بدون حصول أنعزال والتي بالامكان أنتشارها , و ملئ القالب و تغليف حديد التسليح بدون أي رص ميكانيكي حسب متطلبات الجمعية الامريكية 237R للعام 2014. تعد مهاجمة الاملاح الداخلية من أهم المشاكل التي تواجه صناعة الخرسانة في العراق واراضي الخليج العربي والتي تؤدي الى التدهور الذي يسبب تضرر الخرسانة ويؤدي بالنتيجة الى تقليل مقاومة الانضغاط , وزيادة التمدد والذي قد يؤدي الى تشققها و دمارها. البرنامج العملي لهذه الدراسة يبحث تأثير التركيب الكيميائي المختلف لإثنين من السمنت البورتلاندي الاعتيادي ,أضافة نسب من الميتاكاؤلين العالي الفعالية كأستبدال من وزن السمنت (5, 10 و 15)% ونسبة وزن ماء الى سمنت 0,35 .الخلطات الخرسانية ذاتية الرص المستخدم فيها السمنت الاعتيادي الشمالية المصنوع في المملكة العربية السعودية (C3A=7.02%) أظهرت مقاومة اعلى لمهاجمة الاملاح الداخلية مقارنة بالسمنت الاعتيادي طاسلوجة المصنوع في العراق (C3A=4.13%). النتائج تشير الى أن الخلطات الخرسانية ذاتية الرص الحاوية على 15% من الميتاكاؤلين العالي الفعالية اظهرت مقاومة اعلى لمهاجمة الاملاح الداخلية. وهناك علاقة بين نتائج مقاومة الانضغاط للخرسانة ومقاومة شد الانفلاق اوجدت من نتائج هذه الدراسة.

Listing 1 - 10 of 17 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (17)


Language

English (13)

Arabic (2)

Arabic and English (2)


Year
From To Submit

2019 (1)

2018 (2)

2017 (3)

2016 (5)

2015 (1)

More...