Article
Effect of Glass Powder on Some Mechanical Properties of Polymer Matrix Composite Material

Author: Bushra H. Musa
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2014 Volume: 17 Issue: 2 Pages: 108-115
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

This research deals with the study of the effect of adding glass powder of grain size (35μm) with different volume fraction (10%, 20%) to the blend of unsaturated polyester and polyurethane using hand lay-up method, after preparing the matrix from weight fraction (90%) of Unsaturated polyester and (10%) of polyurethane. The results have shown that the addition of particles to the polymer blends lead a great extent in mechanical properties, since testing bending, Shore D hardness and impact strength. It has shown that the values of young modulus, impact strength and hardness were increased with increasing of volume fraction of glass powder. Fracture surface of the samples were examined by using optical microscope with magnification (40 X) and the results showed that the nature of fracture is seems brittle fracture for all samples.

تم في هذا البحث دراسة تأثير إضافة مسحوق الزجاج وبحجـم حبيبـي ( 35) وبكسـور حجميـة مختلفـة(20% 10%,) إلى خليط من راتنج البولي استر غير المشبع والبولي يوريثان والتي أنجزت بواسطة طريقة القولبة اليدوية بعد أن تم تحضير المادة الأساس و بنسبة وزنية (%90( من البولي أستر الغير المشبع و%) 10( من البولي يوريثان. أظهرت لنتائج إن إضافة الدقائق إلى الخليط البوليمري حسن وبشكل كبير الخواص الميكانيكية، حيث تم إجراء اختبار الانحناء وصلادة شور D و مقاومة الصدمة، وقد اظهرت النتائج ان قيم معامل المرونة ومقاومة الصدمة والصلادة لخليط من راتنج البولي استر الغير مشبع والبولي يوريثان يزداد مع زيادة الكسر الحجمي لمسحوق الزجاج. ان سطوح الكسر لجميع العينات تم فحصها بواسطه المجهر البصري وبتكبير (40 X) و لقد أظهرت النتائج ان طبيعة الكسر هو كسر هش لجميع العينات.


Article
Effect of Bio-Fiber Waste Addition on Specifications of Epoxy Composite

Author: Bushra H. Musa
Journal: Iraqi Journal of Applied Physics المجلة العراقية للفيزياء التطبيقية ISSN: 18132065 23091673 Year: 2015 Volume: 11 Issue: 1 Pages: 21-24
Publisher: iraqi society for alternative and renewable energy sources and techniques الجمعية العراقية لمصادر وتقنيات الطاقة البديلة والمستجدة

Loading...
Loading...
Abstract

This study investigated the fabrication of composite from epoxy resin (EP) and waste short chicken feather fiber (CFF) at 5% volume fraction of fibers using hand lay-up method at room temperature. Some mechanical properties of the composite were determined including bending, shore D hardness and compressive strength. The process involved the treatment of the CFF with alkali solution, such as NaOH with 0.5 normality and then the effect of treatment on epoxy composite properties was studied. The results revealed that the addition of CFF to the epoxy resin has only a slight effect on the mechanical properties. It has shown that the values of Young modulus, compressive strength and hardness of EP/CFF composite were increased by the treatment of CFF with NaOH solution compared to pure epoxy and EP/CFF composite without treatment.


Article
The effect of UV – Radiation on Thermal and Mechanical Properties of (PP/LDPE) Blends
تأثير الاشعة فوق البنفسجية على الخصائص الحرارية والميكانيكية لخلائط (PP/LDPE)

Loading...
Loading...
Abstract

UV-rad effected on thermal and mechanical properties (density, Shore D hardness, melt flow index, DSC) properties were studied for polypropylene (PP) blended with low density polyethylene (LDPE) at different ratios (10% PP+90% LDPE), (25%PP+75%LDPE). Results shows decreasing of blend density with increasing of PP content and increasing of it after UV-RAD for (15 hr.), also Shore D hardness decreased at the first ratio of PP (10%) then it increased with increasing of PP contain. Also Shore D increases after UV rad for (15 hr.). Melt flow index (MFI) decreased after UV rad, also the UV rad leads to increasing of crystallinity regions of blends.

تم في هذا البحث دراسة تاثير اشعه UV على بعض الخواص الميكانيكية (شور D , الكثافة ) وكذلك على بعض الخواص الحرارية مثل معامل الانسياب الانصهاري وكذلك تحليل الخواص الحرارية من درجات الانصهار ودرجات التبلور باستخدام المسعر الحراري التفاضلي للبولي اثيلين واطئ الكثافة وخلائطه من البولي بروبلين(LDPE/PP) بنسب خلط مختلفة. اثبتت النتائج نقصان كثافه الخليط مع زياده محتوى البولي بروبلين، وكذلك نقصان كثافه الخليط بعد تعرضه لأشعة UV لمدة(15 hr) ، صلادة شور تقل بعد اول نسبه من الخلط (10%) PP ثم تبدا بالزيادة بزيادة محتوى البولي بروبلين، كما ان اشعة UV تؤدي الى زيادة صلادة شور ، معامل الانسياب الانصهاري يقل بعد تعرض الخليط الى اشعة UV ، كما لوحظ هناك تغير في مناطق ودرجات تبلور الخليط بعد التعرض لأشعة UV ، حيث لوحظ هناك زيادة في مناطق تبلور الخليط وزياده في درجات التفكك الحراري للخليط.

Keywords

LDPE blends --- Melt flow index --- UV rad --- shore D --- DSC


Article
Preparation and Characterization of PMMA-HDPE and HDPE-PMMA Binary Polymer Blends

Authors: S.I. Salih --- A.M. Al.gabban --- A.H. Abdalsalam
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2017 Volume: 35 Issue: 4 Part (A) Engineering Pages: 311-317
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

A comparison was made on the mechanical characteristics of binary blends polymethylmethacrylate/ high density polyethylene (PMMA-%HDPE) and vice versa. Analysis of morphology by SEM has been also accomplished. Preparation of polymer blends was performed using melt mixing method by an extruder. Tensile results showed that binary polymer blends (PMMA-%HDPE) indicated an increment in ultimate tensile strength, elastic modulus and shore D hardness compared to (HDPE-%PMMA). The blend of 95%PMMA- 5%HDPE shows superior mechanical properties. SEM results indicated that the prepared blends are not fully compatible with some separated phases of the second polymer dispersed in the matrix.


Article
Effect of Water on Some Mechanical Properties of Epoxy Blends Reinforced With Different Weight Fractions of Nano Titanium Oxide and Nano Silica
تأثير الغمر بالماء على بعض الخواص الميكانيكية لخلائط الايبوكسي المدعمة بكسور وزنية مختلفة من أوكسيد التيتانيوم النانوي والسيليكا النانوية

Author: Rana Mahdi Salih رنا مهدي صالح
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2017 Volume: 58 Issue: 3C Pages: 1675-1685
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Polymer composites were prepared using epoxy resin (EP) and unsaturated polyester (UPE) as a blend matrices, which were mixed together in different percentages (starting from 90:10) of (epoxy/polyester) respectively, and ending with (50:50) of (epoxy/polyester). The optimum mixing ratio (OMR) of the components was decided upon the results of the impact strength value of these blending ratio, which showed the highest value of (16.3) KJ/m2 for the blending ratio (80:20) of (EP/UPE) respectively. The blend with (OMR) was chosen to be reinforced with three different weight fractions of reinforcement; the 1st one was reinforced with nano titanium oxide (TiO2) with a weight fraction (2% wt.), the 2nd one was reinforced with both nano (TiO2) and surface modified nano silica particles (SiO2) with weight fractions (2% & 0.5%) respectively, and the 3rd one was reinforced with nano (TiO2) and surface modified (SiO2) with weight fractions (2% & 1%) respectively. The tested mechanical properties were (flexural strength, impact strength, hardness, and water uptake). Hand lay-up technique was used to prepare the samples, and a magnetic stirrer was used to ensure maximum homogeneity of the nano particles in the blend. All fabricated samples were exposed to water for 10 weeks to investigate the effect of nano powders addition on diffusivity and maximum water uptake, obvious degradation in mechanical properties of the composite consisting of (blend matrix/TiO2 reinforcement) and (blend matrix/TiO2+SiO2 reinforcement) were observed as a result of liquid uptake with less severe impact, but more effect on flexural strength and shore D hardness. Fick’s 2nd law was used to explain diffusion mechanism. All the results were discussed.

تم تحضير خليط بوليمري من مادتي الايبوكسي والبولي استر غير المشبع، حيث استعمل كمادة أساس لمادة متراكبة وحضرت منه 3 قوالب: تم تدعيم المادة المتراكبة الاولى بمادة اوكسيد التيتانيوم النانوية بكسر وزني (2%) وتم تدعيم القالب الثاني بأوكسيد التيتانيوم النانوي وبالسيليكا النانوية المعدلة سطحيا بكسر وزني (2% و 0.5%) على التوالي. اما القالب الثالث تم تدعيمه بأوكسيد التيتانيوم النانوي والسيليكا النانوية المعدلة سطحيا بكسر وزني (2% و1%) على التوالي. استعملت طريقة القولبة اليدوية لتحضير المادة، بمساعدة خلاط مغناطيسي لضمان الحصول على أكبر تجانس ممكن للدقائق النانوية في الخليط. تم بعدها اجراء الاختبارات الآتية على المادة المصنعة لمعرفة خواصها (اختبار متانة الانحناء، اختبار متانة الصدمة، اختبار الصلادة، تغير الوزن نتيجة الغمر بالماء). تم وضع العينات المصنعة جميعها في الماء لمدة 10 أسابيع لبيان مدى تأثير أضافة الدقائق النانوية على انتشارية الماء وتغير الوزن للمادة المصنعة بعد الغمر وتأثير ذلك على الخواص المدروسة. لوحظ تدهور الخواص المذكورة بعد الغمر للخليط المدعم بأوكسيد التيتانيوم والخليط المدعم بكلا من اوكسيد التيتانيوم النانوي والسيليكا النانوية، مع ملاحظة ان التأثير كان أكبر على متانة الانحناء وصلادة شور منه على متانة الصدمة. استخدم قانون فك الثاني لتوضيح ميكانيكية الانتشار. تم مناقشة جميع النتائج.


Article
Effect of Al2O3 Powder on Some Mechanical and Physical Properties for Unsaturated Polyester Resin Hybrid Composites Materials Reinforced by Carbon and Glass Fibers

Author: Reem Alaa Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 12 Part (A) Engineering Pages: 2371-2379
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research is a study of the effect of Al2O3 powder on physical and mechanical properties of the polymer hybrid composites based on unsaturated polyester resin reinforced with carbon and glass fibers. The samples were made by a hand lay-up method according to ASTM standard for various volume fractions of additives. The polymer composites materials reinforced with carbon and glass fibers are the most used in manufacture of components such as pip, part of aerospace, and leisure industries and automotive.The polyester resin matrixwas strengthened with 3% carbon and glass fibers with 1%, 3%, 5%, 7% Al2O3 powders. The water absorption, hardness (shore D), impact test, and flexural strength properties are studied. The results show the specimens (UP+3%C.F+7%Al2O3) and(UP+3%G.F+7%Al2O3) had the maximum hardness (shore D) and water absorptionwhen compared withunfilledpolyester resinspecimen, it can be observed that the specimens(UP+3%C.F+5%Al2O3) and (UP+3%G.F+5%Al2O3) have maximum impact strength and flexural strengthcompared with specimens (UP+3%C.F+7%Al2O3)and (UP+3%G.F+7%Al2O3) .


Article
Mechanical and physical properties of carbon nanotubes with Kevlar fiber reinforced with polyester resin
الخواص الميكانيكية و الفيزيائية لانابيب الكاربون النانوية مع الياف الكفلر المقواة مع راتنج البولي استر

Loading...
Loading...
Abstract

In this research study Hardness (shore D), Water absorption, Flexural, Impact Test, and Fracture Toughness of polymer nano composites.The polymer nano composites based on unsaturated polyester resin reinforced with Kevlar fibers (K.F). The samples are attended by hand lay – up method according to (Rule mixture) for various volume fractions of unsaturated polyester resin, fiber and carbon nanotube. The polyester resin was matrix strengthened with 3% volume fraction from Kevlar fiber and (0.5%, 1%, 1.5%, 2%( volume fractions of carbon nanotube. The water absorption, hardness (shore D), flexural test, impact testand toughness fracture properties were studied. Results showed that the water absorption increase with volume fraction increase of fiber with Carbon Nanotube, the sample (polyester+3%K.F+0.5% CNTs) has lower water absorption than other samples. The hardness (shore D), flexural test, impact testand toughness fracture for the sample (polyester+3%C.F+0.5% CNTs) has higher value for Nano- composites. Nano composites, Carbon nanotube, Kevlar fiber, Hardness (shore D), Water absorption, Flexural Strength, Impact Test, Toughness Fracture.

تم في هذا البحث دراسة الصلادة (شورD), امتصاصية الماء, مقاومة الكسر, اختبار الصدمة و متانة الكسر لمتراكبات نانوية ذات اساس راتنج البولي استر غير المشبع مقواة بألياف الكفلر. العينات جهزت بطريقة الصب اليدوي وفقالقاعدة الخلط لكسور حجمية مختلفة من راتنج البولي استر غير المشبع والالياف وانابيب الكاربون النانوية. راتنج البولي استر كان ارضية مقواة مع 3%كسر حجمي من الياف الكفلر و (0.5 ,1 ,1.5 , 2 ) % كسر حجمي لانابيب الكاربون النانوية. تم دراسة خواص امتصاصية الماء, صلادة (شور(D, اختبار الصدمة ومقاومة الكسر. اظهرت النتائج بان امتصاصيه الماء تزداد مع زيادة الكسر الحجمي للالياف مع انابيب الكاربون النانوية, العينه (بولي استر + 3% الياف كفلر + 0.5 % انابيب اكاربون النانوية) تمتلك اقل امتصاصية ماء من العينات الاخرى. الصلادة (شورD), فحص الكسر, فحص الصدمة ومتانة الكسر للعينه (بولي استر +3% الياف كفلر + 0.5 %انابيب الكاربون انانوية) تمتلك اعلى قيمه للمتراكبات النانوية.

Listing 1 - 7 of 7
Sort by
Narrow your search

Resource type

article (7)


Language

English (7)


Year
From To Submit

2017 (2)

2016 (3)

2015 (1)

2014 (1)