Article
Preparing Lightweight Aggregate for Production Lightweight Insulating Concrete
تحضير ركام خفيف لانتاج خرسانة خفيفة عازلة

Author: Mahmood. F. Abed محمود فاضل عبد
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2009 Volume: 14 Issue: 3 Pages: 194-200
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

This research dealt with preparing of lightweight aggregate by using local materials for manufacturing lightweight insulating concrete. Two materials were used, the first material was the Clay (Montmorillonite), and the other had ability to makes or leaves cavities or pores when subjects to heating which is Sodium Silicate. The mix of 40 % Montmorillonite and 60 % Sodium silicate burnt between 750- 800 centigrade showed good results in manufacturing lightweight clayey aggregate, the density of lightweight aggregate obtained was approximately (0.38 ) gm/cm3 comparison with density of normal aggregate between ( 2.55 – 2.65 ) gm/cm3 . The lightweight insulating concrete produced by using lightweight clayey aggregate had density about (700) kg/m3 and thermal conductivity about (0.296) watt/m.k .

تناول هذا البحث تصنيع ركام طيني خفيف الوزن لانتاج خرسانة خفيفة الوزن وعازلة للحرارة تلبية لحاجة القطر الملحة لمثل هذا النوع من المواد الانشائية.استخدمت مادتين في تصنيع الركام الطيني خفيف الوزن , المادة الاولى هي الطين (Clay ) حيث اختيرت أطيان المونتموريلونايت (Montmorillonite) لتمثل مادة الركام الصناعي الاساسية , اما المادة الثانية فهي مادة لها القابلية على ترك فجوات او فراغات في محلها عند تعرضها الى درجات حرارة معينة وهي سيليكات الصوديوم (Sodium Silicate ) .أظهر خليط اطيان المونتموريلونايت وسيليكات الصوديوم وبنسبة % 40 و % 60 على التوالي والمحروق بدرجة حرارة 750 – 800 درجة مئوية نتائج جيدة في مجال تصنيع الركام الخفيف حيث تراوحت كثافة الركام المحضر حوالي (0.38) غم/سم 3 مقارنة مع كثافة الركام الاعتيادي الذي تتراوح بين ( 2.55-2.65 ) غم /سم3 . تم استخدام الركام الطيني الخفيف المحضر بهذه الطريقة في انتاج خرسانة خفيفة الوزن وعازلة للحرارة بلغت كثافتها بحدود (700 ) كغم/م3 وموصولية حرارية بحدود (0.296) واط/م.ك .


Article
The influence of various pH values on the aerogel physical properties by sol-gel technique
تأثير قيم pH المختلفة على الخصائص الفيزيائية للأيروجل بواسطة تقنية سول-جل

Authors: Baha Fakhry shehab بهاء فخري شهاب --- Wesam A. A. Twej وسام عبد علي تويج
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2019 Volume: 17 Issue: 41 Pages: 75-81
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Hydrophobic silica aerogels were successfully preparation by an ambient pressure drying method from sodium silicate (Na2SiO3) with different pH values (5, 6, 7, 8, 9 and 10). In this study, acidic HCl (1M), a basic NH4OH (1M) were selected as a catalyst to perform the surface modification in a TMCS (trimethylchlorosilane) solution. The surface chemical modification of the aerogels was assured by the Fourier transform infrared (FTIR) spectroscopic studies. Other physical properties, such as pore volume and pore size and specific surface area were determined by Brunauer-Emmett- Teller (BET) method. The effect of pH values on the bulk density of aerogel. The sol–gel parameter pH value in the sol, have marked effects on the physical properties of the silica aerogels produced by this technique. The density and the hydrophobic tendency of the aerogels were significantly influenced.

تم تحضير سيليكا ايروجل بنجاح بواسطة طريقة تجفيف الضغط المحيط من سيليكات الصوديوم (Na2SiO3) مع قيم مختلفة من الدالة الحامضية pH(5، 6، 7، 8، 9 و10). في هذه الدراسة، قمنا باختيار حمض الهيدروكلوريك HCl(1M)، هيدروكسيد الأمونيوم NH4OH القاعدية (1M) كمحفزات، وقام بإجراء تعديل السطح بواسطة محلول TMCS (trimethylchlorosilane)، وتم تأكيد التعديل الكيميائي السطحي لعينات الايروجل بواسطة دراسة طيف تحويل فورير للأشعة تحت الحمراء ( FTIR). تم تحديد الخصائص الفيزيائية الأخرى، مثل حجم المسام ومساحة سطحه بواسطة طريقة بروناور-إيميت-تيلر (BET). تم إثبات تأثير قيم الأس الهيدروجيني على الكثافة الظاهرية لعينات الايروجل المعدة. إن قيمة الرقم الهيدروجيني لمعلمة sol-gel في sol، لها تأثيرات ملحوظة على الخواص الفيزيائية لعينات الايروجل التي تنتجها بهذه التقنية. كانت الكثافة والنزعة الكارهة للماء تتأثر بشكل كبير.


Article
USING LOCAL IRAQI MATERIALS IN PRODUCTION OF REFRACTORY BONDING MORTAR

Authors: Katreen E. Al Hwaidy --- Osama A. Eedan --- Shatha S. Hassan
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2018 Volume: 9 Issue: 2 Pages: 91-102
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

The Iraqi kaolin clay was used as a raw material in this research. three mix proportion was applied, (96:4), (93:7) and (90:10) as (kaolin grog: kaolin binding ). The specimens of mortar were burning at 1500ᵒC, after producing a refractory aggregate (grog) by preparation process mixing with sodium silicate solution as adhesive material with 5% by weight of the mix. The mechanical tests were carried (compressive and bonding) strength, durability investigations (thermal shrinkage, and reheating expansion), and the physical investigation was carried (bulk density, specific gravity, apparent porosity and water absorption). It was found the first mix (96:4) recorded the highest compressive strength befor burning and bonding after burning, and the best physical properties after burning at 1500 ºC, with mix proportion (96: 4), while the highest compressive strength after burning were the mix three (90: 10).


Article
دراسة أمكانية استخدام مادة سيليكات الصوديوم كمادة غروية رابطة بديلة للبولي فنيل أسيتيت في الأصباغ المائية المستحلبة

Authors: حسين شهيد فاضل --- بشير هاشم حليحل --- عبد الكريم عبد اللطيف علي
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2013 Volume: 21 Issue: 5 Pages: 1722-1727
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This includes research Empirical study replace poly vinyl acetate (P.V.A) as a binder material used in emulsion paints textured sodium silicate being manufactured locally and cheaply priced compared textured the P.V.A imported from abroad and prices are expensive. As it has been business model without binder material consists of water (solvent), additives, fillers and pigments was the work of three models of it for research purposes, ensure that the model (1) add P.V.A the proportions of 10%, 20%, 30% of the weight of the original model, while the form (2) added sodium silicate in the proportions 10%, 20%, 30% of the weight, while model (3) mixing model (1) with model (2) ratio of 1:1. Conducted laboratory tests conforming to the standard Iraqi No. 985 special with emulsion paints. The results of the research the possibility of using Article alternative surfaces of internal and external cement and blocks and steel sheets with high efficiency and resistance to rain monsoon and high stability of the climatic conditions changing grades temperature and humidity, and others. also demonstrated the possibility of using this paint against fire.

يتضمن هذا البحث دراسة تطبيقية باستبدال مادة البولي فنيل أسيتيت (P.V.A) المادة الرابطة المستخدمة في الأصباغ المائية المستحلبة (البنتلايت) بمادة سيليكات الصوديوم لكونها تصنع محليا و بأسعار رخيصة الثمن مقارنة بمادة ال P.V.A التي تستورد من الخارج و بأسعار غالية الثمن .إذ تم عمل نموذج بدون مادة غروية رابطة يتكون من الماء (المادة المذيبة) و المضافات المساعدة ثم مواد الحشو و المخضبات و تم عمل ثلاثة نماذج منه لأغراض البحث , تضمن النموذج (1) بإضافةP.V.A بنسب 10% , 20%,30% من وزن النموذج الأصلي, بينما النموذج (2) أضيفت سيليكات الصوديوم بنسب 10% , 20%,30% من وزن النموذج الأصلي ,في حين حضر النموذج (3) بخلط النموذج (1) مع النموذج 2)) بنسبة 1:1 . أجريت الفحوصات المختبرية المطابقة للمواصفة القياسية العراقية رقم 985 الخاصة بالأصباغ المائية المستحلبة وأظهرت نتائج البحث إمكانية استخدام المادة البديلة للأسطح الداخلية و الخارجية للأسمنت و البلوك و الصفائح الحديدية و المغلونة (الجينكو) و بكفاءة عالية و مقاومة للأمطار الموسمية و الثبات العالي للظروف المناخية المتغيرة من درجات الحرارة و الرطوبة و غيرها.كما بينت إمكانية استخدام هذا الصبغ (بالمادة البديلة ) ضد الحريق.


Article
Performance Evaluation of Modified Concrete Layer by Sodium Silicate in Rigid Highway Pavement
تقييم الأداء لطبقة الخرسانة المحسنة بسليكات الصوديوم في تبليط الطرق الجاسئة

Author: Fatimah Fahem Al-khafaji
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2015 Volume: 13 Issue: 1 Pages: 203-218
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

The using of conventional concrete mix in rigid pavement causes costly layer with high maintenance requirement . It is necessary to use additive materials in pavement construction as modifiers which could improves the performance of concrete layer . The major objective of this research is to evaluate the mixing a locally additive on performance of concrete layer in rigid pavement by using sulfate-resisting cement (type V) produced in Iraq . The additive represented by soluble Sodium Silicate also known as " water glass " .Concrete mixture specimen have been prepared with coarse aggregate of maximum size (50)mm and fine aggregate of maximum size (9.5)mm . Soluble Sodium Silicate has been used as an additive with the percentages (5 , 10 , 15) % by weight of cement . The performance of concrete mixture is evaluated using strength tests i.e (compressive and flexural) as well as thermal test (coefficient of thermal expansion) .Results of using such modified concrete mixture show that compressive strength and modulus of rupture are decreased by (1.14 , 1.06) time at 7 days and increased by (1.17 , 1.16) time at 28 days respectively as compared with control mix . The results of coefficient of thermal expansion are decreased by (1.12) times at 28 days when compared with control mix . However, percent of 10% soluble Sodium Silicate in concrete mix shows better performance of concrete pavement corresponding for both strength and thermal properties . This percentage was adopted for all above mentioned comparison . The use of modified concrete mix has significant effect on the thickness design and joint spacing of main layer in rigid pavement .

إن استخدام خلطات خرسانية تقليدية في التبليط الصلد يسبب طبقات مكلفة ذات متطلبات صيانة مرتفعة .اذا من الضروري استخدام مضافات تؤدي الى تطوير اداء الطبقات الخرسانية .ان الهدف الاساسي في البحث هو تقييم خلط مضاف محلي على اداء طبقات الخرسانة ضمن التبليط الصلد وباستخدام السمنت المقاوم للأملاح المنتج في العراق . والمضاف يمثل سليكات الصوديوم ويعرف ايضا ب " ماء الزجاج " . تم اعداد نماذج الخلطات الخرسانية بركام خشن ذو مقاس اقصى 50 ملم وركام ناعم ذو مقاس اقصى 9.5 ملم وتم استخدام سليكات الصوديوم بنسب (5 , 10 , 15 ) % من وزن السمنت . ان اداء الخلطات الخرسانية تم تقييمها بفحوصات المقاومة (الانضغاط والكسر) مع الفحص الحراري(معامل التمدد الحراري) .اظهرت نتائج مقاومة الانضغاط ومعايير الكسر عند استخدام الخلطات الخرسانية المعدلة نقصان بنسبة (1.06 ,(1.14 مرة بعمر 7 ايام وزيادة بنسبة (1.17 ,(1.16 مرة بعمر 28 يوم عند مقارنتها بالخلطات القياسية . ان نسبة 10 % سليكات الصوديوم في الخلطة الخرسانية اشرت اداء احسن لطبقة الرصف لكل من خواص المقاومة والحرارة . وعليه فان تلك النسبة قد اعتمدت لجميع انواع المقارنات المذكورة في اعلاه .ان استخدام الخلطات الخرسانيةالمعدلة له تاثيرفعال على تصميم السمك ومسافةالمفاصل في الطبقةالرئيسية للرصف الصلد .كلمات البحث : التبليط الصلد, سليكات الصوديوم , اضافة المضاف , فحص مقاومة الانضغاط , فحص مقاومة الانثناء , فحص معامل التمدد الحراري .


Article
Studying the Effect of Adding Sodium Silicate and Rock Wool to Concrete Mix on the Properties of Concrete
تأثير أضافة سيليكات الصوديوم والصوف الصخري للخلطة الخرسانية على خواص الخرسانة

Authors: Rami Joseph Aghajan رامي جوزيف أغاجان --- Duriad Fawzi Mahdi دريد فوزي مهدي
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2016 Volume: 12 Issue: 3 - part 1 Pages: 149-162
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

This research is studying effect of adding sodium silicate to water of concrete mix with ratios (2.5%, 3.75%, 5% and 6.25%) by the weight of water concrete mix. Also study effect adding rock wool to concrete mix with ratios (2.5%, 3.75%, 5% and 6.25%) by the weight of cement. After demolding the samples and curing in water 28 days and then dried in air to be ready to test. The samples tested compressive strength and tensile strength and density, the results show increase in compressive strength and tensile strength in ratios (2.5% rock wool and 3.75% of sodium silicate) compared to reference sample, and the density of samples decrease by increase the ratios of additives rock wool and sodium silicate to concrete mix.

تم في هذا البحث دراسة تأثير إضافة سيليكات الصوديوم الى ماء الخلطة الخرسانية بنسب وزنية مختلفة من وزن الماء ( 2.5 ،% 3.75 ،% 5 % و 6.25 %). كذلك تم دراسة تأثير أضافة الصوف الصخري الى الخلطة الخرسانية بنسب وزنية من وزن الإسمنت (2.5 ،% 3.75 ،% 5 % و 6.25%). بعد استخراج العينات من القوالب عولجت بالماء لمدة 28 يوم، بعدها جففت بالهواء لتكون جاهزة للفحص. فحصت قوة الإنضغاط والشد والكثافة للعينات، وأظهرت النتائج زيادة في قوة الأنضغاط والشد عند النسبة (2.5 % للصوف الصخري و 3.75 لسيليكات الصوديوم) مقارنة مع العينة الإعتيادية. إنخفضت الكثافة بزيادة نسبة إضافة الصوف الصخري وسيليكات الصوديوم للخلطة الخرسانية.


Article
Effect of bentonite addition on some properties of porcelain
تأثير أضافة البنتونايت على بعض الخصائص للبورسلين

Authors: Shahad Sarmed Abdull-Razzak شهد سرمد عبد الرزاق --- Shihab A. Zaidan شهاب احمد زيدان
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2019 Volume: 25 Issue: 1 Pages: 84-99
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Porcelain is one of the most important ceramic materials with a wide range of traditional and technical applications. Since most mixtures of porcelain have a high sintering temperature, bentonite has been added in this research to improve the characteristics of sintering and burning. The porcelain mixture consisted of the following Iraqi raw materials: 30% wt kaolin, 30 wt% non-plastic clay (grog), 10% wt sodium feldspar, 10 wt% potassium feldspar and 20 wt% flint. After the mechanical mixing process and transfer the powder mixture to the slurry by adding distilled water, then different weight percentage of the sodium bentonite(0, 2.5, 5, 7.5 and 10) wt% was added. The specimens were prepared by using the solid casting method, and after the drying process, the specimens were burned at1100 oC. The results of x-ray diffraction showed that bentonite reduced the crystallization of the main ceramic phases (mullite, quartz), which stimulates the appearance of amorphous glass phases. Also, the loss of mass on ignition increased when the addition of bentonite from 5.66% to 8.2%. There was also a great convergence between the granules of porcelain when adding bentonite and thus increase the shrinkage of the dimensions from 9.33% to 12.37 %. This led to increasing the bulk density from 1.97 g/cm3 to 2.67 g/cm3 at firing temperature 1100oC, and the porosity was decreased from 17.1% to 1.44%. Diametrical strength and flexural strength (bending) increased with bentonite (14.88 to 34.46MPa), (6.2 to 8.65 MPa), respectively.

يعتبر البورسلين من أهم المواد السيراميكية التي تتميز بمدى واسع من التطبيقات التقليدية والتقنية .ولأن معظم خلطات البورسلين ذات درجات حرارية مرتفعة فقد تم في هذا البحث أضافة البنتونايت لتحسين خصائص التلبيد والحرق.تألفت خلطة البورسلين من الخامات العراقية التالية (%wt 30 كاؤلين و %wt 30 طين محروق و % wt 10 فلدسبار الصوديوم و %wt 10 فلدسبار البوتاسيوم و %wt 20 فلنت) وبعد اجراء عملية الخلط الميكانيكي وتحويل المساحيق الى عالق بأضافة الماء المقطر تم أضافة نسب مختلفة من البنتونايت الصوديومي (wt% 0,2.5,5,7.5,10) وتمت عمليه تشكيل العينات بطريقة الصب الصلب.وحرقت العينات في درجة حرارةoC 1100. أما نتائج حيود الاشعة السينية فقد اوضحت ان البنتونايت قلل من تبلور الاطوار السيراميكية الرئيسية ( المولايت والكوارتز) , حيث ان الكوارتز يعمل على تحفيز ظهور الاطوار الزجاجية العشوائية . كذلك ويسبب الفقدان الكبير في الكتلة للبنتونايت فقد ازداد الفقدان في الكتلة عند اضافة البنتونايت من % 5.66 الى % 8.2 . كذلك حصل تقارب كبير بين حبيبات البورسلين عند اضافة البنتونايت وبالتالي زيادة الانكماش في الابعاد من % 9.33 الى %12.37 وانعكس ذلك على زيادة الكثافة من g/cm31.97 الى g/cm32.67 عند الحرق بدرجة حرارة oC 1100 .اما المسامية فقد تناقصت بشكل واضح وكبير من %17.1 الى % 1.44.اما مقاومةالكسرالمحوري والانحناء ازدادت مع زيادة نسبة البنتونايت ( MPa 34.46-14.88) و(6.2 - 8.65 Mpa) على التوالي.

Listing 1 - 7 of 7
Sort by
Narrow your search

Resource type

article (7)


Language

English (5)

Arabic (1)


Year
From To Submit

2019 (2)

2018 (1)

2016 (1)

2015 (1)

2013 (1)

More...