Solvothermal Synthesis and Characterization of Indium Oxid Nanoparticles
دراسة الخصائص لأوكسيد الأنديوم النانوية

Authors: Rashed T. Rasheed راشد طالب رشيد --- Saryia D. Al-Algawi سارية ذياب العلكاوي --- Layla A. Jaffer ليلى علي جعفر
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2016 Volume: 57 Issue: 4C Pages: 2880-2889
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this study, In2O3 was prepared by Solvothermal technique in autoclave device, which is a simple and inexpensive technique to indicate the best condition. The reaction took place between indium chloride and urea. In(OH)3 as-prepared annealing at 100°C and convert to In2O3 at annealing temperatures 300, 500, 700 °C for 90 min .The physical properties of nanoparticles were characterized by XRD, SEM, AFM, UV/Visible and FTIR spectroscopy measurements. The examination results of XRD for In2O3 powder annealed at different temperature showed the formation of a cubic phase of nanoparticles with high intensity of plane (222). The lattice constant decreases with the increase of annealing temperature (from 10.07 to 10.04 Ǻ). AFM indicated an increase in grain size of In2O3 with increasing of annealing temperatures (from 78.59 to 94.4 nm). The optical properties, transmittance of In2O3 nanoparticles at annealing temperatures 500°C have a high transparent reach to (89%) and Energy gap Increases with increasing annealing temperature in range (3.6 to 4.65 eV).

في هذا البحث، تم تحضير اوكسيد الانديوم بتقنية الضغط الحراري باستخدام جهاز الأوتكليف ، وهي تقنية سهلة ورخيصة للحصول على افضل تفاعل بين كلوريد الانديوم و اليوريا. تم تحويل هايدروكسيد الانديوم الملدن بدرجة حراره 100م° الى اوكسيد الانديوم عند درجات الحراره 300, 500, 700م° لفتره 90 دقيقة. شخصت الخواص الفيزيائية للجسيمات النانوية بواسطة قياسات حيود الأشعة السينيه , المجهر الألكتروني الماسح مجهر القوة الذرية، الأشعة فوق البنفسجية/المرئية و مطيافية الأشعة تحت الحمراء. اظهرت نتائج فحص حيود الأشعة السينية للجسيمات الملدنة عند الدرجات الحرارية المختلفة الى تكون الطور المكعبي للتركيب البلوري لأوكسيد الأنديوم مع ظهور شدة عالية للقمة (222) وتبين ان ثابت الشبيكة يقل بزيادة درجة حرارة التلدين (من 10.07الى 10.04 انكستروم). بينت نتائج فحوصات مجهرالقوة الذرية هناك زيادة في الحجم الحبيبي لاوكسيد الانديوم (من78.59 الى 94.4 نانومتر) مع زيادة درجة حرارة التلدين.اضهرت الخصائص البصرية ان اوكسيد الانديوم النانوي انة يمتلك نفاذية عالية تصل الى (%89) عند درجة تلدين (500 م◦) و زيادة فجوات الطاقة مع زيادة درجات حرارة التلدين لتتراوح (3.6-4.65 الكترون فولت).


Article
Determine the Structural and Optical Properties of ZnO Nanoparticles Prepared by Hydrothermal Method
تحديد الخواص التركيبية والبصرية لجسيمات اوكسيد الزنك النانوية المحضرة باستخدام طريقة Solvothermal

Authors: Dunia K.M.Al-Nasrawy --- Mohammed H.K.AL-Mamoori, --- Ahmed.K.Kodeary
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2015 Volume: 13 Issue: 3 Pages: 236-244
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

In this work ,zinc oxide nanoparticles(powder) with diameter 12.1 nm was prepared using Solvothermal Method. The structural and optical properties of ZnO nanoparticles was studied by X-ray diffraction, atomic force microscopy AFM, EDS, FTIR, UV-Visible absorption spectroscopy and Flourometer spectrum. X-ray diffraction reveal the formation the purity of prepared phase of ZnO particles with hexagonal wurtzite structure . The energy dispersion scattering ( EDS) examination explains the ZnO nanoparticle is purity. The Atomic Force Microscopy ( AFM) shows the spherical shape of nanoparticles with diameter around 60 nm. The optical absorption spectral study identified the blue shift of the sample in comparison to bulk ZnO in three dimensions . fluorescence spectrum at room temperature confirms the strong UV emission around 397 nm and its indicate that the zinc oxide nanoparticles is a purity and don’t contain on a defects.

في هذا البحث ،جسيمات اوكسيد الزنك (باودر) بقطر 12.1 نانومتر حضرت باستخدام طريقة Solvothermal . الخواص التركيبية والبصرية لجسيمات اوكسيد الزنك النانوية المحضرة درست بواسطة حيود الاشعة السينية X-ray Diffraction ، ومطياف القوة الذرية AFM، EDS،FTIR ،UV-Visible absorption spectrophotometer وجهاز قياس طيف الفلورة Fluorescence Flourometer .حيود الاشعة السينية اظهرت ان جسيمات اوكسيد الزنك النانوية المحضرة تكون نقية و ذات تركيب (wurtzite ) السداسي .فحص (EDS) energy dispersion scattering اظهر ان جسيمات اوكسيد الزنك النانوية هي نقية ايضا وخالية من الشوائب .كذلك قياسAtomic Force Microscopy ( AFM) بين ان جسيمات اوكسيد الزنك النانوية ذات شكل كروي بقطر 60 نانومتر .دراسة طيف الامتصاص البصري للجسيمات النانوية بينت وجود ازاحة زرقاء blue shift بالمقارنة مع اوكسيد الزنك الاساسي في ثلاث ابعاد (bulk zinc oxide (.طيف الفلورة عند درجة حرارة الغرفة اظهر انبعاث قوي عند المنطقة فوق البنفسجية ( ( UV-regionحول 397 نانومتروهذا يشير الى ان جسيمات اوكسيد الزنك النانوية المحضرة هي نقية وغير محتوية على شوائب.