Spot Welding Residual Stresses Assessment Using Nonlinear Numerical Technique

Authors: Faiz F. Mustafa --- Somer M. Nacy --- Nabeel K. Alsahib
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2008 Volume: 14 Issue: 1 Pages: 2202-2215
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

A description is given of the resistance spot welding process in terms of internal behavior of the weld as welding takes place. Heat input due to spot welding of steel sheet plate causes temperature gradient in the parent metal. After cooling, residual stresses appear around the welding zone reducing the strength. Residual stresses are a result of the temperature gradient and the dependency of material properties on the temperature, such as yield strength, elasticity modulus, and thermal expansion coefficient. Nonlinear transient heat transfer analysis performed in order to obtain the temperature distribution in the welded part .A nonlinear thermo–plastic stress analysis is then performed to predict the stress and strain fields during and after welding. The material properties such as yield strength, elasticity modulus, convection coefficient, conduction, specific heat, and thermal expansion coefficient are used as a function of temperature. The heat transfer results are compared with experimental results performed within the scope of work of this study. On the other hand, the residual stress results are compared with experimental result obtained from literature .The comparison shows good agreement between numerical and experimental results.

يقدم البحث وصف دقيق لعملية اللحام النقطي على اساس التغيرات الداخليه الحاصله في المعدن أثناء وبعد عملية اللحام, حيث اعتمدت طريقة رقمية لاخطية معتمدة على العناصر المحددة يمكن من خلالها تعيين درجات الحرارة الناجمة عن عملية اللحام النقطي وتغييرها مع المسافة والزمن (( انتقال الحرارة اللاخطي والمعتمد على التغيير مع الزمن )) ومن ثم يمكن بأستخدام طريقة العناصر المحددة اللاخطية (( اللدونة الحرارية )) لتعيين الأجهادات المتبقية في الجزء الملحوم وما حوله بعد عملية التبريد. ان الاجهادات المتبقيه تظهر نتيجة لتغير درجات الحراره وما يصاحبها من تغير في خواص المعدن مثل مقاومة الخضوع, حد المرونه, معامل التمدد الحراري ومعامل التوصيل والحمل مع التغير في درجات الحرارة, ولقد تم اجراء تجارب لقياس درجات الحرارة للجزء الملحوم أثناء وبعد عملية اللحام في اجزاء وأزمنة مختلفة لمقارنتها بالنتائج الرقمية ، وتم الأعتماد على تجارب لقياس الأجهادات المتبقية أجريت في أبحاث أخرى للمقارنة حيث ظهر صلاحية الطرق الرقمية بكفاءة عالية وخاصة لتعيين درجات الحرارة وذلك نتيجة دقة التمثيل الرقمي في وصف وتغيرها مع الحرارة ووصف الظروف المحيطة سواء التمثيل الحراري أو الأجهادات.


Article
OPTIMIZING THE PROCESS OF RESISTANCE SPOT WELDING FOR 2014 – O ALUMINUM ALLOY SHEET
الاختيار الأفضل لمتغيرات لحام المقاومة النقطي لالواح سبيكة الالمنيوم 2014-O

Author: Latfe Y. Zedan لطفي يوسف زيدان
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2008 Volume: 1 Issue: 1 Pages: 46-55
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

There is a strong interest in the use of aluminum alloy sheet for vehicle applications, particularly the body, where resistance spot welding is the principle joining method. The resistance spot welding (R.S.W) quality has a great effected by the process variable such as, welding current, welding time, and electrode pressure beside other variable such as material thickness and type and electrode diameter. In this work the effect of process variable on welding quality was investigated. Trials were conducted on 1.2 mm thick 2014 – O aluminum alloy sheet. The tensile shear strength was used as primary index of welds quality. Experimental investigation show that the best current is 45 KA, best time is 10 cycle, and electrode pressure of 3 KN .

هناك رغبة قوية في استخدام صفائح سبائك الالمنيوم في تطبيقات السيارات وخصوصا البدن حيث ان طريقة الربط الرئيسية هي طريقة اللحام النقطي .إن لحام المقاومة النقطي يتاثر بشكل كبير بمتغيرات عملية اللحام مثل التيار , زمن اللحام وضغط القطب بالاضافة الى متغيرات اخرى مثل سمك المعدن ونوعه وقطر القطب .في هذا العمل تم دراسة تاثير متغيرات اللحام النقطي على جودة اللحام .تم استخدام سبيكة الالمنيوم 2014-O وبسمك 1.2 ملم .استخدمت مقاومة القص كمؤشر على جودة اللحام . نتائج الدراسة العملية اظهرت ان افضل تيار لحام هو ( 45 ) كيلو امبير , وزمن لحام ( 10 ) دورة وضغط قطب ( 3 ) كيلو نيوتن .


Article
Effects of Fusion Zone Size on Failure Modes and Mechanical Performance of Dual Phase (DP600) Steel Sheets Spot Welds.

Authors: Fadhel A. Hashim --- Raid K. Salim --- Hassanen L. Jaber
Journal: Thi-Qar University Journal for Engineering Sciences مجلة جامعة ذي قار للعلوم الهندسية ISSN: 20759746 Year: 2013 Volume: 4 Issue: 3 Pages: 47-61
Publisher: Thi-Qar University جامعة ذي قار

Loading...
Loading...
Abstract

This paper examines the effects of fusion zone size on failure modes, quasi tension -shear test and energy absorption of resistance spot welds (RSW) of dual phase (DP600) steels. Optical microscopy was used for microstructure investigation. The results showed that some samples failed in pullout failure mode and other samples failed in interfacial failure mode and the failure was located at the base metal. The conventional weld size guidance of 4t0.5 and 5t0.5is not sufficient to produce nugget pullout failure mode for DP600 resistance spot welds.

يهدف البحث الى دراسة تأثير حجم منطقة اللحام والتركيب المجهري للوصلات الناتجة من لحام المقاومة النقطي لفولاذ ثنائي الطور و شكل الفشل لهذه الوصلات, تم استخدام المجهر الالكتروني الماسح في دراسة التراكيب المجهرية في حين استخدام اختبار الشد-القص لدراسة الخواص الميكانيكية و تحديد نوع او شكل الفشل.بينت النتائج ان التركيب المجهري لمنطقة الانصهار عباره عن مارتنسايت بقيمة صلاده قدرها 450 فيكرز, اما المنطقة المتأثرة بالحرارة فهي عبارة عن فوق الحرجة و تركيبها مارتنسايت صلادته 420 فيكرز والمنطقة ما بين الحرجة بتركيب مارتنسايتي-فرايتي لتنخفض صلادتها الى 310 فيكرز, كذلك بينت النتائج ان نوع (شكل) الفشل يعتمد على مقدار التيار المستخدم حيث ان الفشل يتحول من بيني الى انجراري (انسحابي) عند قيمة تيار قدرها 8,5.