Resistance of High-Volume Fly Ash SelfCompacting Concrete to Internal Sulfate Attack

Authors: Tareq S. al-Attar --- Ahmed A. Taha
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 12 Part (A) Engineering Pages: 1260-1266
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This paper investigates the durability of high-volume Fly ash selfcompactingconcrete, HVFASCC that exposed to internal sulfate attack. At thepresent work, HVFASCC was produced with two Fly ash replacements: 50 and60% by weight of Portland cement. The internal sulfate attack was simulated byadding natural gypsum (CaSO4) that contain ion (SO3-2) to fine aggregate bytwo weight percentages: 1 and 2%. Limestone dust was used as filler with acontent of 100 kg/m3. The cementitious materials, cement and Fly ash, contentwas 400 kg/m3 and the water to powder ratio for the studied mixes was 0.34 byweight. To ensure the self-compact ability of the mixes, slump flow, T500, Vfunneland L-box tests were done. The Compressive, Splitting and Flexuralstrength Tests were extended to the age of 240 days. The results showed thatthere is no significant difference between 1 and 2% of SO3 content on thebehavior of all mixes. The presence of limestone powder in the paste solutioncould have a role in stabilizing ettringite and reducing paste porosity at earlyages. At later age, 240 days, the harmful effect of SO3 is diminished and thatmay be caused by the depletion of gypsum and the dominant product will becalcium monosulfoluminate hydrates instead of calcium sulfoaluminatehydrates


Article
EFFECT OF SULFATES IN FINE AGGREGATE ON SOME PROPERTIES OF SELF COMPACTING CONCRETE INCORPORATING HIGH REACTIVE METAKAOLINE

Loading...
Loading...
Abstract

Fine aggregate contaminated with interior sulfates is an important problem of concretemanufacture in Iraq. It is difficult to obtain well graded fine aggregate with sulfates content withinstandard specifications. The main objective of this study is to investigate the effect of internalsulfates in sand on some properties of self compacting concrete (SCC) by adding natural gypsum tofine aggregate as a partial replacement by weight. In this work, two basic categories of selfcompactingconcrete are used: (SCC) incorporating limestone powder (LSP) and SCCincorporating 10% high reactivity metakaolin (HRM) Class N plus limestone powder(LSP) .Fourlevels of sulfates contents in fine aggregate were investigated, these levels were ( 0.37, 0.5, 1.0,and 1.5)% which it is equal to(3.74, 3.99, 4.96 and 5.93)% by weight of cement for mixescontained limestone powder (LSP) and it is equal to (3.76, 4.01,4.98 and 5.96) % by weight ofcement for mixes contains high reactivity metakaolin (HRM) Class N plus limestonepowder(LSP). The experimental program is divided into two parts; the first part is devoted toproduce self compacting concrete by using superplasticizers and fillers then determine theworkability. Different test methods are adopted such as slump flow and T50 cm, V-funnel, VFunnelat T5 minutes, L-box and sieve segregation test. The second part is devoted to study themechanical properties such as the compressive strength and splitting tensile strength. The resultsobtained from this work show that the optimum gypsum content was 0.5% by weight of fineaggregate for all mixes which gives increases in the compressive strength by a range(5.9 -10.1)%and in the splitting tensile strength by a range (1.2 – 8.5 )% for mixes of (SSC) with (LSP) and(LSP +HRM).

إن وجود أملاح الكبريتات الداخلية هي من المشاكل المهمة التي تواجه صناعة الخرسانة في العراق. فمن ألصعوبة أيجاد ركام ناعم مطابق للمواصفات مع حدود المواصفات الحالية لحدود أملاح الكبريتات . ألهدف من هذا العمل هو دراسة تأثير أملاح الكبريتات في الركام الناعم على بعض الخواص الميكانيكية للخرسانة ذاتية الرص بإضافة الجبس الطبيعي إلى الركام الناعم كإحلال جزئي من وزنه. في هذا البحث تم استعمال نوعين أساسين من الخرسانة ذاتية الرص وهي : خرسانة ذاتية الرص حاوية على مسحوق الحجر الجيري و خرسانة ذاتية الرص حاوية على 10% ميتاكاؤلين عالي الفعالية و مسحوق الحجر الجيري تم دراسة أربع نسب لمحتوى الكبريتات (0.37, 0.5, 1.0, and 1.5)%. في الركام الناعم والذي يساوي (3.74,3.99,4.96,5.93)% من وزن الإسمنت للخلطات التي تحوي على الحجر الجيري كمادة مالئة ومساوي إلى(3.76, 4.01 ,4.98 and 5.96) % من وزن السمنت للخلطات التي تحوي 10% ميتاكاؤلين عالي الفعالية و مسحوق الحجر الجيري . برنامج ألعمل يقسم إلى جزأين ; ألجزء الأول هو أنتاج خرسانة ذاتية الرص باستعمال الملدنات و المادة المالئة ثم أيجاد قابلية التشغيل . تم استخدام طرق فحص مختلفة مثل فحص جريان الهطول, القمع على شكل حرف V, القمع على شكل حرف Vبعد مرور 5 دقائق , الصندوق على شكل حرف L فحص مقاومة الانعزال. ألجزء الثاني هو دراسةالخواص الميكانيكية مثل مقاومة الانضغاط و مقاومة شد الانشطار. أظهرت النتائج إن محتوى الجبس الأمثل في الخرسانة ذاتية الرص عند نسبة 0.5 % من وزن ألركام الناعم لكل الخلطات والتي تعطي زيادة في مقاومة الانضغاط تراوحت بين (5.9-10.1 )% و( 1.2- 8.5)% في مقاومة شد الانشطار. الزيادة الإضافية في محتوى الكبريتات بعد ألنسبة المثلى يسبب تناقص في المقاومة تتراوح بين ( 1.4 – 7.8 )% في مقاومة الانضغاط و ( 2.1- 3.3)% في مقاومة شد الانشطار عندما تزداد نسبة الكبريتات في الركام الناعم من (0.37 – 1 %(و (6.4- 9.9)% في مقاومة الانضغاط و (3.8-5.6 ) % في مقاومة شد الانشطار عندما تزداد نسبة الكبريتات في الركام الناعم من (0.37 – 1.5) % على التوالي.