Article
The Effect of PVP Addition on the Mechanical Properties Of [84%LLDPE: 15 %(( 100- X) %PP: X%PVP):1%Basalt Particle] Polymer Blend Composites.
دراسة تأثير أضافة (PVP) على الخواص الميكانيكيه للخليط البوليمري المتراكب: [84%LLDPE:15%((100-X)%PP:X%PVP):1%basalt particle]

Authors: Teeb A. Mohammed --- Akram R. Jabur --- Sihama E. salih
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 3 Part (A) Engineering Pages: 573-585
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Polymer blends composites were prepared according to the formula [84%LLDPE:15%((100-X)%PP:X%PVP):1%B.P] with weight ratios selected for X values (0,4,8,12,16 %), as strips by double screw extruder and use press process the strips to prepare the samples according ASTM specification, the mechanical properties were studied for all theprepared samples which are (tensile, flexural, compression, impact, hardness, and creep tests). The results are as following:- results showed increment of mechanical properties as PVP ratio increases except elongation, furthermore the results recorded highest values of fracture strength, young modulus, compressive strength, flexural strength, maximum shear stress, flexural modulus and creep modulus at PVP 8% wt. which are (31.32MPa, 0.14GPa, 27.4MPa,24MPa, 0.6MPa, 1.08GPa and 0.558GPa) respectively.While the highest values of fracture toughness and hardness recorded at 12% wt. (1.4696Pa√m), and at 4% wt. (56.5) respectively.

حضرت المتراكبات ذات أساس الخليط البوليمري الثلاثي, وفق الصيغة [84%LLDPE:15%((100-X)%PP:X%PVP):1%B.P] وبنسب وزنية مختارة لقيم x 16,12 ,8 ,4 ,0) %). وقد تم تحضيرها بشكل شرائط حضرت بعملية البثق بواسطة باثقة ثنائية اللولب واستخدمت عملية كبس الاشرطة لتحضير العينات وفق المواصفة القياسية (ASTM) , درست الفحوصات الميكانيكية للعينات المحضرة والمتمثلة ( فحص الشد والانحناء والانضغاط والصدمة والصلادة والزحف) أظهرت النتائج زيادة في الخصائص الميكانيكية مع زيادة نسبة PVP باستثناء المطيلية وعلاوة على ذلك سجلت النتائج أعلى قيم لمقاومة الشد, معامل الرونة, مقاومة الانضغاط ومقاوة الانحناء واعلى أجهاد قص ومعامل مرونة الانحناء ومعامل الزحف عند نسبة (8% wt) PVPوهي على الترتيب (31.32MPa , 0.14GPa , 0.6MPa , 27.4MPa , ( 0.558GPa , 1.08Gpaفي حين سجلت أعلى قيم لمتانة الصدمة وقيم الصلادة عند نسبةPVP 12% wt.)) (1.696 Pa√m) و 4%wt ((56.5 على الترتيب .


Article
Experimental Investigation and Mathematical Modeling of Tensile Properties of Unsaturated Polyester Reinforced by Woven Glass Fibers
التقصي العملي والنمذجه الرياضيه لخصائص الشد للبولي استر الغير مشبع المقوى بالياف الزجاج الحصيرية

Authors: Jawad Kadhim Oleiwi --- Emad Saadi Al- Hassani --- Alaa Abd Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 3 Part (A) Engineering Pages: 653-666
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research studied the tensile properties of glass fiber reinforced unsaturated polyester with different fiber volume fraction Vf, and angle of fibers for coarse and fine woven fibers reinforcement. The composite specimens were prepared by hand lay-up technique and cutting according to (ASTM D – 638) for tensile test to obtain modulus of elasticity, ultimate tensile strength and elongation percentage of the composite specimens. Mathematical models were done by using statistical analysis which shows the tensile properties of the composite specimens as a function of volume fraction and fiber angle.The results show that the maximum value of the modulus of elasticity was (11.5 GPA) and the maximum value of ultimate tensile strength was (240 MPa) which happed at (11% VF) for fine woven fibers and for (0º/90º) fibers angle, and vice versa for percentage elongation was (2.5%).

في هذا البحث تم دراسة خواص الشد للبولي استر غير مشبع مقوى بالياف الزجاج عند تغير كل من الكسر الحجمي وزاوية الليف لنوعين من التقوية الحصيرة الخشنه والناعمه. حضرت العينات المركبة بالطريقة اليدوية وقطعت وفق المواصفه (ASTM D – 638) لفحص الشد للحصول على معامل المرونة واقصى أجهاد شد والاستطالة النسبية لهذه العينات. تم عمل نماذج رياضية باستخدام التحليل الأحصائي الذي يبين خواص الشد كدالة لكسر الحجمي وزاوية الليف. بينت النتائج بان اقصى قيمة لمعامل المرونة كانت(11.5 GPa) واقصى اجهاد شد كان(240 MPa) يحصلان عند الكسر حجمي (11%) عند التقوية بالحصيرة الناعمة ولزاوية ليف (0º/90º) والعكس بالعكس للاستطاله النسبية حيث كانت 2.5%) ).


Article
Effect of Laser Surface Treatment on Mechanical Properties of CK45 Steel

Authors: Sabah N. mahmood --- Khansaa Dawood Selman
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 8 Pages: 1610-1618
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The research aims to study the effect of laser surface treatment on mechanical properties of CK45 steel which is widely used in Bolts, Axles Various,Connecting Rods and Hydraulic clamps. Trails of laser hardening were carried out by using CW Nd: YAG laser with different powers 2.7, 3.3, and 4.3 Watt. Mechanical tests were done for the specimens who were used in the research before and after treated by laser such as: Tensile test, Micro hardness. Also grain size measurement and microstructural evaluation were done by usingcomputerized optical microscope. The results show that improvement inmechanical properties at laser power 4.3 watt obviously when compared with other laser powers. From tensile test we show that increasing in yield strength, ultimate tensile strength Poisson's ratio and plasticity constant (k). Also decreasing in Young modulus, Rigidity of modulus and strain hardening coefficient (n). While microhardness results show that the highest value was obtained at laser with 4.3watt power and decreased far from the surface. Metallographic of the specimen show that refining in grains size after the treatment with laser.


Article
Mechanical properties of carbon nanotube reinforced Epoxy Resin composites
الخواص الميكانيكية لمتراكبات أنابيب الكاربون النانومترية المدعمة لراتنج الايبوكسي

Author: Sinaa I.Husaen سيناء ابراهيم حسين
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2012 Volume: 9 Issue: 2 Pages: 330-334
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Overlapped have been prepared from epoxy resin material added to carbon Nanotube and percentages weight (0.1, 0.05, 0.01) % Studied the mechanical properties of the composite (bending, tensile and hardness) has been found that the Flexural and tensile modulus of the composites were higher than the pure epoxy resin this may be due to the high mechanical strength of carbon nano tube (CNT). The hardness of the epoxy carbon Nanotube composites increased and the reason is due to increased overlap and stacking between the additives and material basis, which reduces the movement of polymer molecules leading to increased resistance to scratching material and cutting, will become more resistance to plastic deformation.

تم تحضير متراكب من مادة راتنج الايبوكسي مضاف اليه الكاربون النانومتري وبنسب وزنية (0.1,0.05,0.01)%درست الخواص الميكانيكية للمتراكبات ( الانثناءو الشد و الصلادة) وقد وجد ان مرونة الانثناء ومعامل مرونة الشد لمتراكب ايبوكسي كاربون نانومتري اعلى من راتنج الايبوكسي النقي بسبب وجود الكاربون النانومتري ذي الخواص الميكانيكية العالية .ان الصلادة لمتراكبات الايبوكسي الكاربون النانومتري ازدادت والسبب يعود الى زيادة التشابك وا لتراص بين المادة الاساس والمضاف اليه الذي يقلل من حركة جزيئات البوليمر مما يؤدي الى زيادة مقاومة المادة الى الخدش والقطع فتزداد مقاومتها للتشوه اللدن .


Article
دراسة اختباري الشد والكلال لمادة الايبوكسي ومتراكباتها الهجينية

Author: رغد حامد هلال / مدرس
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2013 Volume: 13 Issue: 1 Pages: 144-152
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This research is concerned the use of Epoxy resin( Cy223 ,Hy956 )which supplied from (Giba –Giegy) German company .It is a viscause liquid have a certain properties like high adhesives and low shrinkage at dry condition with addition of the hardener at ratio (1:3 ) of the resin with density about (1150 kg/m3 ) , the matrix resin forced with two type of fibers : glass fiber( E-glass) and carbon fiber (HS )(High Strength) ,the ratio of carbon fiber layers to glass fiber layers is (1:5) with volume fraction (30%) at room temperature to study tensile and fatigue tests. It is noted that the composite materials appears better resistance to the tensile test than the resin due to the resistance of fiber(especially carbon fiber which have a good mechanical properties ) .In the fatigue test , the composite material show good strength to break because of the resistance of carbon fiber at low cycle . The resistance to break remains constant or changed slowly with increasing cycle of fatigue strength depending on supporting ratio.

تم في هذا البحث استخدام راتنج الايبوكسي (HY956 , CY223 ) [Digly Cidyle ether of Bipherio ADGEBA CY 223 ] المجهز من شركة (Giba –Giegy ) الالمانية وهو سائل لزج ذو مواصفات معينة ومنها قابلية التصاق عالية ،أضافة الى قلة الانكماش عند الجفاف ،أما المصلد المستخدم فهو HY956 ، يضاف المصلد الى الراتنج بنسبة ( 1 : 3 )، أما الراتنج فهو ذو كثافة مقدارها (1150 kg/m3 ) كمادة أساس مدعمة بنوعين من الالياف هما ألياف الزجاج نوع (E-glass ) والياف الكاربون (HS ) (High Strength ) وبنسبة عدد طبقات الياف الكاربون الى الزجاج (5 : 1 ) وبكسر حجمي (%30) في درجة حرارة الغرفة لدراسة أختباري الشد والكلال . وقد لوحظ ان مقاومة الشد للمادة المدعمة او المتراكبة اعلى منها في حالة المادة البوليمرية لوحدها بسبب مقاومة الالياف ( خصوصاً الياف الكاربون لامتلاكها خواص جيدة ) .أما بالنسبة لاختبار الكلال تبدي المادة المتراكبة مقاومة جيدة للكلال مقارنة بالمادة البوليمرية لوحدها حيث ان قوة او مقاومة الياف الكاربون للكسر عند الدورات القليلة يؤدي الى عدم تعرض المادة المتراكبة للكسر . اما في الدورات العالية فأن مقاومة الكلال للمادة المتراكبة تبقى على الاغلب ثابتة او تتغير ببطىء مع زيادة عدد دورات الكسر وبالاعتماد على نسبة التدعيم .


Article
Mechanical Behavior of Polyester and Fiber Glass as a Composite Material used in a Vehicle under Dynamic Loading
السلوك الميكانيكي للبولستر والالياف الزجاجية كمواد مركبة استعملت في العربات تحت الاحمال الديناميكية

Author: Ahmed Naif Al-Khazraji* Ali Yasser Hassan* Emad Abdul Hussein Abdul Sahib*
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2014 Volume: 21 Issue: 1 Pages: 19-28
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

The automobile industry has shown increased interest in the replacement of steel spring with fiberglass composite leaf spring due to high strength compared to weight. The aim of this paper is to study two kinds of fiberglass, regular direction (0-90) and random direction immersed in polyester resin. They were tested under static load, as tensile test for their mechanical properties, and under dynamic load in fully reversible bending tests as fatigue test, to estimate S-N curves, and impact test for their mechanical properties. Results from the tensile tests showed that the tensile strength of the regular type is greater than random type. The fatigue test results showed that the number of cycles to failure in regular type of composite material is greater than that of the random type and the endurance limit is also greater than in random, the increase percentage in endurance limit is 7.5%. Results due to impact test showed that there were on increasing in fracture energy for the random type the increase ratio is 13.9%. The Important characteristics of composites that make them excellent for leaf spring instead of steel are higher strength-to-weight ratio, superior fatigue strength. Application of composite structures reduces the weight of leaf spring without any reduction on the load carrying capacity and stiffness in automobile suspension system.

اظهرت صناعة السيارات اهتماما متزايدا بابدال النوابض الورقية الفولاذية بالنوابض الورقية المصنوعة من الالياف الزجاجية المركبة بسبب المتانة العالية مقارنة مع الوزن. يتناول هذا البحث دراسة نوعين من الياف الزجاج هما النوع الاول المنتظم (0-90 ) والنوع الثاني العشوائي مغمور بمادة البوليستر. تم اختبار كلا النوعين للحصول على المواصفات الميكانيكية تحت الحمل المستقر كأختبار الشد وأختبار تحت حمل ديناميكي كاختبار الصدمة. وللحصول على مخططات العمر تم اجراء التجارب تحت حمل ديناميكي متعاكس وهو أختبار الكلال. اظهرت نتائج اختبار الشد ان مقاومة الشد في النوع المنتظم اعلى من مقاومة الشد في النوع العشوائي ومن نتائج اختبار الكلال لوحظ بان عدد الدورات اللازمة للفشل اعلى في النوع المنتظم ,وان نسبة الزيادة في حد الكلال هي 7.5%. اظهر اختبار الصدمة زيادة في الطاقة المصروفة للكسر في النوع العشوائي بنسبة 13.9%. الخصائص المهمة للمواد المركّبه مثل المقاومة العالية نسبة للوزن والتي تعطي مميزات ممتازة للنوابض الورقية عند استخدامها بدلاً مِنْ النوابض الورقية المصنعة من الفولاذِ ، ان استخدام النوابض الورقية المصنعة من المواد المركبة يعطي خفة في الوزن دون أيّ تخفيض على الحملِ والمتانة في نظام التعليق في السيارة.


Article
Effect of Sodium Chloride on Microstructure and Mechanical Properties of Al-Si alloy
تأثير كلوريد الصوديوم على البنية المجهرية والخواص الميكانيكية لسبيكة Al-Si

Authors: Jafer T. Al-Haidary --- Mahdie Mutier Hanon --- Yasir Muhi Abdulsahib
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 9 Part (A) Engineering Pages: 2187-2197
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work, the effect of sodium chloride (NaCl) powder addition with different amounts on microstructure and mechanical properties of Al-12 wt. %Si alloy was investigated. In this technique, modification by NaCl was used because of its availability and low price comparing to other modifiers such as Sr and Sb. A 1000 °C as pouring temperature of molten alloy was used. The present results showed that there is a significant change in the mechanical properties and microstructure compared with unmodified alloy. The optimum properties were found by adding 0.5wt% NaCl to the alloy, and also the modification of microstructure alloy. Mechanical properties and microstructure of Al-12wt. %Si alloys that poured from 1000 °C with NaCl additives were compared with the corresponding alloys but at 800 °C pouring temperature, it is found that alloys poured from 1000 °C have best properties as compared with the same alloys poured from 800 °C.

في هذا البحث تم دراسة تأثير إضافة كميات مختلفة من مسحوق كلوريد الصوديوم (NaCl) على البنية المجهرية والخواص الميكانيكية لسبيكة Al-12wt.%Si. في هذه الطريقة تم اجراء عملية التحوير بواسطة كلوريد الصوديوم وذلك لوفرته ولرخص ثمنه بالمقارنة مع المحورات الاخرى مثل السترونشيوم و الانتيمون. استخدمت درجة حرارة 1000 درجة مئوية لعملية الصهر وصب المنصهر من هذه الدرجة وذلك بسبب حدوث ذوبان المادة المضافة الى المنصهر والتي يعتقد ان الكلور سوف يتطاير كغاز تاركاً الصوديوم في السبيكة المذابة ليؤدي عمله. اظهرت النتائج المستحصلة بان هنالك تغييراً في الخواص الميكانيكية والبنية المجهرية بالمقارنة مع السبيكة غيرالمحورة. تم تحديد الاضافة التي تعطي خواص اعلى والتي كانت عند اضافة نسبة 0.5% من كلوريد الصوديوم الى السبيكة وكذلك تحوير البنية المجهرية. تم مقارنة الخواص الميكانيكية والبنية المجهرية لسبائك Al-12wt.%Si المصوبة من درجة حرارة 1000 درجة مئوية والمضافة اليها كلوريد الصوديوم بنفس السبيكة ولكن بدرجة حرارة صب مقدارها800 درجة مئوية, حيث وجد ان صب السبائك من درجة حرارة 1000 درجة مئوية تعطي خواص افضل من صب السبائك نفسها من درجة حرارة 800 درجة مئوية.


Article
Study of tensile strength and compression strength of binary polymeric blends (High Density poly ethylene /polycarbonate)

Authors: Sanaa A. Hafad --- Balkees M. dyaa --- Mohammed S. Waheed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2008 Volume: 26 Issue: 7 Pages: 812-823
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work, HDPE/PC binary polymeric blends has been made by using the singlescrew extruder machine .The tensile strength measurements showed that this blend have higherresults reflects the homogeneity of the mixture and higher strengthcompared with that of single material the strength like HDPE or PC aloneand these values increase when blending with ratio (80/20) of (HDPE/PC);and increase more when reinforcing with E-glass fibers (1%). Also in thecompressive strength increases for blends of (80/20%) (HDPE/PC)furthermore, a composite of these blends with E-glass fiber these valuesare increased more .

في هذا البحث تم تصنيع الخلائط البوليمرية الثنائية (البولي اثلين عالي الكثافة /البوليكاربونات ) بطريقة ماكنة البثق الأحادية اللولب .مقارنة l حيث أظهرت قياسات مقاومة الشد نتائج عالية تعكس أمتزاجية الخلط ومقاومة عاليةبالمواد الأساسية بصورتها المنفردة مثل مادة البولي أثلين عالي الكثافة والبولي كاربونات20 %)من البولي أثلين عالي الكثافة /البولي / لوحدهما .وان هذه القيم تزداد عند الخلط بنسبة ( 80وبنسبة ( 1%),كما أن E كاربونات كما تزداد هذه القيم أكثر عند التدعيم بألياف الزجاج من نوع20 %)من البولي أثلين عالي الكثافة /البولي / قيم مقاومة الانضغاط تزداد عند الخلط بنسبة ( 80كاربونات وتزداد هذه القيم أكثر عند التدعيم بألياف الزجاج


Article
THEORETICAL AND EXPERIMENTAL INVESTIGATION OF FRICTION STION STIR WELDING FOR COPPER ALLOY
دراسة نظرية وعملية للحام الاحتكاكي لسبائك النحاس

Authors: Nabeel Shallal Thamer --- Ahmed Hadi Abood --- Dr. Hani Aziz Ameen
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2013 Volume: 6 Issue: 3 Pages: 332-351
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

Friction stir welding (FSW) is a relatively new solid-state joining process. Thisjoining technique is energy efficient. In particular, it can be used to join highstrengthaerospace aluminum alloys and other metallic alloys that are hard to weldby conventional fusion welding. In this paper the investigation is made on frictionstir welding process for joining of copper alloy. Friction stir welding experimentswas performed using different pins (pin with straight boundary and pin with curvedboundary). Welding joints efficiencies were found for each set. Mechanical andmicrostructural analysis has been performed experimentally on the welding zone.Non- linear numerical models was built in ANSYS software to simulate thethermal history of a workpiece undergoing friction stir welding by a movingheating source. An accurate prediction of temperature fields is evident. Exclusiveresult for effect of rotating a friction stir tools with respect to boundary conditionson stress-strain curves is presented. The results shown that the friction stir weldingwith pin of curved boundary is more efficient than that of straight boundary

تعتبر عملية اللحام الاحتكاكي من اكفأ عمليات اللحام والتي تستعمل لربط المعادن مثل الالمينيوم والمعادن)FSW( الاخرى والتي من الصعوبة لحامها بالطرق التقليدية . في هذه الدراسة تم تطبيق الحام الاحتكاكيلسبائك النحاس من خلال تصميم وتصنيع نوعين من الأدوات )الدبوس بحواف مستقيمة والدبوس بحوافمنحنية(. وقد وجد ان كفاءة اللحام جيدة لكلا الحالتين وقد تم إجراء تحاليل ميكانيكية ومجهرية على منطقةاللحام . وقد تم انشاء موديل غير خطي ببرنامج الانسز لمحاكاة التأثيرات الحرارية خلال عملية اللحامباستخدام مصدر حراري متنقل . وقد تم الحصول على نتائج الخواص الميكانيكة منحنى )الاجهاد-الانفعال (لكلا الاوادت التي تم تصنيعها. وقد بينت النتائج ان اللحام باستخدام دبوس بحواف منحنية هو اكثر كفاءة منالحواف المستقيمة .


Article
Tensile and Buckling of Prosthetic Pylon made from Hybrid Composite Materials

Authors: Jawad Kadhim Oleiwi --- Shaymaa Jumaah Ahmed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 14 Part (A) Engineering Pages: 2642-2653
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Compared to traditional prosthetic pylon materials (Aluminum, Titanium, or Stainless steel.), composite prosthetic pylon materials are used instead of metals. Vacuum bagging technique was adopted for the preparation of specimens made of Poly methyl methacrylate (PMMA) as matrix with constant Perlon layers and different number of Hybrid (Carbon + Glass) fibers layers as reinforcement materials at (±45º&0º/90º) orientation relative to applied load. Also the finite element method (ANSYS-15) were used by create a model of prosthetic pylon and applied compressive load at heel strike step from gait cycle to known the critical buckling stress. The experimental and numerical results shown that the tensile strength, modulus of elasticity, and critical buckling stress increases with increasing number of Hybrid fibers layers, that equal to (145 MPa, 6.25 GPa, and 670 MPa) respectively, and the percentage of increase in tensile strength, modulus of elasticity, and critical buckling stress for specimen with three Hybrid (Carbon + Glass) layers and Perlon layers in PMMA resin compared with pure PMMA specimen was (302.7% , 300% & 257.22%) respectively, at (0º/90º) fibers orientation relative to tensile force.

Listing 1 - 10 of 20 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (20)


Language

English (16)

Arabic (3)

Arabic and English (1)


Year
From To Submit

2019 (1)

2018 (5)

2017 (1)

2016 (1)

2015 (2)

More...