Article
Impact Strength for the 3D Textiles Fiber Reinforced Cementitious Composites Plates
تحمل الصدمة للصفائح السمنتية المركبة والمسلحة بنسيج زجاجي ثلاثي الابعاد

Loading...
Loading...
Abstract

The use of textile reinforcement made from non-corrosive materials, such as carbon and glass can reduce the required concrete material; this is known as Textile Reinforced Concrete (TRC). This study deals with plate specimens having dimension of 500×500×40mm tested under impact load at 28 and 90 days age under two conditions of ends, simply supported and fixed. Cement mortar with about 60 MPa, 7cm cube compressive strength at 28 days was designed for casting the plates. Plate specimens were divided into four groups, they consist of reference plates (no reinforcement) and plates reinforced with 3D glass fabric having three different thicknesses 6, 10 and 15mm.The results indicate that using 3D textile glass fabric cause an increase in number of blows, reduce in final stage deflection, an improvement in toughness and energy absorption under impact loads. Using 3D textile glass fiber with 10mm thickness gave higher number of blows for 28 and 90 days as compared with 6 and 15 mm. Plates with slice 6mm 3D textile glass fiber in two way reinforced has significantly enhancement in number of blows, the improvement was about (80 - 125%) and (128.5- 114. 3%) for 28 and 90 days respectively. The specimens showed increase in the energy absorption, besides the number and width of cracks was reduced and only few cracks are propagated up to the edge of the plates.

ان استخدام الالياف اوالنسيج بابعاد ثلاثية مصنوعة من مواد زجاجية اوكاربونية ذات طبيعة كيميائية خاملة يؤدي الى تقليل بكمية المواد السمنتية الداخلة بالخلطة الخرسانية. حيث تضمنت هذه الدراسة قياس تحمل الصدمة لصفائح بابعاد 500*500*40 ملم وبعمر 28 و90 يوم بواقع نوعين من الشروط الحدودية (بسيطة وثابتة). وتم صب الصفائح باستخدام مونة اسمنتية ذات مقاومة انضغاط 60 ميكاباسكال بعمر 28 يوم. قسمت الصفائح الى اربع مجاميع مؤلفة من صفائح بدون استخدام اي الياف لغرض المقارنة وصفائح مسلحة بثلاث اسماك مختلفة (6و10و15ملم) من الياف زجاجية ثلاثية الابعاد. فحصت الصفائح تحت تاثير حمل الصدمة واظهرت النتائج ان استخدام نسيج زجاجي ثلاثي الابعاد ادى الى تحسن في خواص الصفائح وذلك بزيادة عدد الضربات وتقليل الانحرافات وزيادة في مقدار الطاقة الممتصة. ان استخدام الياف زجاجية بسمك 10 ملم تطلب زيادة في عدد الضربات المطلوبة للفشل بعمر فحص 28 و90 يوم مقارنة مع سمك 6 و15 ملم. كما ان استخدام نسيج ثلاثي الابعاد على شكل شراح بطبقتين وبسمك 6 ملم ابدى قوى ربط اكبر وتحسن بعدد الضربات ، حيث كان التحسن بمقدار 80-128 % و128.5-114.3% لاعمار 28 و90 يوم اضافة الى ان جميع الصفائح اظهرت زيادة في امتصاص الطاقة ونقصان في سمك وعدد الشقوق خلال الفحص .


Article
Flexural Behavior of Concrete Members Reinforced With 3D-Textile Fibers-A Review
سلوك الانثناء للعناصر الخرسانية المسلحة بالألياف النسيجية الثلاثية الابعاد (ورقة عرض)

Authors: Mays R. Abdulghani ميس ربيع عبد الغني --- Ahmed S. Ali احمد سلطان علي
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2019 Volume: 22 Issue: 3 Pages: 227-232
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Normal concrete is weak against tensile strength, has low ductility and also insignificant resistance to cracking. The addition of diverse types of fibers at specific proportions can enhance the mechanical properties as well as the durability. Discrete fiber, which is commonly used, have many disadvantages such as balling the fiber, random distribution, and limitation of the used Vf ratio. Based on this vision, a new technique was discovered, enhancing concrete by textile-fiber to avoid all the problems mentioned above. This paper presents all important consequence and conclusions obtained from previous studies on how to strengthen concrete with two-dimensional and three-dimensional textile-fibers, and focuses on the flexural behavior of concrete members. The results indicate that there was an improvement in flexural strength, deformation capacity, and toughness with different load conditions when using different types of textile-fiber. It was observed that the effect of textile-fibers would increase when this fiber was coated by epoxy. In TRC system, there is a significant impact on the number of textile-fiber layers used.

الخرسانة العادية ضعيفة ضد قوة الشد، ولديها ليونة منخفضة ومقاومة ضئيلة للتكسير. يمكن أن تؤدي إضافة أنواع مختلفة من الألياف بنسب محددة إلى تعزيز الخواص الميكانيكية بالإضافة إلى المتانة. تحتوي الألياف المنفصلة المستخدمة بشكل شائع على العديد من العيوب مثل تكور الألياف والتوزيع العشوائي والحد من نسبة Vf المستخدمة. بناءً على هذه الرؤية، تم اكتشاف تقنية جديدة لتعزيز الخرسانة بواسطة الالياف النسيجية لتجنب جميع المشكلات المذكورة أعلاه. يستعرض هذا البحث جميع النتائج والاستنتاجات الهامة التي تم الحصول عليها من الدراسات السابقة حول كيفية تقوية الخرسانة بالألياف النسيجية الثنائية الأبعاد والثلاثية الأبعاد، وتركز على سلوك الانحناء للأجزاء الخرسانية. تشير النتائج إلى وجود تحسن في قوة الانحناء، وسعة التشوه، والمتانة مع ظروف تحميل مختلفة عند استخدام أنواع مختلفة من الالياف النسيجية. لوحظ أن تأثير الالياف النسيجية قد زاد عندما تم طلاء هذه الألياف بمادة الايبوكسي. في هذا النظام، هناك تأثير كبير على عدد طبقات الالياف النسيجية المستخدمة.