Article
Effect of Annealing Temperature on The Some Electrical Properties of InSb:Bi Thin Films
تأثيردرجة حرارة التلدين في بعض الخصائص الكهربائية لأغشيةInSb:Bi

Author: Zeinab Jassim Shanan زينب جاسم شنان
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2010 Volume: 7 Issue: 4 Pages: 1416-1420
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

InSb alloy was prepared then InSb:Bi films have been prepared successfully by thermal evaporation technique on glass substrate at Ts=423K. The variation of activation energies(Ea1,Ea2)of d.c conductivity with annealing temperature (303, 373, 423, 473, 523 and 573)K were measured, it is found that its values increases with increasing annealing temperature. To show the type of the films, the Hall and thermoelectric power were measured. The activation energy of the thermoelectric power is much smaller than for d.c conductivity and increases with increasing annealing temperature .The mobility and carrier concentration has been measured also.

تم في هذا البحث تحضير سبيكة InSb ثم حضرت أغشيةInSb:Bi بنجاح باستعمال طريقةالتبخير الحراري على ارضية من الزجاج وبدرجة حرارة 423K Ts=وتم حساب طاقات التنشيط للتوصيلية المستمرة (Ea1,Ea2) للاغشية المحضرة عند درجات حرارة تلدينK ,473,423,373,303)523 (573, بينت النتائج ازدياد طاقات التنشيط مع زيادة درجة حرارة التلدين. أجريت قياسات هول والقدرة الكهروحرارية لمعرفة نوع الاغشية وكذلك تم حساب طاقة التنشيط للقدرة الكهروحرارية ووجد أنها اقل بكثير مما للتوصيلية المستمرة (d.c) كما أنها تزداد بزيادة درجة حرارة التلدين وكما تم حساب تحركية وتركيز حاملات الشحنة.


Article
Electrical characterization of thermoelectric generators based on p-type Yb0.6Co4Sb12 and n-type Fe2.0Co2.0Sb12 thermoelectric materials
التوصيفالكهربائيللمولداتالكهروحراريةعلىأساسالنوع الموجبYb0.6Co4Sb12والنوع السالب Fe2.0Co2.0Sb12منالموادالحرارية

Authors: Mustafa Kadhim Salman مصطفى كاظم سلمان --- ArshadHmoodAbdAlkadhim أرشد حمود عبد الكاظم
Journal: Journal of Kufa - physics مجلة الكوفة للفيزياء ISSN: 20775830 Year: 2019 Volume: 11 Issue: 01 Pages: 106-110
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

In this study, thermoelectric power generation (TEPG) device (D) was fabricated.The device based on p-Yb0.6Co4Sb12 and n-Fe2.0Co2.0Sb12, fabricated by using the solid state microwave. 8-couples of legs connected and attached to alumina substrates by Ag paste–Cu plate–Ag paste electrodes, with dimensions of 25 mm by 25 mm were used to fabricate the device. The maximum output power (Pmax) and the open-circuit voltage (Voc) was estimated based on the temperature difference (∆T) of 210 K and the hot-side temperature (TH) of 603 K for the module. We found the obtained open-circuit voltage (Voc) was 18.046 mV and the maximum output power (Pmax) was 12.732 μW.

فيهذهالدراسة،تمتصنيعجهازمولدالطاقةالكهروحراريةاستندهذاالجهازعلىنوعينمنالمركباتنوعp-Yb0.6Co4Sb12والنوعn-Fe2.0Co2.0Sb12،المحضرةبطريقةمايكرويفالحالةالصلبة. التيتشملثمانية أزواجمنالقظبانالموصلةمعبعضهاوالمرتبطةبقاعدةمنالألومينابواسطة (Ag paste) ومنثماقطابالنحاس ((Cuومنثم ( Ag paste) للأقطابالكهربائية،حيثكانلقاعدةالالوميناأبعاد (25 مليمترX25مليمتر). تمحسابالقدرةالخارجةالعظمى (Pmax) وفولطيةالدائرةالمفتوحة (Voc) أعتمادعلىإختلافدرجةالحرارة 210 درجةمطلقةوكانتدرجةحرارةالجانبالحار 603 درجةمطلقةللجهاز. حيثكانفولطيةالدائرةالمفتوحةالناتجةVoc) ) 18.046 mV،القدرةالخارجةالعظمىالناتجة (Pmax)12.732 μW..