Article
Corrosion Performance of (Ha-Psz) Bio Ceramic Coated Ti-20Co Alloy in Simulated Physiological Media

Authors: Murtdha A. Alsaaidy --- Thair L. Alzubaydi --- Khalid R. Alrawi
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2011 Volume: 14 Issue: 1 Pages: 84-91
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

The present investigation provides experimental results of corrosion performance in simulated
body fluid of Ti-20Co medical alloy coated with hydroxyapatite (HA) and Partially Stabilized
Zirconia (PSZ) composite layer by electrphoretic deposition (EPD) technique. A three mixing ratios
of HA and PSZ powders (namely 90%HA+10%PSZ, 66%HA+34%PSZ and 25%HA+75%PSZ)
were electrophoretically deposited on the surface of a Ti-20Co substrates. Post heat treatment at
800Co in inert environment was performed to improve the adhesion strength of the coated layers.
The coated samples were subjected to electrochemical study in artificial saliva (Modified Carter's
solution) and simulated blood plasma in order to determine the optimum coating conditions that can
give corrosion resistance in simulated body fluid condition. The influence of mixing ratios and
deposition thickness on the corrosion performance of the alloy are discussed in details based on the
Open Circuit Potential (OCP), corrosion potential and corrosion rate using potentiodynamic
polarization. Results showed that the coating efficiency is highly depending on parameters like
composition, coating thickness, layer porosity and adhesion to substrate. The corrosion aspects
resulting from various deposition thicknesses are discussed in details.

تم في هذا البحث دراسة نتائج فحوصات التآكل في محاليل الجسم لسبيكة Ti-2oCo ذات الاستخدام الطبي والمطلية بمادة الهيدروكسي ابتايت (HA) ومركب الزركونيا المثبتة جزيئاً (PSZ)باستخدام تقنية الترسيب بالهجرة للدقائق العالقة(EPD).حضرت ثلاثة نماذج من (Ha)و(PSZ) هي(90%HA+ 10%PSZ, 66%HA+34%PSZ ,5%HA+75%PSZ) والتي تم ترسيبها على سبيكة Ti-2oCo في محيط غاز فاصل وبدرجة 8000c لغرض الحصول على افضل التصاق بين السبيكة والمواد المرسبة.تم دراسة النماذج من خلال الاختبارات الكهروكيميائية من خلال غمرها في محلول اللعاب الصناعي وبلازما الدم والتي تم تحضيرها مختبرياً للحصول على السلوك العام للتآكل عند تعرض هذه المواد لمثل هذه الضروف.النسب المعتمدة والاسماك المهيئة للعينات المستخدمة تم قياس جهد التآكل لها ومعدل التأكل من خلال غمرها في المحلول ومن ثم قياس جهد الدائرة المفتوحة للغرض باستخدام قياس جهد الاستقطاب (OCP) اظهرت النتائج ان كفاءة معدل التآكل يعتمد على عدة عوامل منها النسب المستخدمة لمواد الطلاء وسمك الطلاء والفجوات الحاملة في طبقات الطلاء اضافة الى قوة الالتصاق على السبيكة المستخدمة. وقد تم مناقشة تأثير كل من نسب التركيب وسمك الطلاء خلال تفاصيل البحث.


Article
Effect of (Ta &Nb) on Corrosion Behavior of Nitinol Alloys

Author: Emad S. Al-Hassani
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 9 Part (A) Engineering Pages: 1894-1902
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this research, a study of the effect of Ta and Nb additions on the corrosion behavior and properties of Ni-Ti shape memory alloys prepared by powder metallurgy is presented. It was found that; the transformation temperatures and phase structures of the samples prepared consist of martensitic and austenitic phases at room temperature. Also, Vickers hardness values increased with increasing of Ta and Nb additions. Porosity percentages decreased with increasing of addition of Ta and Nb. Finally, the corrosion rate decreased with increasing of Ta and Nb additions.


Article
Effect of Heat Treatment on Properties of Titanium Biomedical Alloy

Authors: Jassim M. Salman Al-Murshdy --- Bassim Jaber Ghayyib
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2019 Volume: 27 Issue: 1 Pages: 232-546
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The aim of this work to study the effects of heat treatments on the alloy (Ti6Al4V) which produced by powder metallurgy methods and consists of a mixture of the following powders (titanium 90%, aluminum 6% and vanadium 4%).The heat treatments (sintering process) take place in different time of stay.The alloy (Ti6Al4V) used as biomaterials in the medical field due to their excellent properties such as : high corrosion resistance, high wear resistance, high breaking strength, higher ductility, non-toxic and non-magnetic, suitable elasticity coefficient, where used as an alternative to replacing damaged hard tissues such as orthopaedic, osteosynthesis, full hip joint, knee joint and dental implants.The elements were weighed by a highly sensitive electronic balance, the powder was mixed for five hours, Then press with a pressure (700 MPa) to transition to green cylindrical samples with a diameter of 13 mm.The sintering process was carried out at 1100 °C.The porosity of the samples decreases at high temperatures and time of stay to a certain extent and then increase porosity at very high temperatures due to the growth of particle and the expansion of gases.The density of the samples after the sintering process increases with increasing the temperature because increase the mass diffusion of particles and reduces porosities that increase contact points between particles.The sintering processes lead to increase the hardness, where the hardness was tested in the Vickers hardness method. The wear increased by increasing (load, time and sliding distance), and increase the hardness leads to a low volume loss (the amount of metal lost a few) as the relationship between them is inverse.To study the corrosion behavior of the samples that have been sintering processes under different time of stay and to perform this test (tafel Extrapolation test) in 0.9 NaCl solution, where the sample is subjected to high temperature and a long period of stay and therefore This lead to increases the diffusion and increases the contact points between the particles and increase the forces of bonds between the particles and this leads to increased corrosion current and therefore the oxidation process to be a high degree and this leads to the higher rate of corrosion.

الهدف من هذا العمل هو لدراسة تأثير المعاملات الحرارية علىالسبيكة Ti6Al4V)) التي انتجت بطريقة ميتالورجيا المساحيق وتتكون من خليط من المساحيق التالية : تيتانيوم ٪90 المنيوم ٪6 فناديوم ٪4 المعاملات الحرارية (التلبيد) تحدث في فترات مكوث مختلفة •السبيكةTi6Al4V)) تستخدم كمواد حياتية في المجال الطبي نتيجة الى خواصها الممتازة مثل مقاومة تأكل عالية ٬ مقاومة بلى عالية ٬ مقاومة عالية للكسر٬ مطيلية عالية ٬ غير سام وغير مغناطيسي ٬معامل مرونة مناسب حيث تستخدم كبديل لاستبدال الانسجة الصلبة التالفة مثل تقويم و تثبيت العظم ٬مفصل الورك ٬مفصل الركبة و زروعات الاسنان •العناصروزنت بواسطة ميزان الكتروني عالي الحساسية ٬المساحيق خلطت لخمس ساعات ثم ضغط المساحيق بأستخدام جهاز المكبس مع ضغط 700 ميكا باسكال للانتقال الى النماذج الاسطوانية الخضراء مع قطر للعينات 13 ملم . عملية التلبيد تجري بدرجة حرارة 1100 °م. المسامية للعينات تقل في درجات الحرارة العالية وزمن المكوث الطويل الى حد معين ثم تزداد المسامية في درجات الحرارة المرتفعة جدا بسبب النمو الحبيبي وتمدد الغازات. كثافة النماذج بعدعملية التلبيد تزداد مع زيادة درجة الحرارة بسبب زيادة انتشار الجسيمات و نقصان المسامية التي تزيد نقاط التماس بين الجسيمات.عملية التلبيد تؤدي الى زيادة الصلادة ٬حيث الصلادة اختبرت بطريقة فيكرز. البلى يزداد بواسطة زيادة (الحمل ٬الزمن ٬ مسافة الانزلاق).وزيادة الصلادة تؤدي الى انخفاض الحجم المفقود (كمية المعدن المفقود قليلة) حيث العلاقة بينهم علاقة عكسية. لدراسة سلوك التآكل للنماذج التي اجري لها عمليات تلبيد في فترات مكوث مختلفة ولاداء هذا الاختبار (اختبار تافل) في محلول 0٫9 كلوريد الصوديوم ٬ حيث النموذج تعرض الى درجة حرارة عالية وفترة مكوث طويلة وهذا يؤدي الى زيادة الانتشار وزيادة نقاط التماس بين الجسيمات وزيادة قوى الاواصر بين الجسيمات وهذا يؤدي الى زيادة تيار التاكل ولذلك عملية الاكسدة على درجة عالية وهذا يؤدي الى معدل التآكل.