Evaluation of corrosion behavior of bioceramics coated commercially pure titanium and Ti-6Al-4V alloy

Authors: Hanan Ali حنان علي --- Shatha Saleem شذى سليم --- Thair L. Al-Zubaydi ثائر الزبيدي
Journal: Journal of baghdad college of dentistry مجلة كلية طب الاسنان بغداد ISSN: 16800087 Year: 2014 Volume: 26 Issue: 3 Pages: 41-48
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Background: This study report the corrosion behavior of commercially pure titanium and Ti-6Al-4V alloy sampleswithout coating and with hydroxyapatite, partial stabilized zirconia and mixture of partial stabilized zirconia andhydroxyapatite coating and comparison between them through electrochemical polarization tests in 37 0 C Hank'ssolution.Materials and methods: Electrophoretic deposition technique (EPD) was used to achieve the coating from each oneof three types of the coating materials (HAP, PSZ and mixture of 50% HAP and 50%PSZ) on Cp Ti and Ti-6Al-4V alloysamples. The electrochemical corrosion test was performed when samples were exposed to Hank's solution preparedin the laboratory and the polarization potential, corrosion rate and the open circuit potential of the samples weremeasured.Results: The results indicated that the corrosion rate is significantly higher for Ti-6Al-4V than for Cp Ti .The three types ofcoating significantly reduced the corrosion rate for Cp Ti while did not for Ti-6Al-4V alloy .After coating the corrosionrate for Ti-6Al-4V remained significantly higher than the coated Cp Ti samples .The open circuit potential (OCP) forboth Cp Ti and Ti-6Al-4V samples was in the following sequence PSZ > HAP> mixture of HAP and PSZ >uncoated.Conclusions: Cp Ti showed less corrosion rate than Ti-6Al-4V alloy with and without coating .Coating significantlydecreased the corrosion rate of Cp Ti but did not for Ti-6Al-4V alloy

المقدمة: ان تحقق نجاح عملیة زراعة الاسنان سریریا لیس بسبب المتانة المیكانیكیة او الانسجام الحیوي المتمیز لمادة الزراعة وحسب بل بسبب صفات اخرى لمادة الزراعة مثلخواصالسطح وسلوك التاكل.المواد وطریقة العمل: استعمل الترسیب بالھجرة الكھربائیة للحصول على طلاء متجانس لواحد من ثلاثة انوع من طبقات الطلاء (الھایدروكسي ابیتایت ,الزركونیا المثبتة جزئیا وخلیط.(Ti-6Al-4V ) الھایدروكسي ابیتایتاوالزركونیا المثبتة جزئیا)على النماذج المكونة من التیتانیوم النقي وسبیكةاما بالنسبة لاختبارات التاكل الكھروكیمیاوي فقد تم قیاسھا للنماذج في محلول الجسم المماثل المحضر مختبریا وایضا قیاس جھد الاستقطاب ومعدل التاكل وجھد الدائرة المفتوحةعند مقارنتھا مع التیتانیوم النقي .ولقد لوحظ ان معدل التاكل قل بشكل واضح لنماذج التیتانیوم النقي Ti-6Al-4V النتائج: تشیر نتائج ھذة الدراسة الى ان ھناك معدل تاكل عالي لسبیكةبعد الطلاء أعلى من التیتانیوم النقي . Ti-6Al-4V وایضا بقي معدل التاكل لسبیكة .Ti-6Al-4V المطلیة بالطلائات الثلاث بینما ذالك لم یظھر لسبیكةTi-6Al- ثر على سلوك سبیكة θ قبل الطلاء وبعد الطلاء .الطلاء قلل معدل التاكل للتیتانیوم النقي بینما ذالك لم ی Ti-6Al-4V الاستنتاجات: معدل التاكل للتیتانیوم النقي اقل من سبیكة.4V


Article
Surface Modification of Ti-6Al-4V Alloy by Glow Discharge-Plasma Nitriding
تحسين سطوح سبيكة Ti-6Al-4V باستخدام النترتة لبلازما التفريغ التوهج

Loading...
Loading...
Abstract

Titanium alloy (Ti-6Al-4V) samples were nitrided in low pressure (1.3, 3 mbar) dc-glow discharge plasmas of nitrogen. The treating time was 5, 10 and 15 hour and the temperatures range of the samples during the nitriding process was close to 800oC. The obtained microstructures of the nitride layers were studied by x-ray diffraction and optical microscopy. The ε –Ti2N, ζ-Ti3N3-x and η-Ti3N2-x.phases were formed and addition to the solid solution of nitrogen in titanium, α (Ti,N). Micro hardness measurements exhibit an increment for the Ti-alloy specimens which nitrided at 800oC for 10 and 15h.Corrosion measurements were obtained for the Ti-6Al-4V alloy in Ringer solution after plasma nitriding. The clear improving in the corrosion resistance was observed rather than for untreated specimens.

في هذا البحث تمت معاملة عينات من سبيكة Ti-6Al-4V ببلازما النايتروجين بضغوط (3,1.3) ملي بار بمبدأ التفريغ التوهجي للتيار المستمر . اجريت المعاملة للعينات بزمن ( 15,10,5) ساعة وبدرجة حرارة تقريبا 800 درجة مئوية. التركيب البلوري لطبقات النترته فحصت وشخصت بأستخدام حيود الاشعة السينية والمجهر البصري . الاطوار المتشكلة هي , - Ti3N3-X ,-Ti2N  - Ti3N2-Xبالاضافة الى طور الصلب للنايتروجين في التيتانيوم (TiN) . فحوصات الصلادة المايكروية اظهرت زيادة في المقدار لسبائك التيتانيوم المعاملة ببلازما ( لمدة 15,10 ساعة بدرجة 800 درجة مئوية ). قياسات التأكل حصلت باستخدام محلول (Ringer) للعينات المعاملة بالبلازما واظهرت وجود تحسس واضح في مقاومة التأكل للعينات المعاملة بالبلازما مقارنة مع العينات غير المعاملة.


Article
Modeling of Continues Laser Welding for Ti-6Al-4V Alloys Using COMSOL Multiphysics Software

Authors: Haneen A. Salman --- Kadhim A. Hubeatir --- Mohammed M. AL-Kafaji
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 8 Part (A) Engineering Pages: 914-918
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

A model for laser welding process using finite element method, the model was used for this work using the COMSOL Multiphysics software to predict the distribution of the temperature in the joint and to show the four welding zones (the melting zone, partial melting zone, zone affected by heat, and the material base). CO2 continues (CW) Laser used in the model welding thin sheets of titanium alloy Ti-6Al-4V. The results of this simulation work have been compared with the experimental works to show good agreement.