STUDY OF THE EFFECT OF NH4F CONCENTRATION ON THE STRUCTURE OF ELECTROCHEMICALLY PREPARED TiO2 NANOTUBES
دراسة تاثير تركيز NH4F على تركيب الانابيب النانوية لـ (TiO2) المحضرة الكتروكيميائياً

Loading...
Loading...
Abstract

In this study Titania nanotube arrays were prepared at room temperature (~25 ºC) via electrochemical anodization process of pure titanium foil in glycerol base electrolyte, different concentrations of ammonium fluoride salt (0.5 and 1.5wt.%) were added to the electrolyte as a tube enhancing agent. When anodizing Ti in 0.5 wt. % NH4F, nanotubes are formed with 54 ± 10 nm tube diameter, 20 ± 3 nm wall thickness and 1.76 µm tube length. When anodizing Ti in 1.5 wt. % NH4F, nanotubes are formed with 69 ± 10 nm tube diameter, 29 ± 3 nm wall thickness and 2.71 µm tube length. The morphology and structure of the Titania films were studied by scanning electron microscopy (SEM), X-ray diffraction (XRD), and atomic force microscopy (AFM). PACS numbers: 81.65.Mg, 82.45. +z, 81.10.-h.

في هذه الدراسة صفوف التيتانيا نانوتيوب حضرت في درجة حرارة الغرفة ~25 ºC بطريقة الانودة الكهروكيمائية لصفائح التيتانيوم النقي في محلول كهربائي اساسه جليسيرول (glycerol)، تراكيز مختلفة من ملح فلوريد الامونيوم 0.5 and 1.5wt.% اضيفت الى المحلول كعامل محسن للانبوب. عندما يؤكسد التيتانيوم في 0.5 wt%.NH4F ، كان قطر الانابيب النانوية المشكلة 10nm± 54 ، سمك الجدار nm 3± 20 و µm 1.76 طول الانبوب. عندما يؤكسد التيتانيوم في 1.5 wt%.NH4F ، كان قطر الانابيب النانوية المشكلة 10nm± 69 ، سمك الجدار nm 3± 29 و µm 2.71 طول الانبوب. تمت دراسة مورفلوجية وتركيب افلام التيتانيا بواسطة المجهر الالكتروني الماسح، مجهر القوة الذرية و حيود الاشعة السينية.

Listing 1 - 1 of 1
Sort by
Narrow your search

Resource type

article (1)


Language

English (1)


Year
From To Submit

2012 (1)