Article
Synthesis of TiO2 Nan particles by Using Sol-Gel Method and Its Applications as Antibacterial Agents
تصنيع جسيمات ثنائي اوكسيد التيتانيوم النانوية باستخدام طريقة محلول - جل وتطبيقاته كعوامل مضادة للبكتريا

Authors: Zainab N. Jameel --- Adawiya J. Haider --- Samar Y. Taha
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 3 Part (B) Scientific Pages: 418-426
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

TiO2 nanoparticles were prepared from TiCl4 as a precursor with ethanol solution with 1:10 ratio in ambient atmosphere, without additive. Sol-gel synthesized has been dried and calcined at (550-600)C. The structure, morphology and the particle size of the nanoparticles were investigated by X-ray Diffraction and Scanning Electron Microscopy (SEM). The optical properties were studied by UV-Visible Spectrophotometer. Results showed that the anatase phase was only in titanium dioxide powder up to 500. The average grain size of TiO2 nanoparticles was obtained in the range of (3- 30) nm. The synthesized TiO2 nanoparticles in 10-5 and 10-3 concentrations exhibited superior antibacterial activity with two types of bacteria, Escherichia coli (E-coli) and Staphylococcus aurous respectively. TiO2 nanoparticles are more efficient as antibacterial agents with Staphylococcus aurous as compared with E-coli.

تم تحضير جسيمات ثنائي اوكسيد التيتانيوم النانوية من رباعي كلوريد التيتانيوم ومحلول الايثانول بنسبة 10:1 في الظروف الاعتيادية وبدون اضافات. المحلول- جل المصنع يجفف ويسخن الى (550-600) درجة مئوية, ومن ثم تم تشخيص التركيب ومورفولوجيا السطح والحجم الحبيبي للجسيمات النانوية باستخدام جهاز حيود الاشعة السينية والمجهر الالكتروني الماسح والخصائص البصرية (فجوة الطاقة) باستخدام جهاز مطيافية الاشعة فوق البفسجية – المرئية. اظهرت النتائج طور(anatase) يتكون في مسحوق ثنائي اوكسيد التيتانيوم عند500 درجة مئوية. معدل الحجم الحبيبي لجسيمات التيتانيوم النانوية التي تم الحصول عليها كانت بمدى (3-30 ) نانومتر. جسميات ثنائي اوكسيد التيتانيوم المصنعة بالتراكيز 10-5 و10-3 تتصرف بفعالية مضادة للبكتريا فائقة مع نوعين من البكتريا Escherichia coli (E-coli) و Staphylococcus aurous على التوالي. جسيمات ثنائي اوكسيد التيتانيوم النانوية تكون اكثر كفاءة كعوامل مضادة للبكتريا مع Staphylococcus aurous كمقارنة مع Escherichia coli (E-coli).


Article
Synthesis and Characterization of TiO2 Nanoparticles via Sol-Gel Method by Pulse Laser Ablation
تصنیع وتوصیف جسیمات ثنائي اوكسید التیتانیوم النانویة بطریقة الصول-جل بالازالة باللیزر النبضي

Authors: Adawiya J. Haider --- Zainab N. Jameel --- Samar Y. Taha
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 5 Part (B) Scientific Pages: 761-771
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Nanocrystalline titania powder was prepared at room temperature via sol-gel method; using TiCl4 as precursor and absolute ethanol solution. After mixing, the gel solution was formed. Then the sol-gel dried and calcined at different temperatures. The size of the prepared nanoparticles was reduced by Nd-YAG Pulse Laser Ablation (PLA). The characterization of the TiO2 Nanoparticles in two phases was carried out by X-ray Diffraction (XRD) to investigate the phase structure. The Transmission Electron Microscope (TEM) result shows the particle size of nanoparticles after laser ablation less than 10 nm. Scanning Electron Microscopy (SEM) to obtain the surface morphological studies Results showed that anatase was the only phase in titanium oxide powders up to 500 °C, when the calcination increased in the region of 900 °C the phase transformation from anatase to rutile occurred in the TiO2 nanopowders. This paper shows a comparison between two phases of TiO2 Nanoparticles (anatase and rutile). Fourier Transform Infra-Red (FTIR) to study the vibrational frequencies between the bonds of atoms for synthesized TiO2 Nanoparticles. The Crystalline size of TiO2 Nanoparticles obtained was between (15 -70) nm for anatase at 500 °C and rutile at 900 °C. In FTIR analysis, all the peaks observed were around (400-700) cm-1 due to stretching and bending vibrations.

تم تحضیرمسحوق جسیمات ثنائي اوكسید التیتانیوم النانویة االبلوریة بدرجة حرارة الغرفة وبطریقةالصول-جل وباستخدام رباعي كلورید التیتانیوم كمادة اولیة والایثانول النقي, بعد الخلط یتكون الجل ثمیجف ویتعرض للاحراق بدرجات حرارة مختلفة. النتائج توضح بان طور الاناتاس ھو الطور الوحیدالذي یكون عند 500 درجة سیلیزیة وعند زیادة درجة حرارة الاحراق الى 900 درجة سلیزیة یتحولالطور من الاناتاس الى الروتایل وھذا یحدث مع مسحوق ثنائي اوكسید التیتانیوم . ھذا البحث یوضحالمقارنة مابین جسیمات ثنائي اوكسید التیتانیوم النانویة لطوریھا الاناتاس والروتایل. تم تقلیل حجمجسیمات ثنائي اوكسید التیتانیوم النانویة المحضرة باستخدام الازالة باللیزرر الیاك النبضي, وتمتوصیف للجسیمات النانویة بجھاز حیود الاشعة السینیة لمعرفة التركیب الطوري والمجھر الالكترونيالنافذ لقیاس حجم الجسیمات النانویة بعد الازالة باللیزر والمجھر الالكتروني الماسح لدراسةمورفولوجیا السطح وتحویلات فوریر للاشعة تحت الحمراء لدراسة الترددات الاھتزازیة مابین اواصر(70 - الذرات للجسیمات النانویة المحضرة. الحجم البلوري للجسیمات النانویة وجد انھ یقع مابین ( 15نانومتر لطور الاناتاس عند 500 درجة سلیزیة وللروتایل عند 900 درجة سلیزیة . من تحلیلاتcm- فوریر للاشعة تحت الحمراء معظم القمم تم ملاحظتھا مابین 1 700-400 ) نتیجة المط و )الاھتزازات الانحنائیة.

Keywords

TiO2 NPs --- Sol-gel method --- TiO2 phases --- PLA