Search results: Found 11

Listing 1 - 10 of 11 << page
of 2
>>
Sort by

Article
Influence of substrate temperature on structural and optical properties of SnO2 films
تأثير درجة حرارة الأرضية على الخواص التركيبية والبصرية لأغشية SnO2الرقيقة

Loading...
Loading...
Abstract

Tin Oxide (SnO2) films have been deposited by spray pyrolysis technique at different substrate temperatures. The effects of substrate temperature on the structural, optical and electrical properties of SnO2 films have been investigated. The XRD result shows a polycrystalline structure for SnO2 films at substrate temperature of 673K. The thickness of the deposited film was of the order of 200 nm measured by Toulansky method. The energy gap increases from 2.58eV to 3.59 eV when substrate temperature increases from 473K to 673K .Electrical conductivity is 4.8*10-7(.cm)-1 for sample deposited at 473K while it increases to 8.7*10-3 when the film is deposited at 673K

تم ترسيب اغشية (SnO2) بطريقة الرش الكيميائي عند درجات حرارة ارضية مختلفة وقد تمت دراسة تاثير تغيير تلك الدرجات الحرارية على تركيب الاغشية وخصائصها البصرية والكهربائية. أظهرت نتائج حيود الاشعة السينية ان الاغشية المحضرة عند درجة حرارة ارضية (673K) كانت ذات تركيب متعدد البلورات. كان سمك الاغشية المحضرة بحدود (200nm) وقد تم قياسها بطريقة تولانسكي(Toulansky). ازدادت فجوة الطاقة البصرية من 2.58 الى 3.59 الكترون-فولت .كما ان التوصيلية الكهربائية ازدادت من 4.8*10-7(ohm.cm)-1 الى 8.7*10-3 (ohm.cm)-1 عند زيادة درجة حرارة الارضية من 473K الى 673K.


Article
Improvement the efficiency of SnO2/n-Si detector by engraving method using a CNC machine
تحسين كفاءة كاشف SnO2/n-Si بأسلوب الحفر باستعمال ماكينة CNC

Author: Wlla M. Mohammed ولاء محفوظ محمد
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2019 Volume: 17 Issue: 41 Pages: 51-57
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Tin oxide was deposited by using vacuum thermal method on silicon wafer engraved by Computer Numerical Controlled (CNC) Machine. The inscription was engraved by diamond-made brine. Deep 0.05 mm in the form of concentric squares. Electrical results in the dark were shown high value of forward current and the high value of the detection factor from 6.42 before engraving to 10.41 after engraving. (I-V) characters in illumination with powers (50, 100, 150, 200, 250) mW/cm2 show Improved properties of the detector, Especially at power (150, 200, 250) mW/cm2. Response improved in rise time from 2.4 µs to 0.72 µs and time of inactivity improved 515.2 µs to 44.2 µs. Sensitivity angle increased at zone from 40o to 65o.

تم في هذا البحث ترسيب أوكسيد القصدير على قواعد من السليكون المحفور بواسطة ماكينة مسيطر عليها رقمياً بالحاسبة الالكترونية CNC. تمت عملية الحفر بعمق 0.05 mm على شكل مربعات بواسطة برينة من الألماس. الخواص الكهربائية في الظلام بينت زيادة في قيمة التيار الامامي بالنسبة للتيار العكسي مع ارتفاع في قيمة عامل الكشفية من 6.42 قبل الحفر الى 10.4. اما الخواص الكهربائية عند الاضائة بقدرات (50, 100, 150, 200, 250) mW/cm2 فبينت زيادة في قيمة الكشفية وخصوصاً عند القدرات(150, 200, 250) mW/cm2. زمن الاستجابة لنهوض الإشارة تحسن من 2.4 µs الى 0.72 µs وتحسن زمن الخمود من 515.2 µs الى 44.2 µs. اما بالنسبة الى زاوية التحسس للكاشف فبينت النتائج الى زيادة ملحوظة في المنطقة المحصورة بين 40o الى65o .


Article
Effect of Different Oxidation Temperature on Nano and Micro TCO’s Thin Film
تأثيراختلاف درجات حرارة الاكسدة لآغشية اوكسيد القصدير المايكروية والنانوية

Authors: Mohammed S. Mohammed --- Rana Osamah Mahdi --- Evan Tareq Salim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 1 Part (B) Scientific Pages: 7-14
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present work, electrical structural and surface morphology of tin oxide thin films prepared using simple conventional method known as (CTO) was carried out. The obtained result insures the formation of Nano crystalline SnO2 films as a tetragonal structure. The atomic force microscope results show that film roughness depended on oxidation temperature. Minimum electrical resistivity found to be about (5.35 x 10-5 .cm) at (300°C) oxidation temperature.

البحث يتضمن دراسة الخصائص الكهربائية وطبوغرافية السطح لاغشية اوكسيد القصدير المحضرة بتقنية تقليدية بسيطة تعرف (الاكسدة الحرارية التقليدية). النتائج المستحصلة تؤكد ان اغشية اوكسيد القصدير النانوية تمتلك تركيب رباعي. قياسات الفحص المجهري (AFM) اوضحت ان خشونة السط للاغشية المحضرة تعتمد على درجة حرارة الاكسدة. كذلك تبين ومن خلال الخصائص الكهربائية بان اوطأ قيمة للمقاومية الكهربائية كانت بحدود (5.35 x 10-5 .cm) عند درجة حرارة الغرفة تقريبا.


Article
Preparation and Characterization of Tin Oxide Thin Films by Using Spray Pyrolysis Technique
تحضير وخصائص أغشية ثنائي اوكسيد القصدير الرقيقة بواسطة استخدام تقنية الرش الحراري

Authors: Selma M. H. Al-Jawad --- Fadheela H. Oleiwe --- Jabbar .H. Khulaef
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 3 Part (B) Scientific Pages: 528-538
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work, tin oxide thin films have been prepared by Spray pyrolysis technique, using tin chloride over soda – lime glass. Structural and optical properties were studied under different conditions like substrate temperatures of 300, 350 and 400°C, and annealing in air at temperature 300°C for 1 hr. The films were characterized by XRD, SEM, AFM, and UV-VIS analysis. The optical spectra of the films were measured in the wavelength range of 300 –900 nm by UV-VIS Spectrometer device. The X-ray diffraction studies confirmed the films have the orthogonal structure at low substrate temperature change to a tetragonal structure at high substrate temperature. Films prepared with different substrate temperatures were correspond to preferential orientation along the plane (132) and (110) planes for structural orthogonal, tetragonal respectively. The grain size founded( 25.2-9.77nm) for different substrate temperatures range ( 300- 400°C) after annealing , from the (SEM) images the grain size values of the SnO2 thin films are found to be in the range of (32.3-24.2 nm) corresponding to the substrate temperature (350 and 400°C) after annealing and from the AFM the root mean square (RMS) values for the thin film at substrate temperature 350C was found to be 10.4 nm, the surface roughness 8.86 nm. The maximum value of transmittance was found to be 78 % around the wavelength of 900nm at substrate temperatures 300°C also have energy gap (2.9-3.4eV) at substrate temperatures range ( 300- 400°C) after annealing in air at temperature 300°C for 1 hr.

في هذا العمل حضر ثنائي أوكسيد القصدير بطريقة الرش الحراري , باستخدام كلوريد القصدير على قاعدة زجاجية , درست الخصائص التركيبية والبصرية تحت شروط مختلفة مثل درجة حرارة القاعدة (400,350,300) درجة سيلزية ولدنت في الهواء عند درجة حرارة (300) درجة سيلزية ولمدة ساعة . شخصت خصائص الاغشية بواسطة فحص حيود الأشعة السينية والمجهر الالكتروني الماسح ومجهر القوة الذرية وقياسات الأطياف للأشعة المرئية وفوق البنفسجية , الأطياف البصرية للأغشية حسبت عند الطول الموجي (من 300الى900) نانومتر . أكدت دراسة حيود الأشعة السينية ان الاغشية تمتلك تركيب متعامد عند درجات الحرارة الواطئة للقاعدة وتتغير الى تركيب رباعي الزاوية عند درجات الحرارة العالية للقاعدة , وجدت قيمة الحجم الحبيبي تتغير (من 9.77 الى25.2 ) نانومتر عندما تتغير درجة حرارة القاعدة بين ( 300 الى 400) درجة سيلزية بعد التلدين , كذلك وجدت من صور المجهر الالكتروني الماسح قيمة الحجم الحبيبي لأغشية اوكسيد القصدير تساوي (24.2- 32.3) نانومتر الذي يقابل درجة حرارة القاعدة ( 350 و 400) درجة سيلزية بعد التلدين , اظهرت نتائج مجهر القوة الذرية ان قيمة مربع متوسط الجذر تساوي (10.4) نانومتر ومعدل الخشونة يساوي 8.86 نانومتر عندما تكون درجة حرارة القاعدة 350 درجة سيلزية . بالاضافة الى ذلك وجد ان أعلى قيمة للنفاذية تساوي 78% عند الطول الموجي ( 900) نانومتر عند درجة حراة القاعدة 350 درجة سلزية , وتمتلك فجوة طاقة (2.9-3.4) الكترون فولت لاغشية اوكسيد القصدير عندما درجة الحرارة تتغير بين (300- 400) درجة سليزية بعد التلدين لمدة ساعة.


Article
Effect of Indium Tin Oxide (ITO) Nanoparticles on the Optical Properties Of PMMA Polymer
دراسة تأثير إضافة (ITO) كجسيمات نانوية على الخصائص البصرية للبوليمر بولي مثيل مثيكولايت

Authors: Asama Natik.Naje --- Salma M. Hasan --- Estabrak Talib
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2015 Issue: المؤتمر العلمي الثالث لكلية العلوم Pages: 17-23
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

In this work the optical properties of the PMMA polymer doped with different concentrations of ITO nanoparticles had been studied. All samples were prepared by casting technique with thickness of 1 mm. The optical properties ((absorption, transmission, absorption coefficient, extinction coefficient and refractive index) had been investigated. The doped composites have shown shifted toward the visible region. Whereas measured energy gap for pure and doped polymer shows decreases in the energy gap from 5.5eV to 3.5eV. The refractive index of pure polymer decreases as wavelength increase, where the refractive index of the doped polymer increases with increasing ITO concentrations.

في هذا العمل تمت دراسة الخصائص البصرية للبوليمر PMMA الذي تم تطعيمه مع تراكيز مختلفه ل ITO للجسيمات النانويه التي تمت يواسطة تقنية الطلاء مع سمك 1 ملم . تم دراسة الخصائص البصريه ( الامتصاصيه ,النفاذيه,معامل الامتصاص,معامل الانكسار, معامل الاخماد) , لوحظ ازاحة المركبات المطعمه باتجاه المنطقه المرئيه . كما لوجظ ان فجوه الطاقه المقاسه للبوليمرات المطعمه تتناقص من 5.5 الى.eV3.5 بينت الدراسه ان معامل الانكسار للبوليمر النقي يقل بزيادة الطول الموجي, وعند تطعيم البوليمر مع تراكيز مختلفه من الجسيمات النانويه ITO (0.01, 0.03, 0.05) معامل الانكسار يزداد.


Article
Morphological and Optical Properties of In_2 O_3:Sn Thin Films Deposited by Spray Pyrolysis

Authors: Salam Amir Yousif --- Duha Ismail Khalil
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2018 Volume: 14 Issue: 02 Pages: 275-290
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

The morphological and optical properties of indium tin oxide (ITO) thin films have been studied in this paper. Tin doped indium oxide thin films were deposited successfully on glass substrates at (450±10)℃ for various tin doping (0, 5, 10, 15, 20) % by spray pyrolysis technique. Atomic force microscopy has been used to study the surface morphology of In_2 O_3:Sn thin films. The optical properties were calculated by the absorbance and transmittance spectra in the wavelength interval (300-1000) nm. The optical constants such as (absorption coefficient, refractive index, extinction coefficient, real and imaginary parts of dielectric constant and optical conductivity) have been calculated and discussed.


Article
OPTICAL PROPERTIES OF SPRAYED TIN OXIDE FILMS
الخصائص البصرية لطبقة اوكسيد القصدير المرشوشة

Loading...
Loading...
Abstract

AbstractThis research is intended to study the preparation of heat mirror by spray pyrolysis method. Un-doped tin oxide (SnO2) and doped with 0.09%, 0.9%, and 9%, titanium dioxide heat mirror films were deposited on pre-cleaned substrates. The microstructure characterizations were carried out by x-ray diffraction technique. The optical properties were obtained by UV-Visible spectrophotometer. The un-doped samples have displayed average transmittance value of 73% in the visible region. Whereas, the doped samples of 0.09 and 0.9 mol% TiO2 show a good reflectance values of 76% and 80% respectively in the wavelength of 2700 nm.

المستخلصتم في هذه الدراسة تحضير أغشية نقية من ثاني اوكسيد القصدير و أخرى مشوبة بثاني اوكسيد التيتانيوم و9 ) % و مرسبة على أسطح قاعدة من الزجاج و بطريقة الرش الكيماوي ، 0.9 ، بتراكيز ( 0.09الحراري. تم معرفة خصائص هذه الأغشية و بنياتها من خلال الأشعة السينية الحائدة. كما تم الحصول علىخصائصها البصرية باستخدام مطياف الأشعة فوق البنفسجية- المرئية، حيث أعطت الأغشية النقية نفاذيةللأشعة المرئية بحدود 73 %، في حين كانت الانعكاسية للأغشية المشوبة بتراكيز ( 0.09 و 0.9 )% ثانياوكسيد التيتانيوم 76 % و 80 % على التوالي و عند الطول الموجي 2700 نانوميتر


Article
High Quantum Efficiency of (Au/n-SnO2/p-PSi/c-Si/Al) solar cell after annealing of Nd:YAG laser
كفاؤة كمية عالية للخلية الشمسية (Au/n-SnO2/p-PSi/c-Si/Al) بعد التلدين

Authors: Firas Sabeeh Mohammed --- Ban Rashid Ali --- Bahaa Jawad Alwan --- Zahra Sabah Rashid
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 5 Part (B) Scientific Pages: 856-866
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Transparent and conducting SnO2 thin film has been produced on (quartz and porous silicon) substrates using rapid photothermal oxidation of pure Sn in air at 600 oC oxidation temperature and different oxidation time. The structural properties and scan electron microscope of the prepared films were studied. The photovoltage properties of a Au/n-SnO2/p-PSi/c-Si solar cell are investigated under irradiation of Nd:YAG laser pulses. The porous Si layer is synthesized on a single crystalline p-type Si using electrochemical etching in aqueous hydrofluoric acid at a current density of 25 mA/cm2 for a 30-min etching time. The structure of the porous layer is investigated using scan electron microscope. The photovoltage properties are found to be dependent on the laser fluencies.

اكاسيد شفافة موصلة SnO2 محضرة على قواعد مختلفة باستخدام تقنية الاكسدة الحرارية السريعة لمعدن القصدير بالهواء عند درجة حرارة اكسدة 600 oC وازمان اكسدة مختلفة. الخصائص التركيبية تم دراستها في هذا البحث. تم تحضير طبقة اليليكون المسامي في هذا البحث باستخدام سليكون نوع p-type Si بمحلول حامض الهايدروفلوريك عند كثافة تيار مقدارها 25 mA/cm2 لمدة 30-min. حيث تم قياس الخصائص الفولتائية للنبيطة المصنعة بعد اجراء عملية التلدين كخلية شمسية حيث اظهرت كفاؤة عالية جدا بعد التلدين.


Article
Effect of Thickness on Optical Dispersion of SnO2 Thin Films
تأثیر السُمك على عامل التشتت البصري لاغشیة اوكسید القصدیر الرقیقة

Authors: Ibraheem M. Mohammed ابراھیم موسى محمد --- Kameran Y. Qader كامران یاسین قادر
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2014 Volume: 10 Issue: 3 - part 1 Pages: 19-28
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

Highly conducting and transparent SnO2 thin films have been prepared by a simple and low-cost spray pyrolysis technique on glass substrates. The optical properties and dispersion parameters of tin oxide have been studied as a function of film thickness. The changes in dispersion parameters and Urbach tails were investigated. The optical energy gap Eg decreased with increasing film thicknesses from 200 to 350nm ,and this can be attributed to the increase in the density of localized states and cause an expanding in the Urbach tail and consequently decrease the energy gap from 3.60 eV to 3.49 eV. The single-oscillator parameter has been reported.

حُضرت اغشية اوكسيد القصدير ذات التوصيلية العالية والشفافة بطريقة التحلل الكيميائي الحراري وهي طريقة بسيطة وواطئة الكلفة . دُرس تأثير سُمك اغشية اوكسيد القصدير على الخصائص البصرية وعوامل التشتت وقد لوحظ وجود تغير في عامل التشتت وذيول اورباخ ، اذ ان فجوة الطاقة البصرية تقل بزيادة سُمك الغشاء من 200nm الى350nm . ان زيادة المستويات الموضعية تؤدي الى توسع في ذيول اورباخ وبالتالي تقل فجوة الطاقة من 3.60eV الى 3.49eV .


Article
Gas Sensitivity of ITO Composite Prepared by Sol-Gel Method

Authors: R. J . Halbos --- S. AL-Algawi --- R.T. Rasheed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2017 Volume: 35 Issue: 10 Part (A) Engineering Pages: 981-986
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Indium oxide and indium tin oxide composite (ITO) were prepared by sol-gel dip-coating (SGDC) technique. The particles annealed at (200 ◦C, 400 ◦C). The structure and surface morphology of particles were characterized by X-ray diffraction (XRD), Atomic Force Microscope (AFM), FT-IR and UV/visible measurements. The XRD and AFM indicate decreasing in the particle size and improve of optical and electrical properties of composite with increasing of tin oxide addition. The hall measurement were used to obtain information about the type of conductivity of indium oxide and indium tin oxide thin films and carrier concentration and mobility and resistivity, the results of Hall measurements show that the In2O3 and ITO composite have n-type. The thin film of composite ITO at composition (80:20) mole ratio has high sensitivity toward CO gas compared with pure indium oxide.

Listing 1 - 10 of 11 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (11)


Language

English (9)

Arabic (1)

Arabic and English (1)


Year
From To Submit

2019 (1)

2018 (1)

2017 (1)

2015 (3)

2014 (2)

More...