TRIBOLOGICAL PERFORMANCE OF HIGHLY FINE NICKEL-MOLYBDENUM DISULFIDE POWDERS ADDITIVE TO LUBRICANT OIL
دراسة تاثير اضافة مسحوق نيكل – ثنائي كبريتيد المليبدنيوم عالي النعومة على الخواص التريبولوجية لزيوت المحركات

Author: Dr. Haidar Akram Hussien د. حيدر اكرم حسين
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2012 Volume: 5 Issue: 2 Pages: 111-122
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

Wear is a phenomenon which is surface materials damage or loss between two contact solids surfaces in sliding, rolling, or impact movement. In most cases, wear is caused by the interaction of surface asperities. To reduce the energy loss and equipment damage generated due to the mechanical parts friction in the operation, around the world is stepping up developing appropriate lubricants and lubrication technology. Molybdenum is one of the major refractory metals (metals with very high resistance to heat and wear). As already noted, for lubricant compositions as fillers can be used soft powder (anti-friction) of metals – nickel. This work focuses on studying an urgency and favorable prospects of practical use of firm powder additives on the basis of MoS2 which particles are coated with one layer of soft metal (Ni), and their effect on tribological characteristics of lubricant oil (SAE 50) at a range of concentration (2 – 8) wt%. Optimum lubricating effect concluded on the level of concentration of the composite additive powder in the range of (3.5 – 4.5) wt %, by the formation of protective boundary layer between sliding tribosurfaces that prevents wear.Tribological characteristics significantly improved i.e.friction coefficient may drop about (1.5-2) times, and the wear rate about (3-3.5) times compared with the case of usig the lubricant oil without additives.

يعتبر الاستهلاك من الظواهر المهمه الجديره بالدراسه لاسيما بين اسطج الاجزاء المتلامسه، ولتقليل الضياعات الحاصلة في الطاقه والانهيارات الحاصله بسبب التشغيل الميكانيكي والاحتكاك الحاصل بين الاجزاء المنزلقه بدا العلماء بالعمل لايجاد بعض البدائل والحلول لتحسين الخواص التريبولوجيه لمواد التزييت خصوصا في بعض الظروف الخاصه (درجة جراره وضغط عاليين) ويعتبر عنصر المليبدنيوم من العناصرالرئيسيه في هدا المجال بسبب تركيبه البلوري ومقاومته العاليه للحراره والاستهلاك• يتناول هدا البحث دراسة تاثيراضافة مسحوق(نيكل - ثنائي كبريتيد المليبدنيوم ) عالي النعومه (مسحوق مركب معامل كيميائيا بحيث تكون دقائق مسحوق ثنائي كبريتيد المليبدنيوم مغلفه بطبقه رقيقه من المعدن الناعم – النيكل)، الى زيت المحركات نوع (SAE 50)، على الخواص التريبولوجيه للزيت وبتراكيز مختلفه تتراوح بين(2 – 8)% غم/لتر من خلال حساب معامل الاحتكاك بين السطوح المنزلقه ومعدل الاستهلاك• لقد اظهرت النتائج امكانيه عاليه في تحقيق هدف البحث المتمثل بتحسين الخصائص التريبولوجيه للزيت المستخدم بسبب الطبقه الواقيه المتكونه عند الاسطح المتلامسه التي تعمل على زيادة المساحه السطجيه للسطوج المتلامسه وبالتالي نقليل الاحتكاك والاستهلاك، فقد انخفضت قيمة معامل الاحتكاك بحدود ( 1.5 - 2) مره ومعدل الاستهلاك بحدود( 3- 3.5) مره على التوالي ودلك باضافة (3.5- 4.5)% غم/لتر من مسحوق (نيكل - ثنائي كبريتيد المليبدنيوم ) الى الزيت بالمقارنه مع الحاله عند استخدام الزيت بدون اضافات•


Article
Development of High Performance (Mechanical and Wear Properties) of AA 6061-Hybrid Nano Composites Via Liquid Metallurgy Route
تطوير الاداء العالي للخواص الميكانيكية والترايبولجية للمركب النانوي الهجين لسبيكة المنيوم 6061 بواسطة السباكة المتحركة

Loading...
Loading...
Abstract

This research is devoted to study the influence of different weight percent concerning to the additions of Ti and Cu on mechanical and tribological properties of AA6061. The composite materials consist of different weight percentage of Ti (0.2, 0.4, and 0.6) wt% and constant weight percentage of Cu (0.2) wt% which were fabricated by liquid metallurgy route technique. Microstructural characterization and phases have been examined by using SEM (scanning electron microscopic).SEM examination showed uniform distribution of nano Ti and Cu in AA6061. The consequences of mechanical tests demonstrated clear enhancement in mechanical properties, such as ultimate tensile strength, yield strength, young modulus, ductility% and hardness at additive percentage of 0.4% Ti+0.2%Cu nano particles incorporated into molten AA6061. Percentage of enhancement ultimate tensile strength is about 73.3%, yield strength about 82.7%, young modulus is about 21.2%, the Vickers hardness about 42.6% and the decreasing in ductility was about 25.2% compared with the metal matrix (AA6061). The wear rate test was performed by using pin on disc rig for both hybrid nano composite and base metal (AA6061) under various loads (10,15and 20) N with sliding speed (1.282) m/sec at a (10) min’s time. The results showed a decrease in wear rate at 0.4%Ti+0.2%Cu compared with the base metal (AA6061). Improvement percentage of wear rate is about 105% at 20 N load.

اتجه البحث الحالى الى دراسة تأثير نسب وزنية مختلفة للمواد نانوية Ti,Cu بأضافتها الى سبيكة الاساس على الخواص الميكانيكية والترابولجية وتداخل التأكل الكيمياوي الكلالي والموصفات الكهربائية لسبيكة المادة الاساس حيث كان المركب النانوي يحتوي على قيم مختلفة لTiوهي 0.6%,0.4%,0.2% مع ثابت النسبة الوزنية لCu ب .0.2% وتم تصنيع النماذج بطريقة السباكة بالتحريك تم فحص التركيب المجهري بأستخدام المجهر الضوئي والمسحي الالكترونيSEM حيث ان فحص SEM اعطى توزيع منتظم للTi وCu في سبيكة الالمنيوم 6061. الاختبارات الميكانيكة التي اجريت اعطت بشكل واضح تحسن في المواصفات الميكانيكية كمقاومة الشد العظمى واجهاد الخضوع ومعامل يونك والمطيليه والصلادة للتراكيب النانوية، فكانت افضل مواصفات اعطاها هي التركيب النانوي 0.4%Ti+0.2%Cu حيث اعطى نسبة تحسن لمقاومة الشد العظمى حوالي 73.3% واجهاد الخضوع حوالي 82.7% ومعامل يونك 21% وصلادة فيكر حوالي 42.6%وانخفاض في المطيلية حوالي 25.2% مقارنة مع المادة الاساس. تم انجاز فحص معدل البلى بأستخدام جهاز القرص والدبوس للتركيب النانوي الثنائي لتقوية النانو والمعدن الاساس (AA6061 ) تحت عدة احمال (10,15,20 N ) بسرعة m/sec1.282 وبزمن min10 .أوضحت النتائج نقصان في معدل البلى لحالة التركيب النانوي 0.4%Ti+0.2%Cu مقارنة مع المعدن الاساس وأعطت تحسن بمعدل البلى مقداره %105عند الحمل N20 .