The effect of gold nanoparticles on WO3 thin film
تاثير الجزيئات النانوية للذهب على الاغشية الرقيقة للتنكستن

Loading...
Loading...
Abstract

Chemical spray pyrolysis technique was used at substrate temperature 250 ˚C with annealing temperature at 400 ˚C (for 1hour) to deposition tungsten oxide thin film with different doping concentration of Au nanoparticle (0, 10, 20, 30 and 40)% wt. on glass substrate with thickness about 100 nm. The structural, optical properties were investigated. The X-ray diffraction shows that the films at substrate temperature (250 ˚C) was amorphous while at annealing temperature have a polycrystalline structure with the preferred orientation of (200), all the samples have a hexagonal structure for WO3 and Au gold nanoparticles have a cubic structure. Atomic force microscopy (AFM) was used to characterize the morphology of the films. The optical properties of the films were studied using UV-Vis spectrophotometer within the wavelength in the range (300-1100) nm. The optical energy gap of the films was (2.80) eV for WO3 and it decreased at annealing temperature (400 ˚C) equal to (2.65) eV. And finally the optical constants such as refractive index, real and imaginary dielectrics, absorption coefficient, absorption, transmission, and extinction coefficient were investigated.

اُستخدامت طريقة التحليل الكيميائي الحراري عند حرارة 250 ˚Cو لدنت هذه الاغشية لمدة ساعة بحرارة 400 ˚C, لترسيب اغشية رقيقة من اوكسيد التنكستن بتراكيز تطعيم مختلفة من جزيئات الذهب النانوية (0, 10, 20, 30 و 40) % wt., على قواعد زجاجية وبسمك حوالي 100 nm, اُجريت الفحوصات التركيبية والبصرية, بينت من الخصائص التركيبية للاغشية المحضرة على الارضيات الزجاجية باستخدام حيود الاشعة السينية XRD انها تمتلك طور غير متبلور عند حرارة 250 ˚C, وتمتلك تركيب متعدد البلورات وبالطور السداسي لاوكسيد التنكستن وبالاتجاه المفضل 200)) وان اغشية WO3 المشوبة بالذهب لها تركيب في الطور مكعب عند حرارة تلدين 400 ˚C اُستخدم المجهر القوة الذرية لتعيين طبيعة السطح كما درست الخصائص البصرية باستخدام مطياف الاشعة فوق البنفسجية والاشعة المرئية مع طول موجي يتراوح بين nm 300-1100)). وكانت فجوة الطاقة البصرية لاغشية التنكستن (2.80) eV تناقصت مع حرارة التلدين الى .(2.65) eV وتم حساب الثوابت البصریه الاخرى مثل معامل الانكسار, النفاذية, الامتصاصية, معامل الخمود وثابت العزل الحقیقي والخیالي, ومعامل الامتصاص للاغشیه المحضره.


Article
The effect of gold Nanoparticles on Structural and Electrical properties of WO3 thin films
تاثير الجزيئات النانوية للذهب على الخواص التركيبية والكهربائية لاغشية اوكسيد التنكستن الرقيقة

Loading...
Loading...
Abstract

Chemical spray pyrolysis technique was used at temperature 250˚C with annealing temperature at 400C˚( for 1hour) to deposition tungsten oxide thin film with different doping concentration of Au nanoparticle (0, 10, 20, 30 and 40) wt.% on glass substrate with thickness about 100 nm. The structural and electrical properties were investigated. The structure properties shows that the films at substrate by x-ray diffraction (XRD) temperature (250˚C) was amorphous structure while at annealing temperature have a polycrystalline structure with the preferred orientation of (200) , all the samples have a hexagonal structure for WO3 and Au gold nanoparticles have a cubic structure .The mechanisms of dc-conductivity of un-doped WO3 and doped with Au (10,20,30 and 40) wt.% thin films at the range (303 to 473) K have been discussed , there is decrease in conductivity with the increase in the doping concentration and hall measurements show that all films have a negative hall coefficient and nH increases with the increase of Au dopant ratio and decreasing in carrier mobility (μH) with increasing of Au .

اُستخدمت طريقة التحليل الكيميائي الحراري عند حرارة القواعد250˚Cولدنت هذه الاغشية لمدة ساعة بحرارة400˚C, لترسيب اغشية رقيقة من اوكسيد التنكستن بتراكيز تطعيم مختلفة من جزيئات الذهب النانوية (0,10,20,30 and 40) wt.% ,على قواعد زجاجية وبسمك 100 nm , اُجريت الفحوصات التركيبية والكهربائية وتبين من الخصائص التركيبية للاغشية المحضرة على الارضيات الزجاجية باستخدام حيود الاشعة السينية XRD انها تمتلك تركيب غير متبلور عند حرارة250˚C,وتمتلك تركيب متعدد التبلور وبالتركيب السداسي لاوكسيد التنكستن وبالاتجاه السائد 200))وان اغشية WO3 المشوبة بالذهب لها تركيب مكعبي الطور عند حرارة تلدين 400C˚ , كما نوقشت ميكانيكية التوصيلية المباشرة لغشاء التنكستن النقي والمشوب بالذهب بتراكيز مختلفة0,10,20,30 and 40) wt.% ) ولمدى 303-473) K),هناك نقصان في التوصيلية مع زيادة تركيز التطعيم ,وبينت قياسات هول ان كل الاغشية تمتلك معامل هول سالب و( nH ) تزداد مع زيادة نسبة التشويب Au)) ونقصان في تحركية الحاملات ( Hμ) مع زيادة نسبة التطعيم (Au).

Listing 1 - 2 of 2
Sort by
Narrow your search

Resource type

article (2)


Language

English (2)


Year
From To Submit

2018 (2)