Article
Effect of chopped cane sugar fibers on some Mechanical Properties of Phenol-Formaldehyde and Urea-Formaldehyde Composites
تأثيرألياف قصب السكر المقطعة على بعض الخصائص الميكانيكية لمتراكبات الفينول- فورمالديهايد و اليوريا- فورمالديهايد

Author: Mohammad Nadhum B. AL-Baiati
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2012 Volume: 10 Issue: 1 Pages: 110-117
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

This research was carried out by reinforcing the matrix (phenol-formaldehyde and urea-formaldehyde) resins respectively, with natural material (cane sugar fibers) . Each specimen was reinforced with different weight percentage, (5% , 10% , 15% , 20% and 25 % ) of chopped cane sugar fiber . After preparation of composite material, some of the mechanical properties, flexural, tensile and impact tests were studied of prepared specimen.The results obtained from these tests indicated that, 25% from chopped Cane sugar reinforcing with urea-formaldehyde composite has the higher values of mechanical properties, compared with 5% from same composite, and 25% from chopped Cane sugar reinforcing with phenol-formaldehyde composite has the higher values of mechanical properties, compared with 5% from same composite.

في هذا البحث تم تدعيم المادة الاساس ( الفينول- فورمالديهايد و اليوريا - فورمالديهايد ) بمواد طبيعية (ألياف قصب السكر المقطعة ) . جميع النماذج دعمت بنسب وزنية مختلفة (5% , 10% ,15 % ، 20% و 25% ) من ألياف قصب السكر المقطعة . بعد تحضير المتراكبات, تم دراسة بعض الخصائص الميكانيكية للنماذج المحضرة وهي أختبار قوة الأنحناء ، أختبار قوة الشد وأختبارمقاومة الصدمة . أن النتائج التي تم الحصول عليها هده الأختبارات تشير الى أن متراكب اليوريا- فورمالديهايد مع نسبة وزنية 25% من ألياف قصب السكر المقطعة يمتلك قيم أعلى للخواص الميكانيكية ، مقارنة مع نفس المتراكب الحاوي على نسبة وزنية 5% من الألياف . كذلك أظهرت النتائج أن متراكب الفينول- فورمالديهايد مع 25 % من الألياف ، يمتلك قيم أعلى للخواص الميكانيكية ، مقارنة مع نفس المتراكب الحاوي على نسبة وزنية 5% من الألياف .


Article
Synthesis of several Urea plast Resins using Different Aldehydes Preparation of some Alkyde Resins and Empolyment of the prepared Resins as Additives for AZO Dyes
تحضير راتنجات اليوريا بلاست وراتنجات الالكايد وأستخدامهما في تحضير أصباغ جديدة مع بعض مركبات الازو المحضرة

Loading...
Loading...
Abstract

Urea formaldehyde resin was prepared by using basic media by yield 95%. The Remaining of ureaplasts resin were prepared in acetic acid media by high yield. Alkyde resins were prepared by condensation polymerization by react Succinic, Maleic, Phthalic anhydrides with Ethylene glycol or Glycerol. Select samples of the prepared alkyde resins were mixed with Azo dyes in special ratio. The mixtures were used as coatings for wood, and compaised with pure dyes. The Coating that some alkyde resins showed better adhesion from using dyes alone. Preparation of wood coating by mixing ureaplast resins and alkyde resins with Azo dyes in special ratios. The coating showed better adhesion, brighter colors and better resistance to heat from Preceding coat

تم تحضير راتنج اليوريا فورمالدهايد بأستخدام وسط قاعدي وبمنتوج 95%، اما بقية الراتنجات اليوريا بلاست فتم تحضيرها في الوسط الحامضي وبمنتوج عالي. راتنجات الالكايد تم تحضيرها بالبلمرة التكاثفية من خلال مفاعلة أنهدريدات السكسنيك والماليك والفثاليك مع كلايكول الاثيلين أوكليسيرول. تم أختيار بعض راتنجات الالكايد وبعض صبغات الازو المحضرة وخلطت بنسب معينة وأستعملت كطلاء للاخشاب وتم مقارنتها مع الاخشاب المطلية بصبغات الازو فقط، حيث أظهر الطلاء الممزوج بالالكايد ثباتاً لونياً ومقاومة أفضل من تلك الصبغات المستعملة بمفردها. تم تحضير طلاء للاخشاب من خلال مزج راتنجات اليوريا بلاست وراتنجات الالكايد مع صبغة الازو المحضرة وبنسب معينة حيث أظهر مقاومة وثباتاً حرارياً أكبر من الطلاء السابق.تم تشخيص الراتنجات بأطياف U.Vو I.Rوالتحاليل الحرارية TG وDTG وقد دلت النتائج على صحة التراكيب المقترحة.