Article
Workability of Hybrid Fiber Reinforced Self-Compacting Concrete

Authors: Anmar S. Dhaher --- Samer F. Daoud --- Tareq S. Al-Attar
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 2 Part (A) Engineering Pages: 111-116
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The aim of this work is to evaluate the effect of adding different types of fibers on the fresh properties of the self-compacting concrete, SCC. The used types of fibers were steel (with volume ratios of 0.75, 1.0 and 1.25 %) and polypropylene fibers (0.10 and 0.15 %) and a hybrid system of these fibers (0.65 % steel and 0.10 % polypropylene). The conducted tests in the fresh state were slump flow, T500, V-funnel, and L-box. It was noticed that increasing the volume fraction of fibers would lead to decrease in the workability of SCC. According to EFNARC requirements for SCC, many test results were nonconforming. It was also concluded that polypropylene fibers have higher detrimental effect on fresh properties of SCC than steel fibers and that was attributed to the ability of polypropylene to absorb part of mixing water.


Article
The Production of Self-Compacting Concrete with Normal Cement Content
انتاج خرسانة ذاتية الرص ذات محتوى سمنت اعتيادي

Authors: Luma A. G. Al- Rawi --- Tariq S. Al-Attar --- Shakir A. Al-Mishhadani
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 2 Pages: 310-320
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The main object of this work is to evaluate the possibility for using reasonable cementcontent and fine materials to reduce costs of expensive chemical admixtures needed for themanufacturing of self-compacting concrete (SCC). In this work, three values of cement contentare used (rich, medium and lean mixes) with cement content of 400, 300 and 250 kg/m3respectively . Two maximum aggregate sizes of (10 and 20mm) for each cement content areused. The powder content material is (cementations + filler ) is maintained constant (500kg/m3)while the W/cm ratio ranges from 0.43 to 0.68. 10% Reactive Metakaolin Class N is used as apartial replacement by weight of cement. On the other hand, limestone dust was used as apartial replacement by weight of the powder content Tests were carried out on all mixes toobtain the properties of fresh concrete in terms of viscosity and stability. The results showed thatincreasing the percentage of filler (limestone dust) from 20% in rich mixes to50% in lean mixesof the total weight of the powder content reduces the amount of cement in SCC withoutsignificant effect on the fresh properties of the SCC mixes. This conclusion is significant fromthe economical point of view. The mechanical properties of hardened SCC mixes are alsoassessed. (compressive strength, modulus of elasticity ). The results obtained from this workshow that it is possible to produce SCC with different levels of cement content (250 to400kg/m3)using local available materials which satisfy the requirements of this type of concrete .The testdata collected indicate that these materials can be used in the manufacturing of economical SCC.

الهدف الرئيسي لهذا العمل هو تقييم امكانية الأستخدام المعقول لمحتوى السمنت و المواد الناعمة لتقليل الكلف الباهظة للمضافات الكيميائية التي نحتاجها في انتاج الخرسانة ذاتية الرص .في هذا العمل ، هناك ثلأثة قيم300 و ، لمحتوى السمنت ( الخلطات الغنية ، الخلطات المتوسطة ، الخلطات القليلة ) مع محتوى السمنت( 400 20 ملم ، استعمل لكل محتوى اسمنت . محتوى ، 250 كغم /م 3 )على التوالي . و مقاسين من الركام الخشن 1010 % ميتاكاؤلين عالي . ( تتراوح بين ( 0.43 الى 0.68 W/cm المواد المسحوقة ( 500 كغم /م 3) بينما نسبة استعمل كاحلأل جزئي من وزن السمنت ، بينما مسحوق الحجر الجيري استعمل كاحلأل N الفعالية صنف جزئي من وزن محتوى المسحوق الكلي . النتيجة اظهرت بان الزيادة في نسبة الحجر الجيري المطحون من %20 في الخلطات الغنية بمحتوى السمنت الى 50 % في الخلطات القليلة ، من الوزن الكلي لمحتوى المسحوق ادى الى نقصان في محتوى السمنت من غير تاثير يذكر في خواص الخرسانة الطرية ، هذا الأستنتاج مهم جدا من وجهت النظر الأقتصادية .الخواص الميكانيكية للخرسانة ذاتية الرص كانت ايضا تخمينية (مقاومة الانضغاط ،معامل المرونة الستاتيكي ). النتائج في هذا العمل اظهرت امكانية انتاج خرسانة ذاتية الرص بمستويات مختلفة من السمنت من ( 250 الى 400 كغم /م 3) باستعمال مواد محلية متيسرة ، والتي تلبي متطلبات هذا النوع من الخرسانة . نتيجة الفحص التى جمعت بنيت بان تلك المواد يمكن استع مالها في تصنيع خرسانة ذاتية الرص لأغراض اقتصادية .


Article
EFFECT OF SULFATES IN FINE AGGREGATE ON SOME PROPERTIES OF SELF COMPACTING CONCRETE INCORPORATING HIGH REACTIVE METAKAOLINE

Loading...
Loading...
Abstract

Fine aggregate contaminated with interior sulfates is an important problem of concretemanufacture in Iraq. It is difficult to obtain well graded fine aggregate with sulfates content withinstandard specifications. The main objective of this study is to investigate the effect of internalsulfates in sand on some properties of self compacting concrete (SCC) by adding natural gypsum tofine aggregate as a partial replacement by weight. In this work, two basic categories of selfcompactingconcrete are used: (SCC) incorporating limestone powder (LSP) and SCCincorporating 10% high reactivity metakaolin (HRM) Class N plus limestone powder(LSP) .Fourlevels of sulfates contents in fine aggregate were investigated, these levels were ( 0.37, 0.5, 1.0,and 1.5)% which it is equal to(3.74, 3.99, 4.96 and 5.93)% by weight of cement for mixescontained limestone powder (LSP) and it is equal to (3.76, 4.01,4.98 and 5.96) % by weight ofcement for mixes contains high reactivity metakaolin (HRM) Class N plus limestonepowder(LSP). The experimental program is divided into two parts; the first part is devoted toproduce self compacting concrete by using superplasticizers and fillers then determine theworkability. Different test methods are adopted such as slump flow and T50 cm, V-funnel, VFunnelat T5 minutes, L-box and sieve segregation test. The second part is devoted to study themechanical properties such as the compressive strength and splitting tensile strength. The resultsobtained from this work show that the optimum gypsum content was 0.5% by weight of fineaggregate for all mixes which gives increases in the compressive strength by a range(5.9 -10.1)%and in the splitting tensile strength by a range (1.2 – 8.5 )% for mixes of (SSC) with (LSP) and(LSP +HRM).

إن وجود أملاح الكبريتات الداخلية هي من المشاكل المهمة التي تواجه صناعة الخرسانة في العراق. فمن ألصعوبة أيجاد ركام ناعم مطابق للمواصفات مع حدود المواصفات الحالية لحدود أملاح الكبريتات . ألهدف من هذا العمل هو دراسة تأثير أملاح الكبريتات في الركام الناعم على بعض الخواص الميكانيكية للخرسانة ذاتية الرص بإضافة الجبس الطبيعي إلى الركام الناعم كإحلال جزئي من وزنه. في هذا البحث تم استعمال نوعين أساسين من الخرسانة ذاتية الرص وهي : خرسانة ذاتية الرص حاوية على مسحوق الحجر الجيري و خرسانة ذاتية الرص حاوية على 10% ميتاكاؤلين عالي الفعالية و مسحوق الحجر الجيري تم دراسة أربع نسب لمحتوى الكبريتات (0.37, 0.5, 1.0, and 1.5)%. في الركام الناعم والذي يساوي (3.74,3.99,4.96,5.93)% من وزن الإسمنت للخلطات التي تحوي على الحجر الجيري كمادة مالئة ومساوي إلى(3.76, 4.01 ,4.98 and 5.96) % من وزن السمنت للخلطات التي تحوي 10% ميتاكاؤلين عالي الفعالية و مسحوق الحجر الجيري . برنامج ألعمل يقسم إلى جزأين ; ألجزء الأول هو أنتاج خرسانة ذاتية الرص باستعمال الملدنات و المادة المالئة ثم أيجاد قابلية التشغيل . تم استخدام طرق فحص مختلفة مثل فحص جريان الهطول, القمع على شكل حرف V, القمع على شكل حرف Vبعد مرور 5 دقائق , الصندوق على شكل حرف L فحص مقاومة الانعزال. ألجزء الثاني هو دراسةالخواص الميكانيكية مثل مقاومة الانضغاط و مقاومة شد الانشطار. أظهرت النتائج إن محتوى الجبس الأمثل في الخرسانة ذاتية الرص عند نسبة 0.5 % من وزن ألركام الناعم لكل الخلطات والتي تعطي زيادة في مقاومة الانضغاط تراوحت بين (5.9-10.1 )% و( 1.2- 8.5)% في مقاومة شد الانشطار. الزيادة الإضافية في محتوى الكبريتات بعد ألنسبة المثلى يسبب تناقص في المقاومة تتراوح بين ( 1.4 – 7.8 )% في مقاومة الانضغاط و ( 2.1- 3.3)% في مقاومة شد الانشطار عندما تزداد نسبة الكبريتات في الركام الناعم من (0.37 – 1 %(و (6.4- 9.9)% في مقاومة الانضغاط و (3.8-5.6 ) % في مقاومة شد الانشطار عندما تزداد نسبة الكبريتات في الركام الناعم من (0.37 – 1.5) % على التوالي.