Article
Physical and Mechanical Properties of Synthesized Doped Nanoferrite
دراسة الخواص الفيزيائية والميكانيكية للفرايت النانوي المطعم

Authors: Zainab I. Dhary زينب ابتهاج ضاري --- Mohammed S. Hamza محمد صلاب حمزة --- Fadhil A. Chyad فاضل عطية جياد
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2016 Volume: 12 Issue: 2 Pages: 10-17
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Nanoferrite materials have been synthesized by sol-gel auto combustion method. The effect of doping different percentages of Y2O3 (0.34 µm) on the physical and mechanical properties of selected mixed ferrite [(Li2.5Fe0.5) 0.9(Co4Fe2O4) 0.1] by adding 10% Cobalt ferrite was studied. Physical properties (i.e. .density, porosity and water absorption) were affected by the doping, where the density increased about 32% at 6 wt% Y2O3, while porosity has a drastically decreased about 80% at 6% Y2O3 and has a correlation effect on the mechanical properties(Splitting tensile strength and Vickers microhardnss). The fracture strength at 1 % wt. of Y2O3 has doubled value of the undoped sample and then decreased. The same behavior shows with the testing of Vickers micro hardness.SEM ( Scanning electron microscopy ) micrographs revealed that the microstructure of the fracture surface of the samples consist of detached approximately closely packed particles and also showed the formation of micro agglomerated particles with some voids . By doping with Y2O3 the pores decreased and a dense material obtained

حضرت مواد الفرايت النانوية بطريقة ( السول – جيل ) ذاتية الاحتراق وتم دراسة تأثير اضافة نسب مختلفة من اليتيريا ذو حجم حبيبي (0.34) مايكرون على الخواص الفيزيائية والميكانيكية للفرايت المحضر[(Li2.5Fe0.5)0.9(Co4Fe2O4)0.1] . ان الخواص الفيزيائية مثل ( الكثافة والمسامية وامتصاصية الماء ) تأثرت باضافة اليتيريا حيث ازدادت الكثافة بزيادة نسب الاضافة اما المسامية فقد تقلصت بصورة كبيرة والتي لها تأثير على الخواص الميكانيكية مثل ( متانة الشد وصلادة فيكرز ) . تضاعفت متانة الكسر عند بنسبة (1%) من اليتيريا ومن ثم تناقصت . نفس التصرف عند حساب صلادة فيكرز. اظهرت صور الالكتروني الماسح بأن التركيب المجهري لسطح الكسر للنماذج يحتوي تقريبا على حبيبات متجاورة متراصة وكذلك تكوين دقائق مايكروية متجمعة مع وجود فجوات . وبعد باضافة اليتيريا قلت المسامات وتم الحصول على مادة اكثر تراصاً.


Article
Study of Some Mechanical Properties for Aluminum Reinforced by Alumina Fibers

Authors: Shaker Jahel Eddres --- Ali Hubi Haleem --- Newal Muhammad Dawood
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2015 Volume: 23 Issue: 3 Pages: 607-615
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The aim of this research was to study the ability of improving the impact resistance and Vickers microhardness of composite material based on aluminum metal reinforced by 5, 10, and 15wt.% of chopped alumina fibers. Stirring casting method has been used to make composite material by using vortex technique which is used to pull the chopped alumina fibers to inside the melted aluminum and distributed them homogeneously.Regarding the impact test, results shown that the impact resistance of the composite material are more than that in the aluminum metal and these values are increased with increasing of the amount add fibers and they reached maximum values at (10 wt. %). Then they are decreased at (15 wt. %) but these values remain at higher values than that in the aluminum metal. While the Vickers microhardness reached maximum values at (15 wt. %).

يهدف البحث الحالي إلى دراسة تحسين مقاومة الصدمة و صلادة فيكرز المايكروية لمادة مركبة ذات أساس من معدن الألمنيوم مقوى بألياف الألومينا المقطعة وبنسب وزنية (5%, 10%, 15%). وتم استخدام طريقة السباكة بالمزج في تصنيع المادة المتراكبة باستخدام تقنية الدوامة والتي تعمل على سحب ألياف الألومينا ألمقطعه إلى داخل منصهر معدن الألمنيوم وتوزيعها خلاله بشكل متجانس.أظهرت نتائج اختبار الصدم إن مقاومة الصدمة للمادة المركبة أعلى مما هي عليه لمعدن الألمنيوم وتزداد هذه القيم مع زيادة النسب الوزنية لألياف الألومينا والى حد (10%) ثم تسلك سلوكا مغايرا لكنها تبقى محافظة على قيم أعلى مما هي عليه لمعدن الألمنيوم . في حين تصل صلادة فيكرز المايكروية أعلى قيمها عند التقوية بألياف الألومينا المقطعة وبكسر وزني ((15%.