Search results: Found 143

Listing 1 - 10 of 143 << page
of 15
>>
Sort by

Article
The effect of annealing and the influence of Gamma-ray on the optical properties of nanostructure Zinc Oxide Thin Films
تأثير التلدين والتشعيع بأشعة كاما على الخواص البصرية لأغشية اوكسيد الخارصين الرقيقة ذات التركيب النانوي

Author: Nada M. Saeed ندى محمد سعيد
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2010 Volume: 8 Issue: 13 Pages: 82-88
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The semiconductor ZnO is one of II – VI compound group, it is prepare as thin films by using chemical spray pyrolysis technique; the films are deposited onto glass substrate at 450 °C by using aqueous zinc chloride as a spray solution of molar concentration 0.1 M/L. Sample of the prepared film is irradiating by Gamma ray using CS 137, other sample is annealed at 550°C.The structure of the irradiated and annealed films are analyzed with X-ray diffraction, the results show that the films are polycrystalline in nature with preferred (002) orientation. The general morphology of ZnO films are imaged by using the Atomic Force Microscope (AFM), it constructed from nanostructure with dimensions in order of 77 nm. The optical properties of the prepared films are studied by using measurement from UV-VIS-NIR spectrophotometer at wavelength within the range (300-900) nm. The optical results show that the absorption of the prepared films are decreases after annealing and increases after irradiation. The optical constants such as the refractive index and the photoconductivity are calculated before and after annealing as a function of the photon energy. Also the values of the optical energy gap are calculated, it is 3.3 eV and 3.1 eV for the direct and indirect allowed transition respectively; these values are reduced after annealing.

يعتبر اوكسيد الخارصين ( ZnO) احد أشباه الموصلات ضمن المجموعةII – VI , تم تحضير هذا المركب بشكل أغشية رقيقة على أرضية زجاجية بدرجة حرارة أساس 450 °C وذلك باستعمال تقنية الرش الكيماوي الحراري, تم تحضير محلول الرش من كلوريد الخارصين بمولارية مقداره 0.1 M/L, تم تعريض نموذج من الأغشية المحضرة لأشعة كاما ( (γ-ray باستعمال المصدر المشع CS 137 وتم أيضا تلدين بعض النماذج المحضرة من أغشية ZnO عند درجة حرارة 550 مئوي. تم فحص الأغشية الملدنة والمشععة بواسطة حيود الأشعة السينية ومن تحليل النتائج تبين أن جميع الأغشية المحضرة هي نوع متعددة التبلور. (Polycrystalline). تم دراسة تركيب الغشاء بإجراء فحوصات بواسطة المجهر Atomic Force Microscope (AFM) وتبين أن الغشاء ذو تركيب نانوي بمعدل للحجم البلوري 77 nm .درست الخواص البصرية للأغشية المحضرة باستعمال مطياف يعمل ضمن الأطوال الموحية الفوق البنفسجية- المرئية- والقريبة من تحت الحمراء NIR) (UV- VIS- لمدى الأطوال الموحية nm 300-900, أظهرت الدراسة البصرية بان الأمتصاصية تقل بعد التلدين و تزداد عند التشعيع. تم حساب بعض الثوابت البصرية والتي شملت حساب معامل الانكسار ,التوصيلية الضوئية قبل وبعد التلدين كدالة لطاقة الفوتون عند للأطوال الموحية المذكورة وقد تبين أن للتلدين أثر واضح على قيم الثوابت البصرية . تم ايضا حساب قيم فجوة الطاقة البصرية وكانت قيمتها,3.3 eV 3.1 eV لكل من الانتقال الإلكتروني المباشر المسموح والانتقال الإلكتروني الغير مباشر المسموح على التوالي وقد تبين أن قيم فجوة الطاقة البصرية تقل عند التلدين.


Article
Optoelectronic properties of ZnO/PS/n-Si Heterojunctions

Author: Khawla S. Khashan
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2008 Volume: 26 Issue: 4 Pages: 442-448
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work a colloid of nanocrystalline ZnO particles is prepared bychemical method, and then sprayed on porous silicon substrate which is preparedby electrochemical etching under a current density of 15mA/cm2 for 10 min. Theinitial radius of the ZnO particles is found to be (2.2 nm). FTIR spectra exhibit thepresence of Zn – O bond which indicates the formation of ZnO particles. Alsospectra reveals the formation of SiHx (x=1-2) and Si-O bond which indicates thepresence of porous layer. High performance rectifying was obtained, with highphotoresponsivety of 0.54 A/W at 400 nm. The corresponding quantum efficiencywas 166.7%.The results show that ZnO on porous silicon (PS) structures will act asgood candidates for making highly efficient photodiodes.

في ھذا البحث تم تحضیر عالق البلورة الدقیقھ لجزیئة اوكسید الخارصینالكیمیائیة ، وبعد ذلك تم رشھ على سیلكون مسامي محض ر بطریق ھ وج ود الاظھارالكھروكیمی ائيZnO 10 . وج د ان نص ف القط ر الاول ي لجزیئ ات min 10 ل زمن mA/cm تح ت كثاف ة تی ار 2وایضا ان . ZnO والتي تشیر لتكوین جزیئة Zn-O اصرة FTIR 2.2 . یظھر من طیف nm ھووالتي تشیر الى وجود الطبقة المسامیة Si-O واصرة SiHx(x=1- الطیف یكشف تكوین اصرة ( 20.54 ) عن د ( A/W ) .تم الحصول عل ى كف اءة تق ویم عالی ھ م ع أس تجابیھ ض وئیھ عالی ھ تص ل400 ). ھذا یقابل كفاءة كمیة (% 166.7 ) . تبین النتائج ان اوكسید الخارصین على تراكیب nmالسلیكون المسامي سیعمل كبدیل جید لصنع دایودات ضوئیة بكفاءة عالية


Article
Preparation and characterization ZnO nanoparticles and study of morphology at high temperature
تحضير و دراسة خواص المركب النانوي اوكسيد الزنك ودراسة خواصة السطحيه عند درجات حرارة عالية

Author: Mundher.A.Hassan منذر عبد الحسن خضير
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2012 Volume: 10 Issue: 18 Pages: 17-23
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In context of this paper we prepare high purity powder ZnO nanostructures by chemical method at low temperature solution and study the effect off annealing at high temperature, ZnO nanoparticles have been successfully synthesized by chemical method at 0Cᵒ solution. In this method, suddenly reaction is occurred between zinc acetate solution and sodium hydroxide solution at 0Cᵒ, annealing temperature of powder product surfactant plays an important role in morphological changes. The nanostructures have been characterized by X-ray diffraction (XRD), Scanning Electron Microscope (SEM), differential scanning calorimetry(DSC) and UV-visible .analysis Effect of annealing temperatures on the morphology , structure and optical properties is discussed.

في سياق هذا البحث تم تحضير حبيبات بإحجام النانومتر لمادة أكسيد الزنك الشبه الموصلة وبنقاوة عالية وتم استخدام الطريقة الكيميائية في التحضير عند درجات الحرارة المنخفضة (الصفر المئوي ) ويكون إضافة محلول خلات الزنك إلى محلول هيدروكسيد الصوديوم بشكل سريع وفجائي . وتم دراسة الخواص التركيبية لهذه المادة بعد ان تم تعريضها لدرجات الحرارة العالية ودراسة التغيرات التركيبية بواسطة طيف الحيود للأشعة السينية وكذلك باستخدام المكروسكوب الالكتروني ودرست نقاوة المسحوق المحضر باستخدام جهاز التحليل الحراري التفاضلي .وكذلك دراسةخواص الامتصاص البصري باستخدام جهاز امتصاص الأشعة فوق البنفسجية .


Article
PATHOLOGICAL STUDY OF LETHAL CONCENTRATION OF N-ZNO IN COMMON CARP CYPRINUS CARPIO L.
د ا رسة مرضية للتركيز المميت لصغائر اوكسيد الخارصين في اسماك الكارب الشائع Common carp (Cyprinus carpio L.)

Author: S.K.I.AL-Taee A.H.A.AL-Hamdani شهباء خليل اب ا رهيم الطائي ألاء حسين علي الحمداني
Journal: Basrah Journal of Veterinary Research. مجلة البصرة للابحاث البيطرية ISSN: Print:18138497 E; 24108456 Year: 2013 Volume: 12 Issue: 1 Pages: 200-207
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

The lethal concentration of N-ZnO was determined in this study ,juvenile Cyprinus carpio L.mean weight 150±10g which were exposed to different concentration of N-ZnO (10-50 PPM) for 24 hrs ,the mortality rate of fish reached to 100% at 50 ppm concentration while the percentage decreased to 50% when the fish exposure to 30ppm concentration of N-ZnO.The histopathological lesions in the kidney were characterized by hemorrhage in an interstitial nephrotic tissue ,infiltration of inflammatory cells , there was cloudy swelling in the renal tubules . In the gill there were hyper trophy of pillar cells and necrosis in the secondary gill filaments .There were necrosis in the hepatic tissue and hemorrhage and sloughing in the pancreatic tissue.

Keywords

mortality --- necrosis --- N-ZnO.


Article
Fabrication of electro spinning 1D ZnO Nano fibers as UVPhotoconductor
تكوين الياف نانوية لأوكسيد الزنك الاحادي الاتجاه بأستخدام البرم الكهربائي كموصل ضوئي للأشعة فوق البنفسجية

Authors: Raad S. Sabry --- Firas S. Mohammed --- Roonak Abdul Salam A.Alkareem
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 5 Part (B) Scientific Pages: 884-894
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The electrospinning technique was used to fabricate 1D nanofibers of Zinc Oxide (ZnO). Polyvinylpyrrolidone (PVP) ̸ zinc acetate Nano fibers electrospun using solution containing PVP dissolved in ethanol and zinc acetate in distilled water were mixed, followed by calcination at 500°C for 3hours to remove the polymer. XRD pattern show the hexagonal wurtzite structure of ZnO NFs without any impurities. FESEM pictures show a network of nanofibers with diameters less than 100 nm and several micrometers in length of ZnO, these nanostructures increase the ratio of surface area to volume and improve the physical properties of the materials. The Photoluminescence (PL) of the films was studied and the energy gap and the optical properties were estimated. A photoconductor device was constructed by electroding the films with silver conducting electrode (IDE) using screen print method, The result shown that the resistance of the nanofiber films decrease dramatically when exposes to UV light. In addition, the change of conductivity with the change of wavelengths was studied also the photoconductivity was examined under different bias voltage.

تم استخدام تقنية الدوران اللولبي الكهربائي لتحضير الياف نانوية من اوكسيد الخارصين. تم الحصول على الالياف النانوية ل PVP و خلات الزنك من خلال ضخ محلول يتكون من PVP مذاب في الايثانول و خلات الزنك المذاب في الماء المقطر حيث تم مزجهما, يتبعه حرق للغشاء المتكون بدرجة حرارة 500 م° لمدة 3 ساعات للتخلص من البوليمر. يبين نمط ال (XRD) ان اوكسيد الخارصين يكون ذات تركيب سداسي و بدون شوائب. أظهرت صور FESEM شبكة من الالياف النانوية التي تتراوح اقطارها دون ال 100 نانومتر وطولها عدة مايكرومترات. ان هذه التراكيب النانوية تزيد من نسبة المساحة السطحية الى الحجم مما يؤدي الى تحسين الخصائص الفيزيائية للمواد. تم دراسة التألقية الضيائية وكذلك حساب فجوة الطاقة والخصائص البصرية للاغشية المحضرة. تم بناء الموصل الضوئي بعد تقطيب الاغشية ب (IDE) باستخدام طريقة الطباغة على الشبكة واظهرت النتائج انخفاضا كبيرا في مقاومة الالياف النانوية عند تعرضها للضوء ضمن المنطقة فوق البنفسجية


Article
Characterizations study ZnO-TiO2 nano rods thick films as Photo detector
دراسة خصائص الاغشیة السمیكة ZnO-TiO2 النانوية التركيب ك كاشف ضوئي

Authors: Raad Sadoon --- Osama AbdulAzeez
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 6 Part (B) Scientific Pages: 1075-1081
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

First,ZnO nanorod s were su ccessfu lly synthesized by simple evaporationmethod,u sing single stage controllable horizontaltu be fu rnace and qu artz tu be withou tcatalyst.The ZnO nano powd erwas mix ed with (10 and 20%)of TiO2 powd er(weightratio),then ZnO -TiO 2 thickfilms were synthesized u singsimple,low-cost efficient screen print techniqu e. The thick films were heated at 500 C ˚ for one hou rto remove the organic bind erand anyimpu rities.The prepared thickfilms were examined withX -Ray,and FESEM to stu d y the stru ctu raland morphology of the films,the X -ray results show that the films are polycrystalline with sharp and high intensity peaks indicating high crystalinity of the product.The FESEM pictures show nanorods with diameters less than 100 nm and several micrometers in lengthof ZnO withTiO 2 nanoparticles.ZnO -TiO 2 device was built up by electroding the thick films.The I-V characterization of the films were studied in dark and light,then photo detection parameters were estimated and it was found to be efficient and high response in UV range detection

باستخدام تقنیة التبخیر (nanorod s) في البدایة تم تحضیر اوكسید الخارصین بتراكیب نانویةالبسیط باستخدام فرن انبوبي وانبوبة كوارتز بدون عامل مساعد حیث تم تبخیر معدن الخارصین عند10 على التوالي. - درجة حرارة 7 00 م وبوجود غاز الاركون والاوكسجین وبنسبة خلط 90واستمرت العملیة مدة تم تصنیع اغشیة سمیكة من الخلیط باستخدام تقنیة الطباعة على الشبكة وھيبسیطة وذات كلفة واطئة وفعالة، ان ھذه الطریقة تعطینا اي تصمیم او ابعاد للغشاء وبالتصاقیة جیدةبین الغشاء والقاعدة. بعد ذلك تم تسخین الاغشیة المحضرة لمدة ساعة وعند درجة حرارة 500 مللتخل ص من الرابط العضوي واي شوائب اخرى. تم دراسة الخصائ ص التركیبیة و دراسة السطححیث اظھرت فحوصات الحیود X -ray,FESEM للاغشیة المحضرة بفحصھا ب باجھزة البالاشعة السینیة ان الاغشیة ذات تركیب متعدد التبلور مع قمم حادة ذات شدة عالیة مما یدل علىوباقطار اقل من 100 nano rod s تبلور جید للمادة، واظھرت صور المجھر الالكتروني الماسحنانومتر وباطول مختلفة تصل بضعة مایكومترات ل اوكسید الزنك ان اھذه التراكیب النانویة تعززوتحسن من اداء الكاشف. تم بناء الكاشف الضوئي بعد تقطیب الاغشیة وبنفس تقنیة الطباعة علىالشبكة وتم دراسة الخصائ ص الكھربائیة في الظلام والاضاءة وحساب العوامل الكشفیة للجھز حیثاظھر الكاشف استجابة عالیة كفاءة جیدة في منطقة الاشعة فوق البنفسجیة.


Article
The Optical and Structural Properties of ZnO Films Prepared by Spray Pyrolysis
الخصائص البصريه و التركيبية لاغشيه اوكسيد الزنك ZnO المحضرة بطريقة التحلل الكيميائي الحراري

Author: Shatha Shammon Batros Jamil
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 20 Pages: 6061-6073
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Zinc oxide (ZnO) thin film have been prepared by Spray Pyrolysis technique using zinc acetate dehydrate dissolved in methanol, ethanol and deionized water. A number of techniques including X-ray diffraction (XRD), optical transmission microscope (OTM), Fourier transform infrared (FTIR) spectroscopy, UV-visible were used to characterize andstudy the obtained ZnO thin films. The evolution of preferred crystalline orientation in the ZnO films was systematically investigated and the (002) reflection was the preferred orientation. The optical measurement reveal that films have a maximum transmittance of about 90% and a direct band gap of 3.2 eV.

تم نحضير نماذج من اوكسيد الزنك كاغشيه رقيقة باستخدام تقنيه التحلل الكيميائي الحراري باستخدام خلات الزنك المذابة في الميثانول ، الايثانول والماء المؤين . عدد من التقنيات التي تتضمن حيود الاشعة السينية ، المجهر البصري المعتمد على النفاذية وطيف الاشعة تحت الحمراء ، وطيف المنطقة المرئية وتحت البنفسجية اخذت لتشخيص ودراسة اغشية من اوكسيد الزنك ، كذلك تم الاستدلال علىان احسن اتجاهية تبلور للاغشية المحضرة % كانت عند الانعكاس ( 002 ) . القياسات البصرية اشارت الى نفاذية الاغشية هي بحدود 90 واكبر فجوة طاقة مباشرة هي عند 3.2 الكترون فولت


Article
Zinc Oxide Nanowires Prepared by Oblique Angle Deposition Method

Authors: Wafaa K. Khalef --- Ali A. Aljubouri --- Hayfa G. Rashid
Journal: Iraqi Journal of Applied Physics المجلة العراقية للفيزياء التطبيقية ISSN: 18132065 23091673 Year: 2016 Volume: 12 Issue: 1 Pages: 3-9
Publisher: iraqi society for alternative and renewable energy sources and techniques الجمعية العراقية لمصادر وتقنيات الطاقة البديلة والمستجدة

Loading...
Loading...
Abstract

This paper presents a detailed study of the oblique deposition effect on the morphology, structure and optical properties of ZnO nanowires (NWs) prepared by the deposition of zinc metallic films on glass substrates at different angles (0, 50 and 70°) and then oxidized in air at 650°C. Highly transparent ZnO thin films were successfully prepared by the oblique angle deposition (OAD) technique on glass substrates at room temperature. Atomic force microscopy (AFM) results show that the sample obliquely deposited presented greater roughness as compared with normally deposited ZnO NWs (Ө=0). Optical measurements showed a sharp absorption edge, near 380 nm, in both normal and oblique films. When the oblique angle increased, the absorption edge of spectra demonstrated a red shift with a direct band gap (3.11eV). Scanning electron microscopy (SEM) results show that the OAD led to the formation of bent columnar ZnO NWs. These NWs were inclined from the substrate normal in a direction opposite to the incident vapor beam. Due to the OAD technique, surface diffusion enhanced the self-shadowing effect. When oblique Zn thin film was later oxidized in air at 650°C for a longer time, the ZnO NWs had a needle-like structure, as was clearly shown by SEM images obtained.


Article
Zinc Oxide Nanowires Prepared by Oblique Angle Deposition Method
أسلاك أوكسيد الزنك النانوية المحضرة بطريقة الترسيب بزاوية مائلة

Authors: Wafaa K. Khalef --- Ali A. Aljubouri --- Hayfa G. Rashid
Journal: Iraqi Journal of Applied Physics المجلة العراقية للفيزياء التطبيقية ISSN: 18132065 23091673 Year: 2017 Volume: 13 Issue: 1 Pages: 3-9
Publisher: iraqi society for alternative and renewable energy sources and techniques الجمعية العراقية لمصادر وتقنيات الطاقة البديلة والمستجدة

Loading...
Loading...
Abstract

This paper presents a detailed study of the oblique deposition effect on the morphology, structure and optical properties of ZnO nanowires (NWs) prepared by the deposition of zinc metallic films on glass substrates at different angles (0, 50 and 70°) and then oxidized in air at 650°C. Highly transparent ZnO thin films were successfully prepared by the oblique angle deposition (OAD) technique on glass substrates at room temperature. Atomic force microscopy (AFM) results show that the sample obliquely deposited presented greater roughness as compared with normally deposited ZnO NWs (Ө=0). Optical measurements showed a sharp absorption edge, near 380 nm, in both normal and oblique films. When the oblique angle increased, the absorption edge of spectra demonstrated a red shift with a direct band gap (3.11eV). Scanning electron microscopy (SEM) results show that the OAD led to the formation of bent columnar ZnO NWs. These NWs were inclined from the substrate normal in a direction opposite to the incident vapor beam. Due to the OAD technique, surface diffusion enhanced the self-shadowing effect. When oblique Zn thin film was later oxidized in air at 650°C for a longer time, the ZnO NWs had a needle-like structure, as was clearly shown by SEM images obtained.


Article
دراسة الخصائص البصرية لاغشية ((ZnO غير المشوبة والمشوبة بالمنغنيز(ZnO:Mn) باستخدام تقنية الترسيب البخاري الكيميائي عند الضغط الجوي الاعتيادي (APCVD)

Author: د. صلاح قدوري هزاع القيسي هبة راشد شاكر الجامعة المستنصرية- كلية التربية–قسم الفيزياء
Journal: journal of the college of basic education مجلة كلية التربية الاساسية ISSN: 18157467(print) 27068536(online) Year: 2017 Volume: 23 Issue: 97/علمي Pages: 1-10
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Abstract In this research ,undopedZnO and doped with magnesium ZnO:Mn with different weight percentages of (1, 3, 5,7 )% have been prepared on pre-heated glass substrates up to (400 using atmospheric pressure chemical vapor deposition (APCVD) technique. The optical properties of the samples by using UV-VIS spectroscopy have been investigated. The result showed that transmittance increase and both reflectance and absorbance decrease with an increase in wavelength and doping concentration, while the optical optical energy gap increases with increasing doping concentration. Also other important optical constants such as extinction coefficient, refractive index ,real part of dielectric and imaginary part have been calculated and analyzed.Keywords: ZnO;ZnO:Mn; thin films; APCVD; Optical properties.

دراسة الخصائص البصرية لاغشية ((ZnO غير المشوبة والمشوبة بالمنغنيز(ZnO:Mn) باستخدام تقنية الترسيب البخاري الكيميائي عند الضغط الجوي الاعتيادي (APCVD)د. صلاح قدوري هزاع القيسي هبة راشد شاكر الجامعة المستنصرية- كلية التربية–قسم الفيزياءالخلاصةتم في هذا البحث تحضير ودراسة الخصائص البصرية لاغشية ((ZnO غير المشوبة والمشوبة بالمنغنيز (ZnO:Mn)وبنسب وزنية (% 1,3,5,7) باستخدام تقنية الترسيب البخاري الكيميائي عند الضغط الجوي الاعتيادي (APCVD) على قواعد زجاجية مسخنة الى ( 400 ). درست الخصائص البصرية للاغشية المحضرة بواسطة مطياف المجهر الضوئي(UV-VIS spectroscopy). اظهرت النتائج زيادة النفاذية ونقصان كل من الامتصاصية والانعكاسية مع زيادة الطول الموجي ونسبة التشويب , بينما زيادة في فجوة الطاقة البصرية مع زيادة نسبة التشويب.كذلك تم حساب الثوابت البصرية الاخرى المتمثلة بمعامل الخمود ,ثابت العزل الجزء الحقيقي والخيالي وتحليل النتائج.الكلمات المفتاحية: ZnO , ZnO:Mn, الاغشية الرقيقة , APCVD , الخصائص البصرية

Listing 1 - 10 of 143 << page
of 15
>>
Sort by
Narrow your search

Resource type

article (143)


Language

English (114)

Arabic (21)

Arabic and English (5)


Year
From To Submit

2019 (9)

2018 (20)

2017 (25)

2016 (14)

2015 (15)

More...