Corrosion inhibition of zinc in hydrochloric acid solution using Ampicillin
تثبيط تآكل الزنك في محلول حامض الهايدروكلوريك بأستخدام الأمبسلين

Authors: Khulood A.saleh خلود عبد صالح --- Khalil S. Khalil خليل سعد خليل
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2014 Volume: 55 Issue: 2 Pages: 295-303
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The corrosion behavior of Zn in 0.1 M HCl solution containing various concentration of Ampicillin range (2 x 10-4 – 1x10-3) M was investigated. The corrosion rates were measured by using weight loss measurement and polarization curve, The results of polarization method obtained showed that the rate of corrosion of zinc increased with increasing the temperature from 293K to 323K and the values of inhibition efficiency of ampicillin increased with increasing the temperature and AMP concentrations, the results showed that AMP caused to protection efficiency reached to 88.8% when (1x10-3) M AMP concentration was used in 323K. The coverage (θ) of metal surface by AMP could be obtained from the rate of corrosion in the presence and absence of AMP in the acid solution. A linear relationship was found to exist between the value of (C/θ) and the corresponding AMP concentration (C) indicating that the inhibition action to occur via adsorption mechanism. Changes in the free energy, enthalpy and entropy associated with AMP adsorption have been determined. Apparent energies of activation have been calculated for the corrosion process of zinc in the acid from corrosion rates and Arrhenius Plots.

في هذا البحث, سنقوم بدراسة تثبيط تآكل معدن الزنك في محلول 0,1 مولاري لحامض الهايدروكلوريك الذي يحتوي على تراكيز مختلفة من مثبط الامبسلين في مدى (2 x 10-4 – 10-3) مولاري بأستخدام تقنيات مختلفه وهي طريقة فرق الوزن والطريقه الكهربائيه. نتائج الطريقه الكهربائيه اوضحت ان سرعة التآكل تزداد بزيادة درجة الحرارة من 293 كلفن الى 323 كلفن وان كفاءة المثبط ايضا تزداد بأزدياد درجة الحرارة وتركيز الامبيسلين, وان مثبط الامبسلين يعطي حماية بنسبة %88,8 عند درجة الحرارة 323 كلفن, ويتم ايضا حساب التغير في الطاقة الحرة والانثالبي والانتروبي ونوع امتزاز مثبط الامبسلين على سطح معدن الزنك ويتم ايضا حساب طاقة التنشيط لعملية تآكل الزنك في الحامض من سرعة التآكل ومخطط ارينيوس.


Article
Effect of Rubber Treated by Acidic Solution On Some Mechanical Properties of Rubberize Cement Mortar

Authors: Aziz Ibrahim Abdulla --- Salwa Hadi Ahmed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 13 Pages: 2793-2806
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present work, the properties of rubberize cement mortar containingcrumb rubber treated by acidic solution are tested and compared with normal rubberize and normal cement mortar.The rubber, which is treated by different acidic solution such as: (H2SO4, HCl and CH3COOH) is used as a fine aggregate as avolumetric partialreplacement of sand in cement mortar. The percent of replacement ranged from 5 to 30%.Compressive strength, modulus of rupture and modulus of elasticity (static and dynamic) a retested for all mixes. Cubes of cement mortar also tested by ultrasonic pulse velocity (UPV) and hammer tests method to show the effect of treated rubber on the UPV and hammer tests and to demonstrate the possibility of this methods forestimating the compressive strength of rubberize cement mortar.The results show that the treatment of rubber by acidic solution significantly improves the properties of rubberize cement mortar. Moreover the results show that CH3COOH gives better improvement compared withH2SO4. The treatment of rubber by HCl shows negativeeffects on all cement mortar properties.


Article
Study of effect acidic solution (HCl) and (EP/Al2O3 & EP/ TiO2) hybrid on thermal conductivity of epoxy resin.
دراسة تاثير المحلول الحامضي (HCl) والهجين (EP/Al2O3 & EP/ TiO2) على التوصيلية الحرارية لراتنج الايبوكسي

Loading...
Loading...
Abstract

This research studies the effect of adding micro, nano and hybrid by ratio (1:1) of (Al2O3,TiO2) to epoxy resin on thermal conductivity before and after immersion in HCl acid for (14 day) with normality (0.3 N) at weight fraction (0.02, 0.04, 0.06, 0.08) and thickness (6mm). The results of thermal conductivity reveled that epoxy reinforced by (Al2O3) and mixture (TiO2+Al2O3) increases with increasing the weight fraction, but the thermal conductivity (k) a values for micro and Nano (TiO2) decrease with increasing the weight fraction of reinforced, while the immersion in acidic solution (HCl) that the (k) values after immersion more than the value in before immersion.

تم في هذا البحث دراسة تأثير إضافة الدقائق المايكروية والنانوية والهجين بنسبة (1:1) من (Al2O3، TiO2) على راتنج الايبوكسي في اختبارات التوصيل الحراري قبل وبعد الغمر في المحلول الحامضي (HCl ) لمدة (14 يوم) بتركيز (N 0.3) وبكسر وزني (0.02، 0.04، 0.06، 0.08) وسمك (6 mm). أظهرت نتائج اختبار التوصيل الحراري في الحالة الطبيعية أن الايبوكسي المقوى بدقائق المايكروية والنانوية (Al2O3) و الهجين (TiO2 + Al2O3) يزداد مع زيادة النسبة الوزنية، ولكن قيم التوصيل الحراريk) ) لدقائق المايكروية والنانوية (TiO2) تتناقص مع زيادة النسبة الوزنية في حين تكون قيم (k) في حالة الغمر في المحلول الحامضي (HCl) اكبر من القيمة قبل الغمر.