Article
Study the Rates of Corrosion in Aluminium Reinforced By Silicon Carbide
دراسة معدلات التأكل لمكبوسات الالمنيوم المدعمة بمادة كاربيد السيليكون

Authors: محمد سعيد وحيد --- سدير موفق مجيد
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 18 Pages: 834-846
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work production of aluminium matrix composites with silicon carbide (α-SiC) as reinforcement material were fabricate, the particle sizes of (SiC) used were (500μm- 250 μm and125 μm), with weight percentage of (7.5% - 10% - 15%) from silicon carbide for eachparticle size. The single action pressing was used as one of P/M methods then followed by sintering process at temperature of 450 ºC. The samples subjected to the electrochemical corrosion test at room temperature.The medium of corrosion was solution of 3% weight (NaCl+distilled water)solution. It is found from the photograph microscopy and the results test that all samples which reinforced by(SiC) particles have a(craves or pit) which caused by the particles that act as a cathode sites , and when the size and the percentage of particles increase the Icorr through it also increase as shown in the result.

في هذا العمل حضرت مادة متراكبة ذات اساس من الالمنيوم وبأستخدام كاربيد السيليكون -250μm-125 μm) كمادة مدعمة, حيث تم اضافة دقائق كاربيد السيليكون بأحجام مقدارها 7.5 ) واستخدمت طريقة % -10%- 500 ) وبنسب اضافة وزنية مختلفة مقدارها (% 15 μm (Powder metallurgy) الكبس الاحادي للتصنيع كواحدة من طرق ميتالورجيا المساحيق 450 ومن ثم اجري فحص التأكل الكهروكيميائي تحت ºC بعد ذلك تم تلبيد النماذج بدرجة تاثير وسط ملحي بنسبة (% 3 ) وبدرجة حرارة الغرفة ولكل النماذج المصنعة . وجد من التصوير المجهري ونتائج الاختبار ان جميع النماذج المدعمة بدقائق كاربيد السيليكوننتيجة لكون ان الدقائق قد شكلت مواقع لحدوث تفاعل (Pitting) قد ظهر عليها التنقر او الحفر الاختزال وكلما زادت نسبتها وحجمها الدقائقي زادت قيمة التيار المار خلالها ويتبين ذلك من النتائج.


Article
Improve Wear Resistance on Al 332 Alloy Matrix- Micro -Nano Al2O3 Particles Reinforced Composite
تحسين مقاومة البليان لسبيكة الالمنيوم A332 المقواة بدقائق سيراميكية ونانوية من الالومينا

Loading...
Loading...
Abstract

The wear behavior of alumina particulate reinforced A332 aluminium alloy composites produced by a stir casting process technique were investigated. A pin-on-disc type apparatus was employed for determining the sliding wear rate in composite samples at different grain size (1 µm, 12µm, 50 nm) and different weight percentage (0.05-0.1-0.5-1) wt% of alumina respectively. Mechanical properties characterization which strongly depends on microstructure properties of reinforcement revealed that the presence of ( nano , micro) alumina particulates lead to simultaneous increase in hardness, ultimate tensile stress (UTS), wear resistances. The results revealed that UTS, Hardness, Wear resistances increases with the increase in the percentage of reinforcement of Al2O3 when compared to the base alloy A332. The wear rates of the composites were considerably less than that of the aluminum alloy at all applied loads with increasing percentage of reinforcement when compared to the base alloy A332.

ان سلوك البليان لسبيكة المنيوم A332 مدعمة بدقائق سيراميكية من الالومينا وباحجام مختلفة (12 مايكرون، 1 مايكرون، 50 نانومتر ) و بنسب وزنية مختلفة (0,05 ، 0,1، 0,5، 1) % وباستخدام تقنية السباكة احتسبت وباستعمال جهاز فحص العينات .ان خصائص المواصفات الميكانيكية تعتمد على توزيع الدقائق النانوية والمايكروية ، فهذا التوزيع ادى الى تحسن الصلادة وواجهاد الشد الاعلى ومقاومة البليان حيث ان مقاومة البليان تزداد بزيادة نسبة الالومينا. ان معدل البليان للمتراكبات يعتبر اقل من سبائك الالمنيوم تحت تاثير نفس الحمل مع زيادة نسبة الالومينا مقارنة بالسبيكة الاصلية.