Improving Anodizing Efficiency by Adding Different Amounts of Aluminum Powder to Anodizing Electrolyte for Pure Aluminum and Aluminum Alloy (6063)

Authors: Uday Sami Mohammad --- Sami A. Ajeel
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2008 Volume: 26 Issue: 7 Pages: 842-865
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Different amounts of aluminum powder (5, 7, 9 and 11g/l) were added to sulfuricacid solution of the specimens under ideal conditions previously obtained (1) and theeffect of these additions was studied to find out it's benefit on anodizing efficiency forpure aluminum and aluminum alloy (6063).The specimens were examined in different conditions using optical microscope,roughness and hardness measurements.The study shows the anodizing process was improved by adding aluminumpowder with ideal conditions and the best value of aluminum powder was 9g/l,where the thickness improved from 72.25μm at ideal conditions to 81.25μm withadding 9g/l aluminum powder and the coating ratio improved from 1.481 at idealconditions to 1.541 with adding 9g/l aluminum powder for pure aluminum, while thethickness improved from 74.56μm at ideal conditions to 82.29μm with adding 9 g/laluminum powder and the coating ratio improved from 1.417 at ideal conditions to1.471 with adding 9g/l aluminum powder for aluminum alloy (6063).The study also shows that the effective anodic current efficiency was increasedabout 12.50% when adding aluminum powder of 9g/l compared with ideal conditionsfor pure aluminum, while this value was increased about 10.20% when addingaluminum powder of 9g/l compared with ideal conditions for aluminum alloy (6063)without adding aluminum powder.It is found that the surface roughness and hardness value of specimens with addingaluminum powder of 9g/l gives the best result compared with the specimens at idealconditions and bare specimens.

أُضيفت كميات مختلفة من مسحوق الألمنيوم تتراوح بين ( 5,7,9,11 ) غم/لتر إلى حامضالكبريتيك للعينات الخاضعة للظروف المثالية التي اخذت نتائجها من بحث سابق ( 1) وتأثير هذه.( الأضافة على كفاءة الأنودة للألمنيوم النقي وسبيكة الألمنيوم ( 6063أُجري الفحص المايكروسكوبي وقياس الخشونة والصلادة للعينات بظروف مختلفة. أظهرتالدراسة بأن عملية الأنودة تحسنت بأضافة مسحوق الألمنيوم مع الظروف المثالية وأفضل قيمة لها81.25 عند μm 72.25 تحت الظروف المثالية الى μm هي 9 غم/لتر حيث تحسن السمك من74.56 تحت الظروف μm أضافة 9 غم/لتر من مسحوق الألمنيوم بالنسبة للألمنيوم النقي ومن82.29 عند أضافة 9 غم/لتر من مسحوق الألمنيوم بالنسبة لسبيكة الألمنيوم μm المثالية الى.(6063)وتحسنت نسبة التغطية من 1.481 و 1.417 للظروف المثالية الى 1.541 و 1.471 عند أضافة 9غم/لتر من مسحوق الألمنيوم بالنسبة للألمنيوم النقي وسبيكة الألمنيوم ( 6063 ) على التوالي.أظهرت الدراسة أيضًا بأن كفاءة التيار الآنودي المؤثر أزدادت حوالي % 12.50 عند أضافة 9غم/لتر من مسحوق الألمنيوم مقارنة مع الظروف المثالية بالنسبة للألمنيوم النقي, في حين أزدادتحوالي % 10.20 عند أضافة 9 غم/لتر من مسحوق الألمنيوم مقارنة مع الظروف المثالية بالنسبةلسبيكة الألمنيوم ( 6063 ) بدون أضافة المسحوق.وجد بأن قيمة خشونة وصلادة السطح للعينات المضاف اليها 9 غم/لتر من مسحوق الألمنيومأفضل بالنتيجة مقارنة مع العينات التي أُجري لها أنودة تحت الظروف المثالية والعينات التي لمتجرى لها عملية أنودة..


Article
دراﺳة ﺗﺄﺛﻴر إﺿﺎفة ﻣﺴﺤوق اﻷلمنﻴوم علﻰ ﺑعﺾ الﺨواص المﻴﻜﺎﻧﻴﻜﻴة وﻣﻘﺎوﻣة اﻻﺣﺘراق للﺒولي اﺳﺘر ﻏﻴر المشﺒﻊ

Author: أﲪﺪ ﺟﺎﺳﻢ ﳏﻤﺪ
Journal: Albahir journal مجلة الباهر ISSN: 23125721 Year: 2018 Volume: 7 Issue: 13-14 Pages: 61-70
Publisher: AL-Abbas Holy Shrine العتبة العباسية المقدسة

Loading...
Loading...
Abstract

The study of the effect of aluminum powder on the mechanical properties of unsaturated polyester which is manufactured in the Turkey, as function of the percentages of aluminum powder (0.5%, 0.8%, 1%, 1.5%, 2%, 2.5%), at particular size (150) µm, were investigated through several variables, such as, young’s modules, strength, elongation and the flame resistance. The obtained results were the properties (unsaturated polyester/aluminum powder) composites were analyzed as a function of the filler amount. All prepared composites showed improved filler dispersion in the unsaturated polyester matrix, the results lead to that the strength at break will be affected little till the percentage (1.5%), and lowered after that with increasing the percentage also indicate an lowered in young’s modules at the percentage (1%). The proportional limit was (2095) N for (0.8%), and the observe that the average time of burning starts strong impact when (0.5%) as increasing to(168 sec) and then begins to decline behavior when increasing proportions weighted and then increasing behavior when increasing proportions when (2.5%) as increasing to (195) sec.

اﳋﻼﺻﺔ ) وعند حجم دقائق 2.5%,2%,1.5%,% 1,% 0.8,0.5% تم إضافة مسحوق الألمنيوم كحشوات مالﺌة وبنسب وزنيه ( لبوليمر البولي استر غير المشبع ذو المنشأ التركي. في هذا البحث قمنا بدراسة بعﺾ mm )150للحشوات مساو او اقل من ( الخصائص الميكانيكية للخليط مثل معامل يونك والمرونة ومقاومة اللهوبية وقوه الشد عند القطع، ومن النتائج العملية قد تم تحليل الحشوات كدالة لكمية من كمية مسحوق المضاف. وأﻇهرت جميع النماذج المحضرة تحسن في انتشار المضاف بشكل متجانس %) تضفي زيادة 1.5في البولي استر غير المشبع، وان زيادة نسبة المضاف من مسحوق الألمنيوم مع البولي استر عند النسبة المﺌوية ( ) بأن سلوك 1.5صفة الصلادة على بقية النماذج عند النسب الوزنية المختلفة للخليط، وبينت النتائج العملية عند النسبة الوزنية (% قوة الشد عند القطع للخليط يكون ذو تأثير قوي، وبعدها يهبط قيمته عند زيادة النسب الوزنية للمضاف. وتكون قيمة معامل %) منخفضة مما يعكس مرونة البولي استر المضاف إليه مسحوق الألمنيوم والذي يكون له مدى واسع 1يونك للخليط عند النسبة ( نيوتن) للنسبة الوزنية) % 2095التطبيقات الصناعية. أقﴡ قيمة لحد التناسب التي تم الحصول عليها من النتائج العملية هي ( ) ثانية وبعدها يبدأ السلوك 168 %) إذ تصل قيمته إلى ( 0.5، ونلاحﻆ بان معدل زمن الاحتراق يبدأ بتأثير قوي عند النسبة (0.8( ) ثانية.. 195 %) إذ تصل قيمته إلى ( 2.5بالانخفاض عند زيادة النسب الوزنية وبعدها يزداد إلى إن يصل إلى أقﴡ قيمة عند النسبة