Strength Evaluation of CO2-Cured Cellulose Date Palm Fiber Reinforced Cementitious Boards

Authors: Maan Salman Hassan --- Shakir Ahmed Salih --- Isam Mohamad Ali
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 6 Part (A) Engineering Pages: 1029-1046
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In recent years there has been an increasing demand to recycle wastes produced by the agricultural and industrial processing. The aim of this paper is to investigate the suitability of date palm (Phoenix dactylifera) as lignocellulosic materials for the production of wood-cement composite boards, in addition to enhance their compatibility with cement using physical pretreatment processes and accelerated carbonation curing. Experiments were performed to assess the physical properties (as density, flexural strength, toughness and E-modulus), and micro structural properties (as determined by scanning electron microscopy) of the produced cement boards. The results show an improvement in the physical and microstructural properties of cellulosic fiber-cement composites by using accelerated CO2 curing method. In addition, excessive carbonation rate associated with pure gas carbonation does not necessarily lead to high strength and even detrimental strength development was found, which was shown by cement paste.


Article
Studying the Improvement of the Solubility of Cellulosic Fibers
دراسة تحسين ذوبانية الالياف السليلوزية

Author: Asem Hassan Mohammed عاصم حسن محمد حسن
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2016 Volume: 22 Issue: 7 Pages: 21-37
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This study focuses for improving the increase the solubility of fiber cellulose in sodium hydroxide solution in concentrations ranging from (4- 12%), from one point of view and from other point of view in (sodium hydroxide and urea) solution concentration (6% NaOH + 4% urea), under low temperature (- 15, - 20 Co) , depending on the principle of reducing the degree of polymerization for fiber cellulose, which is represented in our tests cotton linter who its represent (Whatman filter paper, Grade 1), some samples subjected to chemical pretreatment as simulation the method of decomposition of cellulosic materials by white or brown fungi that grow on trees, this method involves the use of chemical materials, including hydrogen peroxide (H2O2) , oxalic acid C2H2O4 and ferrous sulfate FeSO4 to be reaction known ( Fenton reaction or Fenton's reagent) which produce free radicals helps the decomposition of cellulose fibers. The results were as follows: The solubility of cellulose fiber in sodium hydroxide solution was up to 42% cellulose and the best sodium hydroxide concentration is 8% for treated simples in Fenton solution and for untreated simples were the best solubility of cellulose fiber up to 28% and the best temperature is -20 Co for both. For the solubility of cellulose fibers in sodium hydroxide and urea solution (6% NaOH + 4% urea) was more than 60% of treated cellulose in Fenton reaction , while for untreated cellulose was the best solubility ratio up to 35% and it was the best temperature - 15 Co

في هذه الدراسة تركز عملنا على تحسين زيادة ذوبانية الياف السليلوز في محلول هيدروكسيد الصوديوم بتراكيز تتراوح بين ( 4- 12 % ) هذا من ناحية ومن ناحية اخرى في محلول هيدروكسيد الصوديوم واليوريا بتركيز ( 6% NaOH + 4% يوريا ) تحت درحات حرارة منخفضة ( -15 , - 20 ) درجة مؤية . معتمدين بالدرجة الاساس في هذا البحث على مبدأ تقليل درجة البلمرة (Degree of polymerization) لزغب القطب ( Cotton Linter ) والذي يمثله في تجاربنا ورق الترشيح رقم -1- (Whatman filter paper, Grade 1 ) , بعض النماذج سوف نستخدم فيها معالجة اولية ( Pretreatment ) لزغب القطن بطريقة كيمياوية تحاكي طريقة تحلل المواد السليلوزية التي تستخدهما الفطريات التي تنمو على الاشجار , هذه الطريقة تتضمن استخدام مواد كيمياوية تشمل بيروكسيد الهيدروجين (H2O2 ) حامض الاوكسالك (C2H2O4) و كبريتات الحديدوزالثنائية ( FeSO4) ليكوّن لنا تفاعل يعرف بكاشف فينتون (Fenton's reagent ) ينتج من هذا التفاعل جذور حرة تساعد على تحلل الياف السليلوز. وكانت النتائج كما يلي : بالنسبة الى ذوبانية الياف السليلوز في محلول هيدروكسيد الصوديوم بتركيز هو 8% كانت افضل نسبة اذابة تصل 42% للسليلوز المعالج في كاشف فينتون اما بالنسبة للسليلوز الغير معالج فكانت افضل نسبة ذوبان تصل الى 28% و كانت افضل درجة حراراة لعملية اذابة الياف السليلوز المعالج والغير معالج هي بحدود - 20 درجة مؤية .أما بالنسبة الى ذوبانية الياف السليسلوز في محلول هيدروكسيد الصوديوم واليوريا (NaOH/urea ) والذي كان بتركيز( 6% NaOH + 4% يوريا ) فكانت نسبة الاذابة تصل اكثر من 60% للسليلوز المعالج في كاشف فينتون و للسليلوز الغير معالج فكانت افضل نسبة ذوبان تصل الى 35% وكانت افضل درجة حراراة لعملية الاذابة هي - 15 درجة مؤية .