Article
Horizontal Shear Transfer between Concrete and Bricks

Authors: Hakim S. M. Al-Kurayshi --- Dhurgham Abdul Jaleel Resool
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2016 Volume: 9 Issue: 1 Pages: 11-22
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

Horizontal Shear transfers through interfaces between two materials need to be studied accurately especially when the interface separates two different materials. In this study the two materials are concrete and bricks. This interaction can be formed in the regions where concrete is rested on brick walls in so many positions in construction. The study focuses on an experimental work through a series of push-off tests for ( concrete to bricks, cement mortar to bricks ) taking into consideration that the shear connectors are steel bars. Throughout push–off tests and due to the applied horizontal forces as slip had been attained. This forces and slips are recorded and graphically drawn. A statistical regression was made to find the most representative formula of the mechanism of shear transfer between concrete with bricks and between cement mortar with bricks. The predominant factor in shear transfer between concrete and bricks is the amount of shear connectors because as number of dowel bars increases the shear strength increases. The value of force recorded at 2mm slip for concrete to concrete was around three to four times that for concrete to bricks in existence of steel bars or steel dowels. This means that concrete to bricks is weaker than that between two concretes.


Article
Fabrication of Advanced Cement Mortar for Building Anti-Bacterial Applications
تصنيع مونة الاسمنت المتقدمة لتطبيقات البناء المضادة للبكتريا

Authors: Noor A. Hmeed نور عبد الناصر حميد --- Alaa A. Abdul-hamead ألاء علاء الدين --- Farhad M. Othman فرهاد محمد عثمان
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2019 Volume: 15 Issue: 1 Pages: 89-96
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research, we have added nano anatase TiO2 as a partial replacement of Portland cement by a weight percentage of (0.25 to 1%) for the development of properties for protection against bacteria. The control mix was made by using "the cement to sand" proportion about (1: 2.75) with the "water to cement" proportion of (0.5) to study the structure, porosity, water absorption, density, mechanical properties, as well as anti-bacterial behavior. Inspections have been done such as scanning electron microscopy (SEM), and atomic force microscope (AFM) for mortar. Experimental results showed that after the addition of Nano powders in cement mortar, the structural properties improved significantly with the development of hydration of cement mortar at early age, reduction of porosity and the increase of density as well as enhancement in compressive and anti-bacteria properties that make the preparation of nano material very suitable for protection against bacteria.

في هذا البحث تم اضافة نانو تيتانيه طور (anatase) بوصفه كمادة استبدال جزئي للسمنت البورتلاندي بنسب وزنية ( 1% to 0.25 ) لأجل تطوير خصائص (الحماية ضد البكتريا) وتم إجراء مزيج مرجعي مع نسبة الأسمنت إلى الرمل 2.75:1)) . تم الحفاظ على نسبة المياه في الاسمنت عند 0.5 و تم اجراء فحوصات الكثافة، المسامية، معامل الامتصاص فظلا عن الى ذلك الخواص التركيبية AFM ,SEM وفحوصات Anti-bacteria بينت النتائج ان الملاط الاسمنتي يمتلك بنية منتظمة ومعامل خشونة انخفظت بعد اضافة الماده النانوية وتحسنت الكثافة و انخفاض في معامل الامتصاص والمسامية مما يجعل الملاط المحضر ملائماً لتطبيقات (الحماية ضد البكتريا).


Article
DRYING SHRINKAGE OF CEMENT MORTAR REINFORCED WITH WASTE OFFICE PAPER FIBERS
انكماش الجفاف لمونة السمنت المسلحة بألياف مخلفات ورق المكتب

Author: Zainab Hasan Abdulabbas زينب حسن عبد العباس
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2016 Volume: 7 Issue: 3 Pages: 110-130
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

In this investigation, the influence of using waste office paper fibers (WOPF) on the behavior of drying shrinkage in cement mortar have been presented. Cement mortar specimens size of (25×25×285) mm and a length change measuring apparatus including a dial gauge capable of measuring the length accurately to ±0.002 mm have been used to study free drying shrinkage of cement mortar according to ASTM C596 – 01 method. The workability of cement mortar reinforced with WOPF was assessed by using flow table test method. WOPF was added to the cement mortar in five ratios (0.2%, 0.4%, 0.6%, 0.8%, and 1%) by weight of cement with two categories. In first one WOPF added after being soaked in water for 24 hours while in the second one WOPF added after being soaked in cooking oil for 48 hours. The total mixes were 10 in addition to the reference mix (the 11th mix) which is made without WOPF. The results of the study indicated that the increase in WOPF ratio led to reduce in workability. In first category, when WOPF ratio increased to 0.4%, the flow percent still within 110±5%, and when WOPF ratio increased to 0.6% and above the flow percent clearly reduced. While in second category, when WOPF added, the flow percent dropped obviously for all ratios. Drying shrinkage percent increased when WOPF was added to mixes compared with reference mix for all ratios used in both categories except the fifth ratio (i.e. WOPF 1%) in which the drying shrinkage percent decreased at age of drying 11, 18, 25 days for first category and at age of 18 and 25 days for second category. Drying shrinkage percent of mixes has equal ratio of WOPF in the both categories had the same tendency in variation with time. The loss of weight percent variation for all the mixes is approximately linear. The loss of weight percent of category I is more than that of category II.

في هذا البحث، تم عرض تأثير استخدام مخلفات ورق المكتب كألياف (WOPF) على سلوك انكماش الجفاف في مونة السمنت. وقد استخدمت عينات من مونة السمنت بحجم (25 × 25 × 285) ملم، وجهاز قياس التغير بالطول (DIAL GAUGE) بدقة ± 0.002 ملم لدراسة انكماش الجفاف الحر لمونة السمنت طبقا للمواصفة ASTM C596 - 01. تم تقييم قابلية التشغيل لمونة السمنت المسلحة بـ WOPF باستخدام اختبار الانسياب. وأضيفWOPF لمونة السمنت بخمس نسب (0.2٪، 0.4٪، 0.6٪، 0.8٪، 1٪) من وزن السمنت وعلى فئتين: في الفئة الأولى وأضيف WOPF الى المونة بعد نقعه في الماء لمدة 24 ساعة. بينما في الفئة الثانية أضيف WOPF الى المونة بعد نقعه في زيت الطعام لمدة 48 ساعة. عدد الخلطات الكلي 10 خلطات بالإضافة إلى الخلطة المرجعية (الخلطة الحادية عشر) من دون WOPF. وأشارت نتائج الدراسة إلى أن الزيادة في نسبة WOPF يحد من قابلية التشغيل. في الفئة الأولى، عندما زادت نسبة WOPF إلى 0.4٪، بقيت نسبة الانسياب ضمن 110 ± 5٪ وعندما زادت نسبة WOPF إلى 0.6٪ وأكثر, نسبة الانسياب انخفضت بشكل واضح. بينما في الفئة الثانية، عندما اضيف WOPF، انخفضت نسبة الانسياب بشكل كبير في كل النسب. نسبة انكماش الجفاف زادت عندما أضيف WOPF للخلطات مقارنة مع الخلطة المرجعية لكل النسب المستخدمة في كلا الفئتين ما عدا النسبة الخامسة (أي WOPF 1٪) والتي انخفضت فيها نسبة انكماش الجفاف في اعمار تجفيف 11 و 18 و 25 يوم للفئة الاولى وفي عمر 18 و 25 يوم للفئة الثانية. نسبة انكماش الجفاف للخلطات التي تحتوي نسبة متساوية من WOPF في كلا الفئتين لها نفس النزعة في التغاير مع الوقت. تتغاير نسبة الفقدان في الوزن لجميع الخلطات بشكل خطي تقريبا. فقدان الوزن في المئة من الفئة الأولى أكثر منه في فئة الثانية.


Article
EFFECT OF FIRE FLAME ON GLASS FIBER REINFORCED MORTAR SLAB SPECIMENS
تأثير لهب النار على نماذج بلاطات مونة مسلحة بالألياف الزجاجية

Authors: Mahdi S. Essa Al-Saegh --- Zainab H. Abdul-Abaas
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2010 Volume: 1 Issue: 2 Pages: 119-134
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

This study aims to reveal the effect of fire flame on the behavior of glass fiber reinforced mortar slab specimens. The experimental work included casting and testing six of glass fiber reinforced fiber mortar slab specimens with dimensions of (600×600×40)mm. In addition to nine cubes with dimensions of (70×70×70)mm for compressive strength test, and six prisms of (25×25×250)mm dimensions for flexural strength test. The specimens were divided to three series; A1 tested at 25˚C, A2 and A3 subjected to direct fire flame at the lower surface and heated to 500˚C. The burning periods were 30 min and 60 min for A2 and A3 respectively. Based on the results of this work, it was found that the most reduction in compressive and flexural strengths occurs at the first 30 min of burning. The reduction in flexural strength is more pronounced than that in compressive strength. The percentage of residual compressive strength was 76% and 69% and the percentage of residual flexural strength was 60% and 57% for A2 and A3 respectively. In addition, it was found that the deflection increases with the increasing burning time under a certain load. The ultimate load capacity of the reinforced slab specimens decreased with the increase in burning time. The percentage of residual ultimate load was 96% and 94% for A2 and A3 respectively.

تهدف هذه الدراسة لكَشْف تأثير لهب النار على سلوك نماذجِ بلاطات مونة مسلحة بألياف الزجاج. تَضمّنَ العمل التجريبي صب واختبار ستّة مِنْ نماذجِ بلاطات مونة الألياف المدعومةِ بأبعادِ (600 ×600 ×40) مليمتر. بالإضافة إلى تسعة مكعّبات بأبعاد (70×70 ×70) مليمتر لفحص مقاومة الانضغاط، وستّة موشورات بأبعاد (25 ×25 ×250) مليمترِ لفحص مقاومة الانثناء. النماذج قُسّمتْ إلى ثلاثة مجاميع، A1 فحصت عند 25˚C ، A2 و A3خضعتا لتَوجيه لهب نار على السطحِ السفلي وسخنتا إلى 500 درجة سيليزية. فترات الحرق كَانتْ 30 دقيقة و60 دقيقة لـ A2 و A3 على التوالي. بالاستناد على نتائج هذا العملِ، وجِد إن اكبر انخفاض في مقاومة الانضغاط ومقاومة الانثناء يَحْدث في أول 30 دقيقة من الحرق. إنّ الانخفاض في مقاومة الانثناء أكثر وضوحاً مِنْ ذلك في مقاومة الانضغاط. النسبة المئوية للمتبقي مِن مقاومة الانضغاط كَانتْ 76 % و69 % والنسبة المئوية للمتبقي مِن مقاومة الانثناء كَانتْ 60 % و57 % لـ A2 و A3 على التوالي. بالإضافة إلى ذلك، وُجِد إن الهطول يزداد بزيادة مدة الحرق تحت تأثير حمل معين. قيم الحمل الأقصى لنماذج السقوف انخفضت بزيادة فترة الحرق. النسبة المئوية للمتبقي مِن الحمل الأقصى كانت 96% و 94% لـ A2 و A3 على التوالي.


Article
Effect of Rubber Treated by Acidic Solution On Some Mechanical Properties of Rubberize Cement Mortar

Authors: Aziz Ibrahim Abdulla --- Salwa Hadi Ahmed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 13 Pages: 2793-2806
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present work, the properties of rubberize cement mortar containingcrumb rubber treated by acidic solution are tested and compared with normal rubberize and normal cement mortar.The rubber, which is treated by different acidic solution such as: (H2SO4, HCl and CH3COOH) is used as a fine aggregate as avolumetric partialreplacement of sand in cement mortar. The percent of replacement ranged from 5 to 30%.Compressive strength, modulus of rupture and modulus of elasticity (static and dynamic) a retested for all mixes. Cubes of cement mortar also tested by ultrasonic pulse velocity (UPV) and hammer tests method to show the effect of treated rubber on the UPV and hammer tests and to demonstrate the possibility of this methods forestimating the compressive strength of rubberize cement mortar.The results show that the treatment of rubber by acidic solution significantly improves the properties of rubberize cement mortar. Moreover the results show that CH3COOH gives better improvement compared withH2SO4. The treatment of rubber by HCl shows negativeeffects on all cement mortar properties.


Article
Effect of Using Plastic and Rubber Wastes as Fine Aggregate on Some Properties of Cement Mortar

Authors: Basil S. Al-Shathr --- Iqbal N. Gorgis --- Rafid F. Motlog
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 8 Part (A) Engineering Pages: 1688-1699
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research describes the production of lightweight cement mortar using four types of fine aggregates including chopped rubber tires, chopped plastic wastes, a mixture from the previous types by 1:1, and a mixture composed from substitution of 10% from the previous type by natural sand. Theuseofthese wastes has rolein getting rid oftheir hugequantitieswhich constitute a fundamentalenvironmental problembecause of the difficulty of itsdegradation.Four, cement to aggregate ratios have been used. They are1:0.5, 1:0.7, 1:1, and 1:1.2 for each aggregate type mentioned above, with changing w/c ratio and superplasticizer content to have a constant flow of about 23%. Also, the effect of curing samples by different methods, including continuous submerge in water, autoclave curing for 3 hours, and carbonation curing by 50% and 100% CO2 at 75oC for 90 minutes, was studied.The results indicated that it is possible to produce lightweight cement mortar, using any type of aggregates mentioned above, with compressive strength satisfying the requirements of clay brick class C of Iraqi Standard, that used in partitions, for a mix proportion of 1:1, except when using chopped rubber tires that need using mix proportion of 1:0.5 to satisfy the strength requirements, where the use of this aggregate type needs higher w/c ratio and superplasticizer content to get the required flow, which leads to lower strength in comparison with the other types. As for chopped plastic aggregate, although it needs lower water and superplasticizer content to get the required flow and strength, care should be taken to balance betweenthe amount of waterand superplasticizer addedto avoidthe possibility of segregation in it. So it was found that using the mixture of chopped plastic and rubber aggregate give the best properties. Results also indicated that using all aggregate typeswith cement: aggregate mix proportion 1:1 satisfy the flexural strength requirements of American Standards for cellulosic fiber insulating boards, and were with thermal conductivity valueslower than that for brick and concrete having density lower than 2000 kg/m3. The results indicated that partial replacement of 10% mixed waste aggregates by normal sand cause increase in strength but in the same time increase density and thermal conductivity for the produced mortar.Results also indicated that curing by autoclave or curing with 50% or 100% CO2 cause increase in the 7 days strength compared with those cured by water but they show almost the same strength at 28 days age.


Article
Effect of Glass Wool Addition on Some Properties of Cement Mortar

Author: Hussein Alaa Jaber
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 14 Part (A) Engineering Pages: 2685-2691
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This work presents an investigation of possible incorporation of the glass wool (fiberglass insulation) in cement mortar as an insulating building material. Mortar of ordinary Portland cement of (1:3) cement to sand ratio was mixed with glass wool at different weight percentages ranged between (0 – 0.24) wt%. Density, water absorption, thermal conductivity, compressive strength and flexural strength experimentally were investigated for mortar specimens after curing for (28 days). The results showed that the incorporation of glass wool decreases the density, thermal conductivity and compressive strength, but the flexural strength of cement mortar enhances. Thermal conductivity of the cement mortar has decreased by about 44 % by increasing of glass wool content up to 0.24 wt%. Thus, utilization of glass wool as constituents in cement mortar appears to be a promising opportunity that enables applying as thermal insulation materials in constructions.


Article
EXPERIMENTAL INVESTIGATION ON PROPERTIES OF CEMENT MORTAR INCORPORATING EGGSHELL POWDER
التحري العملي لخواص مونة الاسمنت الحاوية على مسحوق قشور البيض

Author: Rawaa A. Al-Safy
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2015 Volume: 19 Issue: 6 Pages: 198-209
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The use of waste materials in buildings is an innovative approach towards sustainability. The objective of this paper is to study the properties and behaviour of cement mortar using eggshells wastes. Various low concentrations of eggshell powder (ESP) (0,1,3 ,5, 7 and 10 wt%) were used as partial replacement of cement in mortar of (1:2) mixing ratio by weight. The maximum particle size of ESP is 75 μm. Soundness of cement in ESP-cement pastes was evaluated using Le Chatelier method. The influence of ESP on strengths of cement mortar was investigated by means of compression and flexural tests at various curing periods. It was found that, there was no negative impact of ESP on soundness of cement. A significant enhancement in compressive strength was recorded for all ESP-cement mortars at 7 days and 28 days. The highest improvements, (31.63%) and (11.65%), were observed for samples with 10wt% and 5 wt% of ESP respectively. At moderate periods of curing, samples with 1 wt% of ESP have the highest enhancements in compressive strength of about (8.93%) and (1.75%) for 42 days and 56 days respectively. A reduction in compressive strength was observed for all samples at late ages (70 days and 90 days). In terms of flexural strength, the addition of ESP (up to 5 wt%) results in improvement in the flexural strength when compared with the control samples. The highest enhancement (21.20%) was recorded when cement was replaced with only 1 wt% at 7 days.

ان استخدام مواد المخلفات في البناء هو نهج مبتكر نحو االستدامة.ان الهدف من هذا البحث هو دراسة خواص و سلوك مونة االسمنتباستخدام مخلفات قشور البيض. استخدمت نسب اضافة قليلة و مختلفة من مسحوق قشور البيض )ESP( )0 ، % 1 ، % 3 ، %5 ،%7 %و10 %وزنا( كبديل جزئي عن االسمنت في مونة ذات نسبة خلط وزنية )2:1 .)ان الحجم الحبيبي االقصى لمسحوق قشور البيض كان 75 مايكرون. تم التحري عن ثبات عجينة االسمنت الحاوية على ESP باستخدام طريقة لي شاتليه. ان تأثير ESP على مقاومة مونة االسمنت تم التحري عنهبواسطة فحصي االنضغاط و االنثناء و العمار انضاج مختلفة. لقد وجد بانه ال يوجد تاثير سلبي ل ESP على ثبات االسمنت. فيما يخص مقاومةالالنضغاط ، فقد زادت زيادة ملحوظة عند استخدام نسب مختلفة من ESP و العمار انضاج 7 أيام و 28 يوما. أعلى زيادة سجلت كانت بحدود)63.31 )%و )65.11 )%و لنماذج مونة االسمنت الحاوية على 5 %و 10 %وزنا من ESP على التوالي. اما في الفترات المعتدلة من المعالجة،فقد وجد ان النماذج الحاوية على 1 %وزنا من ESP اظهرت أعلى زيادة في مقاومة االنضغاط و كانت حوالي )93.8 )%و )75.1 )%والعمار انضاج 42 يوما و 56 يوما على التوالي. ولوحظ وجود انخفاض في مقاومة االنضغاط و لجميع العينات في اعمار انضاج متاخرة )70يوما و 90 يوما(. فيما يخص مقاومة االنثناء، فقد وجد بان إضافة ESP( إلى حد 5 %بالوزن( يؤدي الى تحسن مقاومة االنثناء عند مقارنتها معالنماذج المرجعية. وسجلت أعلى زيادة )20.21 )%عندما تم استبدال األسمنت فقط مع 1 %بالوزن و لعمر انضاج 7 أيام.


Article
Recycling waste papers in green cement mortars
اعادة تدوير النفايات الورقية لانتاج مونة سمنتية خضراء

Author: Aseel B. Al-Zubaidi اسيل باسم الزبيدي
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2019 Volume: 17 Issue: 40 Pages: 135-144
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This work investigates the utilization of waste papers (natural and industrial) i.e (citrus aurantium and papers A4) mortars containing specified contents 0.5%, 1%, 1.5% of waste papers were prepared and cured. Mechanical characteristics such as compressive and bending strengths, hardness and water absorption were determined for the mortars mixed with the waste papers and compared with those obtained from the pure mortars. Results showed that the addition of waste paper leads to increase the hardness to (69 - 68.5) shore D for (natural and industrial) wastes materials respectively comparing with pure specimen 66 shore D. The compressed strength of the mortar cement specimen cured for 28 days from 13 MPa to (17-18) MPa for (natural and industrial) wastes materials, respectively.

يهدف البحث الى الاستفادة من النفايات الورقية (الطبيعية والصناعية) أي (أوراق الحمضيات كالنارنج والأوراق الصناعية (A4 واعادة تدويرها في إعداد مونة السمنت باضافات محددة 0.5%, 1%, 1.5% من أوراق النفايات. وقد تم تحديد الخصائص الميكانيكية مثل قوة الانضغاط وقوة الانحناء والصلابة وامتصاص الماء لمونة السمنت الخضراء الممزوجة مع أوراق النفايات ومقارنة مع المونة السمنتية النقية بدون اضافات و أوضحت النتائج أن إضافة النفايات الورقية يؤدي إلى زيادة الصلابة إلى (69-68.5) شور D لمواد النفايات (الطبيعية والصناعية) على التوالي مقارنة مع العينة النقية 66 شورD. ان قوة الانضغاط لعينة الأسمنت المغمورة بالماء لمدة 28 يوم ازدادت من 13 ميكا باسكال إلى (17-18) ميكا باسكال لمواد النفايات الورقية (الطبيعية والصناعية) على التوالي.


Article
Adding Polymer to Mortar Mixture According to the Procedure Recommended by ASTM C 1439
إضافة البوليمر لمونه السمنت وفقا للطريقه التي توصي بها

Author: Zainab M. I. Kammouna زينب محمد اسماعيل كمونه
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2011 Volume: 14 Issue: 1 Pages: 13-18
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Polymers are considered one of the admixture kinds which they are used to improve the quality and the performance of mortar and concrete. In this study the Styrene Butadiene Rubber (SBR) was used as a polymer to see its effects on the mortar. The (SBR) is considered as a water resistance polymer and bonding agent.Four cement mortar mixes were made in this study, the first one was considered as a reference mix which is not include (SBR) while the other mixes were included (SBR) in deferent percentages. The (SBR) was added as a percentage of cement weight. The amount of mixing water was varied to achieve the same flow which was accomplished in the reference mix throughout carrying out flow table test. Flow table test was adopted according to ASTM C 1439-99 (1) recommendations. For each mix, two prisms were prepared to carry out the drying shrinkage test, nine cubes for the compressive strength test and three cubes for the total water absorption test.It was found that when the quantity of (SBR) increases, the physical properties of mortar under study (drying shrinkage, compressive strength and total water absorption) deteriorate which is adverse to the proposal of advantages due to adding (SBR). This result leads to that the recommendation of ASTM C 1439-99 (1) that adopt the flow table as criteria of adjusting the amount of adding water accompanying with deferent percentages of (SBR) is not adequate

تعتبر البوليمرات احد أنواع المضافات التي تستخدم لتحسين نوعية وأداء المونه أو الخرسانه. ضمن هذه الدراسه تم استخدام الستايرن بيوتادين ربر كبوليمر لمعرفة تأثيراته على المونه، ويعتبر الستايرن بيوتادين ربر ماده مقاومه للماء وعامل ربط.لقد تم عمل أربع خلطات من مونة السمنت ضمن هذه الدراسه، تم اعتبار الاولى خلطه مرجعيه والتي لا تحتوي على مادة الستايرن بيوتادين ربر أما الخلطات الاخرى فتم إضافة الستايرن بيوتادين ربر لها بكميات مختلفه. تم اضافة الستايرن بيوتادين ربر كنسبه من وزن السمنت وكانت كمية ماء الخلط تختلف لتحقق نفس مقدار ألانتشار الذي تم تحقيقه في الخلطه المرجعيه خلال فحص طاولة ألانسياب (flow table). وقد تم اعتماد فحص طاولة ألانسياب (flow table) ليكون المسيطر والموجه خلال العمل وذلك كما توصي به الجمعيه الامريكيه للفحص والمواد ( ASTM C 1439-99 (1)).لكل خلطه تم صب موشورين لإجراء فحص انكماش الجفاف وثلاث مكعبات لاجراء فحص مقاومة الانضغاط وثلاث مكعبات لاجراء فحص الامتصاص الكلي. ولقد وجد انه كلما زادت كمية الستايرن بيوتادين ربر فان مواصفات المونه قيد هذه الدراسه ( انكماش الجفاف ومقاومة الانضغاط والامتصاص الكلي ) تتدهور، وهو عكس ما يفترض ان تكون الفائده المرجوه من أضافة الستايرن بيوتادين ربر. تقودنا هذه النتيجه ان فحص طاولة ألانسياب (flow table ) الذي توصي به الجمعيه الامريكيه للفحص والمواد ( ASTM C 1439-99 (1)) ليكون المعيار لتعديل كمية ماء الخلط الذي تتم أضافته مع نسب مختلفه من مادة الستايرن بيوتادين ربر هو فحص غير ملائم

Listing 1 - 10 of 25 << page
of 3
>>
Sort by
Narrow your search

Resource type

article (25)


Language

English (18)

Arabic and English (3)

Arabic (1)


Year
From To Submit

2019 (2)

2018 (3)

2017 (1)

2016 (8)

2015 (5)

More...