Partial and Full Replacement of Silica Sand by Fine Recycled Glass in Cementitious Composites
الإستبدال الجزئي والكلي لرمل السيليكا في المركبات الأسمنتية بزجاج ناعم معاد

Loading...
Loading...
Abstract

One of the major concerns currently and within the close future is the adequate management and efficient reuse and recycling of wastes, which reduces the natural sources and energy consumption. Millions of tons of waste glass are discharged around the world annually. One of the successful policies of the recycling of waste glass is the use in the construction industry where it can be used as aggregate or cement replacement. In the current study, fine recycled glass with granular size of 0.075 to 0.3 mm was used as silica sand replacement in cementitious composites incorporated fly ash and no coarse aggregate. Cube and prism specimens were prepared with four replacement ratios of 0, 25, 50, and 100% to evaluate the compressive strength, the modulus of rupture, and the expansion. The test results showed that 50% and 100% replacements of silica sand by fine glass enhanced both the compressive strength and the modulus of rupture. For mixtures with 100% fine recycle glass, the compressive strength and the modulus of rupture increased by 25% and 33.6%, respectively, compared to mixtures with 100% silica sand. Moreover, the expansion was found to be reduced by approximately 30% as the silica sand was fully replaced by fine glass

إحدى أهم المشاكل الحالية وفي المستقبل القريب هي الإدارة السليمة والتدوير وإعادة الاستخدام الكفوءة لمخلفات المدن والذي يؤدي الى تقليل استهلاك الموارد والطاقة. في كل عام يتم طرح ملايين الأطنان من مخلفات الزجاج حول العالم. إحدى أهم السياسات في تدوير مخلفات الزجاج تكمن في إستخدامها في الصناعات الإنشائية حيث يمكن إستخدامها كتعويض عن الركام او الأسمنت. تم إستخدام ركام زجاج ناعم بقياس 0.075 الى 0.3 ملم في هذه الدراسة كتعويض عن رمل السيليكا في المركبات الأسمنتية التي تحوي رماد متطاير ولا تحوي ركام خشن. تم إعداد نماذج مكعبة وموشورية بأربعة نسب تعويض تساوي 0, 25, 50 و 100% لدراسة مقاومة الانضغاط, معاير الكسر والتمدد. بينت نتائج الفحوصات أن تعويض رمل السيليكا بركام الزجاج الناعم بنسب تساوي 50 و 100% حسنت كل من مقاومة الإنضغاط و معاير الكسر. في الخلطات التي تحوي على 100% ركام الزجاج الناعم إزدادت مقاومة الإنضغاط ومعاير الكسر بمقدار 25% و 33.6% على التوالي مقارنة مع الخلطات التي تحوي 100% رمل السيليكا. بالإضافة الى ذلك فإن التمدد قل بما يقارب 30% في حالة التعويض الكامل لرمل السيليكا بركام الزجاج الناعم.


Article
Flexural Performance of Hybrid Fiber Reinforced Cement Composites Under Elevated Temperatures
أداء االنثناء لل لواح اإلسمنتية المسلحة باأللياف الهجينة تحت تأثير درجات الحرارة العالية

Authors: Isam Mohamad Ali عصام محمد علي --- Ali Hadi Adheem علي هادي عظيم
Journal: Muthanna Journal of Engineering and Technology(MJET) مجلة المثنى للهندسة والتكنولوجيا ISSN: 25720317 25720325 Year: 2018 Volume: 6 Issue: 2 Pages: 113-119
Publisher: Al-Muthanna University جامعة المثنى

Loading...
Loading...
Abstract

Historically, the flexural behavior of hybrid fiber cement composites is not completely understood using the traditional test methods. This research presents the results of an experimental investigations on a high performance cement composites (HPCC) containing both micro steel fibers (SF) and micro polypropylene fibers (PP) before and after elevated temperature exposure. The experimental program was developed to study the flexural performance (flexural strength, toughness and stiffness) under high temperature using mono and hybrid (SF) and (SF + PP) fibers. Mixtures were divided into eight different groups, with constant w/c of 0.28 and different fibers content.Based on the results of this research, the replacing of micro (SF) in high performance cement composites by 15 % of micro (PP) fibers is recommended at high temperature exposure due to the fact that all hybrid fiber HPCC specimens show slight decreasing in flexural behavior compared to samples reinforced with 1% volume fraction of mono steel fibers after high temperature exposure.

تاريخيا يعد سلوك االنثناء للمركبات السمنتية المسلحة باأللياف الهجينة غير مفهوم بصورة متكاملة باستخدام ًالفحوصات التقليدية. بينت هذه الدراسة نتائج مختبرية اجريت على مركبات سمنتية عالية االداء احتوت على الياف حديدية مع الياف البولي بروبيلين قبل وبعد التعرض لدرجات الحرارة العالية. طور البرنامج العملي من اجل دراسة اداء االنثناء )مقاومة االنثناء والصالبة والصالدة( تحت تاثير درجات الحرارة العالية باستخدام الياف الحديد االحادية والياف الحديد-البولي بروبيلين الهجينة. قسمت الخلطات الى ثمان مجاميع مختلفة بنسبة ماء الى سمنت 0.28 على نتائج هذه الد ارسة فان من الضروري استبدالًومحتوى الياف متغير بناءاجزء من الياف الحديد المستخدمة في االلواح السمنتية المركبة بـ 15% من الياف البولي بروبيلين عند التعرض لدرجات الحرارة العالية. بصورة عامة، بالمقارنة مع نماذج احادية التسليح بـ 1% من الياف الحديد في خواص االنثناء بعد التعرض الى درجاتًاظهرت جميع االلواح السمنتية المسلحة بااللياف الهجينة تحسناالحرارة العالية.