Effects of Different Types of Fillers on Dry Wear Characteristics of Carbon-Epoxy Composite
تأثير الحشوات السيراميكية على خواص البلى للمواد المتراكبة للايبوكسي- كاربون

Loading...
Loading...
Abstract

Experimental investigations had been done in this research to demonstrate the effect of carbon fiber and Ceramic fillers contents on the tribological behaviour of (15% volume fraction) carbon-epoxy composite system under varying volume fraction, load, time and sliding distance. The wear resistance were investigated according to ASTM G99-05standard using pin on disc machine to present the composite tribological behaviour. The influence of three ceramic fillers, granite, perlite and calcium carbonate (CaCO3), on the wear of the carbon fabric reinforced epoxy composites under dry sliding conditions has been investigated. The effect of variants in volume fraction, applied load, time and sliding distance on the wear behaviour of polymer composites is studied by measuring the weight changes . In the experiments with wear test pin having flat face in contact with hardening rotating steel disc, sliding speed, time and loads in the range of 200 RPM, 300–900s and 40–60 N respectively was used. It is observed that the wear resistance increase with the increasing of reinforcement material volume fraction while, the wear rate increases with increasing of applied load, time and sliding distance. The results showed that the filler of granite perlite and CaCO3 as filler materials in carbon epoxy composites will increase the wear resistance of the composite greatly than carbon fiber fillers epoxy composite only and granite filled CE Composite exhibited the maximum wear resistance.

في هذا البحث تمت دراسة تأثير الياف الكاربون والحشوات السيراميكية على الخواص الترايبولوجية لراتنجات الايبوكسي المقواة بالياف الكاربون عمليا وعند كسر حجمي 15%. تم دراسة مقاومة البليان وفقا للمواصفةASTM G99-05 باستعمال جهاز المسمار مع القرص الدوار وعند احمال 40–60 N ومسافات انزلاقm 942-1507.2 وازمان مختلفة 300–900s وبعد اجراءالاختبارات لوحظ بان مقاومة البليان تزداد مع زيادة الكسر الحجمي لمواد التدعيم بينما معدل البلى بصورة عامة يزداد بزيادة الحمل المسلط والزمن ومسافة الانزلاق، ويكون معدل البليان للعينات الغير مدعمة اعلى بكثير من العينات المدعمة بالياف الكاربون فقط والعينات المدعمة بنسبة 15% الياف كاربون مع الحشوات السيراميكية المختلفة وان مقاومة البليان للعينات المحتوية على حشوات سيراميكية تكون اعلى من العينات المدعمة بالياف كاربونية فقط وان مقاومة البليان لمجموعة العينات المقواة بالياف كاربون مع كرانيت بلغت اعلى قيمة لها تليها ألعينات المدعمة بالبرلايت ثم عينات كاربونات الكالسيوم. نستنتج من ذالك اضافة الحشوات السيراميكية مع الياف الكاربون يحسن بشكل كبير من مقاومة البليان.


Article
Effects Of Different Types Of Ceramic Fillers On Wear Characteristics Of Glass Fibres-Epoxy Composite
تأثيرات الحشوات السيراميكيه المختلفة على خواص البلى للمواد المتراكبة للايبوكسي- زجاج

Loading...
Loading...
Abstract

Experimental investigations had been done in this research to demonstrate the effect of glass fiber and Ceramic fillers contents on the tribological behaviour of (15% volume fraction) glass-epoxy composite system under varying volume fraction, load, time and sliding distance. The wear resistance were investigated according to ASTM G99-05 (reapproved 2010) standard using pin on disc machine to present the composite tribological behaviour. The influence of three ceramic fillers granite, perlite and calcium carbonate (CaCO3) on the wear of the glass fiber reinforced epoxy composites investigated under dry sliding conditions. The effect of variants in volume fraction, applied load, time and sliding distance on the wear behaviour of polymer composites is studied by applied pin –on-disc method . In the experiments with wear test pin having flat face in contact with hardening rotating steel disc, sliding speed, time and loads in the range of 200 RPM, 300–900s and 40–60 N respectively was used. It is observed that the wear resistance increase with the increasing of reinforcement material volume fraction while, the wear rate increases with increasing of applied load, time and sliding distance. The results showed that the filler of granite, perlite and CaCO3 as filler materials in glass epoxy composites will increase the wear resistance of the composite by 76.15%, 73.8%, 71.8% respectively and greatly than glass fiber fillers epoxy composite only and granite filled GE Composite exhibited the maximum wear resistance.

في هذا البحث تمت دراسة تأثير ألياف الزجاج و الحشوات السيراميكية على الخواص الترايبولوجية لراتنجات الايبوكسي المقواة بألياف الزجاج عمليا وعند كسر حجمي 15 %. تم دراسة مقاومة البليان وفقا للمواصفة ASTM-G99-05 باستعمال جهاز المسمار مع القرص الدوار وعند أحمال40–60 N ومسافات انزلاق 942-1507.2 وازمان مختلفة 300–900s وبعد إجراء الاختبارات لوحظ بان مقاومة البليان تزداد مع زيادة الكسر الحجمي لمواد التدعيم بينما معدل البلى بصورة عامة يزداد بزيادة الحمل المسلط والزمن ومسافة الانزلاق . ويكون معدل البليان للعينات غير المدعمة أعلى بكثير من العينات المدعمة بالياف الزجاج فقط والعينات المدعمة بنسبة 15% ألياف زجاج مع الحشوات السيراميكية المختلفة وان مقاومة البليان للعينات المحتوية على حشوات سيراميكية تكون اعلى من العينات المدعمة بالياف زجاجية فقط وان مقاومة البليان لمجموعة العينات المقواة بألياف زجاج مع كرانيت بلغت اعلى قيمة لها تليها ألعينات المدعمة بالبرلايت ثم عينات كاربونات الكالسيوم. نستنتج من ذالك إضافة الحشوات السيراميكية مع ألياف الزجاج يحسن بشكل كبير من مقاومة البليان.