Article
DEVELOPEMENT THE PERFORMANCE OF CERAMIC CANDLE FILTERS FOR WATER PURIFICATION USING LOCALLY MATERIALS

Author: Zyad Rafaa Zair
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2013 Volume: 13 Issue: 1 Pages: 63-76
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This research presents an investigation on the technical feasibility of design and manufacturing the ceramic water candle filters made from Iraqi raw materials to improve the domestic water quality to standards suitable for human consumption in villages and country side, the performance assessment is based on its porosity, turbidity reduction, bacteria removal, ease of flow, hardness and undesired ions reduction, so number of experiments were done by mixing different percent of the raw materials of which activated kaolin clay 15 to 45 wt%,coal 15 to 40 wt%, and porcelanite 15 to 40 wt%, with same grain sizes less than 75 microns. All of these mixtures were molded under constant firing temperature and hydraulic compression pressure (1200 0C, and 1325 kg/cm2). The effect of different feed percent for each material gave the optimum percent of 25%wt activated kaolin clay, 35%wt coal, 40%wt porcelanite reaching to the better tests results, number of tests also is made over the experiments range such as apparent density, porosity, wettability, turbidity, TDS, E Coli, water ions examination tests, the produced filter porosity was 62.3%, water turbidity reduced from 167 NTU to less than 5 NTU.

ُقدّمُ هذا البحثِ تحقيقاً على العمليةِ التقنيةِ لتصميمِ وتصْنيعُ مرشحاتَ الماءِ الخزفيةِ الشمعيةِ والمصنعة مِنْ المواد الأوليةِ العراقيةِ لتَحسين نوعيةِ الماءِ المحليةِ إلى المقاييس المناسبةِ للإستهلاكِ البشري في القُرى والمناطق النائيه، تقييم الأداءَ للمرشحات الخزفيةِ الشمعيةِ المصنعة أستند على المسامية، تخفيض مستوى العكورةِ، إزالة البكتيريا المرضية, تحقيق سهولة في التدفقِ والجريان، تخفيض آيوناتِ العسرة والغير مرغوب فيها، أعتمد عدد من التجاربِ بخَلْط نسب مختلفةِ من المواد الأوليةِ الداخلة ومنها طينَ الكاولينِ المنشط والمفعل بنسبة وزنية تتراوح بين 15 إلى 45 %، فحم الخشب بنسبة 15 إلى 40 %، ومادة البورسيلينات من 15 إلى 40 wt %، بحجومِ حبيبية ثابتة أقل مِنْ 75 ميكرونِ. كُلّ هذه الخلطاتِ شكلت تحت درجةِ حرارة حرق ثابتةِ 1200 درجةِ مئوية وضغطِ هيدروليكيِ ثابت قدرة 1325 كيلوغرام / سنتيمتر مربع. ان مع أختلاف النسب المئوية تم تحديد أفضل النسب للمواد الداخلة في أستخدام الطين المفعل بنسبة 25 % ، الفحم بنسبة 35 % ، البورسيلينات بنسبة 40 % للوصِول إلى نَتائِجِ الإختباراتِ الأفضلِ، كذلك تم أجراء عدد من الفحوصات اللازمة لجميع التجارب مثل فحص الكثافةِ الظاهريةِ، فحص المسامية , فحص الامتصاصية, فحص العكورة، فحص المواد الصلبة الذائبة الكلية، فحص البكتيريا البرازية، فحص آيوناتِ ماءِ السالبة والموجبة. كان نموذج المرشح المثالي الناتج بمساميةَ 62.3 %، أما درجة عكورة الماءِ فقد أنخفّضتْ مِنْ 167 إلى أقل مِنْ وحدة عكورة قياسية.

Keywords

Candle --- Filters --- Filtration --- Ceramic filters


Article
Rotating Ceramic Water Filter Discs System for Water Filtration
منظومة اقراص مرشحات الماء الخزفية الدوارة لترشيح المياه

Authors: Riyadh Z. Al Zubaidy رياض زهير الزبيدي --- Mahmoud Al-Khafaji محمود صالح الخفاجي --- Riyadh J. M. Al-Saadi رياض جاسم محمد السعدي
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2017 Volume: 23 Issue: 4 Pages: 59-78
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This work aimed to design, construct and operate a new laboratory scale water filtration system. This system was used to examine the efficiency of two ceramic filter discs as a medium for water filtration. These filters were made from two different ceramic mixtures of local red clay, sawdust, and water. The filtration system was designed with two rotating interfered modules of these filters. Rotating these modules generates shear force between water and the surfaces of filter discs of the filtration modules that works to reduce thickness of layer of rejected materials on the filters surfaces. Each module consists of seven filtration units and each unit consists of two ceramic filter discs. The average measured hydraulic conductivity of the first module was 13.7mm/day and that for the second module was 50mm/day. Results showed that the water filtration system can be operated continuously with a constant flow rate and the filtration process was controlled by a skin thin layer of rejected materials. The ceramic water filters of both filtration modules have high removal efficiency of total suspended solids up to 100% and of turbidity up to 99.94%.

هدف هذا العمل هو تصميم وانشاء وتشغيل منظومة جديدة بمقياس مختبري لترشيح المياه. استخدمت هذه المنظومة لفحص كفاءة اثنين من المرشحات الخزفية كوسط لترشيح المياه. تم تصنيع هذه المرشحات الخزفية من اثنين من الخلطات الخزفية من الطين الاحمر المحلي مع نشارة الخشب والماء. صممت منظومة الترشيح باثنين من وحدات ترشيح متداخلة ودوارة من هذه المرشحات. يعمل تدويرهذه الوحدات على توليد قوة قص بين الماء وسطوح اقراص الترشيح التي تعمل على تقليل سمك طبقة المواد المرفوضة على سطوح المرشحات. تتألف كل وحدة من سبعة مفردات من المرشحات، وكل مفردة تتألف من اثنين من اقراص المرشحات الخزفية.كان معدل الايصالية الهيدروليكية المقاسة للوحدة الاولى 13.7 ملم/اليوم وللوحدة الثانية 50 ملم/اليوم. بينت النتائج ان منظومة ترشيح المياه لها القابلية على العمل باستمرار بمعدل تصريف ثابت وان عملية الترشيح محكومة بطبقة رقيقة من المواد المرفوضة المتراكمة على اسطح المرشحات. تمتلك مرشحات الماء الخزفية لكل من وحدتي الترشيح كفاءة عالية في ازالة المواد العالقة الكلية تصل الى 100% وفي ازالة العكورة تصل الى 99.94%.


Article
Effect of Sintering Process and Starch Amount on the Porosity and Permeability of Al2O3-ZrO2 High Porous Oil Filters

Authors: S.A. Ajeel --- N.E. Abdul Latiff --- A.A. Al-Attar
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2017 Volume: 35 Issue: 9 Part (A) Engineering Pages: 887-893
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Alumina-Zirconia is prepared for oil filter. Oil filters are used to separate oil derivatives from each other using separation principles depending on the size of the holes. These filters work on the principle of separation depending on the density and viscosity of liquid or on the difference in impurity crystals size. This work involves preparation of filters from Alumina-Zirconia powder materials by a hybrid freeze casting and space-holder method. These filters have excellent properties such as stability at high temperature, excellent corrosion resistance; withstand static stresses, and other unique thermal properties. Alumina-Zirconia powder is mixed with different amounts of (zero, 15, 25, and 35 vol. %) of starch powder. Powder mixture has been blending with water using an electric mixer to obtain homogeneous slurry. Solid: liquid ratio of slurry of 30:70 is poured in a cylindrical metal molds and freezed by liquid nitrogen chamber. The solidified material was heat treated at 300 °C for 60 min then sintered at 1550 °C, 1600 °C and 1700 °C under vacuum for 120 min. Hot samples were cooled inside furnace until room temperature. The sintered materials were examined to show the effect of starch adding and sintering process on the porous structure and permeability ratio of the fluid using Archimedes method and SEM image analyzed by J-image program. Best permeability and homogeneous porous structure are obtained at 1600 °C sintering temperature with 24 vol. % of starch powder.


Article
Study The Effect of Changed The Sand Percentage and its Particales Size on Apparent Porosity& Comprassive Strength of Ceramic Filters
دراسة تأثير تغير نسبة رمل السليكا وحجمه الحبيبي على المسامية الظاهرية و مقاومة الانضغاط للمرشح السيراميكي

Author: Ansam Ali Hashem Al-Hasnawy انسام علي هاشم الحسناوي
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2014 Volume: 7 Issue: 3 Pages: a73-a90
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

The objective of this research is to study the effect of Percentage on apparent porosity and compressive strength of ceramic filters. In this research, using ceramic raw materials to produced the filters. Filters made from the raw materials (Sand, Kaolin, and Calcium Carbonate), which obtained from Um Urdhuma and Al- Deuechla in the west of Iraq. Sand was the basic material used to make filters. Selective some of sand particle size (150µm, 125µm, 100µm, 75µm, 50µm), In addition to the binder material that consisted (65% Kaolin + 35% Calcium Carbonate), in different weight percentage (60% Binder + 40% Sand, 50% Binder + 50% Sand, 40% Binder + 60% Sand) ), and used the semidry compaction to forming the laboratory samplesThe samples dried in (110 ºC) for (24 hours), and fired or sintered at 1200ºC for soaking time (1hour),then we extracted compressive strength and apparent porosity. The experimental result led to the relationships between (rate of sand, particle size of sand) and apparent porosity and compressive strength of ceramic filter. . Increased the rate of sand increased apparent porosity, but it decreased compressive strength. ). Increased particle size of sand decreased apparent porosity, but it increased compressive strength. The rustles show the maximum apparent porosity (41.328%) at the maximum weight percentage of sand (60%)), and minimum particle size of sand (50µm).The highest compressive strength( 11.831MPa) at lowest weight percentage of sand (40%), and maximum particle size of sand (150µm) .

ان الهدف من هذا البحث هو دراسة تأثير نسبة رمل السليكا الداخل في تصنيع المرشح السيراميكي على مساميته الظاهريه و مقاومة انضغاطه. تم استخدام مواد أولية سيراميكية لانتاج المرشحات, وهذه المواد متوفرة في غرب العراق وهي رمل أم أرضمة وكاؤلين الدويخلة و كاربونات الكالسيوم. تم استخدام الرمل وذلك بعد فصله الى عدة حجوم لجسيمات رمل السليكا (150µm,125µm,100µm,75µm,50µm) كمادة اساسية اضافة الى المادة الرابطة Binder المكونة من (65% الكاؤلين + 35% كاربونات الكاسيوم) وبنسب مختلفة (40% Sand+60% Binder ) , (Sand 50 % +50% Binder) و(60% Sand +40% Binder Binder) تم استخدام طريقة الكبس شبه الجاف في تشكيل النماذج المختبرية . جففت نماذج المرشحات في درجة حرارة (110 ºC) ولمدة(24 ساعة) ومن ثم لبدت أو حرقت بدرجة حرارة 1200 ) ) وفترة مكوث (1ساعة) .ومن ثم تم استخراج المسامية و مقاومة الانضغاط. وبالاعتماد على النتائج العملية تم التوصل الى العلاقة بين (نسبة رمل السليكا و حجم حبيبات الرمل ) و(المسامية الظاهرية و مقاومة الانضغاط للمرشح السيراميكي) . بالنسبة لتأثير نسبة رمل السليكا فتكون علاقتها طردية مع المساميه الظاهريه بينما تكون علاقتها عكسيه مع مقاومة الانظغاط. يؤثر الحجم الحبيبي على الخواص الفيزياوية و الميكانيكية للنموذج,حيث عند زيادة حجم الجسيمات تقل المساميه الظاهرية وتتحسن مقاومة الانظغاط. حيث اظهرت النتائج أن أعلى مساميه ظاهرية (41.328) وذلك عند أعلى نسبة لرمل السليكا (60%) وأصغر حجم لجسيمات الرمل(50µm). وأعلى مقاومة انظغاط(11.831MPa)وذلك عندأقل نسبة نسبه لرمل السليكا(40%),و أكبر حجم لجسيمات الرمل(150µm)

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (3)

Arabic (1)


Year
From To Submit

2017 (2)

2014 (1)

2013 (1)