Abstract

Magnesium oxide (MgO) is regarded as a biocompatible material. A composite material from MgO oxide prepared by mixing MgO powder with TiO2 (rutile phase) (2, 5, 10)Wt.% using powder metallurgy technique. It is used to be bioceramic material. The compressed samples were dried and sintered at (1200) ᵒC. porosity measurement showed that the porosity decreasing with increasing TiO2% . X-ray showed the presence of Mg2TiO4 in the composite structure of MgO with (5, 10)%TiO2 samples. The mechanical study showed an increasing in compressive strength, hardness, wear resistance and biodegradation resistance with increasing TiO2% content in the limit of used percentage. The prepared composite material didn’t present antibacterial activity while previous researches showed opposite result because of using nanoscale particle size of MgO.

يعتبر أوكسيد المغنيسيوم (MgO) مادة متوافقة حيويا. تم إعداد مادة مركبة من اوكسيد المغنيسيوم عن طريق خلط مسحوق MgO مع (2، 5، 10 ( ٪ TiO2طورrutile باستخدام تقنية تكنولوجيا المساحيق لإنتاج مادة حياتية. تم تجفيف العينات المضغوطة وتلبيدها بدرجة حرارة 1200مᵒ. اظهرت قياسات المسامية انخفاض المسامية بزيادة نسبة TiO2 المضافة. وأكدت نتائج الأشعة السينية ظهور الطور( Mg2TiO4) في هيكل عينات MgO مع (5، 10(٪ TiO2.وأظهرت دراسة الخواص الميكانيكية زيادة في مقاومة الانضغاط، ،الصلادة ،مقاومة البلى و مقاومة التحلل مع زيادة محتوى TiO2ضمن مدى الاضافة في البحث. ولم تظهر المادة المركبة نشاط مضاد للجراثيم في حين أظهرت الأبحاث السابقة نتيجة عكسية بسبب استخدام حجم الجسيمات النانوية من MgO


Article
Characterization,Mechanical, and In Vitro Bioactivity Properties of Hydroxyapatite/Bioactive Glass Composite

Authors: Ola Salih Mahdi --- Isra Qahtan Sabri
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2016 Volume: 24 Issue: 4 Pages: 820-831
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Bioactive ceramic materials can help bone reparation and regeneration by offering support to bone growth. Biological hydroxyapatite powder was prepared by burning animal bone followed by studying the mechanical properties of hydroxyapatite (HA)/ (20wt.%, and 40wt.%) of binary bioactive glass (70% SiO2- 30% CaO) in order to evaluate the influence of composition on the compressive strength and hardness. HA-composite material exhibited increasing density, microhardness, and compressive strength with increasing amount of glass addition. X-ray diffraction after sintering at 1200°C showed no alter of HA to secondary phases while the hydroxyapatite/ bioactive glass composites contained a HA phase and different amounts of wollastonite phase, depending on the amount of bioglass added.In vitro tests, the samples were soaked in simulated body fluid (SBF) for ten days in order to evaluate the change in compression strength, weight loss, and pH. The HA composite reinforced with 40 wt % bioglass showed highest compression strength, and lowest weight loss.

تساعد مواد السيراميك الحياتية في ترميم واعادة بناء العظم بكونها تدعم نموالعظم. تم تحضيرمسحوق مادة الهيدروكسي ابتايت من عملية حرق عظام الحيوانات واستخدمت كمادة اساس لتحضيرمادة حياتية مركبة تتكون من الهيدروكسي ابتايت/الزجاج النشط بيولوجيا بنسبة (20%و40%) وذلك لتقييم تاثيراضافة الزجاج الحياتي على مقاومة الانضغاط والصلادة ومقارنتها مع مثيلاتها لمادة الهيدروكسي ابتايت.اظهرت اختبارات الاشعة السينية ان عملية التلبيد بدرجة 1200°م لاتسبب تحلل لطور الهيدروكسي ابتايت في حين اظهرت وجود طور wollastonite في المادة المركبة بكميات تختلف باختلاف نسبة الزجاج المضافة رافقها زيادة في الكثافة والصلادة ومقاومة الانضغاط للمادة المركبة .اجريت الاختبارات البايولوجية بتحضير SBF ثم اجراء عملية الغمر لمدة عشرة ايام تم خلالها قياس pH يوميا للوسط وقياس التغير بالوزن ومقاومة الانضغاط في نهاية فترة الغمر ثم اجراء الاشعة السينية للنماذج الثلاث حيث وجد ان العينات الحاوية على 40% من الزجاج النشط بيولوجيا تمتلك اعلى مقاومة انضغاط واقل فقدان بالوزن.