The Effects of Chemical Treatment of Wood Cinder on the Mechanical Properties of the Composite Materials(Polyester-Wood Excelsior)
تأثير المعالجة الكيمياوية لنفايات الخشب على الخواص الميكانيكية للمادة المركبة (بولي استر-نشارة خشب)

Loading...
Loading...
Abstract

The Mechanical properties of reinforced composite materials depend on bonding strength between reinforcements and matrix , improving the bonding strength can be achieved by surface treatment or sizing . In this investigation chemical treatment for wood excelsior carried out by using (H2O , NaCl , NaOH) solution to increase the surface roughness for excelsior surface . Group of tests was carried out to study the effect of this treatment on the mechanical (bending and compression) properties of a material composed of unsaturated polyester reinforced by (10 % wt) of treated wood excelsior . Also Calculation of the weight loss and executing of microscopic photo . The results show :- Increase of the bending strength of treated wood excelsior reinforced composite materials with a maximum percentage of (228 %) compared with samples reinforced with untreated excelsior . This maximum percentage was found when the excelsior are treated at room tempreature for (H2O) and (2 day) .- Increase of the bending strength of treated wood excelsior reinforced composite materials with a maximum percentage of (40 %) compared with samples reinforced with untreated excelsior , this maximum percentage was found when the excelsior are treated at room tempreature for (10 % NaCl+90%H2O) and (8 day) .- Increase of the bending strength of treated wood excelsior reinforced composite materials with a maximum percentage of (177 %) compared with samples reinforced with untreated excelsior , this maximum percentage was found when the excelsior are treated at room tempreature for (10 % NaOH+90%H2O) and (4 day) .- Increase of the compression strength of treated wood excelsior reinforced composite materials with a maximum percentage of (18 %) compared with samples reinforced with untreated excelsior , this maximum percentage was found when the excelsior are treated at room tempreature for (H2O) and (4 day) .- Increase of the compression strength of treated wood excelsior reinforced composite materials with a maximum percentage of (10 %) compared with samples reinforced with untreated excelsior , this maximum percentage was found when the excelsior are treated at room tempreature for (10 % NaCl+90%H2O) and (8 day) .- decrease of the compression strength of treated wood excelsior reinforced composite materials with a minimum percentage of (25 %) compared with samples reinforced with untreated excelsior , this minimum percentage was found when the excelsior are treated at room tempreature for (10 % NaOH+90%H2O) and (8 day) .- Increase of the weight loss to treated wood excelsior with (NaOH) more than weigth loss of.treated wood excelsior with (NaCl , H2O) .

تعتمد الخواص الميكانيكية للمواد المركبة المقواة على مقاومة الربط بين التقويات والارضية يتم تحسين مقاومة الربط بالمعاملة السطحية (Surface treatment) اوبالاكساء (Sizing) . حيث تم في البحث الحالي معالجة كيمياوية لنشارة الخشب باستخدام محاليل (H2O , NaOH , NaCl) لزيادة الخشونة السطحية لسطح النشارة وبالتالي زيادة التلاصق بين النشارة والارضية . اجريت مجموعة من الاختبارات لدراسة تأثير المعالجة الكيمياوية على الخواص الميكانيكية (انحناء وانضغاط) للمادة المركبة ذات اساس من البولي استر غير المشبع المقواة ب(10 %wt.) نشارة خشب معالجة . كذلك تم حساب الفقدان بالوزن واجراء تصوير مجهري . اظهرت نتائج الاختبارات ارتفاع مقاومة الانحناء لعينات المواد المركبة المقواة بنشارة خشب معالجة بنسبة اقصاها (228 %) عند المعالجة ب(H2O) مقطر ولمدة (2 day) , ارتفاع مقاومة الانحناء لعينات المواد المركبة المقواة بنشارة خشب معالجة بنسبة اقصاها (40 %) عند المعالجة ب (10% NaCl+90%H2O) ولمدة (8 day) , ارتفاع مقاومة الانحناء لعينات المواد المركبة المقواة بنشارة خشب معالجة بنسبة اقصاها (177 %) عند المعالجة ب(10% NaOH+90%H2O) ولمدة (4 day). كما اظهرت نتائج الاختبارات ارتفاع مقاومة الانضغاط لعينات المواد المركبة المقواة بنشارة خشب معالجة بنسبة اقصاها (18 %) عند المعالجة ب(H2O) مقطر ولمدة (4 day) , ارتفاع مقاومة الانضغاط لعينات المواد المركبة المقواة بنشارة خشب معالجة بنسبة اقصاها (10 %) عند المعالجة ب(10% NaCl+90%H2O) ولمدة (8 day) , في حين انخفضت مقاومة الانضغاط لعينات المواد المركبة المقواة بنشارة خشب معالجة بنسبة اقصاها (25 %) عند المعالجة ب(10% NaOH+90%H2O) ولمدة (8 day) . كذلك اظهرت النتائج ارتفاع نسبة الفقدان بالوزن لنشارة الخشب المعالجة ب(NaOH) اكثر من النشارة المعالجة ب(H2O , NaCl) .

Listing 1 - 1 of 1
Sort by
Narrow your search

Resource type

article (1)


Language

Arabic (1)


Year
From To Submit

2010 (1)