The Inhibition Effect of Peach Juice on Corrosion of Low Carbon Steel in Hydrochloric Acid at Different Temperatures

Authors: Hadeel F. Ibraheem --- Aprael S. Yaro ابرائيل سركيس يارو
Journal: Iraqi Journal of Chemical and Petroleum Engineering المجلة العراقية للهندسة الكيمياوية وهندسة النفط ISSN: 19974884/E26180707 Year: 2010 Volume: 11 Issue: 1 Pages: 65-76
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The corrosion inhibition of low carbon steel in1N HCl solution in the presence of peach juice at temperature (30,40,50,and 60)°C at concentration ( 5, 10, 20, 30, 40and 50 cm3/L)were studied using weight loss and polarization techniques. Results show that the inhibition efficiency was increased with the increase of inhibitor concentration and increased with the increase of temperature up to 50ºC ,above 50ºC (i.e. at 60 ºC) the values of efficiency decreases. Activation parameters of the corrosion process such as activation energies, Ea, activation enthalpies, ∆H, and activation entropies, ∆S, were calculated. The adsorption of inhibitor follows Langmuir isotherm. Maximum inhibition efficiency obtained was a bout 91% at 50ºC in the 50 cm3/L inhibitor concentration. The polarization curves show that peach Juice is a mixed inhibitor


Article
Surface Plasmon Resonance study of Ag nanoparticles colloidal
دراسة رنين بلازمون السطح لسائل الفضة الجسيمات النانوية الغروية

Authors: Waleed k. Mahmood وليد خالد محمود --- Rawa k. Ibrahim روى خليل ابراهيم --- Asama N. Naje اسامه ناطق ناجي
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2017 Volume: 58 Issue: 4B Pages: 2090-2097
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Silver nanoparticles (Ag-NPs) have been prepared using the electro-chemical method. The experimental setup of this technique consist of two electrodes of pure silver (99.2 %), the applied voltage on the electrodes is 20 V and the current through the colloidal was about 0.4 Amp. The silver nanoparticles crystallization has been studied; the crystalline structure appears Face center Cubic. The optical properties of silver nanoparticles are strongly affected by the Local Surface Plasmon Resonance (LSPR). The wavelength of maximum absorption band for an Ag NPs have a range (~350nm-550nm).

تم تحضير الجسيمات الفضة النانوية باستخدام الطريقة الكهروكيميائية. الإعداد العملي لهذه التقنية يتكون من قطبين من الفضة النقية (99,2%), والفولتية المسلطة على القطبين 20 فولت والتيار المار خلال الغراء بحدود (0,4 امبير). وقد تمت دراسة تبلور جسيمات الفضة النانوية ، ويظهر التركيب البلوري مكعب متمركز الوجه. الخصائص البصرية لجسيمات الفضة النانوية تتأثر بقوة بالرنين الموضعي لبلازمون السطح ,والطول الموجي لأقصى امتصاص لجسيمات الفضة النانوية يقع ضمن المدى (350-550 ) نانومتر.


Article
Synthesis and Characterization of Nano-Aluminum Oxide Via Biological and Electrochemical Methods

Authors: Barakat A. F. Kamel --- Shaimaa H. Jaber --- Amel S. Mahdi --- Mohammed A. K. Alsouz --- et al.
Journal: Al-Mustansiriyah Journal of Science مجلة علوم المستنصرية ISSN: 1814635X Year: 2018 Volume: 29 Issue: 4 Pages: 67-72
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

In this research work, the nanoparticles of aluminum oxide were synthesized by two ways. The first way is the biological by using (Pseudomonas aeruginosa) bacteria with a rate diameter (102.35) nm. The second way is the electrochemical with a rate diameter (62) nm. These nanoparticles were characterized by Atomic Force Microscopy (AFM), X-Ray diffraction technique (XRD), Transmission Electron Microscopy (TEM) and Scanning Electron Microscopy (SEM). Alumina nanoparticles are thermodynamically stable particles over a wide temperature range. The biological activity of these nanoparticles toward different species of pathogenic bacteria (Staphylococcus aureus) and (Pseudo monas) has been investigated. The nanoparticles prepared by chemical way was more effective in the inhibition of bacteria compared with that nanoparticles prepared by biological way.

تم في هذا البحث تحضير الدقائق النانوية لاوكسيد الالمنيوم بطريقتين: الطريقة الاولى هي الطريقة البايولوجية بأستخدام بكتريا (Pseudomonas aeruginosa) وبمعدل (102.35) نانومتر. اما الطريقة الثانية فهي الطريقة الكهروكيميائية وبمعدل (62) نانومتر. تم تشخيص هذه الجسيمات باستخدام اجهزة ( مجهر القوة الذرية، تقنية الاشعة السينية، مجهر الانتقال الالكتروني ومجهر الماسح الالكتروني) ووجد ان هذه الجسيمات مستقرة ثرموديناميكيا على نطاق حراري واسع. كما ودرست الفعالية البايولوجية للجسيمات النانوية تجاه انواع مختلفة من البكتريا المسببة للامراض مثل (Staphylococcus aureus) و (Pseudo monas) ووجد ان الدقائق النانوية المحضرة بالطريقة الكهروكيميائية اكثر فعالية في تثبيط هذه الانواع من البكتريا مقارنة بالدقائق النانوية المحضرة بالطريقة البايولوجي


Article
Electrodeposition of NiCr Nanowires Using Anodic Aluminum Oxide

Authors: Rana Afif Anaee dr.rana_afif@yahoo.com --- Alaa H. Ali --- Ahmed Rajih Hassan
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 1 Pages: 55-59
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This research highlights fabrication of NiCr nanowires by electrochemical deposition. The deposition was achieved using anodic aluminum oxide AAO template with 70 nm diameter of pores. The anodization was performed using oxalic acid with two steps to obtain AAO template. 72.3Ni27.7Cr nanowires were obtained using nickel and chromium sulfate. The nanowires were characterized by SEM and TEM. The obtained nanowires with 70 nm diameter and 420-500 nm length.

يشير هذا البحث الى تصنيع اسلاك نانوية لسبيكة نيكل-كروم بواسطة الترسيب الكهروكيميائي. انجز الترسيب الكهروكيميائي على اساس من اوكسيد الالمنيوم المؤنود ( AAO ) ذات ثقوب نانوية قطرها ( 70 nm ). تمت عملية الانودة للالمنيوم بأستعمال حامض الاوكزالك وذلك بخطوتين من الانودة للحصول على الاساس AAO ثم تلاها ترسيب سبيكة نيكل-كروم من املاح كبريتات النيكل وكبريتات الكروم وكانت نسب العناصر الناتجة للسبيكة هي 72.3Ni27.7Cr . الاسلاك النانوية الناتجة تم تشخيصها بأستعمال المجهر الالكتروني SEM والمجهر الالكتروني TEM.ان الاسلاك النانوية الناتجة تمتلك قطر بمقدار( 70 nm ) وطول ( 420-500 nm ).