Article
Studying The Dielectric and Structural Properties of Baxsr1-Xtio3 (BST) Ferroelectric System Prepared by Using Oxalic Acid Route
دراسة الخصائص الكهربائية والتركيبية للنظام الفيروكهربائي BaxSr1-xTiO3 المحضر بطريقة حامض الاوكزاليك

Authors: Sabah M. Ali Ridha --- Rawa A. Helal
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 10 Pages: 2015-2026
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

BaxSr1-xTiO3 (BST) ferroelectric nano, poly crystalline systems wereprocessed with three concentrations (x = 0.5, 0.7 and 0.9) using a technique knownas oxalic acid route. The XRD spectra were analyzed, and used Scherer formula toestimate the crystallite size of the products, which reached to 15.4 nm at x = 0.5. Itis found that increasing of Sr+2 cations help to decrease the crystallite size ofBaxSr1-xTiO3 system and the tetragonality c/a increases when the crystallite sizeincreases. In physical tests we conclude that the oxalic acid method is a goodmethod to prepare a BST ferroelectric phase with high density (5.05, 5.5 and 5.45)gm/cm3, and small porosity (16, 8, and11) % for (x = 0.5, 0.7 and 0.9)respectively.

(BST) BaxSr1-xTiO تم تحضير مادة فيروكهربائية نانوية ذات النظام متعدد التبلور 3باستخدام طريقة الحامض الاوكزاليكي.تم تحليل (x = 0.5, 0.7 and وبثلاثة تراكيز هي ( 0.9للنماذج وبتطبيق معادلة شيررأمكن حساب حجم ال XRD طيف حيود الاشعة السينيةx = القيمة 15.4 نانومتر عند التركيز crystallite وفي هذا البحث بلغ حجم ال .crystalliteيساعد في أنقاص حجم (BST) 0.5 , كما وجد أن زيادة تركيز ايونات السنترونتيوم في النظامومن خلال .crystallite مع أزدياد حجم ال c/a ولوحظ أزدياد ألاستطالة crystallite الالاختبارات الفيزيائية تم ألاستنتاج بان طريقة الحامض الاوكزاليكي طريقة جيدة لتحضيرمادة(16, 5.05 ),ومسامية قليلة , 8 , 5.5,and 5.45) gm/cm الفيروكهربائية بكثافة عالية 3 BSTعلى التوالي. (x = 0.5, 0.7 and للتراكيز ( 0.9 and11) %

Keywords

ferroelectric --- polar materials --- BST


Article
SOME OF DIELECTRIC PROPERTIES OF POLYMER/FERROELECTRIC COMPOSITES

Author: Inaan M. Abdulmajeed
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2012 Volume: 12 Issue: 1 Pages: 63-72
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

BaTiO3, synthesized in polycrystalline form, using stoichiometric mixture of oxide with traditional ceramic technique and characterized by X-ray diffraction, tetragonal structure of prepared powder were found. Moreover, particle size of ceramic powder determined using laser particle size analyzer. The particle size distribution was found in the range (0.427-3.195)µm. The epoxy ceramic composite system was prepared. BaTiO3 with content 10%, 20%, 30%, 40%, 50% wt and 60% wt. respectively used as filler. Permittivity of the composites was investigated at frequencies from 2KHz to 5 MHz The dielectric loss tangent (tanδ) was determined as a function of frequency, compositions. It was found that the weight percent of BaTiOcomposite effect on the dielectric properties. At low frequencies, BaTiO33 filler in ceramic/epoxy /Epoxy composites have much higher dielectric constant. Dielectric constant increases considerly with the addition of BaTiO3 fillers, however, the higher conductivity of BaTiOconductivity with increases BaTiO33 than epoxy lead to an increase in ac content, the increase in both properties was attributed to the presence of the high permittivity ferroelectric phase


Article
Interfacial Adhesion of PZT Ferroelectric Thin Films Determined by Nano-Indentation Method

Authors: X.J. Zheng --- Y.C. Zhou
Journal: Iraqi Journal of Applied Physics المجلة العراقية للفيزياء التطبيقية ISSN: 18132065 23091673 Year: 2009 Volume: 5 Issue: 1 Pages: 46-48
Publisher: iraqi society for alternative and renewable energy sources and techniques الجمعية العراقية لمصادر وتقنيات الطاقة البديلة والمستجدة

Loading...
Loading...
Abstract

We propose an elastic groundsill beam model with piezoelectric effectconsidered to assess the interfacial adhesion of ferroelectrics thin films,complemented and validated by nano-indentation fracture test onPb(Zr0.52Ti0.48)O3 (PZT) thin films. It was observed from the loadindentationdepth curves and atomic force microscopy (AFM) images thatthe fracture failure of PZT thin films induced by nano-indentations can bedivided into three typical stages: no damage, bulging and spallation. Thedelamination of thin film systems was modeled as an interfacial crackpropagation problem, with the energy release rate determined from theelastic groundsill beam model. For PZT thin films deposited on single Sisubstrate with thickness of 350nm and 450nm, the energy release rates perunit new crack area are in the range of 3.399~52.432J/m2 and the phaseangles are constant of 13.3570.


Article
Preparation and study the structure of pure and impure barium titanate with Mg2+ ion
تحضير ودراسة تركيب الباريوم تيتانيت النقي والمشوب بايون المغنيسيوم (Mg2+)

Authors: Mojahid Mohammed Najim مجاهد محمد نجم --- Wasan Abd Alsatar Hekmt وسن عبد الستار حكمت
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2018 Volume: 16 Issue: 37 Pages: 190-198
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Pure and doped barium titanate with Mg2+ ion at two molar ratios x= (5%, 10%) mol. has been synthesized by solid state reaction technique. The powders sintered at two temperatures (1000 °C and 1400 °C). An XRD technique was used in order to study the crystal structure of pure and doped barium titanate, which confirmed the formation of the tetragonal phase of BaTiO3, and then calculate the lattice parameters of pure and doped barium titanate, the addition of magnesium ion Mg2+ can lead to decreases lattice parameters.

تم تحضير ودراسة التركيب البلوري للباريوم تيتانيت النقي و المشوب بايون المغنيسيوم Mg2+ والمضاف بنسبة مولارية x= (5%, 10%) والتي حضرت بتقنية تفاعل الحالة الصلبة. تم تلبيد المساحيق المحضرة عند درجتي حرارة(1000 °C, 1400 °C) و أجريت فحوصات XRD لدراسة التركيب البلوري للباريوم تيتانيت النقي والمشوب حيث أظهرت النتائج تكون الطور الرباعي للباريوم تيتانيت, وتم حساب معاملات الشبيكة للباريوم تيتانيت النقي والمشوب حيث أظهرت النتائج إن إضافة ايون المغنيسيوم Mg2+ يؤدي إلى حدوث تناقص بمعاملات الشبيكة.


Article
Preparation and Study the Structure of Pure and Impure Barium Titanate with Zr4+ Ion

Authors: Mojahid M. Najim --- Wasan A. Hekmat
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2019 Volume: 37 Issue: 1part (B) Science Pages: 21-24
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Abstract: In this research, pure and impure barium titanate with Zr4+ ion with twomolar ratios x= (5, 10) % have been synthesized by solid-state reaction technique.The powders calculations at two temperatures (950°C and 1400°C). An XRDtechnique was used in order to study the crystal structure of pure and impurebarium titanate, which confirmed the formation of the tetragonal phase of BaTiO3,then calculate the lattice parameters of pure and impure barium titanate, theaddition of zirconium ion Zr4+ lead to increases lattice parameters.


Article
Fabrication and study of the structural and spectral properties of the composites (y) Mn0.6 Zn0.4 Fe2O4 + (1-y) PZT prepared by the powder technology method
تصنيع ودراسة الخواص التركيبية والطيفية لمركبات Mn0.6 Zno.4 Fe2O4 +(1-y)PZT(y) المحضرة بطريقة تكلوجيا المساحيق

Loading...
Loading...
Abstract

Ferrite-ferroelectric composites holds following chemical formula (y) Mn0.6 Zn0.4 Fe2O4 + (1-y) PZT with different weight rations (y=0.15, 0.30 and 0.45) are prepared by the powder technology method at annealing temperature (1000 °C) for (12hrs). The structural properties are also studied representing by the lattice constants (a, c), particle size (Dt), apparent density (ρa), and X-ray density (ρx). It has been shown that increasing the concentration of the ferrite phase contributes to an increase in the lattice constant, apparent density and X-ray density which in turn contribute in decreasing porosity that plays a role in improving the physical properties of the samples as well as the weight ratios of the mixture after the final sintering with reference to x-ray diffraction technique. In addition, the spectral properties were also studied represented by the vibration force constant and regions of optical absorption in terms of IR technique.

تم تحضير مركبات الفرايت–الفيروكهربائية ذات الصيغة الكيميائية Mn0.6 Zno.4 Fe2O4 + (1-y) PZT (y) وبنسب وزنية مختلفة (= 0.15, 0.30, 0.45 y) بطريقة تكنلوجيا المساحيق عند درجة تلدين (1000 ̊C) لمدة (12hr). كما تم دراسة الخواص التركيبية المتمثلة بثوابت الشبيكة (a, b) والحجم الحبيبي (Dt) والكثافة الفيزياوية الظاهرية (ρ_a) والكثافة بدلالة حيود الاشعة السينية (ρ_x) أذ تبين ان زيادة تركيز نسبة طور الفرايت يساهم في زيادة ثابت الشبيكة والكثافة الظاهرية والحقيقية التي بدورها تساهم في تقليل المسامية التي تلعب دور في تحسين الخواص الفيزياوية للنماذج وكذلك النسب الوزنية للخليط بعد التلبيد النهائي بدلالة تقنية حيود الاشعة السينة. كما تم دراسة الخواص الطيفية المتمثلة بثابت القوة الاهتزازية ومناطق الامتصاص البصرية بدلالة تقنية IR.


Article
Study structural, dielectric and ferroelectric properties of Pb (Zr1-x Tix)O3 ceramics near the morphotropic phase boundary
"دراسة الخواص التركيبية والعزلية والفيروكهربائية لسيراميكPb(Zr(1-x)Tix)O3 بالقرب من الاطوار الحدودية"

Author: Abdulsamee Fawzi Abdul Aziz AL-Bayati عبدالسميع فوزي عبدالعزيز البياتي
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2016 Volume: 21 Issue: 3 Pages: 125-134
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

In the present work, Pb(Zr(1-x)Tix) ceramics (x = 0.50, 0.48, 0.45 and 0.42) were prepared using the solid state reaction method, at the sintaring temperature (1100 oC ) for (6hr).X-ray diffraction results demonstrate that all the samples lie within the morphtropic phase boundary (MPB) region in the pure perovskite tetragonal structure with Miller transactions (100), (110), (111), (200), (210), (211), (220), (103) and (311) that the prevailing trend is (110) and the results of plasticity microwave very close sense of distance intra-convergent also relatively few crystalline defects. Increasing the bulk density of the true density of altered concentration of zirconium and titanium. Results of the examination microscope also showed that the particle size (Dnm) be tight between the samples and the homogeneity of the granules, as well as increasing the homogeneity of compositional structure, causing an improvement in the structural and electrical properties. Shown technique results EDAX compound of the interacting elements of the composition and there is little difference between the real weight and the weight is noticeable. The temperature and concentration of titanium dependences of the dielectric constant of the ceramics has been investigated in detail. Excellent dielectric properties have been obtained for the selected compositions. Polarization-Elctric field hysteresis studies were carried out for all compositions at room temperature. It was found that with the increase of concentration of titanium content in the composition the remnant polarization decreases and ferroelectric loops get constricted.

تم تحضيرسيراميك تيتانات زركونات الرصاص ذات الصيغة الكيميائية O3(Zr1-x Tix)Pb حيث أنّ (x = 0.5,0.48,0.45,0.42) وذلك بإستخدام طريقة تفاعلات الحالة الصلبة حيث تم تلبيد النماذج المحضرة عند درجة حرارة (1100˚C) ولمدة (12hr). حيث أظهرت نتائج حيود الاشعة السينية ان جميع النماذج الواقعة ضمن منطقة الاطوار الحدودية كانت ذات تراكيب بروفسكايت رباعية نقية ومعاملات ميلر (001), (100) , (110) , (111) ,(002) , (200) , (210) , (211) ,(220),(221), (103) وأن الإتجاه السائد هو(110) ونتائج المطاوعة الميكروية متقاربة جداً بمعنى المسافة البينية متقاربة أيضاً والتشوهات البلورية قليلة نسبياً. زيادة الكثافة الظاهرية عن الكثافة الحقيقية بإختلاف تركيز الزركونيوم والتيتانيوم. كما أظهرت نتائج فحص المجهر الألكتروني أنّ الحجم الحبيبي (Dnm) يكون متقارب بين النماذج وتجانس الحبيبات, بالاضافة الى ان زيادة تجانس البنية التركيبية قد سبب تحسننا في الخواص التركيبية والكهربائية. ان نتائج تقنية EDAX قد اظهرت تكوين المركب من العناصر المتفاعلة ، مع وجود اختلاف قليل بين الوزن الحقيقي والوزن الملاحظ . كما تم دراسة تاثير كل من درجة الحرارة وتركيز التتانيوم على ثابت العزل الكهربائي للمركبات السيراميكية بشكل مفصل. كما تم دراسة حلقات الهسترة الكهربائية ( P-E loop ) لجميع المركبات عند درجة حرارة الغرفة . أذ تبين ان زيادة تركيز نسبة التيتانيوم في المركبات الى تناقص مقدار الاستقطابية المتبقية والحصول حلقات محدودة.


Article
Studying the effect of Strontium Titanate on the Dielectric Constant of the Barium Titanate
دراسة تأثير اضافة تيتانات السترونتيوم على ثابت العزل الكهربائي لتيتانات الباريوم

Author: كنعان محمد موسى
Journal: journal of al-qadisiyah for pure science(quarterly) مجلة القادسية للعلوم الصرفة (فصلية). ISSN: 19972490 Year: 2016 Volume: 2 Issue: 21 Pages: 169-176
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

In this study, the effect of adding strontium titanate (SrTiO3) on the dielectric constant of the barium titanate (BaTiO3) was investigated. For this purpose, the BaTiO3 powder was first prepared by mixing barium carbonate (BaCO3) with titanium dioxide (TiO2) and sintering by vacuum furnace at 1200 ºC under Argon. Then, the SrTiO3 powder was prepared by mixing strontium carbonate (SrCO3) with titanium dioxide (TiO2) and sintering at 1150 ºC. Different weight percentages (5-50 %) of SrTiO3 were added into the BaTiO3 and mixed for 72 hour to prepare different mixtures of (BaSr)TiO3 for electrical insulators. All samples of (BaSr)TiO3 insulators were compacted and sintered at 5 tons and 1350 ºC, respectively. The crystalline structural characterizations of the prepared powders as well as the (BaSr)TiO3 mixtures were analyzed by the X-ray diffraction (XRD). Values of the dielectric contacts and the bulk density for all prepared mixtures were measured. The results showed that the electrical insulators made from the mixture of 30 % SrTiO3 and 70 % BaTiO3 revealed the highest electric constant with a reasonable density.

في هذا البحث, تمت دراسة تأثير إضافة تيتانات السترونتيوم (SrTiO3) على ثابت العزل الكهربائي للتيتانات الباريوم (BaTiO3). لهذا الغرض، تم تحضير مسحوق تيتانات الباريوم أولاً من خلط كاربونات الباريوم (BaCO3) مع ثاني أوكسيد التيتانيوم (TiO2) وتلبيدها بواسطة فرن مفرغ تحت الأركون عند 1200 درجة مئوية . ومن ثم تحضير تيتانات السترونتيوم عن طريق خلط كاربونات السترونتيوم (SrCO3) مع ثاني أكسيد التيتانيوم (TiO2) وتلبيدها بدرجة 1150 مئوية. تمت إضافة نسب وزنية مختلفة (5-50٪) من تيتانات السترونتيوم الى تيتانات الباريوم وخلطها لفترة 72 ساعة من اجل اعداد خلطات مختلفة من (BaSr)TiO3 لتصنيع العوازل الكهربائية. جميع العينات حضرت بضغط كبس مقداره 5 طن ولبدت بدرجة حرارة مقدارها 1350 مئوية. تم اجراء تحليل حيود الأشعة السينية (XRD) للمساحيق المحضرة ولمسحوق (BaSr)TiO3 المعتمد لتحضير العوازل, كذلك قياس قيم ثابت العزل الكهربائي والكثافة الظاهرية لجميع الخلطات المحضرة. أظهرت النتائج أن العوازل الكهربائية المصنوعة من خليط 30٪ SrTiO3 و 70٪ BaTiO3 بانها تمتلك أعلى ثابت عزل كهربائي بكثافة معقولة.

Listing 1 - 8 of 8
Sort by
Narrow your search

Resource type

article (8)


Language

English (7)

Arabic (1)


Year
From To Submit

2019 (1)

2018 (2)

2016 (2)

2012 (1)

2010 (1)

More...