Article
EFFECT OF GLASS ADDITION AND HEAT TREATMENT ON MECHANICAL PROPERTIES AND WEAR RATE OF ALUMINUM - 2% GRAPHITE
تأثير النسب الوزنية لمادة الزجاج والمعاملة الحرارية على الخواص الميكانيكية ومعدل البلى لمتراكبات الألمنيوم - 2% كرافيت

Author: Hashim Shukur Hammood هاشم شكر حمود الكرغولي
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2017 Volume: 10 Issue: 4 Pages: 33-41
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

This research studied the effect of the Heat Treatment on the Mechanical Properties and the Wear Rate of the pure Aluminum with a particle size of (≤53μm). The Aluminum is reinforced by graphite with a particle size of (≤63μm) with an addition of glass particles with different weight ratios of (3, 6, 9, and 12) Wt. % and a particle size was (≤ 53μm).Powder metallurgy technique has been used to manufactured the samples, where the samples are pressed uniaxial at room temperature with (500 Map), then sintering at (550 C0) for (2 hr.). After that, heat treatment is applied on the samples at (500 OC) for one hour and Quenched in water.There was a great improvement of the mechanical properties such as the hardens and the compressive strength. This improvement was proportional with the Weight ratio of the glass particles before and after the Heat Treatment.On the other hand, there was a decrease of the wear rate versus the increase of the Weight ratio of the glass particles and heat treatment.

يهدف هذا البحث الى دراسة تأثير اضافة دقائق الزجاج بنسب وزنية مختلفة Wt%(3,6,9,12) بحجم (≤53 μm) مع اضافة نسبة وزنية ثابتة % 2 من كرافيت بحجم جسيمي(≤ 63 μm) وتأثير المعاملة الحرارية على الخواص الميكانيكية ومعدل البلى للالمنيوم النقي وبحجم جسيمي (≤53 μm) .استُخدمت تقانة ميتالورجيا المساحيق لتصنيع النماذج اذ كبست النماذج على البارد بضغط كبس ( Mpa500) تم تلبيدها بدرجة حرارة (550 Co) ولمدة ساعتين ثم سُخنتْ النماذج الى درجة حرارة (500 Co) لمدة ساعة واحدة ثم بردت بالماء.بعدَ اجراء فحص الصلاده ومقاومة الانضغاط اظهرت النتائج حدوث تحسن كبير في الصلاده ومقاومة الانضغاط مع زيادة نسب اضافة دقائق الزجاج الى المتراكب قبل وبعد المعاملة الحرارية.تبين من خلال اختبار البلى حدوث انخفاض واضح مع زيادة نسب الاضافة قبل وبعد المعاملة الحرارية.


Article
الخصائص الحرارية لمتراكبات البولي أستر غير المشبع المدعم ببعض المخلفات الصناعية

Author: حيدر عبد فرج، وداد صالح الفياض، هادي سلمان اللامي
Journal: Albahir journal مجلة الباهر ISSN: 23125721 Year: 2017 Volume: 6 Issue: 11+12 Pages: 69-72
Publisher: Shiite Endowment ديوان الوقف الشيعي

Loading...
Loading...
Abstract

Unsaturated polyester )UP( composites reinforced with different percent of some industrialwastes like glass particles and sawdust were prepared to study their thermal properties. Thermalgravimetric analysis )TGA( results indicated an increase composites thermal stability with anincrease in the percentage of fillers and are greatest when the proportion (20%) glass particlescompared with sawdust, accompanied with an increase in the decomposition temperature and thetemperature of 50% weight loss )T50%( of composites reinforced with sawdust is higher than thatreinforced with glass particals.Differential scanning calorimetry) DSC( referred to higher value of glass transition temperature)Tg( of these composites compared with )UP( alone. Also the Tg of UP reinforced with glass particlesis higher than UP reinforced with sawdust.

الخلاصةالمُدعم ببعض المخلفات الصناعية )Unsaturated polyester-UP( حُضرت متراكبات البولي أستر غير المشبعوبنسب وزنيه مختلفة وذلك )Wood( flour ونشارة الخشب )Glass Particles( الدقائق الزجاجية )Industrial Wastes(لدراسةخصائصها الحرارية.إلى ازدياد الثبات الحراري للمتراكبات مع ازدياد نسبة المالئات وتكون اكبر ) TGA ( أشارت نتائج التحليل الحراري الوزنيما يمكن عند نسبة )% 20 ( من الدقائق الزجاجية مقارنة مع نشارة الخشب، كما يمكن ملاحظة أن درجة حرارة التفكك الابتدائيةونسبة المئوية للتفحم وطاقة التنشيط لعملية التفكك )T والعظمى ودرجة حرارة التي يفقد عندها المتراكب نصف وزنه )% 50المُدعم بنشارة الخشب )UP ( الى T تزداد مع زيادة نسبة المواد المالئة،كما تم ملاحظة أن قيم درجات حرارة التفكك العظميو % 50المُدعم بالدقائق الزجاجية. )UP ( أعلى منهالالى ارتفاع في )DSC-Differential Scanning Calorimetry( كذلك أشارت منحنيات المسح التفاضلي المسعريللمتراكبات المدعمة )Tg ( للمتراكبات عن قيمتها للبولي استر الغير مشبع , ويلاحظ إن قيم )Tg ( قيم درجة الانتقال الزجاجيبالدقائق الزجاجية اعلى من قيمها للمتراكبات المدعمة بنشارة الخشب.