The Effect of Pure Aluminum Weight Percent on Different Properties of a New Cermet Material Made of Al-Machinable Glass Ceramic

Author: Bayda,a Abdul-Hassan Khalaf
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 4 Pages: 805-813
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this research high pure aluminum metal with the following weight percent(1,2,3,4,5) has been added to machinable glass-ceramic, after the preparation of thesamples by pressing then firing the effect of this addition on the density, hardness,young modulus, and polishing and grinding time of the machinable glass-ceramichave been studied. It has been found that the increasing in aluminum percent lead toslightly increase in density while the hardness, young modulus, and polishing andgrinding time decreased.


Article
Studying and Modeling The Effects of Quartz Addition and Heat Treatment on Corrosion Properties of Ceramic Coating

Authors: Ali H. Ataiwi --- Ibtihal A. Mahmood --- Jabbar H. mohmmed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 12 Pages: 2564-2579
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work, a new glass-ceramic coating has been developed and applied, as a single coat without prior chemical treatment of the surface, by using the dipping technique on metal substrate. the coating are designed for application on varies grades of low alloy steel, the selected substrate was low carbon low alloyed steel with (0.2)%C. Various heat treatments at temperatures ( 500,550, and 600˚C ) at different times (60 & 120)min and with quartz addition in the range (0-15)% were used to obtain a glass-ceramics that have the optimum coating properties. These coating have been characterized by x-ray diffraction analyses and the results showed presence of a number of microcrystalline phases which are formed during the heat treatments. The results of corrosion resistance tests indicated that the acid resistance was greatly improved by addition of quartz into enamel frit but at same times decreased the alkali corrosion resistance, while the heat treatments improved both acid and alkali resistance for all cases, this is attributed to the formation of complex network from crystalline phases. The results also indicated that the heat treatment at 600˚C for 120min with 15% quartz addition brought the optimum values for acid resistance property which are improved by 86.66%, while the optimum values for alkali resistance property was brought with free quartz added samples which were treated at 600˚C for 120min. Mathematical modeling is implemented and regression equations are obtained by using ( SPSS ) software to predict the experimental data for acid and alkali corrosion rate. Comparing the predicted and measured values gives high prediction accuracy. The accuracy of prediction has been (82.58%, and 96.7%) for acid and alkali resistance properties respectively.


Article
Studying and Modeling the Effects of Quartz Addition and Heat Treatment on Mechanical Properties of Glass-Ceramic Coating
دراسة ونمذجة تأثيرات اضافة الكوارتز والمعاملة الحرارية على الخواص الميكانيكية لطلاء الزجاج السيراميكي

Authors: Ali H. Ataiwi --- Ibtihal A. Mahmood --- Jabbar H. mohmmed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 7 Part (A) Engineering Pages: 1811-1824
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work, a new glass-ceramic coating has been developed and applied, as a single coat without prior chemical treatment of the surface, using the dipping technique on metal substrate. the coating are designed for application on varies grades of low alloy steel, the selected substrate was low carbon low alloyed steel with (0.2)%C. Various heat treatments at temperatures ( 500,550, and 600˚C ) at different times (60 & 120)min and with quartz addition in the range (0-15)% were used to obtain a glass-ceramics that have the optimum coating properties. These coating have been characterized by x-ray diffraction analyses and the results showed presence of a number of microcrystalline phases which are formed during the heat treatments. The results showed the suitability of this coating for protection the metal substrate which was used in present work. The results of tests also indicated that the mechanical properties ( hardness, adhesion strength, and thermal stability) of resultant coating were greatly improved by both addition of quartz into enamel frit and heat treatments for all cases, this is attributed to the formation of complex network from crystalline phases(Li2SiO3, Li2TiSiO5, NaAlSi2O6, and SiO2) which are the main phases in the resultant glass-ceramic coating. It has been found that the heat treatment at 600˚C for 120min with 15% quartz addition brought the optimum values for ( hardness, adhesion strength, and thermal stability) of resultant coating which are improved by (70.58%, 33.84%, and 39.68%) respectively. Mathematical modeling is implemented and regression equations are obtained using ( SPSS ) software to predict the experimental data for mechanical properties of resultant coating. Comparing the predicted and measured values gives high prediction accuracy. The accuracy of prediction has been (98%, 98.5%, and 97.4%) for ( hardness, adhesion strength, and thermal stability) respectively.

في هذا العمل تم تطوير طلاء سيراميكي جديد واستخدامه، كطبقة طلاء واحدة بدون معاملة كيميائية مسبقة للسطح، باستخدام طريقة التغطيس على المعدن الاساس. صمم الطلاء للاستخدام على الانواع المختلفة للفولاذ المنخفض السبك، المادة الاساس المختارة كانت فولاذ منخفض السبك منخفض الكاربون (0،2)% كاربون. تم استخدام معاملات حرارية مختلفة عند درجات حرارة (500، 550، 600) درجة مئوية وبازمان مختلفة(60، 120) دقيقة مع اضافات كوارتز بحدود (0-15)% للحصول على الخواص المثلى لطلاء السيراميك الزجاجي. تم توصيف هذه الطلاءات باستخدام تحليل حيود الاشعة السنية حيث اثبتت النتائج وجود عدد من الاطوار البلورية الدقيقة والتي تكونت خلال المعاملات الحرارية. بينت النتائج ملائمة هذا الطلاء لحماية المعدن الاساس المستخدم في هذا العمل. كذلك بينت نتائج الاختبارات ان الخواص الميكانيكية ( الصلادة، متانة الالتصاق، والاستقرارية الحرارية) للطلاءات الناتجة قد تحسنت بصورة كبيرة من خلال كلا من اضافة الكوارتز الى مادة الطلاء (الفرت) وكذلك من خلال المعاملة الحرارية وفي جميع الحالات. هذا التحسن مرتبط بتكون شبكة معقدة من الاطوار البلورية (Li2SiO3 Li2TiSiO5, NaAlSi2O6, and SiO2) والتي كانت الاطوار الرئيسية في طلاءات السيراميك الزجاجي الناتجة. وقد وجد ان المعاملة الحرارية عند (600) درجة مئوية واضافة (15)% كوارتز قد جاءت بالقيم المثلى ل (الصلادة، متانة الالتصاق، والاستقرارية الحرارية) للطلاء الناتج حيث تحسنت بنسبة (70،58%، 33،84%، و 39،68%) على التوالي. تم استخدام موديل رياضي والحصول على معادلات الانحدار باستخدام برنامج(SPSS) للتنبا بالبيانات العملية للخواص الميكانيكية للطلاء الناتج. اعطت المقارنة بين قيم النتائج المنتبئة والمقاسة دقة تنبأ عالية. حيث كانت دقة التنبأ (98%، 98،5%، و 97،4%) لخواص (الصلادة، متانة الالتصاق، والاستقرارية الحرارية )على التوالي.


Article
Study the effect of gamma radiation on the some properties of glass and glass-ceramic immobilize nuclear waste
تأثير اشعة كاما على بعض خواص الزجاج والزجاج – سيراميك المستعمل لتثبيت النفايات المشعة

Loading...
Loading...
Abstract

Vitrifications process one of the important methods to immobilize nuclear waste. In this research nuclear waste (Strontium Oxides) with molecular weight (5%) was immobilized by vitrification methods in two types of borosilicate glass (c-type) which are glass and glass-ceramics. To investigate the physical, chemical and mechanical properties of glass and glass-ceramic after immobilize nuclear waste these samples irradiated by gamma ray radiation. Co-60 was used as gamma a irradiation with dose rate 0.38 kGy/hr for different period of time. It’s found that gamma radiation affected the glass and glass-ceramic properties. From phase analysis by the x-ray diffraction for glass-ceramic samples proved that at doses 343kGy change the crystalline glass to amorphous glass. A conclusion from these ionization studies is that the limited magnitude of Strontium ion leaching associated with ionization damage does not appear to pose any direct problems for the safe storage of nuclear waste glass.

ان عملية معالجة النفايات المشعة بواسطة تثبيتها في الزجاج واحدة من الطرق المهمة لمنع حركة النفايات النووية. في هذا البحث استعمل أوكسيد السنترنتيوم بنسبة وزنية 5% كنفايات مشعة، زجج في نوعين من الزجاج: البورسليكات )نوع (C الزجاج والزجاج-السيراميك. وتم دراسة الخواص الفيزيائية والكيميائية للزجاج والزجاج-السيراميك بعد تزجيج النفايات النووية المشعة بواسطة تشعيعها بأشعة كاما. تم استخدام الكوبلت-60 كنظير باعث لاشعة كاما بمعدل جرعة 0.38 كيلو كراي/ ساعة لفترات مختلفة من الزمن. وجد أن أشعة كاما أثرت على خواص الزجاج والزجاج-السيراميك، وعند الجرعة الاشعاعية 343 كيلو كراي تحول الزجاج-السيراميك من الطور البلوري الى زجاج عشوائي.ومن نتائج هذه الدراسة تبين أن نضوح أيون السترونتيوم بعد التعرض لاشعة كاما يكون قليل جدا بحيث لايشكل خطر، لذلك فان خزن النفايات المشعة في الزجاج تكون طريقة جيدة.


Article
Wear Resistance of a New Glass Ceramic Coating
مقاومة البلى لطلاء سيراميك زجاجي جديد

Authors: Jabbar H. mohmmed --- Ibtihal A. Mahmood --- Ali H. Ataiwi
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 6 Part (A) Engineering Pages: 1472-1484
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

A new wear resistance glass-ceramic coating system iron (low alloyed low carbon steel) based substrate was developed. The effects of heat treatment conditions and mill additions on wear resistance of developed coatings resistance were studied. The coating materials showed excellent properties for protection the iron substrate from wear. Also, in this work mathematical modeling is implemented and regression equations are obtained by using ( SPSS ) software to predict the experimental data for wear rate. Comparing the predicted and measured values gives high prediction accuracy.

في هذا البحث تم تطوير طلاء سيراميك زجاجي جديد مقاوم للبلى لمعدن الحديد(فولاذ منخفض السبك منخفض الكاربون) كمادة اساس. تم دراسة متغيرات المعاملة الحرارية زاضافات الطحن على مقاومة البلى للطلاءات المطورة. ابدى الطلاء المستخدم خواص حماية ممتازة لمادة الاساس الحديد ضد البلى. كذلك في هذا البحث تم عمل موديل رياضي وتم الحصول على معادلات انحدار باستخدام برنامج (SPSS) للتنبأ بالبيانات العملية لمعدل الطلاء. اعطت مقارنة النتائج المقاسة بالنتائج المتنبئة دقة تنبأ عالية.


Article
Modeling of The Corrosion Behavior of Enamel Coatings in Different Aggressive Media
نمذجة سلوك التاكل لطلاءات المينا في اوساط اكالة مختلفة

Authors: Ibtihal A. Mahmood --- Jabbar H. mohmmed --- Bayda'a A. Khalaf
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 6 Part (A) Engineering Pages: 1530-1543
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this study an attempt has been made to formulate materials for glass ceramic enamel coating that can be applied directly onto cast iron substrate for corrosion control. Different 'proportions(4.95) %wt. to form four batches. The batches were mixed with water to form slips which were used to coat already prepared cast iron surfaces and were allowed to dry in the oven. The coated cast iron plates were fired at temperatures of 850˚C to mature and factually heat treated at 680˚C. The coatings were observed and also chemical tests were conducted to determine the corrosion properties of the resultant coatings. The chemical tests were evaluated using a suitable standard methods and special attention was paid to the type of aggressive solution, and temperature.The results show that the coatings matured and adhered very well to the sub strateand showed good corrosion resistance in H2SO4,HCl,C6H8O7, H3PO4, and NaOH solutions. The results indicated that the corrosion rate in both acid and alkali media was increased strongly with the increasing temperature.The coatings prepared with the zircon showed better results in terms of acidcorrosion resistance than those prepared with the other crystalline agents. However, the corrosion rate of the zircon containing coating in sulfuric acid was higher than that in hydrochloric acid. Also, it is found that there is absolutely no weight loss for any of the four types of the coating in neither citric nor phosphoric acids. At the same time, the results for alkali corrosion resistance indicate that the act of the four series is very similar to each other, for the four coatings there is no high corrosion rate until the temperature exceed 100˚C after that the rate increases in a very quick manner. From the results it is found that the enamel with lithium oxide was not affected by the alkali solution at all, this behavior is associated with the presence of crystalline β-Spodumene, and β-Eucryptite, which have an extremely high corrosion resistance especially for alkali medium. Mathematical modeling is implemented and regression equations are obtained by using (SPSS) software to predict the experimental data for acid and alkali corrosion rate. Comparing the predicted and measured values gives high prediction accuracy.

في هذه الدراسة تم عمل محاولة لتكوين خلطة مواد مناسبة لطلاءات السيراميك الزجاجي والتي يمكن استخدامها بصورة مباشرة على الحديد الزهر للسيطرة على التآكل. تم اضافة عوامل تبلور مختلفة(Li2O،TiO2، ZrSiO4، و CaO.Al2O3.2SiO2) وبنسب ثابتة (4.95)% لتكوين اربع خلطات. تم خلط هذه الخلطات مع الماء لتكوين مادة الطلاء ال(slip) والتي يتم بها طلاء اسطح حديد الزهر المحضرة ثم تترك لتجف في فرن التجفيف. بعدها الواح الحديد الزهر المطلية تحرق عند درجة 850مْ للاندماج واخيرا تعامل حراريا عند درجة 680مْ.الطلاءات تم ملاحظتها وكذلك تم اجراء الفحوص الكيميائية عليها لتحديد خواص التاكل لها. تم اجراء الفحوص الكيميائية باستخدام طرق قياسية ملائمة وتم توجيه انتباه خاص لنوع المحلول الاكال المستخدم وكذلك لدرجة الحرارة. بينت النتائج ان الطلاءات قد اندمجت والتصقت بصورة جيدة جدا بالمعدن الاساس واظهرت مقاومة تاكل جيدة في المحاليل (H2SO4، HCl، C6H8O7، H3PO4، وNaOH). بينت النتائج ان معدل التاكل قد ازداد بصورة كبيرة مع زيادة درجة الحرارة في كلا من الاوساط الحامضية والقاعدية. اظهرت النتائج كذلك ان الطلاءات المحضرة من الزركون لها خواص افضل من ناحية مقاومة التاكل الحامضي مقارنة مع الطلاءات الاخرى. لكن معدل التاكل للطلاءات المحتوية على الزركون في حامض الكبريتيك يكون اعلى منه في حامض الهايدروكلوريك. كذلك، وجدنا عدم حدوث أي فقدان بالوزن للطلاءات الاربعة في حامض النتريك او الفسفوريك. في نفس الوقت بينت نتائج مقاومة التاكل في المحاليل القاعدية ان السلوك كان متشابه جدا للطلاءات الاربعة، حيث لم يلاحظ أي معدل تاكل عالي حتى درجة 100مْ بعدها ازداد معدل التاكل بصورة سريعة جدا. وقد وجدنا من خلال النتائج ان الطلاء الحاوي على اوكسيد الليثيوم لم يتاثر بالمحلول القاعدي بصورة تامة، وهذا نتيجة وجود الاطوار البلورية (β-Spodumene، وβ-Eucryptite) والتي لها مقاومة تاكل عالية جدا وخصوصا للاوساط القاعدية. تم أيضا استخدام موديل رياضي و تم الحصول على معادلات انحدار باستخدام برنامج (SPSS)والتي تكونت لغرض التنبؤ بالبيانات المختبرية لخواص الطلاء. بينت النتائج من خلال المقارنة بين القيم المتنبئة والحقيقية إن هذا البرنامج يعطي دقة تنبؤ عالية.


Article
Experimental Study for the Effects of Crystalline Agents on Properties of Glass-Ceramic Coating

Authors: Ibtihal.A. Mahmood --- Ahmed.A.Zainulabdeen --- Jabbar.H. Mohmmed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 2 Part (A) Engineering Pages: 179-184
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work, four series of glass-ceramic coatings were developed and applied by using the dipping technique to cast iron sheets. The influence of different types of crystallization agents (Li2O, TiO2, ZrSiO4, and CaO.Al2O3.2SiO2) was investigated in relation to the mechanical features of the coatings. The resultant coating is characterized using X-ray diffraction analysis. The properties of micro-hardness and adhesion strength are evaluated using suitable standard tests. The X-ray analysis of resultant coatings showed the existence of some of crystalline phases formed depending on the type of the crystallization agent. The results also indicated that the coating properties were strongly dependent on composition and concentration of crystallization agent. Coating with feldspar gives the highest value of hardness and adhesion index. In general, properties of the resultant coatings were improved in all cases; this is related to the formation of a complicated network from crystalline phases.


Article
Studying The Effect of Zircon Dioxide on The Corrosion Resistance of Porcelain Enamel
دراسة تأثير أوكسيد الزركونيوم على مقاومة تأكل الطلاء البورسليني

Author: Nagham Salman Hassan نغم سلمان حسن
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2011 Volume: 14 Issue: 2 Pages: 189-198
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Among various coating systems for industrial and engineering applications, glass–ceramic coatings have advantages of chemical inertness, high temperature stability and superior mechanical properties such as abrasion, impact etc as compared to other coating materials. Besides imparting required functional properties such as heat, abrasion and corrosion resistance to suit particular end use requirements, the glass–ceramic coatings in general also provide good adherence, defect free surface and refractoriness. This research tends to produce a cheep and effective glass- ceramic coating from glass cullet and different percent of crystallization agents ZrO2, and study the final corrosion resistance properties of them. After several set of acid resistance testing at temperatures range (25, 50, 75,100,125 oC) it has been found that porcelain enamel with (4 wt %) ZrO2 has the best acid corrosion resistance.

من ضمن انظمة الطلاء المختلفة للتطبيقات الهندسية والصناعية, طلاءات الزجاج السيراميكي لها ميزة المقاومة الكيميائية, والاستقرارية في درجات الحرارة العالية والخواص الكيميائية المدهشة مثل القشط, والصدمة الى اخره مقارنة مع مواد الطلاء الاخرى. اضافة الى باقي الخواص الضرورية للاغراض التطبيقية مثل الحرارة , مقاومة القشط , والتاكل لتلائم متطلبات التطبيق النهائية, طلاءات الزجاج السيراميكي بصورة عامة توفر التصاقية جيدة وسطح خالي من العيوب وعازل حراريا. هذا البحث يهدف الى انتاج طلاء من الزجاج السيراميكي يكون فعالا ومنتج من مخلفات الزجاج ونسب مختلفة من عامل التبلور ZrO2, ودراسة خواص مقاومة التاكل النهائية. بعد سلسلة متعددة من اختبارات مقاومة الحامض في درجات حرارية تتراوح بين (25, 50, 75,100,125 oC) وجد ان الطلاء ذو (4% نسبة وزنية) من ZrO2 له احسن مقاومة تاكل.


Article
Evaluation of the effect of surface treatments on shear bond strength between lithium disilicate ceramic and dentin

Loading...
Loading...
Abstract

Purpose: To evaluate the effect of different surface treatments on shear bond strength between dentin and IPS e.max lithium disilicate glass-ceramic.Materials and Methods: Eighteen extracted third molars were embeded in epoxy resin. The tooth was sectioned vertically in mesiodistal direction using a low speed hard tissue microtome. The buccal and lingual surfaces of each section were ground flat using 600 grit Silicone carbide paper. Eighteen ceramic discs consisted of lithium disilicate glass-ceramic were prepared with a diameter of 4.7mm and height of 2.2mm. The discs were divided in two groups (n=10): (1) IPS e.max treated with hydrofluoric acid and Monobond Plus (MBP) and (2) IPS e.max treated with Monobond Etch &Prime (MBEP). The tooth was cemented with Multilink Automix and stored for 24hours at room temperature before thermocycling and subsequently loaded to failure in Universal Testing Machine. Failure mode were recorded for each specimen.Result: Bond strength analysis and t-test analysis MBEP demonstrated the higher shear bond strength (SBS). MBP and MBEP showed no statistically significant difference were found between them. One-way ANOVA and t-test was used to determine differences in bond strength within and between the groups. Cohesive failure in resin cement was predominant with higher results while adhesive and mixed with lower and equal.Conclusion: Surface treatment with Monobond Etch and Prime has a favorable effect on SBS between dentin and lithium disilicate glass-ceramic with resin cement compared with Monobond Plus.


Article
Improvement the Chemical Resistance of Furnaces Bricks for Petroleum Refineries by ZrO2-Nano- Glass-Ceramic Coated

Authors: S.A. Zaidan --- H. Y. Abed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2017 Volume: 35 Issue: 10 Part (A) Engineering Pages: 999-1002
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Partial Stabilized Zirconia (PSZ) was prepared from adding 3 wt % of MgO or adding 8 wt% of Y2O3 to 90 wt % ZrO2 Powder and mixed by wet method, then dried and firing mixture to 1500C to obtain PSZ ceramic powder. Glass-Ceramic (Li2SiO3) and (LiAlO2) prepared by dissolve lithium carbonate and lithium hydroxide with Nano-Silica (SiO2) and Nano-Alumina (Al2O3) respectively. Those glass-ceramic mixed with PSZ in different percentage (2.5,5,7.5,10) and sprayed on furnaces bricks for petroleum refineries. An increase in the chemical resistance of the acid on the surface of the Refractory bricks was observed when coating with the glass-ceramic mixture, as well as increasing the hardness and thermal shock resistance. Lithium silicate coated specimens are more spared and homogeneous on the surface compared to lithium laminate coated.

Listing 1 - 10 of 13 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (13)


Language

English (12)

Arabic and English (1)


Year
From To Submit

2018 (1)

2017 (2)

2016 (2)

2014 (4)

2013 (1)

More...