Article
Pyrolysis of High-density Polyethylene for the Production of Fuel-like Liquid Hydrocarbon

Authors: Sawsan D. A. Shubar --- Ammar S. Abbas عمار صالح عباس
Journal: Iraqi Journal of Chemical and Petroleum Engineering المجلة العراقية للهندسة الكيمياوية وهندسة النفط ISSN: 19974884/E26180707 Year: 2008 Volume: 9 Issue: 1 Pages: 23-29
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Pyrolysis of high density polyethylene (HDPE) was carried out in a 750 cm3 stainless steel autoclave reactor, with temperature ranging from 470 to 495° C and reaction times up to 90 minute. The influence of the operating conditions on the component yields was studied. It was found that the optimum cracking condition for HDPE that maximized the oil yield to 70 wt. % was 480°C and 20 minutes. The results show that for higher cracking temperature, and longer reaction times there was higher production of gas and coke. Furthermore, higher temperature increases the aromatics and produce lighter oil with lower viscosity.


Article
Studing The Mechanical Properties Of Ternary Blends Of Hdpe/Pp/Abs

Authors: Zanaib.Y.Shnea --- Nabeela A. Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2008 Volume: 26 Issue: 7 Pages: 885-893
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work a type of polymer blend has been prepared from mixing differentpercent (40,50,60, and 70) % of High-density polyethylene, polypropylene and adding 6%weight percent of acrylonitril-butadiene-styrene by using single-screw extruder. Theextrusion process concentrated on the homogeneous mixing manner among materialsthrough a regular selection of machine screw revolution per minute and temperature used inextrusion process. Some of mechanical properties such as impact strength, modulus ofelasticity and shore hardness of polymer blend, were determined at different weight fractionof blend. It was found that the addition (6%wt) of ABS to the binary blends HDPE/PP leadsto increase the modulus of elasticity, the impact strength and shore hardness.On the other hand increasing % HDPE content from 40 to 70wt% in HDPE/PPternary blends leads to increase the modulus of elasticity from 166.35 Mpa to 186.25 Mpa,and impact strength increase from o.o52 to o.o6 J/mm2 while decreases the shore hardnessfrom 89 to 69.

في البحث الحالي تم تحضير خلائط بوليمرية جديدة والتي هي عبارة عن مخلوط بوليمري،40,50 ) من البولي اثلين العالي الكثافة مع البولي , يتكون من مزج نسب وزنية مختلفة%( 60,70بروبلين مع إضافة نسبة وزنية%( 6) من اكريلونتريل-بيوتا دين-ستايرين(وذلك باستخدام جهاز الباثقةالمنفرد).تم استخدام عملية البثق في تحضير المواد المتراكبة وذلك بواسطة استخدام ماكنة البثق أحاديةاللولب حيث ركزت على أسلوب الخلط المتجانس بين المواد من خلال تحديد سرعة دوران اللولب الماكنةودرجات الحرارة المستخدمة في عملية البثق. وبعد ذلك جرت دراسة بعض الخصائص الميكانيكية مث لمقاومه الصدم ،معامل المرونة وصلادة شور ولجميع خلائط بوليميرية المحضرة. والنتائج التي تم الحصولعليها أوضحت عند إضافة%( 6) من اكريلونتريل-بيوتا دين-ستايرين الى خلائط ثنائي( البولي اثلين العاليالكثافة –البولي بروبلين) ادى الى زيادة معامل المرونة ,قوه الصدمة وصلادة شور. من ناحية أخرى وجدبأن زيادة اضافة البولي اثيلين عالي الكثافة من( 40 الى 70 )% إلى خلائط ثلاثية (البولي اثيلين عاليالكثافة-البولي بروبلين - اكريلونتريل-بيوتا دين-ستايرين) تحسنت الكثير من الخواص الميكانيكية حيثادى الى زيادة معامل المرونة م ن( 166,35 )إلى ( 186,25 )ميكاباسكال وقوه الصدمة م ن.( 0,053 الى 0,060 )جول/مليملتر 2 . بينما قلت صلادة شور من ( 89 ) إلى (


Article
EFFECT OF ADDITIVE MATERAILS IN MINIMIZING
تأثير المواد المضافة في تقليل الشقوق الانعكاسية

Author: DR. GANDHI GANEM SOFIA HANAA KHALEEL A. AL-BAITI
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2009 Volume: E Issue: first conf./ eng. coll. Pages: 746-760
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Reflection cracks through a road structure is one of the main causes ofpremature pavement deterioration which which shortens the service life of overlays. This phenomenon, which often appears when a layer of asphaltic material isplaced on top of a discontinuous base, can have many different aspects, in accordancewith the large number of factores governing the mechanism of crack initiation andpropagation through a road structure. A number of additives appear to be promising in plying an important role inimproving the properties and performance of paving mixtures. Wheel tracking testing techniques were developed to examine one type with different contents of asphalt modifier additives (High-density polyethylene) overlaysfor situations where reflection cracking may normally developed. The prime objective of this research is to investigate the potential role of HighDensityPolyethyleneasadditivein retardingorminimizingreflectivecracking.Atotalof120 MarshallSpecimensispreparedandtestedbyMarshall,IndirecttensileandCreeptestsatdifferenttemperaturedecrease.Tosimulatetheoverlayperformanceundera rollingtire,18compactedasphaltconcretebeamsamplesaretestedusingwheeltrackingapparatusaftermodification.Itcanbeconcludedthatmodifiedmixeswith9%ofHigh-DensityPolyethylene(bywt.ofasphalt)givesthemaximumresistancetoreflectioncracking.


Article
IMPROVED SOME PROPERTIES OF HIGH DENSITY POLYETHYLENE SYNTHESIS USING FIBER GLASS FOR PIPES AND RESERVOIRS APPLICATIONS
تحسين بعض خصائص البولي أثيلين عالي الكثافة باستخدام الألياف الزجاجية لتطبيقات الأنابيب والخزانات

Loading...
Loading...
Abstract

In this paper, the effect of surface modification of short glass fiber on some properties of high-density polyethylene composite was investigated. The chemical treatment of short glass fiber (SGF) with solvent ethanol was achieved, and composites with weight fraction (0.5, 2.5, 4wt. %) were fabricated. Mechanical behavior tests include (tensile strength, impact, and hardness tests) and structure test (FTIR) were used. Values of mechanical tests for treated short glass fiber – reinforced High density polyethylene composites were much better than the neat high density polyethylene. The tensile strength value of composite from (37 to 41 MPa), impact strength from (83 J/m² to 100 J/m²), and hardness from (64 to 86 N/m²). Result of FTIR test showed physical reaction without the formation of new peaks.

في هذه البحث ، تمت دراسة تأثير معالجة سطح الالياف الزجاج القصيرة على بعض الخواص للمواد المركبة والمقواة بالألياف الزجاج المعالجة. تمت عملية المعالجة الكيميائية لألياف الزجاج القصيرة باستخدام مذيب الايثانول، وتم تصنيع المواد المركبة مع نسب وزنيه (0.5, 2.5, and 4 wt. %) . تم استخدام فحوصات الميكانيكية تشمل (معامل المرونة، الصدمة والصلادة) والفحص التركيبي FTIR)). كانت قيم الفحوصات الميكانيكية لعينات المواد المركبة المقواة بالألياف الزجاجية القصيرة المعالجة اعلى من قيمتها للمادة البولي اثيلين عالي الكثافة. قيم معامل المرونة لعينات المواد المركبة من ( MPa 37 الى MPa 41) , متانة الصدمة من (83 J/m² الى 100 J/m²) , و الصلادة من ( N/m² 64 الى N/m² 86 ) . أظهرت نتيجة فحص FTIR حدوث تفاعل فيزيائي دون ظهور قمم جديدة.


Article
MECHANICAL AND PHYSICAL PROPERTIES OF HIGH DENSITY POLYETHYLENE FILLED WITH CARBON BLACK AND TITANIUM DIOXIDE
الصفات المیكانیكیة و الفیزیاویة لمزیج البولي اثلین العالي الكثافة مع ثاني اوكسید التیتانیوم – اسود الكاربون

Author: Zanaib.Y.Shnean زینب یوسف شنین
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2012 Volume: 5 Issue: 1 Pages: 147-159
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

ABSTRACT:- In this work composite material composed of high density polyethylene and inorganic pigment (carbon black and titanium dioxide) was prepared. Different amounts of carbon black and titanium dioxide (2– 15) wt% were added as filler. The preparation of filled and unfilled (High density polyethylene /Carbon black and titanium dioxide) composite was carried out using a single – screw extruder operated at a temperature of (170 – 190)oC.The incorporation was performed in a single screw extruder and sheets specimens were obtained by hot compression from extruded materials. Many mechanical and physical tests were used to determine the properties of the prepared composite material which involved compression strength, impact strength and modulus of elasticity for all the preparation composite. An untreated HDPE sheet is used for the purpose of comparison. In this study, the influence of addition of Carbon black and titanium dioxide, on the mechanical ,electrical and thermal a properties test of high-density polyethylene (HDPE). The results show that the use of pigments, carbon black and TiO2 in appropriate concentration ratios give a reliable improvement in the mechanical properties. The weight fraction of the carbon blacks and titanium dioxide ranged from 0.0 up to 15 wt % with the high density polyethylene. By discharging a high voltage through the composite it was found that the resistivity of the composite decreased. Carbon black and titanium dioxide –highdensity polyethylene composites show significant differences from the neat high-densitypolyethylene measured in the frequency range. It was found that the carbon black and titanium dioxide/ high-density polyethylenecomposites have better thermal properties than the neat high-density polyethylene.Keyword: high density polyethylene. Titanium dioxide, Carbon black, Electrical properties, Thermal conductivity, Mechanical properties

الخلاصةفي البحث الحالي تم تحضیرالمواد المتراكبة بواسطة مزج البولي اثلین العالي الكثافة مع نسب وزنیة مختلفة من (2– 15)) كحشوة. باستخدام جهاز الباثقة الاحادیة wt% ( الاصباغ لاعضویة(ثنائي اوكسید التیتانیوم-اسود الكاربونفي هدا البحث تم دراسة تاثیر اضافة ثنائي اوكسید التیتانیوم , اسود الكاربون (190 - o 170 ) م - بدرجة حرارة تتراوح بین ( على الخصائص المیكانیكیة لبولي اثلین العالي الكثافة . تم أجراء العدید من الاختبارات المیكانیكیة والفیزیائیة لغرض تحدید خواص المادة المتراكبة المحضرة، حیث تضمنت تلك الاختبارات: مثل مقاومة الانضقاطیة ومقاومة الصدم ومعامل المرونة، ولجمیع المتراكبات المحضرة وقورنت النتائج المستحصلة مع تلك التي تعود لمادة الأساس بمفردة . من النتائج التي تم الحصول علیها تبین ان استخدام الاصباغ لاعضویة (ثنائي اوكسید التیتانیوم،اسود الكربون) أعطى تحسن في الخصائص المیكانیكیة . في هذا البحث تم دراسه خواص التوصیل الحراري والكهربائي لبولي الاثلین العالي الكثافه المدعم باسود الكاربون واوكسید التیتانیوم بنسب مئویه وزنیه تتراوح من ٠ الى ١٥ % .وجد عند امرار فولتیه عالیه خلال النماذج المدعمة حدوث انخفاض واضح في المقاومه النوعیه مقارنه بنماذج البولي الاثلین العالي الكثافه غیر المدعمه باسود الكاربون واوكسید التیتانیوم .. وو جد تحسن في خواص التوصیل الحراري لمتراكبات البولي الاثلین العالي الكثافه المدعم باسود الكاربون واوكسید التیتانیوم مقارنه باالبولي الاثلین العالي الكثافه غیر المدعم .


Article
Injection Temperature Effects on the Properties of High Density Polyethylene Crates
تأثير درجة حرارة الحقن على خواص صناديق التعبئة المصنعة من مادة متعدد الاثلين العال الكثافة

Author: Sawsan D. A. Shubbar سوسن ضياء احمد شبر
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2013 Volume: 19 Issue: 6 Pages: 752-763
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This study was undertaken to provide more insight on the optimum injection temperature used for the production of PE crates, thereby saving time and money, and improving part quality. The work included processing trails of HDPE crates in an injection molding machine at five temperatures ranged from 220 to 300°C. Both Rheological and mechanical characterization was conducted in order to understand the effect of injection temperature on the properties of crates. Oven aging was also applied for (4 weeks) to evaluate the long-term thermal stability. The results revealed that producing the crates at a temperature range of (260-280 °C) gives the best rheological and mechanical result. The lowest drop in thermal stability has been observed for the crates produced at this temperature range.

تم اجراء هذا البحث لغرض توفير معرفة لدرجة حرارة الحقن الامثل المستعملة لانتاج صناديق البولي اثلين، وبالتالي توفير الوقت والمال وتحسين نوعية المنتج.تضمن العمل انتاج الصناديق باستعمال البولي اثلين عالي الكثافة بماكنة قولبة وحقن باستعمال خمس درجات حرارة تتراوح من 220 الى 300 درجة سلليزية .وتم قياس الخواص الميكانيكية وخواص السيولة لغرض فهم ودراسة تاثير درجات حرارة الحقن المختلفة على مواصفات الصناديق المختلفة. بالاضافة الى تعريض الصناديق الى عملية تقادم حراري في فرن ولمدة 4 اسابيع لتحديد الثبوتية الحرارية لها على المدى الطويل. افرزت النتائج ان انتاج الصناديق بالمدى 260- 280 درجة سلليزية تعطي احسن الخواص الميكانيكية وخواص السيولة ، وكذلك فان الصناديق المنتجة في هذا المدى ابدت اقل نسبة تدهور في الثبات الحراري عند فحص التقادم.


Article
Effect of high and low density polyethylene on some mechanical properties of concrete
تأثير البولي ايثيلين ذو الكثافة المرتفعة و المنخفضة على بعض الخواص الميكانيكية للخرسانة

Authors: Nada Mahdi Algalawi ندى مهدي الجيلاوي --- Hadel Ibraheem Ahmad هديل ابراهيم احمد
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2014 Volume: 20 Issue: 8 Pages: 20-33
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The increasing use of plastics in various aspects of modern life resulted in the availability of enormous amount of wastes, including a negative effect on the environment and humans. So it is necessary to find solutions to deal with these wastes and ensure to use them as solutions to use in concrete mix . In this research the production of concrete containing high and low density polyethylene has been used by (5, 10, 15)% as a replacement of part of the volume of sand, so as to obtain concrete good compressive strength as well as other benefits such as improved possibility of pumping concrete and reduce the loss of concrete for workability polymer is a material that is non-absorbable of water . It is also intended to dispose of these wastes positively to achieve benefits to the environment and humans alike .

ان تزايد استخدام اللدائن البلاستيكية في مختلف جوانب الحياة العصرية اسفر عن توفر كم هائل من مخلفاتها وبما يؤثر بشكل سلبي على البيئة و الانسان . لذا كان لابد من ايجاد حلول لمعالجة هذه المخلفات وبما يضمن الاستفادة منها وكأحد هذه الحلول محاولة استخدامها الخلطة الخرسانية . تم في هذا البحث استخدام الفحوصات المختبرية لإنتاج خرسانة حاوية على مثروم البولي ايثيلين ذو الكثافة المرتفعة و المنخفضة وقد استخدم بمقدار (5 ، 10 ، 15) % كنسبة استبدال جزئي من حجم الرمل وذلك للحصول على خرسانة اخف وزناً وذات مقاومة انضغاط جيدة فضلاً عن فوائد اخرى مثل تحسين امكانية ضخ الخرسانة وتقليل سرعة فقدان الخرسانة لقابلية تشغيلها كون ان هذا البوليمر مادة غير قابلة لامتصاص الماء والاستفادة ايضاً من هذه المخلفات الضارة بشكل ايجابي يحقق فوائد للبيئة و الانسان على حد سواء .


Article
Preparation and Properties of the Chitosan/PVA Blend for Heavy Metals Chelation

Author: Zuhair Jabbar Abdul Ameer
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2016 Volume: 24 Issue: 3 Pages: 531-538
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Current research based on the use of extracted chitosan mixed with Polyvinyl alcohol to manufacture blend that can been used in water purification from heavy metals such as copper, this due to chitosan properties and its ability to chelation these metals because of the presence of the functional groups in their structure. The blend has been treated with borax to increase the viscosity, and then high density polyethylene granulated coated with polymer solution to increase the surface area for chelation. The ultraviolet test showed the efficiency of blend to chelation of copper ions through lower the copper ions absorbance peak after each stage where the solution of copper ions pass on the polymer blend containing chitosan.

يستند البحث الحالي على مزج مستخلص الجتوسان مع البولي فينيل الكحول لتصنيع مزيج بوليمري يمكن استخدامه في عمليات تنقية المياه من المعادن الثقيلة مثل النحاس, وذلك لخواص الجتوسان وقابليته على اقتناص هذه المعادن بسبب وجود مجاميع فاعلة في تركيبه. المزيج البوليمري عولج بواسطة البوراكس لزيادة لزوجته, ولزيادة مساحة الاقتناص السطحية تم طلاء حبيبات من البولي اثلين العالي الكثافة بمحلول المزيج البوليمري. اختبار الاشعة الفوق البنفسجية اثبت كفاءة الجتوسان على اقتناص ايونات النحاس من خلال انخفاض بيك الامتصاصية لايونات النحاس بعد كل مرحلة يمرر فيها محلول ايونات النحاس على المزيج البوليمري المحتوي على الجتوسان.


Article
The Energy of Break or Deformation in Some Semi- Crystalline Polymers
طاقة الكسر أو التلف لبعض البولیمرات شبھ – بلوریة

Author: Widad H. Jassim وداد حمدي جاسم
Journal: Ibn Al-Haitham Journal For Pure And Applied Science مجلة ابن الهيثم للعلوم الصرفة والتطبيقية ISSN: 16094042 Year: 2015 Volume: 28 Issue: 1 Pages: 24-32
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The aim of the current study is the investigation of tensile behavior of the semi -crystalline polymers : polypropylene (PP ) , high density polyethylene(HDPE) and lowdensity polyethylene (LDPE) .The energy to break or deformation was determined as a function of extension rates ,( PP) was break at extension rate (5) mm/min but (HDPE) break at higher extension rates(25) mm/min while( LDPE) not break even at very high extension rates but it is deformationor failure

ان الهدف من الدراسة الحالية , هو البحث في طبيعة العلاقة ( القوة – الاستطالة ) للبوليمرات شبه-بلورية مثل البولي بروبلين(pp) ،البولي أثيلين عالي الكثافة و البولي أثيلين واطى الكثافة. وأنجزت فحوصات الشد لقياس طاقة الكسر أو فشل الأنموذج دالة لمعدل السحب ،ينكسر البولي بروبلين بمعدل سحب 5)mm/min) ولكن البولي أثيلين عالي الكثافة ينكسر عند معدلات عالية جدا للسحب 25)mm/min) ، بينما لا ينكسر البولي أثيلين واطى الكثافة حتى عند المعدلات العالية جدا للسحب ولكنه يتلف .

Listing 1 - 9 of 9
Sort by
Narrow your search

Resource type

article (9)


Language

English (7)

Arabic (1)


Year
From To Submit

2018 (1)

2016 (1)

2015 (1)

2014 (1)

2013 (1)

More...