LABORATORY EVALUATION OF MOISTURE DAMAGE AND DURABILITY OF HOT MIX ASPHALT (HMA)
تقييم مختبري لأضرار الرطوبة و الديمومة للخلطة الاسفلتية (HMA)

Authors: Doaa M. Azeez --- Yasir M. AL-Badran --- Namir G. Ahmed
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2017 Volume: 21 Issue: 2 Pages: 149-162
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The increasing of road material demand particularly on mineral filler and additives has been followed-up by finding the new alternative materials. Local materials such as Portland cement, and lime may potentially use to substitute current need. Therefore, it is essential to study the performance and durability of these materials in HMA mixture. To find the durability index, the specimens are immersed around 0 (unconditioned) to 14 days at 60ºC and tested by using Marshall and ITS tests. Based on Marshall test, the index values for mixes variations; DCF, DPC, DL, DPF, and DC are found to be; 42.965%, 36.59%, 36.582%, 35.68%, and 33.42% respectively.

أن زيادة الطلب على مواد انشاء الطرق و بصورة خاصة لانواع المادة المالئة المستخدمة في الخلطة الاسفلتية و كذلك المضافات دفع لأيجاد مواد بديلة. ان المواد المتوفرة محليا كالأسمنت البورتلاندي و الجبس يمكن ان تكون بديلا للحاجة الحالية. لذلك، فمن الضروري دراسة أداء وديمومة هذه المواد في الخلطة الاسفلتية. للحصول على مؤشر قوة التحمل، العينات تم غمرها لمدة 0 (غير معرض للغمر) الى مدة 14 يوما في درجة حرارة 60ºC و فحصها باستخدام طريقة مارشال. قيم المؤشر للخلطات المختلفة التي تم استخدامها هي DCF, DPC, DL, DPF, DC هي 42.965%, 36.59%, 36.582%, 35.68%, and 33.42% تباعا.

Keywords

Durability --- Cement --- Lime --- performance.


Article
Hardness Removal from Drinking Water

Authors: Ahmed A. M. Ali --- Nawar O. A. Nasser
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2006 Volume: 12 Issue: 2 Pages: 405-413
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This study included three trials that were made during December 2003 by using lime, of 98% w/w calcium hydroxide to find the relation between lime doses to be added and the hardness removed .The trials were performed by adding various doses of lime and measuring the hardness, electrical conductivity and pH in water produce by three plants, Nissan in the north of Baghdad, Al-Karama and Al-Wathba water treatment plant in Baghdad center. The objective of this study is to find the optimum lime dose that gives the minimum hardness content.The results indicate a non linear relation between lime dose added and the hardness removed . The results represented a 36% removal in hardness when using an optimum dose of lime 200 ppm in Nissan water treatment plant, while a percentage removal of 34% was obtained in both Al-Karama and Wathba water treatment plants with 300 ppm dose of lime.The low percentage removal indicates the presence of non-carbonate hardness which could not be removed by lime alone.

تضمنت هذه الدر اسه ثلاث محاولات أجريت خلال كانون الأول 2003باستخدام هيدروكسيد الكالسيوم 98% نسبه وزنيه لإيجاد العلاقة بين جرعة هيدروكسيد الكالسيوم وإزالة العسرة ,المحاولات تمت بإضافة جرع مختلفة من هيدروكسيد الكالسيوم وقياس العسرة والتوصيل الكهربائي وقوة أيون الهيدروجين للماء المسحوب من ثلاث محطات لتصفية ماء الشرب وهي مشروع نيسان شمال مدينة بغداد ,مشروع الكرامة ومشروع الوثبة مركز مدينة بغداد ,الهدف من هذه الدر اسه هو إيجاد الجرعة القصوى من هيدروكسيد الكالسيوم التي تعطي اقل تركيز للعسره. النتائج أظهرت أن هناك علاقة لا خطيه بين جرع هيدروكسيد الكالسيوم المضافة والعسره المزالة ,النتائج تمثلت بإزالة 36% من العسره عند إضافة أقصى جرعه من هيدروكسيد الكالسيوم 200 ملغملتر في مشروع نيسان بينما نسبة أزاله 34% تم الحصول عليها في مشروعي الكرامة والوثبة لجرع 300 ملغملتر النسبة القليلة للازاله أشارت إلى وجود عسره لا كاربونيه والتي لا يمكن أزالتها باستخدام هيدروكسيد الكالسيوم لوحده


Article
Lime Stabilization of Expansive
تحسين التربة الانتفاخية بالنورة

Author: Ishraq Khudhair Abass اشراق خضير عباس
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2013 Volume: 17 Issue: 1 Pages: 219-232
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Expansive soils occurring in arid and semi-arid climate region of the world cause serious problems on civil engineering structures. To avoid such damages prior to construction, expansive clays may be stabilized. Soil stabilization using chemical additives is the oldest and most widespread method of ground improvement. In this study, hydrated lime was used for stabilization of a laboratory-prepared heavy clays (natural soil +bentonite). The following percentages (0, 3, 6, 9, 12 and 15 %) of lime have been added to the expansive soil. A series of laboratory experiments have been implemented (such as consistency limits, grain size distribution, specific gravity, compaction test, and swelling oedometer tests). The result showed that the addition of lime was effective in improving the swelling behavior of the expansive soil. Lime was therefore found as an excellent choice for stabilization of swelling soils propertie

تحدث الترب الانتفاخية في منطقة المناخ الجاف وشبه الجاف من العالم ويمكن إن تسبب مشاكل خطيرة على هياكل الهندسة المدنية. لتجنب مثل هذه الأضرار يتم تحسين الترب الانتفاخية قبل الشروع بالبناء. إن استخدام المضافات الكيميائية هي الطريقة الأقدم والأكثر انتشارا لتحسين التربة . في هذه الدراسة تم استخدام ألنوره المطفأة لتحسين خواص ترب انتفاخية معده مختبريا وذلك بخلط تربه طبيعيه غير انتفاخيه مع اخرى انتفاخيه (بنتونايت). تم اضافه النسب الاتيه (0,3 ,6 , 9, 12 و 15%) من النوره الى التربه الانتفاخيه. اجريت سلسله من التجارب ألمختبريه مثل (حدود قوام الطين ,التصنيف الحبيبي للتربه , الكثافه النوعيه , فحص الرص وفحوص الانتفاخ باستخدام جهاز الاودوميتر). أظهرت النتائج أن إضافة ألنوره كان فعالا في تحسين السلوك الانتفاخي للتربة. وعليه وجد أن ألنوره اختيار ممتاز لتحقيق الاستقرار في خصائص الترب الانتفاخية.


Article
EXTRACTION OF ALUMINA FROM IRAQI COLORED KAOLIN BY LIME-SINTER PROCESS
استخلاص الألومينا من أطيان الكاوؤلين العراقية الملونة بطريقة التلبيد مع النوره

Loading...
Loading...
Abstract

In this work lime -sinter method was investigated to recover alumina from Iraqi colored kaolinitic claystone. The claystone was intimately mixed with limestone and the mixture was sintered. The annealed sintered material dusts to a fine powder which required no grinding. This material was leached with sodium carbonate solution, and an alumina extract (sodium aluminate solution) was obtained. By bubbling carbon dioxide gas into this extract solution, gibbsite [Al(OH)3] precipitated and on calcinations at 1350 °C ,alumina in the form of alpha (α – Al2O3) of high purity (98%) can be obtained. In the course of this investigation, the effect of sintering temperature and time, concentration of sodium carbonate solution, leaching time and sintered powder to sodium carbonate solution ratio were studied. About 85% of the alumina in the claystone was extracted at the optimum conditions. The alumina obtained in this method assaying 98% Al2O3, 1.45% SiO2, 0.04% Fe2O3, and 0.13% CaO and, 0.15% Na2O.

في هذا العمل جرى البحث لاستخدام عملية التلبيد مع النوره لاستخلاص الألومينا من أطيان الكاوؤلين العراقية الملونة، بمزج الكاوؤلين مع حجر الكلس بشكل جيد وتلبيده في فرن كهربائي وعند تبريد المادة الملبدة تتفتت ذاتياً الى مسحوق ناعم دون الحاجة للجوء لعملية الطحن. ويتم معاملة هذا المسحوق مع محلول من كاربونات الصوديوم لإذابة واستخلاص الالومينا بإمرار غاز ثاني أوكسيد الكاربون خلال محلول الاستخلاص الناتج من الإذابة يترسب هيدروكسيد الالومنيوم [Al(OH)3] والذي بعد حرقه عند درجة حرارة 1350 م° يتحول الى الومينا من نوع الفا (α – Al2O3) في هذا البحث تم دراسة تأثير كل من العوامل (درجة حرارة، زمن التلبيد، تركيز محلول كاربونات الصوديوم، زمن الإذابة ونسبة مسحوق المادة الملبدة الى محلول كاربونات الصوديوم) على نسبة استخلاص الألومينا. وعند الظروف المثلى أمكن استخلاص حوالي 85% من الألومينا الموجودة في الكاؤولين. المواصفات الكيميائية للألومينا المستحصله بهذه الطريقة هي:Al2O3 98%, SiO2 1.45%, Fe2O3 0.04%, CaO 0.13% and Na2O 0.15%

Keywords

Kaolin --- Alumina --- Lime-sinter --- Iraq


Article
MECHANISTIC EVALUATION OF LIME-MODIFIED ASPHALT CONCRETE MIXTURES

Author: Amjad H. Albayati
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2011 Volume: 17 Issue: 6 Pages: 1444-1460
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Frequently, Load associated mode of failure (rutting and fatigue) as well as, occasionally, moisture damage in some sections poorly drained are the main failure types found in some of the newly constructed road within Baghdad as well as other cities in Iraq. The use of hydrated lime in pavement construction could be one of the possible steps taken in the direction of improving pavement performance and meeting the required standards.
In this study, the mechanistic properties of asphalt concrete mixes modified with hydrated lime as a partial replacement of limestone dust mineral filler were evaluated. Seven replacement rates were used; 0, 0.5, 1, 1.5, 2, 2.5 and 3 percent by weight of aggregate. Asphalt concrete mixes were prepared at their optimum asphalt content and then tested to evaluate their engineering properties which include moisture damage, resilient modulus, permanent deformation and fatigue characteristics. These properties have been evaluated using indirect tensile strength, uniaxial repeated loading and repeated flexural beam tests. Mixes modified with hydrated lime were found to have improved fatigue and permanent deformation characteristics, also showed lower moisture susceptibility and high resilient modulus. The use of 2 percent hydrated lime as a partial replacement of mineral filler has added to local knowledge the ability to produce more durable asphalt concrete mixtures with better serviceability.

أظهرت بعض الطرق المبلطة حديثا بالخرسانة الاسفلتية قي بغداد وباقي محافظات القطر تدهورا مبكرا بالاداء نتيجةفشل الكلل والتشوهات الدائمية وفي بعض الاحيان نتيجة الفشل تحت تاثير الدور المخرب للماء. ان استخدام الجير المطفأفي انتاج الخرسانة الاسفلتية ممكن ان تكون واحدة من الخطوات التي يمكن اتخاذها في اتجاه تحسين الخصائص (Ca(OH)2)المتعلقة بالاداء للتبليط الاسفلتي لجعله يطابق متطلبات المواصفة من خلال توفير المقاومة اللازمة لانواع الفشل المذكورة انفا.لقد تم في هذه الدراسة تقييم الخصائص الميكانيكية لخلطات الخرسانة الاسفلتية والتي تحوي على نسب مختلفة من الجير المطفأوهذه النسب هي ( ٢,٥ ، ٢,٠ ،١,٥ ،١,٠ ، ٠,٥ ، ٠,٠ و ٣ % من وزن الركام)، وتمت الاضافة عن طريق الاستبدالالجزئي للمادة المالئة التقليدية ( مطحون حجر الكلس). حيث تم اجراء فحوصات الشد غير المباشر، المرونة الاستردادية،الحمل المحوري المتكرر وكذلك فحص الانحناء المتكرر للنماذج المختبرية والتي اعدت باستخدام النسب المثلى للاسفلت لتقييمالخصائص المتعلقة بضرر الماء ، معامل المرونة الاستردادي، التشوهات الدائمية وكذلك خاصية الكلل.لقد بينت النتائج بان استخدام الجير المطفأ يحسن الى حد كبير خصائص الاداء المتعلقة بضرر الماء وكذلك يحسنمعامل المرونة الاستردادي ومقاومة التشوهات الدائمية والكلل. ان استخدام نسبة ٢% من الجير المطفأ كاستبدال جزئي للمادةالمالئة التقليدية قد أضاف إلى الخبرة المحلية المتوفرة في هذا المجال إمكانية أنتاج خرسانة إسفلتية لاغراض التبليط بديمومةأعلى ومستوى خدمة أفضل.


Article
Studying some of the Geotechnical Properties of Stabilized Iraqi Clayey Soils
دراسة بعض الخواص الجيوتكنيكية لترب طينية عراقية محسنة

Author: Ishraq Khudhair Abass
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 6 Part (A) Engineering Pages: 1117-1130
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In many road construction projects, if weak soils exist, stabilization and improvement of their properties is necessary. The stabilization process aims at increasing the soil strength and reducing its permeability and compressibility. An experimental program was undertaken to study the effect of engineering properties of kaolin clayey soils ((the kaolin was supplied by the General Company of Geological Survey and Mining which originally obtains from Al-Dewiekhla near Aukashat district in the west of Iraq)) when blended with lime (L) and Silica Fume (SF). A series of laboratory experiments have been implemented for varieties of samples: 2.5%, 5.0%, 7.5% and 10.0% for (Lime) and 2.0%, 4.0% and 6.0% for(Silica Fume). These experiments are: consistency limits test, specific gravity test, compaction test, unconfined compression test and California bearing ratio test. For each test, the optimal quantity of Lime (L) and the optimal percentage of Lime Silica Fume (LSF) combination were determined. The results revealed that: the optimal percentage of LSF combination was attained at a (2.5%L+6.0%SF), which served as control in this study. This optimal percentage: decrease the liquid limit, plasticity index, specific gravity and maximum dry density; and raise the optimum moisture content, unconfined compressive strength and California bearing ratio. These results showed also, that the combination of LSF stabilization at (2.5% L+6.0% SF) is better than the optimal one which achieved by Lime alone: 2.5%L for plasticity index, 10.0%L for specific gravity, maximum dry density and optimum moisture content, 5.0%L for unconfined compression stress and 7.5%forCaliforniabearingratio. All of these results indicated that the engineering properties of clayey soils can be enhanced, by blending Lime and Silica Fume together.

في العديد من مشاريع تشييد الطرق،إذا ما وجدت تربة ضعيفة، فأن تثبيت وتحسين خواصها أمر ضروري. أن عملية التحسين تهدف إلى زيادة متانة التربة وتقليل النفاذية الانضغاطية. تم اعتماد برنامج تجريبي لدراسة تأثر الخواص الهندسية لتربة طين الكاؤلين ((زود طين الكاؤلين من قبل الشركة العامة للمسح الجيولوجي والتعدين حيث يجلب بالأصل من منطقه الدويخله بالقرب من عكاشات غرب العراق)) عند امتزاجها مع النورة ومادة أل (Silica Fume) وقد تم تنفيذ سلسلة من التجارب المعملية لعينات من التربة بإضافة النسب التالية من النورة: 2.5٪، 5.0 ٪، 7.5٪ و 10.0٪. ونسب أخرى من مادة أل (Silica Fume): 2.0٪، 4.0٪ و 6.0٪. التجارب هي : حدود قوام الطين، الكثافة النوعية, فحص الرص، فحص مقاومه الانضغاط غير المحصور واختبار نسبة تحمل كاليفورنيا . وتم تحديد الكمية المثلى من ألنورة والنسبة الأمثل للنورة ومادة أل (Silica Fume) معا. أظهرت النتائج ما يلي: تم تحقيق النسبة الأمثل من مزيج ألنورة وومادة أل( (Silica Fume تلك ألنسبه هي :2.5% نوره+6.0% مادة أل (Silica Fume)التي كانت بمثابة نسبه سيطرة في هذه الدراسة. هذه النسبة المثلى: قللت من قيم مؤشر اللدونة، الكثافة النوعية والكثافة الجافة القصوى. بينما أدت إلى زيادة محتوى الرطوبة الأمثل، ومقاومه الانضغاط غير المحصور و نسبة تحمل كاليفورنيا . وأظهرت هذه النتائج أيضاأن لمزيج ألنورة ومادة أل (Silica Fume)تأثير أفضل من أضافه ألنورة بمفردها . النسبة المثالية للنورة هي 2.5% لمؤشر اللدونة و10% للكثافة النوعية وللكثافة الجافة العظمى ومحتوى الرطوبة الأمثل .بينما كانت 5.0٪ لتحسين مقاومه الانضغاط غير المحصور و 7.5% نسبة تحمل كاليفورنيا . أشارت كل من هذه النتائج إلى أمكانيه تحسين الخواص الهندسية للتربة الطينية، عن طريق مزج ألنورة ومادة أل (Silica Fume)معا.

Keywords

Soil --- Soil Stabilization --- Lime --- Silica Fume


Article
MODIDICATION OF LEACHET CHARACTERISTCS IN LANDFILL USING MIXXTURE OF LIME AND SAWDUST WASTE
تعديل خواص عصارة مكب النفايات باستخدام خليط من الجير و نفايات نشارة الخشب

Loading...
Loading...
Abstract

Landfill bioreactor is a modified technique comparing with the conventional landfill processes due to its ability to reduce time for decomposition and enhancing the biogas generation. The basic goal of this paper is to investigate the performance of a three lab-scale bioreactors under anaerobic conditions. Three types of reactors differ in its internal composition were experimented ,bentonite clay was used as a cover material. First reactor was filled with organic solid waste only; second reactor was filled with a mixture of organic solid waste, Lime and sawdust, while the third reactor was filled with mixture of solid waste and lime. Leachate characteristics traced includes pH, EC, TDS, TSS, Heavy metals (Cr, Fe, Mn, Zn, and Mo), Sulfate SO-24 and Phosphate PO-34. Experiments were conducted from October 2014 to march 2015, Results shows a significant variation in removal efficiency for each reactor, heavy metals removal for the first reactor was (Mn 58.6%, Cr 13.4%, Mo 0%, Zn 27.2%, Fe 58.6%),and the second reactor removal efficiency was (Mn 77.2%, Cr 67.5%, Mo 69.19%, Zn 67.9%, Fe 56.7%), while for the third reactor was (Mn 30.1%, Cr 13.8%, Mo 18.48%, Zn 29.8%, Fe 70%). The results show that the solid waste, Lime and sawdust enhanced the removal of heavy metals in the 2nd reactor which gave best removal efficiency for heavy metals. While the lime addition in the 3rd reactor increase the removal efficiency of iron to 70%. It can be conclude that this modified landfill bioreactor enhance leachate characteristics and so enhancing the solid waste stabilization.

المفاعل الحيوي هو أسلوب معدل لعملية الطمر الصحي مقارنة مع عمليات طمر النفايات التقليدية نظرا لقدرته على تقليل الوقت المطلوب لعمليات التحلل وكذلك تعزيز توليد الغاز الحيوي. الهدف الأساسي من هذه الورقة هو للتحقيق في أداء ثلاثة مفاعلات حيوية مختلفة تحت الظروف اللاهوائية، تختلف هذه المفاعلات الحيوية الثلاثة في تكوينها الداخلي و لجميعها فقد تم استخدام طين البنتونيت كمادة غطاء. شغل المفاعل الأول مع النفايات الصلبة العضوية فقط، المفاعل الثاني تم تشغيله مع خليط من النفايات الصلبة العضوية والجير ونشارة الخشب، في حين تم تشغيل المفاعل الثالث مع خليط من النفايات الصلبة والجير. خصائص العصارة التي تم تتبعها شملت درجة الحموضة، التوصيلية الكهربائية، المواد الذائبة الكلية، المواد العالقة الكلية، المعادن الثقيلة (Cr, Fe, Mn, Zn, Mo )، الكبريتات (SO-24 )، و الفوسفات (PO-34). أجريت التجارب للفترة من أكتوبر 2014 إلى مارس 2015، اطهرت النتائج تفاوت كبير في كفاءة الإزالة لكل مفاعل من المفاعلات الثلاث، كانت كفاءة إزالة المعادن الثقيلة للمفاعل الأول (Mn 58.6%, Cr 13.4%, Mo 0%, Zn 27.2%, Fe 58.6%), اما المفاعل الثاني (Mn 77.2%, Cr 67.5%, Mo 69.19%, Zn 67.9%, Fe 56.7%), ، في حين أن كفاءة الازالة في المفاعل الثالث كان (Mn 30.1%, Cr 13.8%, Mo 18.48%, Zn 29.8%, Fe 70%).. أظهرت النتائج أن مزيج النفايات الصلبة، والجير ونشارة الخشب في المفاعل الثاني عززت إزالة المعادن الثقيلة. في حين أن إضافة الجير فقط في المفاعل الثالث ادى الى زيادة كفاءة إزالة الحديد إلى 70٪. يمكن من خلال نتائج البحث التوصل الى استنتاج الى ان التعديلات المقترحة للتركيبة الداخلية للمفاعلات قيد البحث حسنت فعاليتها في تعزيز خصائص العصارة و بالتلي تعزيز تثبيت النفايات الصلبة.

Keywords

Leachate --- Landfill --- Bioreactor --- Lime --- Sawdust --- Anaerobic


Article
The Effects of Lime Addition and Fineness of Grinded Clinker on Properties of Portland Cement

Authors: Nadia S. Ismael --- Mostafa N. Ghanim
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2016 Volume: 23 Issue: 2 Pages: 86-95
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

Two types of Portland Cement Clinker "PCC" were used in this study: high fineness grinded and low fineness grinded , and after grinding of PCC, hydrated lime was used in 5%,10% and 15%; by weight, as a replacement of the blend cement with a constant 3% addition of gypsum by the blend weight. The importance of this study is to show the influences of different fineness on the physical properties of the blended cement, and to find the probability of using hydrated lime (that could be a by-product) in cement and declare its effects on the blend, so the solid waste "lime" and air pollutant of cement factories will reduce. In this research, the low fineness blend exhibited about 87% from compressive strength of high fineness blend at 28 days age. The results show that the using of hydrated lime up to 10%; by weight, as a replacement of cement will give good compressive strength and workability, and will reduce moderately the setting time, but the use of hydrated lime by more than 10% will reduce the compressive strength and increase the unsoundness of the blend (from 3mm expansion at 10% hydrated lime to 29mm expansion at 15% hydrated lime).


Article
Strength, Durability And Hydraulic Properties Of Clayey Soil Stabilized With Lime And Industrial Waste Lime
المقاومة والديمومة والخصائص الهيدروليكية لتربة طينية مثبتة بالنورة ومخلفات النورة

Loading...
Loading...
Abstract

AbstractThis research aims to study the effect of utilization of industrial waste/lime (by-product of sugar factory) on some engineering properties of clayey soil selected from Mosul city. These characteristics are unconfined compressive strength, permeability, soil-water characteristic curve and Durability. The tests were performed at different percentages of lime (2, 4 and 6) % and industrial waste/lime (2, 4, 6 and 8) % by dry weight of soil. Results showed a decrease in the plasticity, swelling pressure and swelling potential of treated soil. The soil became non plastic at optimum lime, waste lime contents of (4, 6) % respectively. Unconfined compressive strength (UCS) increased with increasing of curing time and stabilizer contents and reached a maximum value at optimum stabilizer contents. The (UCS) of soil stabilized with industrial waste lime was more than that stabilized by lime at different curing times. Durability tests (immersion and slaking) showed that the treated soil with lime was more durable than that treated with waste lime. The Permeability of treated soil was found to be more than that of natural soil. On the other hand, the permeability of soil treated with waste lime was more than that of treated by lime at different curing time and it reached a maximum values at (4, 2)% for the soil treated with waste lime and lime respectively. The soil-water characteristic curve showed that the soil ability to hold water increased with increasing lime and industrial waste contents. Keywords: clayey soil, lime, industrial waste lime, strength & durability, hydraulic properties.

يهتم البحث بدراسة مقارنة تأثير إضافة النورة والمخلفات الصلبة/نورة لمعمل السكر والخميرة على الخواص الهندسية لتربة طينية في مدينة الموصل، وقد اضيفتا بنسب (6،4،2)% نورة و (8،6،4،2)% مخلفات النورة وزنا من التربة الجافة.اظهرت النتائج انخفاض في لدونة التربة، نسب وضغط الانتفاخ للتربة المعاملة، حيث اصبحت التربة عديمة اللدونة عند نسب التثبيت المثلى للنورة والمخلفات (6،4)%على التوالي. مقاومة الانضغاط غير المحصور تزداد مع زيادة كل من فترة الانضاج،نسبة النورة والمخلفات بحيث تصل الى اعلى قيمة عند نسب التثبيت المثلى للنورة والمخلفات. لوحظ ان مقاومة الانضغاط غير المحصور للتربة المعاملة بالمخلفات اعلى منها للتربة المعاملة بالنورة عند فترات الانضاج المختلفة. نتائج فحص الديمومية اظهرت انخفاض مقاومة الانضغاط للتربة المعاملة وكانت بمقدار اكبر منه للتربة المعاملة بالمخلفات نتيجة الغمر، كما بين فحص التآكل ان الفقدان بالوزن للتربة المعاملة بالمخلفات اكبربكثير منه للتربة المعاملة بالنورة.من جهة اخرى،وجد ان نفاذية التربة المعاملة اعلى منها للتربة الطبيعية، كما وجد ان نفاذية التربة المعاملة بالمخلفات اعلى منها للتربة المعاملة بالنورة عند فترات الانضاج المختلفة، فقد وصلت الى اعلى قيمة عند النسب (2،4)% للنربة المثبتة بالمخلفات والنورة على التوالي.اخيراً ومن منحنيات خاصية التربة-الماء وجد ان قابلية التربة للاحتفاظ بالرطوبة تزداد مع زيادة النورة والمخلفات، لكن قابلية التربة المعاملة بالمخلفات للاحتفاظ بالرطوبةاقل منها للتربة المعاملة بالنورة.


Article
Removal of Heavy Metals Using Chemicals Precipitation

Authors: Balasim A. AbiD --- Mahmood M. BrbootI --- Najah M. Al-ShuwaikI
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 3 Pages: 595-612
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The single component and multi-component hydroxide precipitation andadsorption were studied for different heavy metals namely Iron (III), Chromium(III), Copper (II), Lead (II), Nickel (II), and Cadmium (II) from aqueous solutions.By using the jar tester Magnesia (MgO) was used as a precipitator at differentdoses and compared with other chemicals like lime (CaO) and caustic soda(NaOH). The treatment involves the addition of either magnesia or lime-watersuspensions (combined with cationic polyelectrolyte, CPE) in various doses, 1.0 –5.0 g/l for the metal samples to study the effect of varying doses on the treatmentefficiency. The results show that the percent removal of metal ions increases toabout 99 % with increasing the MgO dose to some limits. The optimum values ofMgO doses were found to be 1.5-3.0 g/l. The pH value ranges are 9.5 to 10 withMgO precipitant and pH of 11.5 to 12 with CaO precipitant. In the jar experimentthe rotation speed, N, 180-200 rpm, (G of 460-480 s-1) of mixing for two minuteswas the most favorable speed of rapid mixing and the slow mixing speed of 15-30rpm, G of (14-35 s-1), for twenty minutes gave the best results.At the best operatingconditions of the pilot plant, the removal efficiency of metal ions was more than97% at doses of MgO (1.0-4.0 g/l).

Listing 1 - 10 of 50 << page
of 5
>>
Sort by
Narrow your search

Resource type

article (50)


Language

English (38)

Arabic and English (8)

Arabic (3)


Year
From To Submit

2019 (3)

2018 (3)

2017 (4)

2016 (11)

2014 (4)

More...