Article
PRODUCTION OF GEOPOLYMER CONCRETE FROM LOCAL MATERIALS

Authors: Thaer J. Mohammed --- Ikram A. Saeed
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2018 Volume: 9 Issue: 4 Pages: 174-186
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

Geopolymer concrete is still a new construction material in Iraq and needs tremendous research to get more information about the production technique. In this study, the foreign fly ash and local fly ash produced from Baghdad south gas power plant were used with good specifications to obtain geopolymer concrete. Also, the local attapulgite clay as a pozzolan material is used to investigate the possibility for production the geopolymer concrete. The experimental results showed that the method of curing of geopolymer concrete has a significant effect on the development of compressive strength. Water immersion curing is not recommended. The heat treatment method is the best due to accelerating the reactions and formation of geopolymer concrete. The attapulgite is the best suited locally for geopolymerization in terms of compressive strength and tensile strength.


Article
SYNTHESIS OF FELDSPAR SUBSTITUTES VIA UTILIZATION OF LOCAL MATERIALS
تحضير بدائل الفلدسبار باستخدام مواد محلية

Loading...
Loading...
Abstract

Four varieties of sodium feldspar substitutes have been prepared. Different percentages of kaolin, silica and sodium salts are milled, mixed and submitted to heat treatment. The reacted powders are then grinded and tested by x-ray diffraction. The results show the existence of feldspar phase. The densities were measured and show close agreement to the reported values. The final result is establishing a technological root for the synthesis of feldspar substitute utilizing local materials.

تم تحضير اربعة انواع من بدائل الصوديوم فيلدسبار. وقد تم طحن نسب مختلفة من الكاؤولين والسيليكا وأملاح الصوديوم ثم الخلط والتعريض للمعالجة الحرارية. وتم طحن المساحيق المتفاعلة وفحصها بحيود الأشعة السينية. وقسيت الكثافات الناتجة ووجد انها قريبة جدا من القيم الموثقة. وتم الوصول الى نتيجة نهائية باستحداث مسلك تكنولوجي لصناعة بدائل الفيلدسبار باستثمار المواد المحلية.


Article
STUDY THE EFFECT OF USING LOCAL MATERIALS AS REFRACTORY BONDING MORTAR IN IRAQI
دراسة تأثير استخدام المواد المحلية كمونة رابطة حرارية

Authors: Katreen E. Al Hwaidy كاترين عيسى عزيز --- Shatha S. Hassan شذى صادق حسن --- Osama A. Eedan اسامة عبد الامير عيدان
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2018 Volume: 9 Issue: 1 Pages: 143-157
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

In this research, Iraqi bauxite was used as raw material, after preparation the producing a grog. The mix proportion was applied, (96:4), (93:7) and (90:10) as (bauxite grog: kaolin binding ), and the sodium silicate solution as adhesive material 5% by weight of the mix.The burning temperatures for specimens' producing were 1450ᵒC. The physical investigation was carried such as (bulk density, specific gravity, apparent of porosity and water absorption). While the mechanical tests (compressive, bonding) strength, durability investigations such as (thermal shrinkage, reheating expansion and thermal shock). It was found the third group recorded the highest compression and bonding strength and thermal shock resistance and the best physical properties after burning at 1450 ºC, with mix proportion (90: 10).

في هذا البحث تم استخدام اطيان البوكسايت العراقي كمادة اولية بعد تحضيرها لانتاج الركام الحراري (كروك). تم ) ( ركام البوكسايت الحراري: المادة الرابطة الكاؤولين) وكذلك محلول 10 :90) و (7 :93( ,)4 :96تطبيق ثلاث نسب ( )1450% من وزن العينة لكل خلطة . كانت درجة حرارة حرق العينات تصل الى (5سليكات الصوديوم كمادة لاصقة بنسبة درجة مئوية . تم اجراءالتحريات الفيزيائية مثل ( الكثافة الظاهرية , الوزن النوعي, المسامية الظاهرية, و امتصاص الماء) . بينما الفحوصات الميكانيكية التي اجريت على العينات هي ( مقاومة الانضغاط , مقاومة الربط) وكذلك فحوصات الديمومة مثل ) اعلى مقاومة 10:90 (الانكماش الحراري, التمدد بعد اعادة الحرق والصدمة الحرارية ) حيث سجلت الخلطة الثالثة ( م.º 1450للانضغاط والربط والصدمة الحرارية وافضل خواص فيزيائية بعد الحرق بدرجة.