Experimental Investigation to Improve Metal Removal Rate (MRR) and Surface Roughness in Electrochemical Machining
تحقیق تجریبي لتحسین معدل إزالة المعدن (MRR) والخشونة السطحیة في التشغیل الكھروكیمیائي

Authors: Saad Kariem Shather --- Baqer Ayad Ahmed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 11 Pages: 1948-1959
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Electrochemical machining (ECM) is a non-traditional machining processwhich is the controlled removal of metal by anodic dissolution in an electrolyticcell in which the workpiece is the anode and the tool is cathode. In ECM, metalremoval rate (MRR) takes place due to atomic dissolution of work material.Electrochemical dissolution is governed by Faraday’s laws.I n this study the ECMis used to remove metal from the internal hole of the workpiece from aluminumalloy using NaCl solution. The rates of improvement in MRR are (6.48, 1.81, 3.74,13.24, 3.11) % for current densities of (2.82, 4.24, 5.65, 7.07, 8.48) A/cm2respectively, when compared with the stationary tool, and the rotating electrodegives better surface finish than the stationary electrode, were the enhancement ratesin roughness are (7, 31.72, 7.91, 15.49, 1.34)% for current density values of (2.82,4.24, 5.65, 7.07, 8.48) A/cm2 respectively.

والدي من (ECM) التشغيل الكهروكيميائي يطلق على نوع من أنواع التشغيل اللاتقليديخلاله تتم إزالة معدن مسيطر عليها بواسطة التحلل الانودي في خلية الكتروليتية حيث إن القطعةالمشغلة هي الانود والعدة هي الكاثود وفي التشغيل الكهروكيميائي تتم أزالة المعدن بطريقةفي إزالة المعدن (ECM) الأدابةوحسب قوانين فراداي . في هذا البحث استخدمت طريقةAl Zn Mg Cu1.5-DIN ) لتوسيع الثقب الموجود في القطعة المشغلة من سبيكة الألمنيومإن نسب التحسين في معدل إزالة المعدن .(NaCl) 1725-1 ) باستخدام المحلول الالكتروليتيهي ( 3.11، 3.74،13.24، 1.81، 6.48 )% لقيم كثافة التيار ( 4.24،5.65، 2.82 (MRR)8.48 ،7.07 ) أمبير/سم 2 بالتتابع. وعند مقارنة العدة الدوارة مع العدة الثابتة أعطت نتائج ،أفضل بالنسبة لخشونة السطح . حيث ان نسب التحسن بالخشونة هي ( 7.91،15.49، 31.72 ،71.34 )% لقیم كثافة التیار ( 8.48 ،7.07، 4.24،5.65، 2.82 ) أمبیر/سم 2 بالتتابع.


Article
ENHANCEMENT OF METAL REMOVAL RATE (MRR) AND SURFACE FINISH IN ELECTROCHEMICAL MACHINING
تحسين معدل إزالة المعدن (MRR) والإنهاء السطحي في التشغيل الكهروكيميائي

Loading...
Loading...
Abstract

Electro chemical machining (ECM) is a non traditional process that can machine difficult to cut material. This paper was focused on methods which are used to enhance metal removal rate (MRR) and surface finish during experimental investigations, were the work materials are two aluminum alloy ( AL Zn Mg Cu 1.5-DIN 1725-1) and aluminum 1100 with using brass and steel ck35 tools, also NaCl solution as electrolyte was used. Experiments prove that increasing electrolyte flow rate from 6-14 l/min at electrolyte concentration 200g/l lead to increase metal removal rate reach to (63.07%) and enhancement of surface finish by reducing roughness from (5.07 to 3.25 µm ) minimum and from (6.63 to 1.2 µm) maximum using work material from aluminum alloys to perform that . Also there are another factors influencing in metal removal rate and surface finish such as voltage and frequency when increasing them from (10-30)V lead to increase MRR about (29.45%) and frequency from (100-500)HZ improved MRR by (34.17%)

التشغيل الكهروكيميائي هو أحد العمليات الغير تقليدية والتي تستخدم في قطع المواد الصعبة. ركز البحث على الطرق المستخدمة لتحسين وزيادة المعدن المزال وتحسين الانهاء السطحي من خلال التجارب المتحققة حيث ان القطع المشغلة هي سبيكتين من الالمنيوم أحداهما سبيكة ( AL Zn Mg Cu 1.5-DIN 1725-1) والاخرى سبيكة الالمنيوم 1100 مع استخدام عدتين من البراص والاخرى من الفولاذ CK35 والمحلول المائي NaCl كألكتروليت. وقد اثبتت التجارب ان زيادة تدفق المحلول الألكتروليتي يؤدي الى زيادة المعدن المزال ليصل الى نسبة (63,07%) عند (6-14) لتر/دقيقة وتركيز يبلغ 200 غرام/لتر مع تحسين خشونة السطح من خلال تقليل الخشونة من (5,07-3,25) مايكرون كحد ادنى وكذلك من (6,63-1,2) مايكرون كحد أعلى باستخدام عينات من سبائك الالمنيوم لأتمام ذلك. كما ان هناك عوامل اخرى مؤثرة في زيادة المعدن المزال وتحسين الانهاء السطحي مثل الفولتية والتردد حيث ان زيادتها يؤدي الى زيادة المعدن المزال وتحسين السطح من( 10-30) فولت تؤدي الى الزيادة (29,45%) والتردد من (100-500) هرتز مع تحسين في المعدن المزال بنسبة (34,17%).

Listing 1 - 2 of 2
Sort by
Narrow your search

Resource type

article (2)


Language

English (2)


Year
From To Submit

2013 (1)

2012 (1)