Polyaniline (PANI ) was used as a basic material in this research where nano-films of Polyaniline were deposited on n-type silicon wafers. The thickness of the PANI films was controlled by the spin coating process. Different thickness of PANI( 225,107, 90, 74 and 61)nm were obtained by using different spin speed(1000, 2000, 3000, 4000 and 5000) rpm, respectively. The current density-voltage(J-V) characteristics were achieved in both light (100 mw/cm2) and dark conditions. The parameters of the photovoltaic samples, that is, open circuit voltage (Voc) ,short–circuit current density (Jsc) ,fill factor (FF),and energy conversion efficiency (ɳ) were calculated. sWe found that the best thickness of PANI film is 107 nm to get best energy conversion efficiency, short–circuit current density and maximum power point .

استخدم البولي انيلين كمادة أساسية في هذا البحث حيث تم ترسيب أغشية نانوية من الانيلين على شرائح من السليكون نوع n. تم الحصول على سمك مختلف من أغشية البولي انيلين وهي(225و107 و90و74و61) nm من خلال استخدام سرع مختلفة من البرم وهي(1000 و2000 و3000 و4000 و5000 )rpm على الترتيب .تم الحصول على منحنيات كثافة التيار– الفولتية (J-V) بظرف الضوء 100 mw/cm2)) والظلام .تم حساب معلمات خرج الخلية الشمسية وهي فولتية الدائرة المفتوحة (Voc) وكثافة تيار دائرة القصر (Jsc) وعامل الملئ(F.F) وكفاءة التحويل (ɳ). وجدنا ان استخدام البولي انيلين ذو سمكnm 107 يؤدي إلى الحصول على أفضل النتائج من حيث كفاءة التحويل و كثافة تيار دائرة القصر والقدرة العظمى الخارجة

polyaniline --- nano – films --- current density --- بولي انيلين ، اغشية نانوية --- كثافة التيار

The research includes the study of the effect of some preparing factors (time of deposition and temperature) on structural, topographic and optical properties of zinc sulfide (ZnS) nanoscale film. Nanofilms prepared by using a chemical bath deposition .The compositional properties included: pictures of X-ray diffraction (XRD), also included the topographic characteristics: pictures of the optical microscope (ORM) and pictures of the atomic force microscope (AFM), while the included optical properties: transmittance, absorption coefficient, the optical energy gap. The results of X-ray examinations (X-ray) to prepare films by (CBD) method have amorphous structure. It has been observed that increasing the time of deposition led to decrease values of the forbidden energy gap, while it was observed that the increase in temperature led to a increase in the values of the forbidden energy gap .

تضمن البحث دراسة تأثير بعض عوامل التحضير (زمن الترسيب ودرجة الحرارة) على الخصائص التركيبية والطبوغرافية والبصرية لغشاء كبريتيد الخارصين (ZnS) النانوي. الأغشية النانوية حضرت بأستخدام طريقة ترسيب الحمام الكيميائي. وقد تضمنت دراسة الخواص التركيبية: صوراً لحيود الأشعة السينية (XRD)، كما تضمنت الخواص الطبوغرافية: صوراً للمجهر الضوئي(ORM) وصوراً لمجهر القوة الذرية (AFM)، فيما تضمنت الخواص البصرية: النفاذية، معامل الأمتصاص، فجوة الطاقة البصرية. بينت نتائج فحوصات الأشعة السينية (X-ray) أن الأغشية المحضرة بطريقة (CBD) ذات تركيب عشوائي (Amorphous). وقد لوحظ أن زيادة زمن الترسيب أدى الى تقليل قيم فجوة الطاقة الممنوعة، بينما لوحظ أن زيادة درجة الحرارة أدى الى زيادة قيم فجوة الطاقة الممنوعة.

chemical bath deposition --- ZnS --- Nano films --- Deposition Time --- Temperature. --- الترسيب بالحمام الكيميائي،ZnS ، أغشية نانوية، زمن الترسيب، درجة الحرارة.