Article
FABRICATION OF MO NANORODS ON SILICON WAFER USING GLANCING ANGLE DEPOSITION TECHNIQUE
تصنيع قضبان المولبدينيوم النانوية على رقائق السليكون باستخدام تقنية الترسيب الزاوي الخاطف.

Authors: Dr.Mohammed D. Salman --- Dr. Mushtaq I. Hasan --- L.Haider J. Abid
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2013 Volume: 6 Issue: 2 Pages: 139-147
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

Array of silicon nanorods with a circular cross section onto Mo nanopillars arrangement were grown using glancing angle deposition (GLAD) on Si (100).Deposition technique was used to fabricate Mo thin film on silicon flat surface. Teflon deposited on the tips of Mo nanorods at normal incident evaporation (θdep.is 0oC) with deposition time of (5 min.) to study the hydrophoposity and hydroplilicity of the surface. Morphology of Mo and Mo/Teflon nanocomposite was carried out using scanning electron microscope (SEM) which indicates a (100 nm) of mo thin film and Mo nanorods on silicon substrate. Contact angle measurement on nanocomposite Mo nanorods with Teflon grown on their tips exhibited contact angle values as high as (116o) indicating an increase in the hydrophopocity of original hydrophilic Mo nanostructures that had an angle of (40o).

تم تحضير مجموعة من اسطح السليكون بالمستوى النانوي من خلال ترسيب شريحة دائرية من اعمدة المولبدينيوم النانوية على تلك الاسطح باستخدام تقنية (GLAD). استخدمت تقنية الترسيب الاعتيادي لصنع طبقة رقيقة من الموليبيديوم على اسطح السيليكون المسطحة. رسب التفلون على اطراف اعمدة الموليبيديوم النانوية والتي سقطت بزاوية تبخر اعتيادية مساوية للدرجة صفر وبزمن (5) دقائق. لدراسة اسطح السليكون الكارهة والمحبة للماء. مورفولوجية اسطح الموليبيديوم و الموليبيديوم/تيفلون تمت دراستها باستخدام المجهر الالكتروني الماسح والذي اشار إلى وجود (100) نانومتر كطبقة رقيقة من المولبدينيوم و كذلك اعمدة المولبدينيوم النانوية على اسطح السيليكون. قياس زاوية الاتصال بين قطرة الماء و اعمدة المولبدينيوم النانوية المغطية بطبقة التفلون على نهاياتها اظهرت زاوية عالية تصل الى (116) درجة مظهرة اسطح نانوية كارهة للماء مقارنة مع الاسطح النانوية بدون التيفلون المحبة للماء بزاوية (40) درجة.

Keywords

nanorods --- molybdenum --- Teflon --- GLAD


Article
Low-Temperature Aqueous Chemical Growth of Inorganic-Organic Hybrid Junction with ZnO Nanorods/Polyfluorene Structure

Authors: W. Wei --- B. Jiming --- S. Yinglan --- C. Chuanhui --- et al.
Journal: Iraqi Journal of Applied Physics المجلة العراقية للفيزياء التطبيقية ISSN: 18132065 23091673 Year: 2013 Volume: 9 Issue: 1 Pages: 29-32
Publisher: iraqi society for alternative and renewable energy sources and techniques الجمعية العراقية لمصادر وتقنيات الطاقة البديلة والمستجدة

Loading...
Loading...
Abstract

In this paper, we report the inorganic-organic hybrid junction synthesized on ITO glass substrate, which was consisted of an n-type ZnO nanorods (NRs) grown by low-temperature aqueous chemical growth method and a p-type Polyfluorene (PF) organic film fabricated by spin-coating. The results indicate that densely and uniformly distributed ZnO nanorods were successfully grown on the PF layer. The thickness of the PF layer plays a dominant role for the current–voltage (I-V) characteristic of the ZnO NRs/PF inorganic-organic hybrid junction device, and a p-n junction with obviously rectifying behavior was achieved with optimal PF layer thickness. The photoluminescence (PL) spectrum covering the broad visible range was obtained from the n-ZnO nanorods/p-polyfluorene (PF) structure, which was originated from the combination of the PF-related blue emission and the ZnO-related deep level emission.


Article
Growth and Characterization of CdTe Nanorods Flower-like shape
تنمية و تشخيص القضبان النانومترية للكادميوم تيلوريد بشكل زهرة

Authors: Fatima A. Hassan فاطمة عامر حسن --- Asama N. Naje اسامة ناطق ناجي --- Rawa K. Ibrahim روى خليل أبراهيم
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2016 Volume: 57 Issue: 2B Pages: 1198-1202
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

CdTe nanorods were prepared by using aqueous chemical synthesis. The influences of reaction time (1-3 hours) on the optical and structural properties were studied. The UV-visible absorption spectrum reflects a wide absorption range in the visible spectrum. The energy gap calculations show decrease in the energy gap with increasing reaction time. The SEM images show that the CdTe appears as flower of nanorods-like.

تم تحضير قضبان الكادميوم تيلوريد النانومترية باستخدام التقنية الكيميائية المائية. تمت دراسة تأثير زمن التفاعل (1-3 ساعات) على الخصائص البصرية و التركيبية. طيف الامتصاص الفوق بنفسجي-المرئي عكس امتصاص واسع ضمن مدى الطيف المرئي. حسابات فجوة الطاقة اظهرت نقصان في فجوة الطاقة بزيادة زمن التفاعل. صور المجهر الألكتروني الماسح اظهرت ان شكل الكادميوم تيلوريد هو زهرة من القضبان النانومترية.


Article
Preparation and Characterization of Yttrium Oxide Nanoparticles at Different Calcination Temperatures from Yttrium Hydroxide Prepared by Hydrothermal and Hydrothermal microwave Methods
تحضيروتشخيص دقائق اوكسيد الاتريوم النانوية في درجات حرارة تلدين مختلفه من هيدروكسيد الاتريوم المحضر بطريقتي الهيدروحرارية والهيدروحراريه ـ الموجات الدقيقة

Authors: Ahlam J. Abdulghani احلام جميل عبد الغني --- Waleed M. Al- Ogedy وليد مظلوم العكيدي
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2015 Volume: 56 Issue: 2C Pages: 1572-1587
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The Synthesis of yttrium oxide nanoparticles have been achieved via calcination of yttrium hydroxide produced from the reaction of aqueous solutions of yttrium nitrate and sodium hydroxide at pH = 13 using hydrothermal and hydrothermal microwave methods. Effect of heat treatment of the resulted yttrium hydroxide powder on the morphology and crystallinity of the resulting oxide was studied at calcination 500, 700 and 1000°C to obtain. The resulted products were characterized by means of X-ray diffraction (XRD), scanning electron microscope (SEM), atomic force microscope (AFM), Fourier transform infrared spectrometer (FTIR) and thermal analyses (TG).

تم تحضير دقائق اوكسيد الاتريوم النانوية من تسخين هيدروكسيد الاتريوم المحضر من نترات الاتريوم مع هيدروكسيد الصوديوم في الدالة الحامضية 13 باستخدام طريقتي الهيدروحراري الاعتيادي والهيدروحراري باستخدام اشعة الموجات الدقيقة .تمت دراسة تاثير المعاملة الحرارية للهيدروكسيد الناتج على الهيئة البلورية واشكال مسحوق الاوكسيد النانوي الناتج في درجات التلدين 500و700و1000◦ م. شخصت النواتج باعتماد تحاليل حيود الاشعة السينية والمجهر الالكتروني الماسح ومجهر القوة الذرية ومطيافية الاشعة تحت الحمراء والتحاليل الحرارية


Article
Preparation of TiO2 nanorods by Sol–Gel template method and measured its photo- catalytic activity for degradation of methyl orange
تحضير قضبان نانوية من ثاني اوكسيد التيتانيوم بطريقة السول-جل وحساب فعالية التحفيز الضوئي لها من خلال تحلل المثيل البرتقالي

Authors: Ban M.Al-Shabander بان مازن مزاحم --- Zainab R.Musleem زينب رحيم مسلم --- Ekram A. Ajaj اكرام عطا عجاج
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2015 Volume: 13 Issue: 26 Pages: 171-177
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Titanium dioxide nanorods have been prepared by sol-gel template method. The structural and surface morphology of the TiO2 nanorods was investigated by X-ray diffraction (XRD) and atomic force microscopy (AFM), it was found that the nanorods produced were anatase TiO2 phase. The photocatalytic activity of the TiO2 nanorods was evaluated by the photo degradation of methyl orange (MO). The relatively higher degradation efficiency for MO (D%=78.2) was obtained after 6h of exposed to UV irradiation.

تم تحضير ثاني اوكسيد التيتانيوم قضبان نانوية بطريقة السول-جل. درس التركيب البلوري و طبيعة السطح لاوكسيد التيتانيوم نوع قضبان نانوية باستخدام حيود الاشعة السينية ومطياف القوة الذرية. لقد وجد ان ثاني اوكسيد التيتانيوم من نوع قضبان نانوية هو من طور الانتاس. كما تمت دراسة التحفيز الضوئي لثاني اوكسيد التيتانيوم من خلال التحلل الضوئي لصبغة المثيل البرتقالي، ان مقدار التحلل العالي لصبغة المثيل البرتقالي 78.2% حدث بعد مرور6 ساعات من التعرض للاشعة فوق البنفسجية.


Article
Production of TiO2 Nanoparticles in Different Phases and Shapes by using PLA and Hydrothermal Method

Authors: Abbas K. Jarallah --- Raad S. Sabry --- Wisam J. Aziz
Journal: Al-Mustansiriyah Journal of Science مجلة علوم المستنصرية ISSN: 1814635X Year: 2018 Volume: 29 Issue: 2 Pages: 175-178
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Titanium dioxide was prepared using pulsed laser ablation (PLA) and hydrothermal method. Scanning electron microscopy images showed that the product from hydrothermal method had a nanotube shape, whereas those from PLA in liquid were nanoparticles. The optical properties in the absorption curve of product from the hydrothermal method were slightly greater than those from the PLA method, and the energy gaps were 3.39 and 3.26 eV for the hydrothermal method and PLA, respectively. XRD results showed that the TiO2 prepared through PLA showed one phase (rutile), whereas those prepared through hydrothermal method showed two phases (anatase and rutile). Moreover, the product from hydrothermal method had smaller particle size smaller than that from PLA. Furthermore, the product yield and the required reaction time of the hydrothermal method were higher than those of PLA.

في هذا البحث تم تحضير مادة اوكسيد التيتانيوم بطريقة القشط بالليزر النبظي وطريقة الهايدروثيرمال. اظهرت صور المجهر الالكتروني الماسح بان التشكيل المتكون على السطح بطريقة الهايدروثيرمال هي اشكال انابيب دقيقه ولكن الاشكال الظاهرة بطريقة القشط بالليزر هي اشكال كرويه.الخصائص البصريه اظهرت من خلال منحني الامتصاص بان الامتصاصيه بطريقة الهايدروثيرمال هي اكبر بقليل من الامتصاص الناتج بطريقة القشط بالليزر وان فجوة الطاقه كانت (3.26 eV -3.39 eV ) للنماذج المحضره بطريقة الهايدروثيرمال والليزر على التوالي. نتائج حيود الاشعه السينيه اظهرت بان ثنائي اوكسيد التيتانيوم الناتج بطريقة الليزر كان بطور واحد هو الروتايل بينما كان بطورين هما ( الروتايل والاناتاس ) بطريقة الهايدروثيرمال اضافة الى ذلك فان حجم الجسيمات الناتجه بواسطة الهايدروثيرمال كان اصغر من حجم الجسيمات الناتجه بطريقة الليزر وكذلك الزمن المطلوب لاتمام التفاعل بطريقة الهايدروثيرمال يكون اطول من الزمن اللازم بطريقة الليزر.


Article
Enhanced Ultraviolet Photodetector Based on Mg-Doped ZnO Nanorods Films

Authors: Hussein Abdullah Hameed --- J. J. Hassan --- H. L. Saadon
Journal: Al-Mustansiriyah Journal of Science مجلة علوم المستنصرية ISSN: 1814635X Year: 2018 Volume: 29 Issue: 3 ICSSSA 2018 Conference Issue Pages: 158-167
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Magnesium-doped zinc oxide (ZnO: Mg) nanorods and nanotubes films were prepared by hydrothermal method deposited on glass substrates. X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), photoluminescence (PL), and optical absorption spectroscopy (UV) were performed to characterize the prepared films. X-ray diffraction analysis showed a decrease in the lattice parameters of Mg doped ZnO NRs. The Photoluminescence of the undoped and Mg-doped ZnO NRs displayed a near band edge. At 10 V bias, the metal-semiconductor-metal (MSM) ultraviolet (UV) photodetector performance of the Mg-doped ZnO prepared for various Mg concentrations of 0.0, 0.02, and 0.06 was investigated under radiation of 40μW/cm2 at the wavelengths of 365 and 385 nm UV light. The responsivity, detectivity and quantum efficiency of Mg-doped based on MSM detector were 0.118A/W, 1.0579*1012 and 40.05157 under UV of wavelength 365nm respectively.

تم تحضير اغشية أوكسيد الزنك النقي والمشوب بالمغنيسيوم بتراكيز مختلفة على قواعد زجاجية بالطريقة الحرارية المائية . تم اجراء فحوصات حيود الأشعة السينية (XRD) ، المسح المجهري الإلكتروني (SEM) ، (EDX) ، (PL) ، UV) لتوصيف واختبار الاغشية المحضرة. أظهرت تحليلات حيود الأشعة السينية(XRD) بان جميع النماذج متعددة البلورات ذات تركيب سداسي بالاتجاه (002). تم دراسة تأثير تشويب المغنيسيوم على الخصائص التركيبية والكهربائية والبصرية لأغشية اوكسيد الزنكZnO ، ولوحظ التحسن الواضح على التبلور وكذلك زيادة في فجوة الطاقة البصرية. عند تحيز 10 V ، تم فحص أداء كاشف (MSM) للزنك اوكسايد النقي والمشوب بالمغنيسيوم بتراكيز مختلفة من 0.0 و 0.02 و 0.06 تحت اشعة الفوق البنفسجية ذات شدة 40 μ واط / سم 2 عند أطوال موجية 365 و 385 نانومتر . كانت الاستجابة والكشفية والكفاءة الكمية لكاشف الزنك المشوب بالمغنيسيوم بتركيز ,0.06 A / W 0.118, *10121.0579 و 40.05157 عند الطول الموجي nm365 للأشعة الفوق البنفسجية على التوالي.


Article
Influence of Complexing Agents on Structural Properties of PbS Thin Films Prepared by CSD Method

Authors: Zoalfakar Almahmoud --- Ibrahim Alghoraibi
Journal: Iraqi Journal of Applied Physics المجلة العراقية للفيزياء التطبيقية ISSN: 18132065 23091673 Year: 2016 Volume: 12 Issue: 1 Pages: 23-26
Publisher: iraqi society for alternative and renewable energy sources and techniques الجمعية العراقية لمصادر وتقنيات الطاقة البديلة والمستجدة

Loading...
Loading...
Abstract

In this work, the influences of complexing agents and their molar concentrations on the structural properties of lead sulfide (PbS) nanostructures prepared by chemical solution deposition (CSD) method were studied. Other experimental parameters, such as concentration of reactants, pH of solution and bath temperature, were kept constant during deposition process. The structure of the prepared samples was analyzed by x-ray diffraction (XRD). It was found that the structural form of PbS nanorods is strongly influenced by the complexing agent and its molar concentration as an improvement in the structural quality was observed with changing the concentration of the complexing agent. However, too high concentration of complexing agent could lead to the degradation in the structural quality of the prepared samples.


Article
Influence of Complexing Agents on Structural Properties of PbS Thin Films Prepared by CSD Method
تأثير العوامل المعقدة على الخواص التركيبية لأغشية كبريتيد الرصاص الرقيقة المحضرة بطريقة ترسيب المحلول الكيمياوي

Authors: Zoalfakar Almahmoud --- Ibrahim Alghoraibi
Journal: Iraqi Journal of Applied Physics المجلة العراقية للفيزياء التطبيقية ISSN: 18132065 23091673 Year: 2017 Volume: 13 Issue: 1 Pages: 23-26
Publisher: iraqi society for alternative and renewable energy sources and techniques الجمعية العراقية لمصادر وتقنيات الطاقة البديلة والمستجدة

Loading...
Loading...
Abstract

In this work, the influences of complexing agents and their molar concentrations on the structural properties of lead sulfide (PbS) nanostructures prepared by chemical solution deposition (CSD) method were studied. Other experimental parameters, such as concentration of reactants, pH of solution and bath temperature, were kept constant during deposition process. The structure of the prepared samples was analyzed by x-ray diffraction (XRD). It was found that the structural form of PbS nanorods is strongly influenced by the complexing agent and its molar concentration as an improvement in the structural quality was observed with changing the concentration of the complexing agent. However, too high concentration of complexing agent could lead to the degradation in the structural quality of the prepared samples.


Article
Photocatalytic Characterization of TiO2 Nanorods and Nanotubes Synthesized by Sol Gel Template Method

Authors: Ban M. Al-Shabander --- Asma Sh. Khalil --- E. A. Al-Ajaj
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 2 Part (C) Pages: 153-158
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Titanium dioxide nanorods (TNR) and nanotubes (TNT) wereprepared by sol gel method using anodic aluminium oxide (AAO)membrane as template and calcined at 550°C. The structural of TiO2nanorods and nanotubes investigated by X-ray diffraction (XRD), thesurface topography and the morphology of the samples werecharacterized by atomic force microscopy (AFM), and scanning electronmicroscopy (SEM). The photocatalytic activity of the TiO2 nanostructureswere evaluated by the photodegradation of methyl orange (MO) solutionat different concentrations 10, 20 and 35 ppm under UV irradiation. Thecrystallinity and anatase phase of the TiO2 nanorods and nanotubes areconfirmed by XRD measurements. Average diameter size of TiO2nanorods and TiO2 nanotubes obtained from AFM histogram were 96.14,132.34 nm respectively. A high photocatalytic activity of TiOR2Rnanostructures were obtained at the three different concentrations underUV irradiation.

Listing 1 - 10 of 11 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (11)


Language

English (11)


Year
From To Submit

2018 (4)

2017 (1)

2016 (2)

2015 (2)

2013 (2)