Article
Mechanical properties of carrot fiber - epoxy composite
الخصائص الميكانيكية لمتراكبات الياف الجزر –ايبوكسي

Authors: Sewench N. Rafiq سه وينج نور الدين رفيق --- Wafaa A. Hussain وفاء عبد الخالق حسين
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2012 Volume: 9 Issue: 2 Pages: 335-340
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Interest has largely centered on the use of plant fibers to reinforce plastics, because these fibers are abundant and cheap. Carrot fibers (Curran) have been extracted from carrot, left over from carrot juice manufacture. The fibers of two sizes fine (50<µm) and coarse (100-150 µm) have been mixed with epoxy in four levels of loading (10, 20, 30, 40 wt %) respectively. Impact test, shore d hardness test and three point bending test of epoxy and carrot fiber-epoxy composites samples have been determined. The impact strength values of samples prepared with fine and coarse fibers increased as compared with pure epoxy sample. Hardness values increased, and the Young’s modulus values decreased with fiber content of both sizes.

هنالك اهتمام كبير باستخدام الياف النباتات لتقوية البلاستك, لان هذه الالياف متوفرة ورخيصة. تم استخراج الياف الجزر من الجزر المتبقي من عملية عصره. خلطت الالياف بحجمين(µm>50) و (µm 150-100) مع الايبوكسي باربعة نسب (10 , 20, 30, 40 نسبة وزنية %) على التوالي. تم قياس اختبار الصدمة واختبار الصلادة واختبار الانحناء الثلاثي النقط لنماذج الايبوكسي ومتراكبات الياف الجزر-ايبوكسي. زادت قيم مقاومة الصدمة للنماذج المحضرة بالالياف الناعمة والخشنة مقارنة مع نمودج الايبوكسي لوحده. هنالك زيادة في قيم الصلادة ونقصان في قيم معامل يونك مع زيادة نسبة الالياف لكلا الحجمين.


Article
Study On the Flexural and Impact Properties of Short Okra Natural Fiber Reinforced Epoxy Matrix Composites
دراسة خواصالانحناء والصدمة للمادة المركبة ذات الأساس من الایبوكسي المقواة بألیاف نبات البامیة

Authors: Aseel Mahmood Abdullah --- Ahmed Mudhafar Hashim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 10 Pages: 1696-1706
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The okra natural fiber reinforced epoxy matrix composites were prepared byhand-lay-up. The weight fractions of okra fiber are (1, 3, 6, 9, and 12% by weightwt). The flexural properties and impact resistance of composites were determinedby the flexural and impact tests. The maximum modulus of elasticity is (844.93MPa) at the weight fraction of (12 % wt) of okra fiber, comparison with (91.25MPa) for virgin epoxy material. The maximum impact energy is (0.75 J) at theweight fraction of I(12 % wt) of okra fiber, comparison with (0.05 J) for virginepoxy material.

في الدراسة الحالیة تم تحضیر المادة المركبة ذات الأساس من الایبوكسي المق واة بألی اف نب ات1) بطریق ة الص ب الی دوي ، وم ن ث م دراس ة , 3, 6, 9, 12 % wt) البامیة بكسور وزنیة مختلفةخواص الانحناء والصدمة لنماذج المادة المركبة. وقد بین ت النت ائج أن أعظ م ق یم لمعام ل الإنحن اء12 % )من ألیاف نبات البامیة مقارنةً wt) 844.93 ) وذلك للمادة المركبة المقواة ب MPa) كانت91.25 ) للایبوكسي غیر المقوى. أما بالنسبة لنتائج اختبار مقاومة الصدمة فقد كانت أعظم MP) ب12 % ) من ألیاف نبات البامیة wt) 0.75 ) وذلك للمادة المركبة المقواة ب J) قیمة للطاقة الممتصة0.05 ) للایبوكسي غیر المقوى. J) مقارنة بً


Article
Preparation and studying of some properties of polymer composites reinforced with natural and artificial fibers
تحضير ودراسة بعض الخواص لمتراكبات بوليمرية مسلحة بالياف طبيعية وصناعية

Authors: Awham M. Hameed أوهام محمد حميد --- Saad Ali Fouad سعد علي فؤاد
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2016 Volume: 14 Issue: 31 Pages: 138-147
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This work concerns the thermal and sound insulation as well as the mechanical properties of polymer matrix composite reinforced with glass fibers. These fibers may have dangerous effect during handling, for example the glass fibers might cause some damage to the eyes, lungs and even skin. For this reason the present work, investigates the behavior of polymer composite reinforced with natural fibers (Plant fibers) as replacement to glass fibers. Unsaturated Polyester resin was used as matrix material reinforced with two types of fibers, one of them is artificial (Glass fibers) and the other type is natural (Jute, Fronds Palm and Reed Fibers) by hand lay-up technique. All fibers are untreated with any chemical solvent. The Percentage of mixing was (90 wt. %) of the matrix while the weight fraction of each type of fibers was fixed (10 wt. %). The mechanical tests included impact and flexural strength tests. The results showed that the impact strength and flexural strength of the composites reinforced with Jute fibers is higher than that of Glass fibers and other natural fibers. The coefficients of thermal conductivity of the composites were measured by Lee's disc apparatus, the results show that the thermal insulation of the composite reinforced with jute fibers is higher than that of glass fibers and other natural fibers.The acoustic insulation of the composites reinforced with Jute fibers showed excellent result in insulation compared with glass fibers and other natural fibers.

أهتمت العديد من البحوث في دراسة الخواص العزل الحراري والصوتي و الخواص الميكانيكية لمتراكبات بوليمرية مسلحة بالياف الزجاج علما بأن هذه الالياف لها مضار عند التعامل معها فهي قد تضر بالعينين والرئتين وكذلك الجلد لذا ارتأينا اجراء دراسة خواص لمتراكبات البوليمر المقواة بألياف طبيعية (نباتية) كبدائل عن الياف الزجاج ومقارنة خواص كليهما وتحديد النتائج.استخدم راتنج البولي استر غير المشبع كمادة اساس وتم تسلسحه مع نوعين من الالياف, صناعية (الياف الزجاج) وطبيعية (الياف الجوت, وسعف النخيل, والياف القصب) جميع الالياف استخدمت بدون معاملة كيميائية, بواسطة تقنية الصب اليدوي. الكسر الوزني للرتنج كانت 90% نسبة وزنية بينما كان الكسر الوزني لجميع للأياف ثابت وهو 10% نسبة وزنية, الاختبارات الميكانيكية الي تم اجرائها هي اختبار الصدمة بطريقة جاربي واختبار مقاومة الكسر لحساب قيمة مقاومة الصدمة ومقاومة الكسر لهذه المتراكبات, النتائج اضهرت ان المتراكبات المسلحة بالياف الجوت (الطبيعية) لها مقاومة صدمة ومقاومة كسر اعلى من الياف الزجاج والاياف الطبيعية الاخرى. كذلك تم اجراء فحص التوصيلية الحرارية لهذه المتراكبات باستخدام جهاز(قرص لي) واوضحت نتائج اختبار التوصيلية الحرارية بأن العزل احراري للمتراكبات المسلحة بألياف الجوت اعلى من المتراكبات المسلحة بألياف الزجاج وكذلك اعلى من الالياف الطبيعية الاخرى, بينما نتائج فحص العزل الصوتي للمتراكبات المسلحة بألياف الجوت كانت ممتازة مقارنة بالمتراكبات المسلحة بالياف الزجاج وكذلك المتراكبات المسلحة بالاياف الطبيعيه الاخرى.


Article
Study Compression and Impact Properties of PMMA Reinforced by Natural Fibers Used in Denture

Authors: Jawad K. Oleiwi --- Sihama I. Salih --- Hwazen S. Fadhil
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 6 Part (A) Engineering Pages: 652-655
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The fracture in dentures prepared from acrylic resin occurs frequently during the accidental damage or service through heavy occlusal force [1]. Impact failures usually occur out of the mouth as a result of accidental dropping due to cleaning, coughing or sneezing or a sudden blow to the denture [2]. This paper is focused on the effect of natural fibers on the mechanical properties of PMMA by changing two parameters (content of fibers and length of fibers). Fibers were treated with alkaline solution to improve the interfacial adhesion. Composite specimens were prepared by using hand lay-up method. The results were showed that the increasing the weight fraction of both fibers lead to increase compression strength and decrease impact strength of composite specimens. While, increasing fiber length of both fibers lead to decrease compression strength and increase impact strength of the composite specimens. The largest value obtained for bamboo specimens at (2mm) fiber length and (9wt. %) and reach (530 MPa.). The main goal of this research is studying the impact and compression properties of PMMA reinforced by natural fibers (siwak and bamboo) by varying length and concentration of both kinds of fibers.