Article
SOME PROPERTIES OF FIBER REINFORCED NO FINE CONCRETE

Author: Hussam A. A. Rehman حسام الدين عبدالرحمن
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2012 Volume: 5 Issue: 4 Pages: 439-450
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

This work focus on studying the mechanical characteristics of polypropylene and carbon fiber reinforced no fine aggregate concrete, containing different percentages of fiber. This work was carried out using several tests. These tests were workability fresh and hardened density, compressive strength, splitting tensile strength and modulus of rupture. Tests were performed for specimens at ages of (7, 28) days. The test results indicated that the inclusion of fiber to the pervious concrete mixes did not affect the compressive strength significantly, while the splitting tensile strength and the modulus of rupture were improved significantly. Test results indicated that, the modulus of rupture of (5%) carbon fiber pervious concrete specimens are three times that of the control specimens, while the modulus of rupture of (5%) polypropylene fiber pervious concrete specimens are two times that of the control specimens. The percentage increase in tensile strength for polypropylene mixes containing fiber by volume fraction of (1%, 3%, 5%) were (93%, 101% and 129%) respectively and the percentage increase in tensile strength for carbon mixes containing fiber by volume fraction of (1%, 3%, 5%) were (170%, 177% and 220%) respectively.

إن هذا البحث يركز على دراسة الخواص الميكانيكية للخرسانة الخالية من الركام الناعم و المسلحة بألياف البولي بروبلين وألياف الكربون والتي تحتوي على نسب مختلفة من هذه الألياف. هذا البحث قد تم انجازه من خلال إجراء عدة فحوص وهذه الفحوص كانت كالأتي : قابلية التشغيل وكثافة الخرسانة المتصلبة ومقاومة الانضغاط ومقاومة شد الانشطار ومعامل الكسر وقد تم أجراء هذه الفحوص على النماذج بعمر معالجة (7 و 28) يوم . لقد بينت نتائج الفحوص إن إضافة الألياف إلى الخرسانة الخالية من الركام الناعم لم يوثر بشكل كبير على مقاومة الانضغاط بينما تحسنت كل من مقاومة شد الانشطار ومعامل الكسر بشكل ملحوظ. لقد أشرت النتائج لنسبة (5%) من الألياف (وهي أعلى نسبة) لكل من البولي بروبلين والكربون أن معامل الكسر قد ازداد بثلاث مرات في حالة ألياف الكربون ومرتين في حالة ألياف البولي بروبلين عن قيمة معمل الكسر في نماذج السيطرة. إن نسب الزيادة التي تمت ملاحظتها في مقاومة الشد في حالة ألياف البولي بروبلين لنسبة ألياف (1%, 3% و5%) كانت (93%, 101% و129%) على التوالي. أما بالنسبة للزيادة التي تمت ملاحظتها في مقاومة الشد في حالة ألياف الكربون لنسبة ألياف (1%, 3% و5%) كانت (93%, 101% و129%) على التوالي


Article
NO-FINE LIGHTWEIGHT AGGREGATE CONCRETE MODIFIED WITH STYRENE BUTADIENE RUBBER
الخرسانة الخالية من الركام الناعم المصنوعة من الركام خفيف الوزن والمطورة بالبوليمر

Authors: Ali T. Jasim --- Qusay A. Jabal
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2010 Volume: 1 Issue: 2 Pages: 33-44
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

No-fines concrete is a form of lightweight concrete obtained when fine aggregate is omitted. No-fine concrete mainly used for both load bearing and non-load bearing for external walls and partitions and in in-filling panels in framed structures. The essential objective of this work is to investigate the effect of incorporation of polymer (SBR) on the performance of no-fine concrete made from lightweight aggregate (porcelinite) and to suggest possible applications of this type of concrete. Three concrete mixes with different aggregate/cement ratios (A/C) (6:1, 8:1 and 10:1) by volume were selected. Each of these mixes included six mixes which differed in polymer/cement ratios, (0%, 5%, 10%, 15% and 20%) by weight to find the optimum polymer/cement ratio. Density, compressive strength, splitting tensile strength and drying shrinkage were conducted on all concrete mixes. The test results showed that the compressive strength of no-fine lightweight aggregate concrete increased with the increase in polymer/cement ratio up to 15%, and the compressive strength reduced at polymer /cement ratio of 20% . At polymer/cement ratio of 15%, the percentage of increase in compressive strength measured relative to reference mixes was about 50%. On the other hand, the splitting tensile strength was increased with the increase in polymer/cement ratio for all mixes. The percentage of increase in splitting tensile strength compared with reference mixes increased from about 30 to 90% with the increase of polymer/cement ratio from 5 to 20 %. Also the drying shrinkage strains of no-fine concrete decrease, with the increase in polymer/cement ratio. The percentages of decrease in drying shrinkage strain at 56 days were from 5 to 30% with the increase of polymer/cement ratio from 5 to 20%.

تعد الخرسانة الخالية من الركام الناعم احد أنواع الخرسانة خفيفة الوزن حيث يتم ا لحصول عليها بحذف الركام الناعم من الخرسانة الاعتيادية. . ان الهدف الرئيسي من هذا البحث هو دراسة تأثير إضافة احد أنواع البوليمر المعروف باسم ستايرين بيوتادين على اداء الخرسانة الخالية من الركام الناعم والمصنوعة أيضا من الركام خفيف الوزن ومن ثم اقتراح التطبيقات المناسبة لهذا النوع من الخرسانة. تم استعمال ثلاث خلطات خرسانية بنسب مختلفة من الركام/ الاسمنت (( 10:1, 8:1 , 6:1 وكل خلطة من هذه الخلطات تضمنت نسب مختلفة من البوليمر/ الاسمنت (5 ,10 ,15 , و20%). بعد المعالجة الرطبة تم إجراء فحوصات الكثافة الجافة, مقاومة الانضغاط, مقاومة الشد الانشطاري, وانكماش الجفاف. أظهرت النتائج بان مقاومة الانضغاط تزداد بزيادة نسبة البوليمر/ الاسمنت ولغاية نسبة 15% بعد هذه النسبة تبدأ بالانخفاض إن نسبة الزيادة في مقاومة الانضغاط عند نسبة البوليمر/ الاسمنت 15% كانت تقريبا 50%. من جانب أخر إن مقاومة الشد الانشطاري تزداد بزيادة نسبة البوليمر/ الاسمنت حيث تراوحت الزيادة من 30 إلى 90% عند زيادة نسبة البوليمر/ الاسمنت من 5 إلى 20% . أشارت النتائج أيضا إن قيم انكماش الجفاف تنخفض بزيادة نسبة البوليمر/ الاسمنت حيث لوحظ بان نسبة الانخفاض بعمر 56 يوم تراوحت من 5 إلى 30% عند زيادة نسبة البوليمر/ الاسمنت من 5 إلى 20%.


Article
Some Properties of No-Fines Concrete Produced by Using Demolished Concrete as Recycled Coarse Aggregate

Authors: Sh. A. Salih --- I.N. Gorgis --- W.F. Abd
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2017 Volume: 35 Issue: 7 Part (A) Engineering Pages: 741-748
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This paper investigate some mechanical properties of no-fines concrete produced by using demolished concrete as coarse aggregate after crushing to different sizes. Different no-fine mixes were considered using Portland cement type I with two types of coarse aggregates, crushed natural gravel and crushed demolished concrete were used with two ratios by weight (1:5 and 1:7) cement/aggregate. Single size and graded aggregate were used with a maximum size of 20 mm. W /C ratio was kept as 0.4 for all mixes and supper plasticizer was used to keep the same flow and compaction factor value for all mixes . Using demolished concrete as coarse aggregate in no fine concrete led to decrease in the workability. As a comparison with natural coarse aggregate mixes, the average percentages of decreases for the flow, compaction factor and the fresh density were 2%, 2.3% and 6.4%, respectively. As well as the test results indicated that the compressive strength, splitting tensile strength, flexural strength and oven dry density for no fine made with crushed demolished concrete at age 28 days were decreased by about 29%, 22 %, 21% and 4% respectively as compared with no fine made by natural crushed aggregate.


Article
The Ultimate Strength Of Double Short Composite Columns Under Concentric Loads
المقاومة القصوى للأعمدة القصيرة المركبة المزدوجة تحت تأثير الأحمال المركزية

Author: Ragheed Fatehi Makki رغيد فتحي مكي
Journal: Muthanna Journal of Engineering and Technology(MJET) مجلة المثنى للهندسة والتكنولوجيا ISSN: 25720317 25720325 Year: 2014 Volume: 3 Issue: 1 Pages: 11-24
Publisher: Al-Muthanna University جامعة المثنى

Loading...
Loading...
Abstract

No-Fine concrete filled double steel tube columns (CFDST) are being increasingly used for structural applications. It has been used for submerged tube tunnels, nuclear containment, liquid and gas retaining structures, vessels under external pressure in very deep water and for compression members in offshore construction, this is due to the aesthetic appearance, ease of maintenance and simple of construction. The (CFDST) columns also have excellent resistance to seismic loads and fire. This paper comprises of an experimental study on the structural behavior of double steel tubular columns filled with No-Fine concrete under axial load. Eight samples of double steel circular tubes with different diameters for the inner and outer tubes are used, with different slenderness ratios (L/r), different ultimate strengths of No-Fine concrete . Also two cases are study for (CFDST) samples first with hollow inner tube and second with completely filled inner and outer tubes with No-Fine concrete.The experimental results show that the effect of height (the slenderness (L/r) ratio) on the ultimate strength of CFDST columns will have a reverse relation. While the effect of uniaxial compressive strength and the effect of fully filling the core of internal tube on the ultimate strength of CFDST columns will have an increase relation.

إن الخرسانة المنتجة بدون استعمال الركام الناعم (الرمل) المالئة للأعمدة الحديدية الأنبوبية المزدوجة أصبحت تستعمل وبصورة متزايدة في التطبيقات الإنشائية مثل القنوات الأنبوبية الغاطسة والمنشات النووية وأحواض الخزن الخاصة بالسوائل والغازات المتعرضة الى ضغوط خارجية وبأعماق كبيرة أسفل البحر وكذلك تستعمل في أعضاء الانضغاط (الأعمدة) في المنشات الساحلية، ان السبب في ذلك يعود الى جمالية مظهرها وسهولة صيانتها وبساطة تصنيعها. وبالإضافة الى ذلك فان الأعمدة الحديدية الأنبوبية المزدوجة تمتلك مقاومة إنشائية ممتازة للزلازل والحرائق. ان هذا البحث يتضمن دراسة عملية للتصرف الإنشائي للأعمدة الحديدية الأنبوبية المملوءة بالخرسانة المنتجة بدون استعمال الركام الناعم تحت تأثير الأحمال المحورية، ثمانية نماذج للأعمدة الحديدية المزدوجة الدائرية المختلفة الأقطار (داخليا وخارجيا) تمت دراستها تحت تأثير نسب نحافة متغيرة و مقاومة قصوى للخرسانة متغيرة، وكذلك تمت دراسة حالتين لهذه الأعمدة الأولى بكون العمود الداخلي خالي من الخرسانة و الحالة الثانية بكون العمود الداخلي والخارجي مملوء كليا بالخرسانة. لقد بينت النتائج ان تاثير تغير طول العمود (نسبة النحافة) يكون عكسيا على مقدار المقاومة القصوى لهذه الاعمدة بينما يكون تاثير تغير قيمة مقاومة الخرسانة القصوى وتغير ملئ اللب للعمود الداخلي طرديا.


Article
The Effect of Coarse Aggregate Ratio on the Properties of No Fine Light Weight Concrete
تاثير نسبة الركام الخشن على خواص الخرسانة الخالية من الركام الناعم

Authors: Luma Abdul. Ghani. Zghair --- Hind.H. HAMAD
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2009 Volume: 15 Issue: 4 Pages: 4447 -4462
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The main object of this work is to study the effect of coarse aggregate/cement ratio (A/C) on the property of no fine concrete. In this work, three ratio of A/C were used (6, 9 and 12 by weight).The cement content is maintained constant (125kg/m3) while the w/c ratio ranges from (0.39 to 0.55 by weight). Tests are carried out on hardened concrete to investigate the effect of coarse aggregate/cement ratio on the compressive strength, absorption%, density, porosity%, ultrasonic pulse velocity, acoustic impedance of mixes.The results showed that increasing the percentage of A/C ratio by weight from 6 to 12 for the used mixes reduces the compressive strength, ultrasonic pulse velocity and acoustic impedance, on the other hand the porosity and the absorption percentage, increase with increasing ratio of A/C for all studied mixes.At 28 days the compressive strength , ultrasonic pulse velocity and acoustic impedance tests with A/C ratio of (12) are (2.8.MPa), (2km/sec) and (3×106 Kg/(sec.m2)) respectively while decreasing the ratio to (6) improves these properties to (9.3MPa), (3km/sec) and ( 5.7 ×106 Kg/(sec.m2)) respectively On the other hand the porosity and the absorption % decrease with decreasing the ratio of A/C for all studied mixes . At 28 days the porosity and the absorption % with A/C ratio of (12) are (40%) and (2.7%) respectively with decreasing the ratio to 6 decrease these properties to (19%) and (1%) respectively. The densities of the mixes were tested. At 28 days the density with A/C ratio of (12) are (1512 kg/m3 )with decreasing the ratio to 6 increase the density to(1907 kg/m3 ) Based on the analysis of experimental results, several graphs and tables have been prepared to study the properties of no fine concrete.

الهدف الأساسي لهذا العمل هو دراسة تاثيرنسبة الركام الخشن/ السمنت ( A/C ) على خواص الخرسانة الخالية من الركام الناعم . تم استخدام ثلاثة نسب وزنية من (6,9و12) ، (A/C) محتوى السمنت ثابتاً( 125 كغم/م3) بينما نسبة الماء / السمنت تتراوح بين ( 0.39 الى 0.55) اختير اجراءالفحوصات على الخرسانة المتصلبة لدراسة تاثيرنسبة الركام الخشن/ السمنت على مقاومة الانضغاط ، نسبة الامتصاص ، الكثافة ، المسامية ، فحص الموجات الصوتية و فحص المعاوقة الصوتية .النتائج اظهرت ان زيادة نسبة ( A/C ) من 6 الى 12وزنيا" ادى الى نقصان في مقاومة الانضغاط ، فحص الموجات الصوتية و فحص المعاوقة الصوتية من الناحية الاخرى المسامية و نسبة الامتصاص قد ازدادت عند زيادة نسبة ( A/C ) للخلطات الخرسانية.في عمر 28 يوم مقاومة الانضغاط ، فحص الموجات الصوتية و فحص المعاوقة الصوتية عند نسبة (A/C ) (12) كانت(2.8 ميكاباسكال)،(2كم/ثا) و 3 ×6^10 (كغم/(ثا . م2 ) ) على التوالي بينما نقصان النسبة الى( 6) ادى الى تحسين الخواص السابقة (9.3 ميكاباسكال)، ( 3كم/ثا) و( 5.7 ×6^10 )كغم/(ثا . م2 ) ) على التوالي و من الجانب الاخر المسامية و نسبة الامتصاص قلت مع تقليل نسبة ( A/C ) للخلطات الخرسانية.في عمر 28 يوم المسامية و نسبة الامتصاص عند نسبة ( A/C ) (12) كانت(40%) و 2.7%) (على التوالي بينما نقصان النسبة الى( 6) ادى الى تقليل تلك الخواص الى (19%) و(1%) .تم فحص الكثافة للخلطات الخرسانية في عمر 28 يوم عند نسبة (A/C ) (12) وكانت ( 1512 كغ/م3) بينما نقصان النسبة الى( 6) ادى الى زيادة في الكثافة الى (1907كغ/م3)، اعتمادا على تحليل النتائج مختبريا ، بضع رسومات و جداول اعدت لدراسة خواص الخرسانة الخالية من الركام الناعم.

Listing 1 - 5 of 5
Sort by
Narrow your search

Resource type

article (5)


Language

English (5)


Year
From To Submit

2017 (1)

2014 (1)

2012 (1)

2010 (1)

2009 (1)